Resumo:
Te-rich Si15Te85-xGex (1 <= x <= 11) glasses are found to exhibit an anomalous phase separations with germanium composition. The structural transformation of o-GeTe crystalline phase from o-GeTe with a = 11.76 angstrom, b = 16.59 angstrom, c = 17.44 angstrom, to high pressure o-GeTe with a new reduced lattice parameters a = 10.95 angstrom, b = 4.03 angstrom, c = 4.45 angstrom, is observed at T-c3 in the composition range 6 <= x <= 11. Raman studies support the possible existence of high pressure o-GeTe phase which is observed in X-ray diffraction experiments. Copyright 2012 Author(s). This article is distributed under a Creative Commons Attribution 3.0 Unported License. http://dx.doi.org/10.1063/1.3696862]
Resumo:
The effect of growth texture on the magnetostriction of ternary Tb0.3Dy0.7Fe1.95 was studied by conducting unidirectional solidification experiments using a zoning set-up. Detailed texture evolutions were studied using X-ray diffraction on samples obtained by varying growth rates from 18 to 72 cm/h, under a temperature gradient of 100 degrees C/cm. The estimated texture co-efficient and pole figures of the samples indicate that during the onset of the solidification, < 110 > and < 331 >/'rotated < 110 >' texture components nucleate and grow in all the samples. However, as the solidification progresses, < 112 > texture component becomes dominant at higher growth rate. This results in an improvement of magnetostriction from 1000 to 1300 microstrains for samples grown at growth rates of 18 and 72 cm/h respectively. The transition of preferred growth direction occurs through intermediate orientations < 123 >. An attempt has been made in this paper to explain the occurrence of different growth texture by considering the stability of growing interface, its planar packing fraction and atomic stacking sequence of several low index planes. (C) 2010 Elsevier Ltd. All rights reserved.
Resumo:
Irradiation of 4-aryl-4-alkylhex-5-en-2-ones (e.g. 1a) or 5-aryl-4-alkylhex-5-en-2-ones (e.g. 2a) adsorbed on montmorillonite K-10 in a commercial microwave oven furnishes the multialkylated naphthalenes (e.g. 3).
Resumo:
The effect of Tb/Dy ratio on the structural and magnetic properties of (Tb,Dy)Fe-2 class of alloys has been investigated using nine alloys of TbxDy1-xFe1.95 (x = 0-1) covering the entire range. Our results indicate that the three phases viz. (Tb,Dy)Fe-2 (major phase), (Tb,Dy)Fe-3 and(Tb,Dy)-solid solution (minor phases) coexist in all the alloys. The volume fraction of pro-peritectic (Tb,Dy)Fe-3 phase however, has a minimum at x = 0.4 and a maximum at x = 0.6 compositions. The volume fraction of this phase decreases upon heat treatment at 850 degrees C and 1000 degrees C. A Widmanstatten type precipitate of (Tb,Dy)Fe-3 was observed for Dy-rich compositions (0 <= x <= 0.5). The microstructural investigations indicate that the ternary phase equilibria of Tb-Dy-Fe are sensitive to Tb/Dy ratio including the expansion of (Tb,Dy)Fe-2 phase field which is in contrast to the pseudo-binary assumption that is followed in available literature to date. The lattice parameter, Curie temperature and coercivity are found to increase with Tb addition. Split of (440) peak of (Tb,Dy)Fe-2 observed in x >= 0.3 alloys indicate, a spin reorientation transition from 100] to 111] occurs with Tb addition. (C) 2012 Elsevier B. V. All rights reserved.
Resumo:
The frequency-dependent dielectric relaxation of Pb0.94Sr0.06](Mn1/3Sb2/3)(0.05)(Zr0.52Ti0.48)(0.95)]O-3 ceramics, synthesized in pure perovskite phase by a solid-state reaction technique is investigated in the temperature range from 303 to 773 K by alternating-current impedance spectroscopy. Using Cole-Cole model, an analysis of the imaginary part of the dielectric permittivity with frequency is performed assuming a distribution of relaxation times. The scaling behavior of the imaginary part of the electric modulus suggests that the relaxation describes the same mechanism at various temperatures. The variation of dielectric constant with temperature is explained considering the space-charge polarization. The SEM indicates that the sample has single phase with an average grain size similar to 14.2 mu m. The material exhibits tetragonal structure. A detailed temperature dependent dielectric study at various frequencies has also been performed. (C) 2013 Elsevier B.V. All rights reserved.
Structural refinement, optical and electrical properties of Ba1-x Sm-2x/3](Zr0.05Ti0.95)O-3 ceramics
Resumo:
Samarium doped barium zirconate titanate ceramics with general formula Ba1-x Sm-2x/3](Zr0.05Ti0.95)O-3 x = 0, 0.01, 0.02, and 0.03] were prepared by high energy ball milling method. X-ray diffraction patterns and micro-Raman spectroscopy confirmed that these ceramics have a single phase with a tetragonal structure. Rietveld refinement data were employed to model BaO12], SmO12], ZrO6], and TiO6] clusters in the lattice. Scanning electron microscopy shows a reduction in average grain size with the increase of Sm3+ ions into lattice. Temperature-dependent dielectric studies indicate a ferroelectric phase transition and the transition temperature decreases with an increase in Sm3+ ion content. The nature of the transition was investigated by the Curie-Weiss law and it is observed that the diffusivity increases with Sm3+ ion content. The ferroelectric hysteresis loop illustrates that the remnant polarization and coercive field increase with an increase in Sm3+ ions content. Optical properties of the ceramics were studied using ultraviolet-visible diffuse reflectance spectroscopy.
Resumo:
Tb0.3Dy0.7Fe1.95 alloy was directionally solidified by using a modified Bridgman technique at a wide range of growth rates of 5 to 100 cm/h. The directionally grown samples exhibited plane front solidification morphology up to a growth rate of 90 cm/h. Typical island banding feature was observed closer to the chilled end, which eventually gave rise to irregular peritectic coupled growth (PCG). The PCG gained prominence with an increase in the growth rate. The texture study revealed formation of strong aOE (c) 311 > texture in a lower growth rate regime, aOE (c) 110 > and ``rotated aOE (c) 110 > aEuroe in an intermediate growth regime, and aOE (c) 112 > in a higher growth rate regime. In-depth analysis of the atomic configuration of a solid-liquid interface revealed that the growth texture is influenced by the kinetics of atomic attachment to the solid-liquid interface, which is intimately related to a planar packing fraction and an atomic stacking sequence of the interfacial plane. The mechanism proposed in this article is novel and will be useful in addressing the orientation selection mechanism of topologically closed packed intermetallic systems. The samples grown at a higher growth rate exhibit larger magnetostriction (lambda) and d lambda/dH owing to the absence of pro-peritectic (Tb,Dy)Fe-3 and formation of aOE (c) 112 > texture, which lies closer to the easy magnetization direction (EMD).