Orientation dependence of the indentation impression morphology in a Mg alloy

The formation of anomalous indentations, with two opposite faces describing a pin-cushion effect and the other two faces normal, in long elongated grains of an extruded Mg-2Al-1Zn alloy is reported. Subsurface microstructural observations combined with Schmid factor calculations suggest that extension twinning accompanied by basal slip are the reasons for these. Johnson's expanding cavity model is invoked for further substantiation. (C) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Enhancement of fatigue life of Ni-Ti-Fe shape memory alloys by thermal cycling

The effect of thermal cycling on the load-controlled tension-tension fatigue behavior of a Ni-Ti-Fe shape memory alloy (SMA) at room temperature was studied. Considerable strain accumulation was observed to occur in this alloy under both quasi-static and cyclic loading conditions. Though, in all cases, steady-state is reached within the first 50-100 cycles, the accumulated steady-state strain, epsilon(p.ss), is much smaller in thermally cycled alloy. As a result, the fatigue performance of them was found to be significantly enhanced vis-a-vis the as-solutionized alloy. Furthermore, under load-controlled conditions, the fatigue life of Ni-Ti-Fe alloys was found to be exclusively dependent on epsilon(p.ss). Observations made by profilometry and differential scanning calorimetry (DSC) indicate that the 200-500% enhancement in fatigue life of thermally cycled alloy is due to the homogeneous distribution of the accumulated fatigue strain. (C) 2010 Elsevier B.V. All rights reserved.

Fatigue in Ti-6Al-4V-B alloys

The addition of small amounts of B to Ti-6Al-4V alloy reduces the as-cast grain size by an order of magnitude and introduces TiB phase into the microstructure. The effects of these microstructural modifications on both the high cycle fatigue and cyclic stress-strain response were investigated. Experimental results show that B addition markedly enhances the fatigue strength of the alloy; however, the influence of prior-beta grain size was found to be only marginal. The presence of TiB particles in the matrix appears to be beneficial with the addition of 0.55 wt.% B to Ti-6Al-4V enhancing the fatigue strength by more than 50%. Strain-controlled fatigue experiments reveal softening in the cyclic stress-strain response, which increases with the B content in the alloy. Transmission electron microscopy of the fatigued specimens indicates that generation of dislocations during cyclic loading and creation of twins due to strain incompatibility between the matrix and the TiB phase are possible reasons for the observed softening. (c) 2010 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

A2MoTiO7−x (Atriple bond; length as m-dashrare earth or Y): a new series of oxide pyrochlores prepared by topochemical reduction of A2MoTiO8 scheelites

A series of anion-deficient pyrochlore oxides of the formula A2MoTiO7−x (xless-than-or-equals, slant0.5), where Atriple bond; length as m-dashSm, Gd, Tb, Dy, Ho, Er, Lu and Y, has been prepared by reduction of A2MoTiO8 scheelites. The scheelite-to-pyrochlore conversion is reversible, indicating that the reaction is likely to be topochemical. The oxidation states of molybdenum and titanium are most probably Mo(III) and Ti(IV) for the limiting composition of the pyrochlores A2MoTiO6.5. The new pyrochlores are non-metallic and paramagnetic as expected.

Analysis of the Gd 4d-XY Auger spectrum using synchrotron radiation

We report the 4d-XY (X, Y = 5p, 4f, and the conduction band) Auger spectra of clean Gd using a monochromatic photon source with energies above and below the 3d threshold. The spectra with higher hv show the existence of intense spectator-hole Auger transitions. Comparison of these spectra with those obtained with a primary electron source allows detailed interpretation of the various features and explains the unusual spin polarization of the electron-induced spectrum reported earlier.

Crystallization studies on amorphous AI-Y-Ni and AI-Y-Cu alloys

AI83Y10Ni7, AI80Y10Ni10 and AI80Y10Cu10 alloys were studied by the rapid solidification processing route. The glass-forming ability was found to decrease in the order of alloys mentioned above. Differential scanning calorimetry (DSC) of these amorphous alloys showed that the amorphous phase in AI-Y-Ni alloys has a higher thermal stability when compared to that in AI-Y-Cu alloys. A four-stage crystallization sequence could be identified for the AI-Y-Ni amorphous alloys. Even though the AI80Y10Cu10 alloy showed four exothermic peaks in the DSC study, a definite crystallization sequence could not be arrived at due to the coexistence of many crystalline phases along with the amorphous phase in the melt-spun condition.

Electron-beam weld microstructures and properties of aluminium-lithium alloy 8090

Lithium-containing aluminium alloys are of considerable current interest in the aerospace and aircraft industries because lithium additions to aluminium improve the modulus and decrease the density compared to conventional aluminium alloys. Few commercial aluminium-lithium alloys have emerged for use in the aerospace industry. One such candidate is 8090, a precipitation-hardenable Al-Li-Cu-Mg alloy. The influence of electron-beam welding on the microstructure and mechanical properties of alloy 8090 material has been evaluated through microscopical observations and mechanical tests. Microscopic observations of the electronbeam welds revealed an absence of microporosity and hot cracking, but revealed presence of microporosity in the transverse section of the weld. Mechanical tests revealed the electronbeam weld to have lower strength, elongation and joint efficiency. A change in microscopic fracture mode was observed for the welded material when compared to the unwelded counterpart. An attempt is made to rationalize the behaviour in terms of competing mechanistic effects involving the grain structure of the material, the role of matrix deformation characteristics, grain-boundary chemistry and grain-boundary failure.

Magnetoresistance of FexNi80-xCr20 (50alloys

The authors have measured longitudinal and transverse magnetoresistance (MR) of crystalline pseudo-binary alloys FexNi80-xCr20 (50alloys have compositions close to the critical composition regime for ferromagnetism. While the Fe-Ni-Cr alloys have a FCC gamma -phase, the binary Fe-Cr alloy has a BCC alpha -phase. This gives an opportunity to compare magnetoresistances for gamma -phase and alpha -phase Fe alloys when they lie close to the critical composition. The experiments were conducted at 4.2 K with magnetic fields up to 7 T. The authors observed that all the alloys show negative magnetoresistance at 4.2 K in fields up to 7 T. However, for the gamma -phase alloys the typical maximum MR ( Delta rho / rho ) is about 1%, while for the alpha -phase alloy it is 10%. In the gamma -phase alloys there is a small but finite anisotropy of MR in the phases with long-range magnetic order which gradually vanishes near the critical region (x=xc approximately=59-63) when it becomes a spin glass. In the range x approximately=xc, Delta rho / rho varies as Mn (M=magnetization) with n approximately=2.

Phase Relations in the System Cu-Gd-O and Gibbs Energy of Formation of CuGd204

The phase relations in the system Cu-Gd-O have been determined at 1273 K by X-ray diffrac- tion, optical microscopy, and electron microprobe analysis of samples equilibrated in quartz ampules and in pure oxygen. Only one ternary compound, CuGd2O4, was found to be stable. The Gibbs free energy of formation of this compound has been measured using the solid-state cell Pt, Cu2O + CuGd2O4 + Gd2O3 // (Y2O3) ZrO2 // CuO + Cu2O, Pt in the temperature range of 900 to 1350 K. For the formation of CuGd2O4 from its binary component oxides, CuO (s) + Gd2O3 (s) → CuGd2O4 (s) ΔG° = 8230 - 11.2T (±50) J mol-1 Since the formation is endothermic, CuGd2O4 becomes thermodynamically unstable with respect to CuO and Gd2O3 below 735 K. When the oxygen partial pressure over CuGd2O4 is lowered, it decomposes according to the reaction 4CuGd2O4 (s) → 4Gd2O3 (s) + 2Cu2O (s) + O2 (g) for which the equilibrium oxygen potential is given by Δμo 2 = −227,970 + 143.2T (±500) J mol−1 An oxygen potential diagram for the system Cu-Gd-O at 1273 K is presented.