Microstructure and compression behavior of chip consolidated magnesium

Chips produced by turning a commercial purity magnesium billet were cold compacted and then hot extruded at four different temperatures: 250, 300, 350, and 400 degrees C. Cast billets, of identical composition, were also extruded as reference material. Chip boundaries, visible even after 49: 1 extrusion at 400 degrees C, were observed to suppress grain coarsening. Although 250 degrees C extruded chip-consolidated product showed early onset of yielding and lower ductility, fully dense material (extruded at 400 degrees C) had nearly 40% reduction in grain size with 22% higher yield strength and comparable ductility as that of the reference. The study highlights the role of densification and grain refinement on the compression behavior of chip consolidated specimens.

Nitrates-melt synthesized LiNi0.8Co0.2O2 and its performance as cathode in Li-ion cells

Layered LiNi0.8Co0.2O2 crystallizing in R (3) over barm space group is synthesized by decomposing the constituent metal-nitrate precursors. Oxidizing nature of metal nitrates stabilizes nickel in +3 oxidation state, enabling a high degree of cation ordering in the layered LiNi0.8Co0.2O2. The powder sample characterized by XRD Rietveld refinement reveals <2% Li-Ni site exchange in the layers. Scanning electron microscopic studies on the as-synthesized LiNi0.8Co0.2O2 sample reflect well defined particles of cubic morphology with particle size ranging between 200 and 250 nm. Cyclic voltammograms suggest that LiNi0.8Co0.2O2 undergoes phase transformation on first charge with resultant phase being completely reversible in subsequent cycles. The first-charge-cycle phase transition is further supported by impedance spectroscopy that shows substantial reduction in resistance during initial de-intercalation. Galvanostatic charge-discharge cycles reflect a first-discharge capacity of 184 mAh g(-1) which is stabilized at 170 mAh g(-1) over 50 cycles.

Anaerobic retting of banana and arecanut wastes in a plug flow digester for recovery of fiber, biogas and compost

Leaves and leaf sheath of banana and areca husk (Areca catechu) constitute an important component of urban solid waste (USW) in India which are difficult to degrade under normal windrow composting conditions. A successful method of anaerobic digestion built around the fermentation properties of these feedstock has been evolved which uses no moving parts, pretreatment or energy input while enabling recovery of four products: fiber, biogas, compost and pest repellent. An SRT of 27 d and 35 d was found to be optimum for fiber recovery for banana leaf and areca husk, respectively. Banana leaf showed a degradation pattern different from other leaves with slow pectin-1 degradation (80%) and 40% lignin removal in 27 d SRT. Areca husk however, showed a degradation pattern similar to other plant biomass. Mass recovery levels for banana leaf were fiber-20%, biogas-70% (400 ml/g TS) and compost-10%. For areca husk recovery was fiber-50%, biogas-45% (250 ml/g TS) and compost-5%. (C) 2012 Elsevier Inc. All rights reserved.

Vanadium pentoxide nanobelts: One pot synthesis and its lithium storage behavior

In this paper, we report a synthesis, characterization and electrochemical properties of V2O5 nanobelts. V2O5 nanobelts have been prepared via hydrothermal treatment of commercial V2O5 in acidic (HCl/H2SO4) medium at relatively low temperature (160 degrees C). The hydrothermally derived products have been characterized by powder X-ray diffraction (XRD), Fourier transform infrared spectroscopy (FT-IR), Raman spectroscopy, X-ray photo electron spectroscopy (XPS), UV-Vis spectroscopy, Scanning/Transmission electron microscopy (SEM/TEM). XRD pattern of V2O5 nanobelts show an orthorhombic phase. From the FTIR spectrum, the peak observed at 1018 cm-1 is characteristic of the stretching vibration mode of the terminal vanadyl, V = O. The UV-Vis absorption spectrum of V2O5 nanobelts show maximum absorbance at 430 nm, which was blue-shifted compared to that of bulk V2O5. TEM micrographs reveal that the products consist of nanobelts of 40-200 nm in thickness and several tens of micrometers in length. The electrochemical analysis shows an initial discharge capacity of 360 mAh g-1 and its almost stabilized capacity is reached to 250 mAh g-1 after 55 cycles. A probable reaction mechanism for the formation of orthorhombic V2O5 nanobelts is proposed.

Increased time-dependent room temperature plasticity in metallic glass nanopillars and its size-dependency

Room temperature, uniaxial compression creep experiments were performed on micro-/nano-sized pillars (having diameters in the range of 250-2000 nm) of a Zr-based bulk metallic glass (BMG) to investigate the influence of sample size on the time-dependent plastic deformation behavior in amorphous alloys. Experimental results reveal that plastic deformation indeed occurs at ambient temperature and at stresses that are well below the nominal quasi-static yield stress. At a given stress, higher total strains accrue in the smaller specimens. In all cases, plastic deformation was found to be devoid of shear bands, i.e., it occurs in homogeneous manner. The stress exponent obtained from the slope of the linear relation between strain rate and applied stress also shows a strong size effect, which is rationalized in terms of the amount of free volume created during deformation and the surface-to-volume ratio of the pillar. (C) 2012 Elsevier Ltd. All rights reserved.

Phonon anomalies and structural transition in spin ice Dy2Ti2O7: a simultaneous pressure-dependent and temperature-dependent Raman study

We revisit the assignment of Raman phonons of rare-earth titanates by performing Raman measurements on single crystals of O18 isotope-rich spin ice Dy2Ti2O718 and nonmagnetic Lu2Ti2O718 pyrochlores and compare the results with their O16 counterparts. We show that the low-wavenumber Raman modes below 250 cm-1 are not due to oxygen vibrations. A mode near 200 cm-1, commonly assigned as F2g phonon, which shows highly anomalous temperature dependence, is now assigned to a disorder-induced Raman active mode involving Ti4+ vibrations. Moreover, we address here the origin of the new Raman mode, observed below TC similar to 110 K in Dy2Ti2O7, through a simultaneous pressure-dependent and temperature-dependent Raman study. Our study confirms the new mode to be a phonon mode. We find that dTC/dP = + 5.9 K/GPa. Temperature dependence of other phonons has also been studied at various pressures up to similar to 8 GPa. We find that pressure suppresses the anomalous temperature dependence. The role of the inherent vacant sites present in the pyrochlore structure in the anomalous temperature dependence is also discussed. Copyright (c) 2012 John Wiley & Sons, Ltd.

Bond Graph Modeling for Energy-Harvesting Wireless Sensor Networks

Researchers can use bond graph modeling, a tool that takes into account the energy conservation principle, to accurately assess the dynamic behavior of wireless sensor networks on a continuous basis.

Spherical and rod-like Gd2O3:Eu3+ nanophosphors-Structural and luminescent properties

A comparative study of spherical and rod-like nanocrystalline GdO:Eu (GdEuO) red phosphors prepared by solution combustion and hydrothermal methods have been reported. Powder X-ray diffraction (PXRD) results confirm the as-formed product in combustion method showing mixed phase of monoclinic and cubic of GdO:Eu. Upon calcinations at 800C for 3 h, dominant cubic phase was achieved. The as-formed precursor hydrothermal product shows hexagonal Gd(OH):Eu phase and it converts to pure cubic phase of GdO:Eu on calcination at 600C for 3 h. TEM micrographs of hydrothermally prepared cubic GdO:Eu phase shows nanorods with a diameter of 15 nm and length varying from 50 to 150 nm, whereas combustion product shows the particles to be of irregular shape, with different sizes in the range 50-250 nm. Dominant red emission (612 nm) was observed in cubic GdO:Eu which has been assigned to transition. However, in hexagonal Gd(OH):Eu, emission peaks at 614 and 621 nm were observed. The strong red emission of cubic GdO:Eu nanophosphors by hydrothermal method are promising for high performance display materials. The variation in optical energy bandgap () was noticed in as-formed and heat treated systems in both the techniques. This is due to more ordered structure in heat treated samples and reduction in structural defects.

Nonstoichiometry, defects and thermodynamic properties of YFeO3, YFe2O4 and Y3Fe5O12

Oxygen nonstoichiometry of three ternary oxides. YFeO3-delta, YFe2O4-alpha and Y3Fe5O12-theta. in the system Y-Fe-O was investigated as a function of oxygen partial pressure by thermogravimetry at high temperature. The defects responsible for nonstoichiometry were identified as oxygen vacancies for YFeO3-delta and YFe2O4-alpha although the manner of variation of nonstoichiometric parameter with oxygen partial pressure for these two oxides is quite different. Cation interstitials are the predominant defects in Y3Fe5O12-theta. Gibbs energies of formation of the three nonstoichiometric oxides were determined using solid-state electrochemical cells in the temperature range from 975 to 1475 K. YFe2O4-alpha was found to be stable only above 1391 K. Gibbs energies of formation of the three stoichiometric compounds from their component binary oxides were obtained by combining information from solid state cells with results of thermogravimetric analysis using the Gibbs-Duhem relation. The results can be summarized as: (1/2)Y2O3 + (1/2)Fe2O3 -> YFeO3;Delta G(f(ox))(O)(+/- 250)(J/mol) = 17, 126-8.263T (1/2)Y2O3 + FeO + (1/2)Fe2O3 -> YFe2O4;Delta G(f(ox))(O)(+/- 260)(J/mol) = -10,352-13.24T (3/2)Y2O3 + (5/2)Fe2O3 -> Y3Fe5O12;Delta G(f(ox))(O)(+/- 780)(J/mol) = -56, 647-31.091T. (C) 2012 Elsevier B.V. All rights reserved.

Development of micro-shock wave assisted dry particle and fluid jet delivery system

Small quantity of energetic material coated on the inner wall of a polymer tube is proposed as a new method to generate micro-shock waves in the laboratory. These micro-shock waves have been harnessed to develop a novel method of delivering dry particle and liquid jet into the target. We have generated micro-shock waves with the help of reactive explosive compound high melting explosive (octahydro-1,3,5,7-tetranitro-1,3,5,7-tetrazocine) and traces of aluminium] coated polymer tube, utilising 9 J of energy. The detonation process is initiated electrically from one end of the tube, while the micro-shock wave followed by the products of detonation escape from the open end of the polymer tube. The energy available at the open end of the polymer tube is used to accelerate tungsten micro-particles coated on the other side of the diaphragm or force a liquid jet out of a small cavity filled with the liquid. The micro-particles deposited on a thin metal diaphragm (typically 100-mu m thick) were accelerated to high velocity using micro-shock waves to penetrate the target. Tungsten particles of 0.7 mu m diameter have been successfully delivered into agarose gel targets of various strengths (0.6-1.0 %). The device has been tested by delivering micro-particles into potato tuber and Arachis hypogaea Linnaeus (ground nut) stem tissue. Along similar lines, liquid jets of diameter 200-250 mu m (methylene blue, water and oils) have been successfully delivered into agarose gel targets of various strengths. Successful vaccination against murine salmonellosis was demonstrated as a biological application of this device. The penetration depths achieved in the experimental targets are very encouraging to develop a future device for biological and biomedical applications.

Performances of single and two-stage pulse tube cryocoolers under different vacuum levels with and without thermal radiation shields

Single and two-stage Pulse Tube Cryocoolers (PTC) have been designed, fabricated and experimentally studied. The single stage PTC reaches a no-load temperature of similar to 29 K at its cold end, the two-stage PTC reaches similar to 2.9 K in its second stage cold end and similar to 60 K in its first stage cold end. The two-stage Pulse Tube Cryocooler provides a cooling power of similar to 250 mW at 4.2 K. The single stage system uses stainless steel meshes along with Pb granules as its regenerator materials, while the two-stage PTC uses combinations of Pb along with Er3Ni/HoCu2 as the second stage regenerator materials. Normally, the above systems are insulated by thermal radiation shields and mounted inside a vacuum chamber which is maintained at high vacuum. To evaluate the performance of these systems in the possible conditions of loss of vacuum with and without radiation shields, experimental studies have been performed. The heat-in-leak under such severe conditions has been estimated from the heat load characteristics of the respective stages. The experimental results are analyzed to obtain surface emissivities and effective thermal conductivities as a function of interspace pressure.

Fabrication of Highly Dense Nanoholes by Self-Assembled Gallium Droplet on Silicon Surface

We report the fabrication of nanoholes on silicon surface by exploiting the solubility of silicon in gallium by local droplet etching. Nanometer-sized gallium droplets yield nanoholes when annealed in ultra-high vacuum at moderate temperatures (similar to 500 degrees C) without affecting the other regions. High vacuum and moderate annealing temperatures are key parameters to obtain well-defined nanoholes with diameter comparable to that of Ga droplets. Self-assembly of Ga droplet leads to a nanohole density of 4-8 x 10(10)/cm(2).

Photo-induced anticancer activity of polypyridyl platinum(II) complexes

Polypyridyl platinum(II) complexes (1-5), viz., Pt(pyphen)Cl]Cl (1), Pt(pyphen)(C CFc)]Cl (2), Pt(pydppz)Cl]Cl (3), Pt(pydppz)(C CPh)]Cl (4) and Pt(pydppz)(C CFc)]Cl (5), where pyphen is 6-(2-pyridyl)-1,10-phenanthroline, pydppz is 6-(2-pyridyl)-dipyrido-3,2-a:2',3'-c]-phenazine, FcC CH is ferrocenyl acetylene and PhC CH is phenyl acetylene, were synthesized, characterized and their DNA binding and photocytotoxic properties studied. The complexes showed strong binding affinity to calf-thymus DNA giving K-app of similar to 10(6)-10(7) M-1. Complexes 4 and 5 showed dual mode of binding to ct-DNA. The pydppz complexes 3-5 having a photoactive phenazine moiety showed photocytotoxicity in HeLa and MCF-7 cells in UV-A light of 365 nm with apoptotic cell death as evidenced from the acridine orange/ethidium bromide dual staining and the FACS data. (C) 2012 Elsevier Masson SAS. All rights reserved.

Electrical transport characteristics of ZnO-Bi2O3-B2O3 glasses

Optically clear glasses in the ZnO-Bi2O3-B2O3 (ZBBO) system were fabricated via the conventional melt-quenching technique. Dielectric constant and loss measurements carried out on ZBBO glasses unraveled nearly frequency (1 kHz-10 MHz)-independent dielectric characteristics associated with significantly low loss (D = 0.004). However, weak temperature response was found with temperature coefficient of dielectric constant 18 +/- 4 ppm A degrees C-1 in the 35-250 A degrees C temperature range. The conduction and relaxation phenomena were rationalized using universal AC conductivity power law and modulus formalism respectively. The activation energy for relaxation determined using imaginary parts of modulus peaks was 2.54 eV which was close to that of the DC conduction implying the involvement of similar energy barriers in both the processes. Stretched and power exponents were temperature dependent. The relaxation and conduction in these glasses were attributed to the hoping and migration of Bi3+ cations in their own and different local environment.

Multidimensional data reconstruction for two color fluorescence microscopy

We propose an iterative data reconstruction technique specifically designed for multi-dimensional multi-color fluorescence imaging. Markov random field is employed (for modeling the multi-color image field) in conjunction with the classical maximum likelihood method. It is noted that, ill-posed nature of the inverse problem associated with multi-color fluorescence imaging forces iterative data reconstruction. Reconstruction of three-dimensional (3D) two-color images (obtained from nanobeads and cultured cell samples) show significant reduction in the background noise (improved signal-to-noise ratio) with an impressive overall improvement in the spatial resolution (approximate to 250 nm) of the imaging system. Proposed data reconstruction technique may find immediate application in 3D in vivo and in vitro multi-color fluorescence imaging of biological specimens. (C) 2012 American Institute of Physics. http://dx.doi.org/10.1063/1.4769058]