Dielectric Studies of laser ablated Ca doped BaTiO3 thin films

Recently, there has been growing interest in Ca modified BaTiO3 structures due to their larger electro-optic coefficients for their use in optical storage of information over conventional BaTiO3 crystals. Barium Calcium Titanate (BCT) shows promising applications in advanced laser systems, optical interconnects and optical storage devices. BaTiO3 thin films of varied Ca (3 at. % - 15 at. %) doping were deposited using pulsed laser ablation (KrF excimer laser) technique over Pt/Si substrates. The stoichiometric and the compositional analysis were carried out using EDAX and SIMS. The dielectric studies were done at the frequency regime of 40 Hz to 100 kHz at different ambient temperatures from 200 K to 600 K. The BCT thin films exhibited diffuse phase transition, which was of a typical non lead relaxor behavior and had high dielectric constant and low dielectric loss. The phase transition for the different compositions of BCT thin films was near the room temperature, showing a marked departure from the bulk phase transition. The C - V and the hysteresis behavior confirmed the ferroelectric nature below the phase transition and paraelectric at the room temperature.

Certain Novel Aspects of Thallium and Bismuth Cuprate Superconductors

Novel superconducting thallium cuprates of the type T1Ca1‐X LnX Sr2 Cu2O6+δ (Ln = Y or rare earth), T1Srn+1‐x Lnx Cun OY and Tl1‐x PbX Srn+1Cun08+δ are described. These cuprates as well as Bi2Ca1‐x Lnx Sr2Cu2O8+δ and TICa1‐xYxBa2 Cu2 O6+δ . show maximum T around a specific composition or oxygen content. They also show interesting changes in the sign and magnitude of the thermopower with the composition. Specially noteworthy is the negative slope of the thermopower‐temperature plots. The thermopower behaviour in these two‐band systems can be understood in terms of entropie and quasiparticle contributions. It appears that Tl1‐x Pbx CaSr2Cu2O6+δ is a genuine high T electron superconductor.

Flow of a stratified fluid in a wavy channel

The flow of a stratified fluid in a channel with small and large deformations is investigated. The analogy of this flow with swirling flow in tubes with non-uniform cross-sections is studied. The flow near the wall is blocked when the Froude number takes certain critical values. The possibility of preventing the stagnation zones in the flow field is also discussed

On the dynamics of activation of mammalian X chromosomes

We have investigated a mathematical model of the process of activation of the X chromosomes in eutherian mammals. The model assumes that the activation is brought about over some definite time interval T by the complete saturation of N receptor sites on an X chromosome by M activating molecules (or multiples of M). The probability λ of a first hit on the receptor site is considered to be very much lower than that of subsequent hits; that is, we assume strong co-operative binding. Assuming further that an incomplete saturation of receptor sites is malfunctional, we can show that for proper activation of X chromosomes in normal diploid males and females, we must have λMT ≥ 3 and 0·96 ≤ N/M ≤ 1. An extension of this analysis for the triploid cases shows that under these conditions, we cannot explain the activation of two X's if the number of activating molecules is fixed at M. This suggests that there must be two classes of triploid embryos differing from each other in a step-wise manner in the number of activating molecules. In other words, triploids with two active X chromosomes would require 2M activating molecules as opposed to M molecules in triploids with a single active X. This interpretation of the two classes of triploids would be consistent with differing imprinting histories of the parental contributions to the triploid zygote.

The Boltzmann collision integrals for a combination of Maxwellians

The gain and loss integrals in the Boltzmann equation for a rigid sphere gas are evaluated in closed form for a distribution which can be expressed as a linear combination of Maxwellians. Application to the Mott-Smith bimodal distribution shows that the gain is also bimodal, but the two modes in the gain are less pronounced than in the distribution. Implications of these results for simple collision models in non-equilibrium flow are discussed.

A kinetic study of the phase transformations in Al2O3 and Na2O · 6Al2O3 by a combined use of 27Al MAS NMR spectroscopy and x-ray diffraction: Importance of nucleation

Phase transformations of Al2O3 and Na2O · 6Al2O3 prepared by the gel route have been investigated for the first time by 27Al MAS NMR spectroscopy in combination with x-ray diffraction. Of particular interest in the study is the kinetics of the γ → α and γ → β transformations, respectively, in these two systems. Analysis of the kinetic data shows the important role of nucleation in both these transformations.

Trends in consanguineous marriage in Karnataka, South India, 1980–89

Analysis of data on 106,848 marriages in the cities of Bangalore and Mysore, South India, between 1980 and 1989 showed that levels of consanguineous marriage varied between cities through time and by religion. The average coefficient of inbreeding was higher in Bangalore (F = 0·0339) than in Mysore (F = 0·0203), principally reflecting large-scale, post-Independence rural migration into Bangalore. Although there was some evidence of a decline in consanguineous marriages in Mysore, there was no convincing support in either city for earlier projections of a rapid reduction in the popularity of unions between close biological relatives.

On the evidence for the effect of bubble interference on cavitation noise

Cavitation-noise measurements from an axisymmetric body with ‘controlled’ generation of cavitation are reported. The control was achieved by seeding artificial nuclei in the boundary layer by electrolysis. It was possible to alter the number density of nuclei by varying the electrolysis voltage, polarity and the geometry of the electrode. From the observed trend of cavitation-noise data it is postulated that there exists an ‘interference effect’ which influences cavitation noise. When the nucleus-number density is high and cavitation numbers are low this effect is strong. Under these conditions the properties of cavitation noise are found to differ considerably from those expected based on theories concerning noise from single-spherical-bubble cavitation.

Kinetic decomposition of Ni2SiO4 in oxygen potential gradients

Nickel orthosilicate (Ni2SiO4) has been found to decompose into its component binary oxides in oxygen potential gradients at 1373 K. Nickel oxide was formed at the high oxygen potential boundary, while silica was detected at the low oxygen potential side. Significant porosity and fissures were observed near the Ni2SiO4/SiO2 interface and the SiO2 layer. The critical oxygen partial pressure ratio required for decomposition varied from 1.63 to 2.15 as the oxygen pressures were altered from 1.01 ⊠ 105 to 2.7X 10−4 Pa, well above the dissociation pressure of Ni2SiO4. Platinum markers placed at the boundaries of the Ni2SiO4 sample indicated growth of NiO at the higher oxygen potential boundary, without any apparent transport of material to the low oxygen potential side. However, significant movement of the bulk Ni2SiO4 crystal with respect to the marker was not observed. The decomposition of the silicate occurs due to the unequal rates of transport of Ni and Si. The critical oxygen partial pressure ratio required for decomposition is related both to the thermodynamic stability of Ni2SiO4 with respect to component oxides and the ratio of diffusivities of nickel and silicon. Kinetic decomposition of multicomponent oxides, first discovered by Schmalzried, Laqua, and co-workers [H. Schmalzried, W. Laqua, and P. L. Lin, Z. Natur Forsch. Teil A 34, 192 (1979); H. Schmalzried and W. Laqua, Oxid. Met. 15, 339 (1981); W. Laqua and H. Schmalzried, Chemical Metallurgy—A Tribute to Carl Wagner (Metallurgical Society of the AIME, New York, 1981), p. 29] has important consequences for their use at high temperatures and in geochemistry.

PL due to Discrete Gap Levels in Some Chalcogenide Glasses- A Configurational Coordinate Diagram Illustration

Photoluminescence (PL) studies were carried out on a-Se and a few Ge20Se80−xBix and Ge20Se70−xBixTe10 bulk glassy semiconductors at 4.2 K with Ar+ laser as excitation source. While a-Se and samples with lesser at% of Bi show fine structured PL with a large Stokes shift, samples with higher at% of Bi did not show any detectable PL. The investigations show at least three radiative recombination transitions. Features extracted by deconvoluting the experimental spectra show that the discrete gap levels associated with the inherent coordination defects are involved in the PL transitions. Absence of PL in samples with higher Bi at% are explained on the basis of nonradiative transition mechanisms. Overall PL mechanism involving gap levels in chalcogenide glasses is illustrated with the help of a configurational coordinate diagram.

Novel metal oxides prepared by ingenious synthetic routes

Several novel oxides have been prepared by the decomposition of carbonate precursors of calcite structure of the general formulas Mn1−xMxCO3 (M = Mg,Co,Cd), Ca1−xMx'CO3, and Ca1−x−yMxMy”CO3.

Three-dimensional laminar compressible boundary layers with large injection

The effect of large mass injection on the following three-dimensional laminar compressible boundary-layer flows is investigated by employing the method of matched asymptotic expansions: (i) swirling flow in a laminar compressible boundary layer over an axisymmetric surface with variable cross-section and (ii) laminar compressible boundary-layer flow over a yawed infinite wing in a hypersonic flow. The resulting equations are solved numerically by combining the finite-difference technique with quasi-linearization. An increase in the swirl parameter, the yaw angle or the wall temperature is found to be capable of bringing the viscous layer nearer the surface and reducing the effects of massive blowing.

Mapping of local electronic properties in nanostructured CMR thin films by Scanning Tunneling Microscopy (STM) and Local Conductance Map (LCMAP)

We have investigated the local electronic properties and the spatially resolved magnetoresistance of a nanostructured film of a colossal magnetoresistive (CMR) material by local conductance mapping (LCMAP) using a variable temperature Scanning Tunneling Microscope (STM) operating in a magnetic field. The nanostructured thin films (thickness ≈500nm) of the CMR material La0.67Sr0.33MnO3 (LSMO) on quartz substrates were prepared using chemical solution deposition (CSD) process. The CSD grown films were imaged by both STM and atomic force microscopy (AFM). Due to the presence of a large number of grain boundaries (GB's), these films show low field magnetoresistance (LFMR) which increases at lower temperatures. The measurement of spatially resolved electronic properties reveal the extent of variation of the density of states (DOS) at and close to the Fermi level (EF) across the grain boundaries and its role in the electrical resistance of the GB. Measurement of the local conductance maps (LCMAP) as a function of magnetic field as well as temperature reveals that the LFMR occurs at the GB. While it was known that LFMR in CMR films originates from the GB, this is the first investigation that maps the local electronic properties at a GB in a magnetic field and traces the origin of LFMR at the GB.

Structural and dielectric properties of Bi2NbxVi−xO5.5 ceramics

Bi2Nbx V1−xO5.5 ceramics with x ranging from 0.01 to 0.5 have been prepared. The crystal system transforms from an orthorhombic to tetragonal at x 3= 0.1 and it persists until x = 0.5. Scanning electron microscopic (SEM) investigations carried out on thermally etched Bi2NbxV1−xO5.5 ceramics confirm that the grain size decreases markedly (18 μm to 4 μm) with increasing x. The shift in the Curie temperature (725 K) toward lower temperatures, with increasing x, is established by Differential Scanning Calorimetry (DSC). The dielectric constants as well as the loss tangent (tan δ) decrease with increasing x at room temperature.

Stresses in Ion Assisted Deposited Oxide Thih Films

Thin films of Ceria, Titania and Ziroonia have been prepared using Ion Assisted Deposition(IAD). The energy of ions was varied between 0 and 1 keV and current densities up to 220 μA/cm were used. It was found that the stress behaviour is dependent on ion species, i.e. Argon or Oxygen, ion energy and current density and substrate temperature apart from the material. While oeria files showed tensile stresses under the influence of argon ion bombardment at ambient temperature, they showed a sharp transition from tensile to compressive stress with increase in substrate temperature. When bombarded with oxygen ions they showed a transition from tensile to compressive stress with increase in energy. The titania films deposited with oxygen ions, on the other hand showed purely tensile stresses. Zirconia films deposited with oxygen ions, however, showed a transition from tensile to compressive stress.