Study of fracture features in foam bearing glass epoxy composites subjected to repeated impacts

The paper reports the failure features observed in low mass repeatedly (pendulum) impacted glass epoxy composites with and without the mid section having either 2-layers or 3-layers of flexible foam. Features such as through width and inclined cracks as well as adhering of foam observed in the experiments are explained. The significance of the foam material in modifying the impact response of the composite is stressed.

Micro and macroscopic features of impact failed defect induced carbon-epoxy composites

Laminated composite structures are susceptible to damage under impacts with attendant properly degradation. While studies on damage tolerance behaviour are emphasised and the findings reported, the citations correlating impacts with the fracture features are limited. In the present study, therefore, attempts have been made to depict how the transition of the fracture features take place depending on the type and extent of defect introduced onto the carbon-epoxy system. The test specimens were subjected to differing levels of low energy pendulum impacts with a view to have specimens with varying levels of intial impacts history. Into such specimens, additional defect in the form of slits of varying depths were introduced by a mechanical process. The test coupons were then allowed to fail by impact. The fracture surface was studied under scanning electron microscope. The fractographic features that appear, based on the induced/inserted defects, are presented in this paper. It was noticed that the energy absorbed for final fracture could be associated with the defect introduced into the system. It was also observed that the size of the mechanically inserted defect had a significant influence on the features of the fracture surface.

Numerical simulations of fracture initiation in ductile solids under mode I, dynamic loading

In this paper, an overview of some recent computational studies by the authors on ductile crack initiation under mode I, dynamic loading is presented. In these studies, a large deformation finite element procedure is employed along with the viscoplastic version of the Gurson constitutive model that accounts for the micro-mechanical processes of void nucleation, growth and coalescence. A three-point bend fracture specimen subjected to impact, and a single edge notched specimen loaded by a tensile stress pulse are analysed. Several loading rates are simulated by varying the impact speed or the rise time and magnitude of the stress pulse. A simple model involving a semi-circular notch with a pre-nucleated circular hole situated ahead of it is considered. The growth of the hole and its interaction with the notch tip, which leads to plastic strain and porosity localization in the ligament connecting them, is simulated. The role of strain-rate dependence on ductile crack initiation at high loading rates, and the specimen geometry effect on the variation of dynamic fracture toughness with loading rate are Investigated.

On the characterisation of syntactic foam core sandwich composites for compressive properties

Sandwich structures, especially those with honeycomb and grid structures as the core material, are very commonly employed in aircraft structures. There is an increasing use of closed-pore rigid syntactic foams as core materials in sandwich constructions because they possess a number of favourable properties. The syntactic foams, owing to their structure and formation, behave differently under compression compared to other traditionally used core materials. In the present study, therefore, syntactic foam core sandwich constructions are evaluated for their behaviour under compression in both edgewise and flatwise orientations. Further, the work characterises the relative performance of two sets of sandwich materials, one containing glass-epoxy and the other, glass/carbon hybrid-epoxy skins. As non-standard geometry test specimens were involved, only a comparative evaluation was contemplated in this approach. The experiments indicate that the nature of the reinforcement fabric in the skin has a bearing on the test results in edgewise orientation. Thus, the tendency towards initiation of vertical crack in the central plane of the core material, which is a typical fracture event in this kind of material, was found to occur after a delay for the specimens containing the glass fabric in the skin. Attempts are made to establish the correlation between observations made on the test specimen visually during the course of testing and the post-compression microscopic examinations of the fracture features.

Re-examination of crack opening model of interface fracture

The complex singularity associated with a crack at the interface between two dissimilar, isotropic and homogeneous materials leads to mathematical artefacts, such as stress oscillations and crack face interpenetrations in the vicinity of the crack tip. To avoid these unrealistic features, Sinclair (Sinclair GB. On the stress singularity at an interface crack. International Journal of Fracture 1980;16(2):111-9) assumed a finite crack opening angle (COA) such that the singularity lambda became real equal to 1/2. This paper extends the COA model by considering real singularities not necessarily equal to 1/2. When COA is 0 degrees: the interface crack singularity is complex with a real part equal to 1/2. On increasing COA, the imaginary part of the singularity decreases and becomes zero at a threshold value of COA; at this point, the singularity is a real, repeated value. A further increase in COA results in a pair of real singularities. Different crack opening configurations and material combinations are studied, and results presented for threshold COAs and associated values of singularity. Stress analyses for these three regimes: (a) complex, (b) real pair and (c) real repeated singularities, are reported. It is seen that additional complexities are present in the last case. Typical results for stress fields are also included for comparing with standard fields. (C) 1999 Elsevier Science Ltd. All rights reserved.

Simplified seepage consolidation test for soft sediments

The consistency of very soft sediments prevents the conventional oedometer test from being applied to study their compressibility and permeability characteristics. The hydraulic consolidation test in existence requires sophisticated instrumentation and testing procedures. The present paper proposes a seepage-force-induced consolidation testing procedure for studying the compressibility and permeability behavior of soft sediments at low effective stress levels. The good agreement that has been observed between the results obtained from the proposed method and the conventional oedometer test at overlapping effective stress levels indicates that the proposed method can be used to study the compressibility and permeability characteristics of soft sediments at low effective stress levels satisfactorily.

Influence of interface properties on fracture behaviour of concrete

Hardened concrete is a three-phase composite consisting of cement paste, aggregate and interface between cement paste and aggregate. The interface in concrete plays a key role on the overall performance of concrete. The interface properties such as deformation, strength, fracture energy, stress intensity and its influence on stiffness and ductility of concrete have been investigated. The effect of composition of cement, surface characteristics of aggregate and type of loading have been studied. The load-deflection response is linear showing that the linear elastic fracture mechanics (LEFM) is applicable to characterize interface. The crack deformation increases with large rough aggregate surfaces. The strength of interface increases with the richness of concrete mix. The interface fracture energy increases as the roughness of the aggregate surface increases. The interface energy under mode II loading increases with the orientation of aggregate surface with the direction of loading. The chemical reaction between smooth aggregate surface and the cement paste seems to improve the interface energy. The ductility of concrete decreases as the surface area of the strong interface increases. The fracture toughness (stress intensity factor) of the interface seems to be very low, compared with hardened cement paste, mortar and concrete.

Compressive fracture features of syntactic foams-microscopic examination

Syntactic foams made by mechanical mixing of polymeric binder and hollow spherical particles are used as core materials in sandwich structured materials. Low density of such materials makes them suitable for weight sensitive applications. The present study correlates various postcompression microscopic observations in syntactic foams to the localized events leading the material to fracture. Depending upon local stress conditions the fracture features of syntactic foam are identified for various modes of fracture such as compressive, shear and tensile. Microscopic observations were also taken at sandwich structures containing syntactic foam as core materials and also at reinforced syntactic foam containing glass fibers. These observations provide conclusive evidences for the fracture features generated under different failure modes. All the microscopic observations were taken using scanning electron microscope in secondary electron mode. (C) 2002 Kluwer Academic Publishers.

Fracture energy and softening behavior of high-strength concrete

An experimental investigation on the fracture properties of high-strength concrete (HSC) is reported. Three-point bend beam specimens of size 100 x 100 x 500 mm were used as per RILEM-FMC 50 recommendations. The influence of maximum size of coarse aggregate on fracture energy, fracture toughness, and characteristic length of concrete has been studied. The compressive strength of concrete ranged between 40 and 75 MPa. Relatively brittle fracture behavior was observed with the increase in compressive strength. The load-CMOD relationship is linear in the ascending portion and gradually drops off after the peak value in the descending portion. The length of the tail end portion of the softening curve increases as the size of coarse aggregate increases. The fracture energy increases as the maximum size of coarse aggregate and compressive strength of concrete increase. The characteristic length of concrete increases with the maximum size of coarse aggregate and decreases as the compressive strength increases, (C) 2002 Elsevier Science Ltd. All rights reserved.

Interactions of interfacial arc cracks

The interaction of two interfacial arc cracks around a circular elastic inclusion embedded in an elastic matrix is examined. New results for stress intensity factors for a pair of interacting cracks are derived for a concentrated force acting in the matrix. For verifying the point load solutions, stress intensity factors under uniform loading are obtained by superposing point force results. For achieving this objective, a general method for generating desired stress fields inside a test region using point loads is described. The energetics of two interacting interfacial arc cracks is discussed in order to shed more light on the debonding of hard or soft inclusions from the matrix. The analysis based on complex variables is developed in a general way to handle the interactions of multiple interfacial arc cracks/straight cracks.

An assessment of creep deformation and fracture behavior of 2.25Cr-1Mo similar and dissimilar weld joints

The evaluation of the creep deformation and fracture behavior of a 2.25Cr-1Mo steel base metal, a 2.25Cr-1Mo/2.25Cr-1Mo similar weld joint, and a 2.25Cr-1Mo/Alloy 800 dissimilar weld joint at 823 K over a stress range of 90 to WO MPa has been carried out. The specimens for creep testing were taken from single-V weld pads fabricated by a shielded metal arc-welding process using 2.25Cr-1Mo steel (for similar-joint) and INCONEL 182 (for dissimilar-joint) electrodes. The weld pads were subsequently given a postweld hear treatment (PWHT) of 973 K for I hour. The microstructure and microhardness of the weld joints were evaluated in the as-welded, postweld heat-treated, and creep-tested conditions. The heat-affected zone (HAZ) of similar weld joint consisted of bainite in the coarse-prior-austenitic-grain (CPAG) region near the fusion line, followed by bainite in the fine-prior-austenitic-grain (FPAG) and intercritical regions merging with the unaffected base metal. In addition to the HAZ structures in the 2.25Cr-1Mo steel, the dissimilar weld joint displayed a definite INCONEL/2.25Cr-1Mo weld interface structure present either as a sharp line or as a diffuse region. A hardness trough was observed in the intercritical region of the HAZ in both weld joints, while a maxima in hardness was seen at the weld interface of the dissimilar weld joint. Both weld joints exhibited significantly lower rupture lives compared to the 2.25Cr-1Mo base metal. The dissimilar weld joint exhibited poor rupture life compared to the similar weld joint, at applied stresses lower than 130 MPa. In both weld joints, the strain distribution across the specimen gage length during creep testing varied significantly. During creep testing, localization of deformation occurred in the intercritical HAZ. In the similar weld joint, at all stress levels investigated, and in the dissimilar weld joint, at stresses greater than or equal to 150 MPa, the creep failure occulted in the intercritical HAZ. The fracture occurred by transgranular mode with a large number of dimples. At stresses below 150 MPa, the failure in the dissimilar weld joint occurred in the CPAG HAZ near to the weld interface. The failure occurred by extensive intergranular creep cavity formation.