Growth and characterization of SrBi2Nb2O9 thin films by pulsed-laser ablation

Polycrystalline films of SrBi2Nb2O9 were grown using pulsed-laser ablation. The ferroelectric properties were achieved by low-temperature deposition followed by a subsequent annealing process. The lower switching voltage was obtained by lowering the thickness, which did not affect the insulating nature of the films. The hysteresis results showed an excellent square-shaped loop with results (Pr = 6 μC/cm2, Ec = 100 kV/cm) in good agreement with earlier reports. The films also exhibited a dielectric constant of 250 and a dissipation factor of 0.02. The transport studies indicated an ohmic behavior, while higher voltages induced a bulk space charge.

Field-induced dielectric properties of laser ablated antiferroelectric (Pb0.99Nb0.02)(Zr0.57Sn0.38Ti0.05)0.98O3 thin films

Niobium-modified lead zirconate stannate titanate antiferroelectric thin films with the chemical composition of (Pb0.99Nb0.02)(Zr0.57Sn0.38Ti0.05)0.98O3 were deposited by pulsed excimer laser ablation technique on Pt-coated Si substrates. Field-induced phase transition from antiferroelectric to ferroelectric properties was studied at different fields as a function of temperature. The field forced ferroelectric phase transition was elucidated by the presence of double-polarization hysteresis and double-butterfly characteristics from polarization versus applied electric field and capacitance and voltage measurements, respectively. The measured forward and reverse switching fields were 25 kV/cm and 77 kV/cm, respectively. The measured dielectric constant and dissipation factor were 540 and 0.001 at 100 kHz, respectively, at room temperature.

Investigations on multimagnetron sputtered Zn1-xMgxO thin films through metal-ferroelectric-semiconductor configuration

The effect of Mg doping in ZnO is investigated through structural, electrical, and optical properties. Zn1−xMgxO (0<×<0.3) thin films were deposited on Si (100) and corning glass substrates using multimagnetron sputtering. Investigations on the structural properties of the films revealed that the increase in Mg concentration resulted in phase evolution from hexagonal to cubic phase. The temperature dependent study of dielectric constant at different frequencies exhibited a dielectric anomaly at 110 °C. The Zn0.7Mg0.3O thin films exhibited a well-defined polarization hysteresis loop with a remnant polarization of 0.2 μC/cm2 and coercive field of 8 kV/cm at room temperature. An increase in the band gap with an increase in Mg content was observed in the range of 3.3–3.8 eV for x = 0–0.3. The average transmittance of the films was higher than 90% in the wavelength region λ = 400–900 nm.

Stress Evolution With Temperature in Titanium-Rich NiTi Shape Memory Alloy Films

The effect of deposition temperature on residual stress evolution with temperature in Ti-rich NiTi films deposited on silicon substrates was studied. Ti-rich NiTi films were deposited on 3? Si (100) substrates by DC magnetron sputtering at three deposition temperatures (300, 350 and 400 degrees C) with subsequent annealing in vacuum at their respective deposition temperatures for 4 h. The initial value of residual stress was found to be the highest for the film deposited and annealed at 400 degrees C and the lowest for the film deposited and annealed at 300 degrees C. All the three films were found to be amorphous in the as-deposited and annealed conditions. The nature of the stress response with temperature on heating in the first cycle (room temperature to 450 degrees C) was similar for all three films although the spike in tensile stress, which occurs at similar to 330 degrees C, was significantly higher in the film deposited and annealed at 300 degrees C. All the films were also found to undergo partial crystallisation on heating up to 450 degrees C and this resulted in decrease in the stress values around 5560 degrees C in the cooling cycle. The stress response with temperature in the second thermal cycle (room temperature to 450 degrees C and back), which is reflective of the intrinsic film behaviour, was found to be similar in all cases and the elastic modulus determined from the stress response was also more or less identical. The three deposition temperatures were also not found to have a significant effect on the transformation characteristics of these films such as transformation start and finish temperatures, recovery stress and hysteresis.

Low threshold voltage ZnO thin film transistor with a Zn0.7Mg0.3O gate dielectric for transparent electronics

A highly transparent all ZnO thin film transistor (ZnO-TFT) with a transmittance of above 80% in the visible part of the spectrum, was fabricated by direct current magnetron sputtering, with a bottom gate configuration. The ZnO-TFT with undoped ZnO channel layers deposited on 300 nm Zn0.7Mg0.3O gate dielectric layers attains an on/off ratio of 104 and mobility of 20 cm2/V s. The capacitance-voltage (C−V) characteristics of the ZnO-TFT exhibited a transition from depletion to accumulation with a small hysteresis indicating the presence of oxide traps. The trap density was also computed from the Levinson’s plot. The use of Zn0.7Mg0.3O as a dielectric layer adds additional dimension to its applications. The room temperature processing of the device depicts the possibility of the use of flexible substrates such as polymer substrates. The results provide the realization of transparent electronics for next-generation optoelectronics.

Dielectric properties of c-axis oriented Zn1-xMgxO thin films grown by multimagnetron sputtering

Zn1−xMgxO (x = 0.3) thin films have been fabricated on Pt/TiO2/SiO2/Si substrates using multimagnetron sputtering technique. The films with wurtzite structure showed a (002) preferred orientation. Ferroelectricity in Zn1−xMgxO films was established from the temperature dependent dielectric constant and the polarization hysteresis loop. The temperature dependent study of dielectric constant at different frequencies exhibited a dielectric anomaly at 110 °C. The resistivity versus temperature characteristics showed an anomalous increase in the vicinity of the dielectric transition temperature. The Zn1−xMgxO thin films exhibit well-defined polarization hysteresis loop, with a remanent polarization of 0.2 μC/cm2 and coercive field of 8 kV/cm at room temperature.

Antiferroelectriclike polarization behavior in compositionally varying (1-x) Pb(Mg1/3Nb2/3)O3–(x) PbTiO3 multilayers

Compositionally varying multilayers of (1−x) Pb(Mg1/3N2/3)O3–(x) PbTiO3 were fabricated using pulsed laser ablation technique. An antiferroelectriclike polarization hysteresis was observed in these relaxor based multilayer systems. The competition among the intrinsic ferroelectric coupling in the relaxor ferroelectrics and the antiferroelectric coupling among the dipoles at the interface gives rise to an antiferroelectriclike polarization behavior. An increment in the coercive field and the applied field corresponding to the polarization flipping at low temperatures, provide further insight on the competition among the long-range ferroelectric interaction and the interfacial interaction in the polarization behavior of these relaxor multilayers.

Growth and ferroelectric properties of Bi2VO5.5 thin films with metallic LaNiO3 electrodes

Novel ferroelectric bismuth vanadate, Bi2VO5.5 (BVO), thin films have been grown between lattice matched metallic LaNiO3 (LNO) layers deposited on SrTiO3 (STO) by the pulsed laser deposition technique. LNO/BVO/LNO/STO and Au/BVO/LNO/STO trilayer structures exhibited c‐oriented (001) growth of BVO. LNO has been found to be a good metallic electrode with sheet resistance ∼20 Ω in addition to aiding c‐axis oriented BVO growth. The dielectric constant, ϵr of LNO/BVO/LNO/STO, at 300 K was about 12. However, when an Au electrode was used on top of BVO/LNO/STO film, it showed a significant improvement in the dielectric constant (ϵr=123). The ferroelectric properties of BVO thin films have been confirmed by hysteresis behavior with a remnant polarization, Pr=4.6×10−8 C/cm2 and coercive field, Ec=23 kV/cm at 300 K.

Improved ferroelectric and leakage properties in symmetric BiFeO3/SrTiO3 superlattice

Symmetric BiFeO3/SrTiO3 superlattices were fabricated by pulsed laser deposition on SrTiO3 (100) substrates. Frequency independent and near saturated P-E hysteresis was observed in the case of a superlattice (periodicity of ∼ 11 nm) as compared to leaky hysteresis observed in epitaxial BiFeO3. Room temperature leakage current density of the superlattice was almost two orders of magnitude lower than that of BiFeO3. Observed leakage current behavior in case of both BiFeO3 and superlattice indicates the dominance of space charge limited conduction. Improvement in ferroelectric property was discussed in connection to enhanced epitaxial strain, reduced leakage current, and electrostatic interaction between BiFeO3 and SrTiO3.

Ferroelectric interaction and polarization studies in BaTiO3/SrTiO3 superlattice

Ferroelectric superlattice structures consisting of alternating layers of BaTiO3 and SrTiO3 with variable interlayer thickness were grown on Pt (111)/TiO2/SiO2/Si (100) substrates by pulsed laser deposition. The presence of superlattice reflections in the x-ray diffraction pattern clearly showed the superlattice behavior of the fabricated structures over a range of 6.4–20 nm individual layer thicknesses. Depth profile conducted by secondary ion mass spectrometry analysis showed a periodic concentration of Ba and Sr throughout the film. Polarization hysteresis and the capacitance-voltage characteristics of these films show clear size dependent ferroelectric characteristics. The spontaneous (Ps) and remnant (Pr) polarizations increase gradually with decreasing periodicity, reach a maximum at a finite thickness and then decrease. The competition between the size effect and long-range ferroelectric interaction is suggested as a possible reason for this phenomenon. The temperature dependence of Ps and Pr shows a single ferroelectric phase transition, and the Curie temperature is estimated to be about 316 K. The curve shows that the ferroelectric superlattice tends to form an artificial material, responding as a single structure with an averaged behavior of both the parent systems.

Bi4Ti3O12–5BiFeO3 Aurivillius intergrowth: Structural and ferroelectric properties

Aurivillus intergrowth Bi4Ti3O12–5BiFeO3 was demonstrated to be ferroelectric that evoked the possibility of achieving high temperature magnetoelectric property in this family of compounds. X-ray diffraction studies confirmed its structure to be orthorhombic [Fmm2; a = 5.5061(11) Å, b = 5.4857(7) Å, c = 65.742(12) Å]. However, transmission electron microscopy established the random incidence of intergrowth at nanoscale corresponding to n = 6 and n = 7 members of the Aurivillius family. Diffuse ferroelectric orthorhombic to paraelectric tetragonal phase transition around 857 K was confirmed by dielectric and high temperature x-ray diffraction studies. Polarization versus electric field hysteresis loops associated with 2Pr of 5.2 μC/cm2 and coercive field of 42 kV/cm were obtained at 300 K.

Ferro electriclike and pyroelectric behavior of CaCu3Ti4O12 ceramics

A ferroelectriclike hysteresis loop was obtained at room temperature for CaCu3Ti4O12 (CCTO) ceramic. The remnant polarization and coercive field for 1100 °C/5 h sintered CaCu3Ti4O12 ceramics were 0.063 μC/cm2 and 195 V/cm, respectively. Remnant polarization increased while the coercive field decreased with increase in sintering temperature/duration, implying that these were microstructural dependent. The observation of the hysteresis loop for CCTO ceramic was corroborated by its pyroelectric behavior, and the pyroelectric current at room temperature was −0.0028 nA. These findings were attributed to the presence of mixed-valent Ti ions, apart from off center displacement of Ti ions in TiO6 octahedra.

Dielectric properties of (110) oriented PbZrO3 and La-modified PbZrO3 thin films grown by sol-gel process on Pt(111)/Ti/SiO2/Si substrate

Highly (110) preferred orientated antiferroelectric PbZrO3 (PZ) and La-modified PZ thin films have been fabricated on Pt/Ti/SiO2/Si substrates using sol-gel process. Dielectric properties, electric field induced ferroelectric polarization, and the temperature dependence of the dielectric response have been explored as a function of composition. The Tc has been observed to decrease by ∼ 17 °C per 1 mol % of La doping. Double hysteresis loops were seen with zero remnant polarization and with coercive fields in between 176 and 193 kV/cm at 80 °C for antiferroelectric to ferroelectric phase transformation. These slim loops have been explained by the high orientation of the films along the polar direction of the antiparallel dipoles of a tetragonal primitive cell and by the strong electrostatic interaction between La ions and oxygen ions in an ABO3 perovskite unit cell. High quality films exhibited very low loss factor less than 0.015 at room temperature and pure PZ; 1 and 2 mol % La doped PZs have shown the room temperature dielectric constant of 135, 219, and 142 at the frequency of 10 kHz. The passive layer effects in these films have been explained by Curie constants and Curie temperatures. The ac conductivity and the corresponding Arrhenius plots have been shown and explained in terms of doping effect and electrode resistance.

Interface dominated biferroic La0.6Sr0.4MnO3/0.7Pb(Mg1/3Nb2/3)O3–0.3PbTiO3 epitaxial superlattices

Superlattices composed of ferromagnetic La0.6Sr0.4MnO3 and ferroelectric 0.7Pb(Mg1/3Nb2/3)O3–0.3(PbTiO3) layers were fabricated on (100) LaAlO3 substrates by pulsed laser deposition technique. The ferromagnetic and frequency independent ferroelectric hysteresis characteristics established the biferroic nature of the superlattices. Influence of magnetic field was observed in tuning the P-E characteristics of the superlattices. A similar effect was observed on application of a high dc electric field to the samples. The nature of the observed ferroelectric properties and their modulation by applied magnetic and electric fields were thus discussed in connection to the ferroelectric/ferromagnetic interfaces.

A Fluidic Drive System for Intra-Aortic Balloon Heart Assist Device

Intra-aortic balloon pumping is a counter pulsation technique for temporary circulatory assistance in cardiogenic shock and other low cardiac output conditions. Conventional systems use a balloon at the end of a catheter driven by a solenoid valve, controlled by patient's ECG or ventricular pressure signal. This results in time delay introducted by solenoid spool inertia, gas inertia, and hysteresis effects of the solenoid. Fluidics, because of their non-moving part operation and high switching speeds, minimizes the inertial effects while contributing high reliability. This communication describes a fluidic system developed for driving the balloon accepting electric control signals.