Electrical, structural and magnetic properties of polyaniline/pTSA-TiO2 nanocomposites

Polyaniline (PANI)/para-toluene sulfonic acid (pTSA) and PANI/pTSA-TiO2 composites were prepared using chemical method and characterized by infrared spectroscopy (IR), powder X-ray diffraction (XRD), scanning electron microscopy (SEM). The electrical conductivity and magnetic properties were also measured. In corroboration with XRD, the micrographs of SEM indicated the homogeneous dispersion of TiO nanoparticles in bulk PANI/pTSA matrix. Conductivity of the PANI/pTSA-TiO2 was higher than the PAN[/pTSA, and the maximum conductivity obtained was 9.48 (S/cm) at 5 wt% of TiO2. Using SQUID magnetometer, it was found that PANI/pTSA was either paramagnetic or weakly ferromagnetic from 300 K down to 5 K with H-C approximate to 30 Oe and M-r approximate to 0.015 emu/g. On the other hand,PANI/pTSA-TiO2 was diamagnetic from 300 K down to about 50 K and below which it was weakly ferromagnetic. Furthermore, a nearly temperature-independent magnetization was observed in both the cases down to 50 K and below which the magnetization increased rapidly (a Curie like susceptibility was observed). The Pauli susceptibility (chi(pauli)) was calculated to be about 4.8 X 10(-5) and 1.6 x 10(-5)emug(-1) Oe(-1) K for PANI/pTSA and PANI/pTSA-TiO2, respectively.

Volumetric behavior of ethylene and ethylene-hydrogen mixtures

A Burnett apparatus deslgned and fabrlcated was used to collect volumetric data for ethylene and ethylene-hydrogen mixtures. Measurements were made In the temperature range 298.15-423.15 K at Intervals of 25 K and In the pressure range 0.3-7.0 MPa. Vlrlal coefflclents derlved from the compresslblllty data are tabulated. The data are fltted to different equations of state.

Pressure and temperature dependence of the electrical resistivity of bulk Al23 Te77 glass

Electrical resistivity of bulk amorphous Al23T77 samples has been studied as a function of pressure (up to 80 kbar) and temperature (down to 77 K). At atmospheric pressure the temperature dependence of resistivity obeys the relation = π0 exp(δE/RT) with two activation energies. In the temperature range 300 K T > 234 K the activation energy is 0.58 eV and for 234 >T 185 K the value is δE = 0.30 ev. The activation energy has been measured as a function of pressure. The electrical resistivity decreases exponentially with the increase of pressure and at 70 kbar pressure the electrical behaviour of the sample shows a metallic nature with a positive temperature coefficient. The high pressure phase of the sample is found to be a crystalline hexagonal phase.

Electrical transport and crystallization studies of glassy semiconducting Si20Te80 alloy at high pressure

The effect of pressure on the electrical resistivity of bulk Si20Te80 glass is reported. Results of calorimetric, X-ray and transmission electron microscopy investigations at different stages of crystallization of bulk Si20Te80 glass are also presented. A pressure induced glass-to-crystal transition occurs at a pressure of 7 GPa. Pressure and temperature dependence of the electrical resistivity of Si20Te80 glass show the observed transition is a pressure induced glassy semiconductor to crystalline metal transition. The glass also exhibits a double Tg effect and double stage crystallization, under heating. The differences between the temperature induced crystallization (primary crystallization) and pressure induced congruent crystallization are discussed.

Electrical Transport Studies in as-se Glasses

The DC and AC conductivity studies of As---Se glasses over a wide range of compositions have been reported and discussed. The contribution to conductivity from transport among extended states has been delineated and the possible existence of a characteristic temperature is indicated. Two conductivity maxima have been observed as a function of composition in AC conductivities at lower temperatures.

Indentation strength of a piezoelectric ceramic: Experiments and simulations

The spherical indentation strength of a lead zirconate titanate (PZT) piezoelectric ceramic was investigated under poled and unpoled conditions and with different electrical boundary conditions (arising through the use of insulating or conducting indenters). Experimental results show that the indentation strength of the poled PZT is higher than that of the unpoled PZT. The strength of a poled PZT under a conducting indenter is higher than that under an insulating indenter. Poling direction (with respect to the direction of indentation loading) did not significantly affect the strength of material. Complementary finite element analysis (FEA) of spherical indentation of an elastic, linearly coupled piezoelectric half-space is conducted for rationalizing the experimental observations. Simulations show marked dependency of the contact stress on the boundary conditions. In particular, contact stress redistribution in the Coupled problem leads to a change in the fracture initiation, from Hertzian cracking in the unpoled material to Subsurface damage initiation in poled PZT. These observations help explain the experimental ranking of strength the PZT in different material conditions or under different boundary conditions.

Annealing Behavior of Isotactic Polybutene-1

The annealing behavior of isotactic polybutene-1 (PB-1) has been studied by differential scanning calorimetry and wide-angle x-ray diffraction. On annealing at 110°C, PB-1 yields thick crystals melting at -140°C which are mainly of Form I. An increase in the heat of fusion (ΔHf) and crystallinity is found for annealing times up to 12 h at 110°C; at longer times these properties decrease with increasing annealing time. The increases in ΔHf and crystallinity are attributed to increases in the lamellar thickness in the chain direction and in crystal perfection, and subsequent decreases to degradation of the polymer.

Phase separation versus spin glass behavior in La0.85Sr0.15CoO3

We present comprehensive studies of dc magnetization, ac susceptibility, and magnetotransport of two sets of La0.85Sr0.15CoO3 samples, one exhibits phase separation and the other exhibits spin glass behavior. Our study reveals that the phase separation in La0.85Sr0.15CoO3 is neither inherent nor ubiquitous; rather, it is a consequence of preparation condition. It is realized that the low temperature annealed sample exhibits phase separation while the high temperature annealed one shows the characteristic of spin glass behavior. This study shows that the most probable magnetic state of La0.85Sr0.15CoO3 is spin glass.

Size dependence and dispersion behavior of the first hyperpolarizability of copper nanoparticles

We have probed the size dependency of the first hyperpolarizability (b) of copper nanoparticles by hyper-Rayleigh scattering (HRS). Our results indicate that second harmonic generation (SHG) originates predominantly at the surface of the nanoparticles as long as the size (d) remains small compared to the wavelength (k). However, volume contribution to the SH response due to the retardation effect becomes important when particle size grows beyond the `small particle limit'. There is a significant dispersion in the b values of copper nanoparticles owing tothe presence of the strong surface plasmon resonance (SPR) band.

Electrical transport in the perovskite solid solution LaNi1-xCoxO3

We have studied the resistivity and thermopower of the solid solution LaNi1-xCoxO3 in the temperature range 1.4K-300K. Effect of interaction and localization are seen in the low temperature transport data for x<0.55. A negative anomaly in the thermopower has been observed at low temperature for 0.1

Nonlinear conduction and electrical switching in one-dimensional conductors

Many one-dimensional conductors show pronounced nonlinear electrical conduction. Some of them show very interesting electrical switching from a low conducting state to a high conducting state. Such electrical switching is often associated with memory. These are discussed with particular emphasis on charge transfer complexestmbine-tcnq, tmpd-tcnq, Cs2(tcnq)3,tea-(tcnq) 2 ando-tolidine-iodine.