Crystallization studies on amorphous AI-Y-Ni and AI-Y-Cu alloys

AI83Y10Ni7, AI80Y10Ni10 and AI80Y10Cu10 alloys were studied by the rapid solidification processing route. The glass-forming ability was found to decrease in the order of alloys mentioned above. Differential scanning calorimetry (DSC) of these amorphous alloys showed that the amorphous phase in AI-Y-Ni alloys has a higher thermal stability when compared to that in AI-Y-Cu alloys. A four-stage crystallization sequence could be identified for the AI-Y-Ni amorphous alloys. Even though the AI80Y10Cu10 alloy showed four exothermic peaks in the DSC study, a definite crystallization sequence could not be arrived at due to the coexistence of many crystalline phases along with the amorphous phase in the melt-spun condition.

Magnetoresistance of FexNi80-xCr20 (50alloys

The authors have measured longitudinal and transverse magnetoresistance (MR) of crystalline pseudo-binary alloys FexNi80-xCr20 (50alloys have compositions close to the critical composition regime for ferromagnetism. While the Fe-Ni-Cr alloys have a FCC gamma -phase, the binary Fe-Cr alloy has a BCC alpha -phase. This gives an opportunity to compare magnetoresistances for gamma -phase and alpha -phase Fe alloys when they lie close to the critical composition. The experiments were conducted at 4.2 K with magnetic fields up to 7 T. The authors observed that all the alloys show negative magnetoresistance at 4.2 K in fields up to 7 T. However, for the gamma -phase alloys the typical maximum MR ( Delta rho / rho ) is about 1%, while for the alpha -phase alloy it is 10%. In the gamma -phase alloys there is a small but finite anisotropy of MR in the phases with long-range magnetic order which gradually vanishes near the critical region (x=xc approximately=59-63) when it becomes a spin glass. In the range x approximately=xc, Delta rho / rho varies as Mn (M=magnetization) with n approximately=2.

Processing maps for hot working of Cu-Ni-Zn alloys. Part I - Alpha-nickel silver

The constitutive behaviour of agr — nickel silver in the temperature range 700–950 °C and strain rate range 0.001–100 s–1 was characterized with the help of a processing map generated on the basis of the principles of the ldquodynamic materials modelrdquo of Prasadet al Using the flow stress data, processing maps showing the variation of the efficiency of power dissipation (given by 2m/(m+1) wherem is the strain-rate sensitivity) with temperature and strain rate were obtained, agr-nickel silver exhibits a single domain at temperatures greater than 750 °C and at strain rates lower than 1s–1, with a maximum efficiency of 38% occurring at about 950 °C and at a strain rate of 0.1 s–1. In the domain the material undergoes dynamic recrystallization (DRX). On the basis of a model, it is shown that the DRX is controlled by the rate of interface formation (nucleation) which depends on the diffusion-controlled process of thermal recovery by climb. At high strain rates (10 and 100s–1) the material undergoes microstructural instabilities, the manifestations of which are in the form of adiabatic shear bands and strain markings.

Processing maps for hot working of Cu-Ni-Zn alloys Part II Alpha-Beta nickel silver

The constitutive behaviour of agr-beta nickel silver in the temperature range 600�850 °C and strainrate range 0.001�100s�1 was characterized with the help of a processing map generated on the principles of the dynamic materials model. On the basis of the flow-stress data, processing maps showing the variation of the efficiency of power dissipation (given by [2m/(m+1)], wherem is the strain-rate sensitivity) with temperature and strain rate were obtained, agr-beta nickel silver exhibits a single domain at temperatures greater than 700 °C and at strain rates lower than 1 s�1 with a maximum efficiency of power dissipation of about 42% occurring at about 850 °C and at 0.1 s�1. In the domain, the agr phase undergoes dynamic recrystallization and controls the deformation of the alloy, while the beta phase deforms superplastically. Optimum conditions for the processing of agr-beta nickel silver are 850 °C and 0.1 s�1. The material undergoes unstable flow at strain rates of 10 and 100 s�1 and in the temperature range 600�750 °C, manifestated in the form of adiabatic shear bands.

Measurement for Thermal Effusivity of AlxGa1-xN Alloys Using Thermoreflectance with Periodic Heating

AlxGa1-xN alloys with x=0.375, 0.398, 0.401, 0.592 and 0.696 were deposited on sapphire substrate by the hydride-vapor-phase epitaxy (HVPE) method. Thermal effusivity measurements were carried out on AlxGa1-xN alloys using a thermal microscope at room temperature. The lag between sinusoidal heating laser wave and thermoreflectance wave was used to measure the thermal diffusivity. Thermal conductivity values of the AlxGa1-xN alloys were also obtained as a function of AIN mole fraction in the alloy. The thermal conductivity was found to decrease with increasing AIN fraction and the experimental data agree with values estimated using the virtual crystal model.

Temperature dependence of hydrogen evolution reaction on nickel oxide electrode in sealed nickel/cadmium cells

The impedance of sealed nickel/cadmium cells around a cell e.m.f. of 0.0 V was measured at five different temperatures between � 10 and +30 °C. The results show that the behaviour is similar at all temperatures. Based on the experimental results, the relation between charge-transfer resistance (Rct) and temperature (T) has been established for the Volmer reaction. Further, the value of cathodic transfer coefficient (?) has been estimated.

The Determination of the Surface Tensions of Liquid-Iron, Nickel and Iron-Nickel Alloys using the electromagnetic Oscillating Droplet Technique

An oscillating droplet method combined with electromagnetic levitation has been applied to determine the surface tensions of liquid pure iron, nickel and iron-nickel alloys as a function of the temperature. The natural frequency of the oscillating droplet is evaluated using a Fourier analyser. The theoretical background of this method and the experimental set-up were described, and the influence of magnetic field strength was also discussed. The experimental results were compared with those of other investigators and interpreted using theoretical models (Butler's equation, subregular and perfect solution model for the surface phase).

The Determination of the Surface Tensions of Nickel Sulfur Alloys using the Electromagnetic Oscillating Droplet Technique

An oscillating droplet method combined with electromagnetic levitation technique has been applied to determine the surface tensions of liquid nickel sulphur alloys as a function of the temperature and composition. The natural frequency of the oscillating droplet is evaluated using a Fourier analyser, and the influence of magnetic field strength on the surface tension was considered. Furthermore, the applicability of Butler's equation and subregular solution model for the surface was shown to predict the surface tension of the systems containing the surface active elements.

An electron diffraction study of quasicrystals in Ti-37 at% Mn and Ti-24 at% Mn-13 at% Fe alloys

Electron diffraction studies were carried out to establish the icosahedral phase formation in rapidly quenched Ti-37 at% Mn and Ti-24 at% Mn-13 at% Fe alloys. Distortions in the diffraction spots and diffuse intensities in the diffraction patterns were investigated. The existence of a rational approximant structure and a decagonal like phase are also reported.

Liquid-Liquid Interphase (Biphasic) as the Reaction Medium in the Assembly of a Hierarchy of Structures of 4,4 `-Azodibenzoic Acid with Zinc and Cadmium

The compounds Zn(C12H8N2)](2)C12N2H8(COO)(2)](2)center dot(C6H12O)center dot(H2O), I, Zn(C12H8N2)]C12N2H8(COO)(2)], II, Cd(C12H8N2)(H2O)]C12N2H8(COO)(2)]center dot(H2O), III, Zn(C10N2H8)]C12N2H8(COO)(2)]center dot 0.5(C10N2H8), IV, Cd(C12N2H8(COO)(2)center dot H2O], V, and Zn-3(mu(2)-O)(mu(3)-O)(3)]C12N2H8(COO)(2)], VI, have been synthesized by using a biphasic approach (I, III, V, VI) or regular hydrothermal method (II, IV). The compounds exhibit one (I and II), two (In), and three dimensionally (IV, V, VI) extended structures. The flexible azodibenzoate ligand gives rise to a 3-fold interpenetration (IV) when the synthesis was carried out using normal hydrothermal methods. The biphasic approach forms structures without any interpenetrations, especially in the three-dimensional structures of V and VI. Formation of Cd2O2 dimers in V and extended M-O(H)-M two-dimensional layers in VI suggests the subtle structural control achieved by the biphasic method. Transformation studies indicate that it is possible to transform I to II. Lewis acid catalytic studies have been performed to evaluate the role of the coordination environment in such reactions. All the compounds have been characterized by a variety of techniques that includes powder X-ray diffraction, infrared, thermogravitric analysis, UV-vis, photoluminescence studies.

Mechanical properties of B-modified Ti-6Al-4V alloys

Minor addition of B to the Ti-6Al-4V alloy reduces the prior beta grain size by more than an order of magnitude. TiB formed in-situ in the process has been noted to decorate the grain boundaries. This microstructural modification influences the mechanical behavior of the Ti-6Al-4V alloy significantly. In this paper, an overview of our current research on tensile properties, fracture toughness as well as notched and un-notched fatigue properties of Ti-6Al-4V-xB with x varying between 0.0 to 0.55 wt.% is presented. A quantitative relationship between the microstructural length scales and the various mechanical properties have been developed. Moreover, the effect of the presence of hard and brittle TiB has also been studied.

Impedance peaks of sealed nickel/cadmium cells at low states-of-charge

The impedance of sealed nickel/cadmium cells is measured at low states-of-charge that correspond to a cell e.m.f. range of 0.0 to 1.3 V. The results show that the impedance exhibits a pronounced maximum between 0.3 and 0.45 V. It is concluded that the impedance maxima are due to physicochemical processes taking place at the nickel oxide electrode. The impedance of the nickel oxide electrode is dominated by three different phenomena: (i) a Ni(II)/Ni(III) reaction between 1.3 and 0.8 V; (ii) a double-layer impedance between 0.8 and 0.3 V; (iii) a hydrogen evolution reaction between 0.3 and 0.0 V.