Ingots with compositions CrSi2-x (with 0 < x < 0.1) were synthesized by vacuum arc melting followed by uniaxial hot pressing for densification. This paper reports the temperature and composition dependence of the electrical resistivity, Seebeck coefficient, and thermal conductivity of CrSi2-x samples in the temperature range of 300 K to 800 K. The silicon-deficient samples exhibited substantial reductions in resistivity and Seebeck coefficient over the measured temperature range due to the formation of metallic secondary CrSi phase embedded in the CrSi2 matrix phase. The thermal conductivity was seen to exhibit a U-shaped curve with respect to x, exhibiting a minimum value at the composition of x = 0.04. However, the limit of the homogeneity range of CrSi2 suppresses any further decrease of the lattice thermal conductivity. As a consequence, the maximum figure of merit of ZT = 0.1 is obtained at 650 K for CrSi1.98.
Resumo:
The recently discovered scalar resonance at the Large Hadron Collider is now almost confirmed to be a Higgs boson, whose CP properties are yet to be established. At the International Linear Collider with and without polarized beams, it may be possible to probe these properties at high precision. In this work, we study the possibility of probing departures from the pure CP-even case, by using the decay distributions in the process e(+)e(-) -> t (t) over bar Phi, with Phi mainly decaying into a b (b) over bar pair. We have compared the case of a minimal extension of the Standard Model case (model I) with an additional pseudoscalar degree of freedom, with a more realistic case namely the CP-violating two-Higgs doublet model (model II) that permits a more general description of the couplings. We have considered the International Linear Collider with root s = 800 GeV and integrated luminosity of 300 fb(-1). Our main findings are that even in the case of small departures from the CP-even case, the decay distributions are sensitive to the presence of a CP-odd component in model II, while it is difficult to probe these departures in model I unless the pseudoscalar component is very large. Noting that the proposed degrees of beam polarization increase the statistics, the process demonstrates the effective role of beam polarization in studies beyond the Standard Model. Further, our study shows that an indefinite CP Higgs would be a sensitive laboratory to physics beyond the Standard Model.
Resumo:
CrSi and Cr1-x Fe (x) Si particles embedded in a CrSi2 matrix have been prepared by hot pressing from CrSi1.9, CrSi2, and CrSi2.1 powders produced by ball milling using either WC or stainless steel milling media. The samples were characterized by powder X-ray diffraction, scanning, and transmission electron microscopy and electron microprobe analysis. The final crystallite size of CrSi2 obtained from the XRD patterns is about 40 and 80 nm for SS- and WC-milled powders, respectively, whereas the size of the second phase inclusions in the hot pressed samples is about 1-5 mu m. The temperature dependence of the electrical resistivity, Seebeck coefficient, thermal conductivity, and figure of merit (ZT) were analyzed in the temperature range from 300 to 800 K. While the ball-milling process results in a lower electrical resistivity and thermal conductivity due to the presence of the inclusions and the refinement of the matrix microstructure, respectively, the Seebeck coefficient is negatively affected by the formation of the inclusions which leads to a modest improvement of ZT.
Resumo:
Recent observations of Sun-like stars, similar to our Sun in their surface temperature (5600-6000 K) and slow rotation (rotational period > 10 d), using the Kepler satellite by Maehara et al. (2012, Nature, 485, 478) have revealed the existence of superflares (with energy of 10(33)-10(35) erg). From statistical analyses of these superflares, it was found that superflares with energy of 10(34) erg occur once in 800 yr, and superflares with 10(35) erg occur once in 5000 yr. In this paper, we examine whether superflares with energy of 10(33)-10(35) erg could occur on the present Sun through the use of simple order-of-magnitude estimates based on current ideas related to the mechanisms of the solar dynamo. If magnetic flux is generated by differential rotation at the base of the convection zone, as assumed in typical dynamo models, it is possible that the present Sun would generate a large sunspot with a total magnetic flux of similar to 2 x 10(23) Mx (= G cm(2)) within one solar cycle period, and lead to superflares with an energy of 10(34) erg. To store a total magnetic flux of similar to 10(24) Mx, necessary for generating 10(35) erg superflares, it would take similar to 40 yr. Hot Jupiters have often been argued to be a necessary ingredient for the generation of superflares, but we found that they do not play any essential role in the generation of magnetic flux in the star itself, if we consider only the magnetic interaction between the star and the hot Jupiter. This seems to be consistent with Maehara et al.'s finding of 148 superflare-generating solar-type stars that do not have a hot Jupiter-like companion. Altogether, our simple calculations, combined with Maehara et al.'s analysis of superflares on Sun-like stars, show that there is a possibility that superflares of 10(34) erg would occur once in 800 yr on our present Sun.
Resumo:
Hydrogeological and climatic effect on chemical behavior of groundwater along a climatic gradient is studied along a river basin. `Semi-arid' (500-800 mm of mean annual rainfall), `sub-humid' (800-1,200 mm/year) and `humid' (1,200-1,500 mm/year) are the climatic zones chosen along the granito-gneissic plains of Kabini basin in South India for the present analysis. Data on groundwater chemistry is initially checked for its quality using NICB ratio (<+/- 5 %), EC versus TZ+ (similar to 0.85 correlation), EC versus TDS and EC versus TH analysis. Groundwater in the three climatic zones is `hard' to `very hard' in terms of Ca-Mg hardness. Polluted wells are identified (> 40 % of pollution) and eliminated for the characterization. Piper's diagram with mean concentrations indicates the evolution of CaNaHCO3 (semi-arid) from CaHCO3 (humid zone) along the climatic gradient. Carbonates dominate other anions and strong acids exceeded weak acids in the region. Mule Hole SEW, an experimental watershed in sub-humid zone, is characterized initially using hydrogeochemistry and is observed to be a replica of entire sub-humid zone (with 25 wells). Extension of the studies for the entire basin (120 wells) showed a chemical gradient along the climatic gradient with sub-humid zone bridging semi-arid and humid zones. Ca/Na molar ratio varies by more than 100 times from semi-arid to humid zones. Semi-arid zone is more silicaceous than sub-humid while humid zone is more carbonaceous (Ca/Cl similar to 14). Along the climatic gradient, groundwater is undersaturated (humid), saturated (sub-humid) and slightly supersaturated (semi-arid) with calcite and dolomite. Concentration-depth profiles are in support of the geological stratification i.e., not approximate to 18 m of saprolite and similar to 25 m of fracture rock with parent gneiss beneath. All the wells are classified into four groups based on groundwater fluctuations and further into `deep' and `shallow' based on the depth to groundwater. Higher the fluctuations, larger is its impact on groundwater chemistry. Actual seasonal patterns are identified using `recharge-discharge' concept based on rainfall intensity instead of traditional monsoon-non-monsoon concept. Non-pumped wells have low Na/Cl and Ca/Cl ratios in recharge period than in discharge period (Dilution). Few other wells, which are subjected to pumping, still exhibit dilution chemistry though water level fluctuations are high due to annual recharge. Other wells which do not receive sufficient rainfall and are constantly pumped showed high concentrations in recharge period rather than in discharge period (Anti-dilution). In summary, recharge-discharge concept demarcates the pumped wells from natural deep wells thus, characterizing the basin.
Resumo:
The effect of annealing on structural defects and d(0) ferromagnetism in SnO2 nanoparticles prepared by solution combustion method is investigated. The as-synthesized SnO2 nanoparticles were annealed at 400-800 degrees C for 2 h, in ambient conditions. The crystallinity, size, and morphology of the samples were studied using x-ray diffraction and transmission electron microscopy studies. The annealing results in grain growth due to coarsening as well as reduction in oxygen vacancies as confirmed by Raman spectroscopy, photoluminescence spectroscopy, and x-ray photoelectron spectroscopy. All the as synthesized and annealed samples exhibit room temperature ferromagnetism (RTFM) with distinct hysteresis loops and the saturation magnetization as high as similar to 0.02 emu/g in as-synthesized samples. However, the saturation magnetization is drastically reduced with increasing annealing temperature. Further the presence of singly charged oxygen vacancies (V-o(-) signal at g-value 1.99) is confirmed by electron paramagnetic resonance studies, which also diminish with increasing annealing temperature. The observed diminishing RTFM and simultaneous evidences of diminishing O vacancies clearly indicate that RTFM is driven by defects in oxide lattice and confirms primary role of oxygen vacancies in inducing ferromagnetic ordering in metal oxide semiconductors. The study also provides improved fundamental understanding regarding the ambiguity in the origin of intrinsic RTFM in semiconducting metal oxides and projects their technological application in the field of spintronics. (C) 2013 AIP Publishing LLC.
Resumo:
We report ferromagnetic resonance (FMR) study on a grid formed with permalloy nanowires to understand the spin wave dynamics. The presence of two sets of magnetic nanowires perpendicular to each other in the same device enables better control over spin waves. The grid was fabricated using e-beam lithography followed by DC-Magnetron sputtering and liftoff technique. It has dimensions of 800 +/- 10 and 400 +/- 10 nm as periods along X and Y directions with permalloy wires of width 145 +/- 10 nm. FMR studies were done at X-band (9.4 GHz) with the field sweep up to 1 Tesla. The in-plane angular variation of resonant fields shows that there are two well separated modes present, indicating two uniaxial anisotropy axes which are perpendicular to each other. The variation in the intensities in the FMR signal w.r.t. the grid angle is used to describe the spin wave confinement in different regions of the grid. We also explained the asymmetry in the magnetic properties caused by the geometrical property of the rectangular grid and the origin for the peak splitting for the modes occurring at higher resonant fields. Micromagnetic simulations based on OOMMF with two dimensional periodic boundary conditions (2D-PBC) are used to support our experimental findings.
Resumo:
Copper(II) complexes Cu(Fc-aa)(cur)] (1-3) of curcumin (Hcur) and N-ferrocenylmethyl-L-amino acids (Fc-aa), viz., ferrocenylmethyl-L-tyrosine (Fc-TyrH), ferrocenylmethyl-L-tryptophan (Fc-TrpH) and ferrocenylmethyl-L-methionine (Fc-MetH), were prepared and characterized. The DNA photocleavage activity, photocytotoxicity and cellular localization in HeLa and MCF-7 cancer cells of these complexes were studied. Acetylacetonate (acac) complexes Cu(Fc-aa)(acac)] (4-6) were prepared and used as controls. The chemical nuclease inactive complexes showed efficient pUC19 DNA cleavage activity in visible light. Complexes 1-3 showed high photocytotoxicity with low dark toxicity thus giving remarkable photodynamic effect. FACScan analysis showed apoptosis of the cancer cells. Fluorescence microscopic studies revealed primarily cytosolic localization of the complexes. (C) 2013 Elsevier Masson SAS. All rights reserved.
Resumo:
Mn0.4Zn0.6Fe2O4 powders were prepared by microwave hydrothermal method. The powders were characterized by X-ray diffraction, transmission electron microscope. The powders were sintered at different temperatures 400, 500, 600, 700, 800 and 900 degrees C/30 min using microwave sintering method. The grain size was estimated by scanning electron microscope. The room temperature dielectric and magnetic properties were studied in the frequency range (100 kHz-1.8 GHz). The magnetization properties were measured upto 1.5 T. The acoustic emission has been measured along the hysteresis loops from 80 K to Curie temperature. It is found that the magneto-acoustic emission (MAE) activity along hysteresis loop is proportional to the hysteresis losses during the same loop. This law has been verified on series of polycrystalline ferrites and found that the law is valid whatever the composition, the grain size and temperature. It is also found that the domain wall creation/or annihilation processes are the origin of the MAE. (C) 2013 Published by Elsevier Ltd.
Resumo:
An alternating copolymer containing dithienylcyclopentadienone, thiophene and benzothiadiazole was synthesized by palladium (0) catalyzed Stille coupling reaction. Structural characterization of the synthesized alternating copolymer was carried out by NMR and FTIR spectroscopy. This solution processable copolymer shows an excellent thermal stability and has a broad absorption range from 300-800 nm. High LUMO energy level and low band gap of the synthesized copolymers suggest that, this copolymer will be a better donor material for application in organic photovoltaics. Particle size analysis and molecular weight determination of the synthesized copolymer through dynamic light scattering experiment indicates that, high molecular weight copolymer was obtained by this polymerization route. Photovoltaic devices were fabricated from the blend of copolymer and phenyl-C61- butyric acid methyl ester as the active material. Fabricated photovoltaic device results show that this alternating copolymer is a promising candidate for use in organic photovoltaics.
Resumo:
A porous layered composite of Li2MnO3 and LiMn1/3Co1/3Ni1/3O2 (composition: Li1.2Mn0.53Ni0.13Co0.13O2) is prepared by reverse microemulsion method employing a soft polymer template and studied as a positive electrode material. The precursor is heated at several temperatures between 500 and 900 degrees C. The product samples possess mesoporosity with broadly distributed pores of about 30 nm diameters. There is a decrease in pore volume as well as in surface area by increasing the temperature of preparation. Nevertheless, the electrochemical activity of the composite increases with an increase in temperature. The discharge capacity values of the samples prepared at 800 and 900 degrees C are about 250 mAh g(-1) at a specific current of 40 mA g(-1) with an excellent cycling stability. A value of 225 mAh g(-1) is obtained at the end of 30 charge-discharge cycles. Both these composite samples possess high rate capability, but the 800 degrees C sample is marginally superior to the 900 degrees C sample. A discharge capacity of 100 mAh g(-1) is obtained at a specific current of 1000 mA g(-1). The high rate capability is attributed to porous nature of the composite samples. (C) 2013 The Electrochemical Society. All rights reserved.
Resumo:
The Y3Fe5O12 (YIG) nanopowders were synthesised at different pH using co-precipitation method. The effect of pH on the phase formation of YIG is characterised using XRD, TEM, FTIR and TG/DTA. From the Scherer formula, the particle sizes of the powders were found to be 13, 19 and 28 nm for pH=10, 11 and 12 respectively. It is found that as the pH of the solution increase the particle size is also increases. It is also clear from the TG/DTA curves that as the pH is increasing the weight losses were found to be small. The nanopowders were sintered at 600, 700, 800 and 900 degrees C for 5 h using conventional sintering method. The phase formation is completed at 800 degrees C/5 h which is correlated with TG/DTA. The average grain size of the samples is found to be similar to 161 nm. The high values of M-s=23 emu g(-1) and H-c=22 Oe were recorded for the sample sintered at 900 degrees C.
Resumo:
In this article, we analyse several discontinuous Galerkin (DG) methods for the Stokes problem under minimal regularity on the solution. We assume that the velocity u belongs to H-0(1)(Omega)](d) and the pressure p is an element of L-0(2)(Omega). First, we analyse standard DG methods assuming that the right-hand side f belongs to H-1(Omega) boolean AND L-1(Omega)](d). A DG method that is well defined for f belonging to H-1(Omega)](d) is then investigated. The methods under study include stabilized DG methods using equal-order spaces and inf-sup stable ones where the pressure space is one polynomial degree less than the velocity space.
Resumo:
We demonstrate an electrochemical technique for the large scale synthesis of high quality few layer graphene sheets (FLGS) directly from graphite using oxalic acid (a weak acid) as the electrolyte. One of the interesting observations is that the FLGS are stable at least up to 800 degrees C and hence have potential application in solid oxide fuel cells as a gas diffusion layer.