Orthorhombic-tetragonal phase coexistence and enhanced piezo-response at room temperature in Zr, Sn, and Hf modified BaTiO3

The effect of Zr, Hf, and Sn in BaTiO3 has been investigated at close composition intervals in the dilute concentration limit. Detailed structural analysis by x-ray and neutron powder diffraction revealed that merely 2mol. % of Zr, Sn, and Hf stabilizes a coexistence of orthorhombic (Amm2) and tetragonal (P4mm) phases at room temperature. As a consequence, all the three systems show substantial enhancement in the longitudinal piezoelectric coefficient (d(33)), with Sn modification exhibiting the highest value similar to 425 pC/N. (C) 2014 AIP Publishing LLC.

Room temperature ferromagnetic and ferroelectric properties of Bi1-xCaxMnO3 thin films

Bi1-xCaxMnO3 (BCMO) thin films with x = 0, 0.1, 0.2, 0.3 and 0.4 are successfully deposited on the n-type Si (100) substrate at two different temperatures of 400 degrees C and 800 degrees C using RF magnetron sputtering. The stoichiometry of the films and oxidation state of the elements have been described by X-ray photoelectron spectroscopy analysis. Dielectric measurement depicts the insulating property of BCMO films. Magnetic and ferroelectric studies confirm the significant enhancement in spin orientation as well as electric polarization at room temperature due to incorporation of Ca2+ ions into BiMnO3 films. The BCMO (x = 0.2) film grown at 400 degrees C shows better magnetization (M-sat) and polarization (P-s) with the measured values of 869 emu / cc and 6.6 mu(C)/cm(2) respectively than the values of the other prepared films. Thus the realization of room temperature ferromagnetic and ferroelectric ordering in Ca2+ ions substituted BMO films makes potentially interesting for spintronic device applications. (C) 2014 Author(s).

Observation of Room Temperature Ferromagnetism in InN Nanostructures

The room temperature ferromagnetic behavior of InN nanosfructures grown by molecular beam epitaxy (MBE) is explored by means of magnetization measurements. The saturation magnetization and remanent magnetization are found to be strongly dependent on the size of the nanostructures. This suggests that the ferromagnetism is essentially confined to the surface of the nanostructures due to the possible defects. Raman spectroscopy shows the existence of indium vacancies which could be the source of ferromagnetic ordering in InN nanostructures.

Room Temperature-Processed TiO2 MIM Capacitors for DRAM Applications

We report the room temperature fabrication of Ta/TiO2/Ta metal-insulator-metal (MIM) capacitors (mainly, for DRAM applications). The fabricated devices show high capacitance density (similar to 15 fF/mu m(2)), and low leakage current density of 6.4 X 10(-8) A/cm(2) (27 degrees C) and 3.3 x 10(-6) A/cm(2) (125 degrees C) at -1 V. We analyze the electrical and material characteristics of the fabricated capacitors, and compare the device performance of these capacitors with other TiO2 and TiO2-based MIM capacitors reported in recent literature.

Room Temperature Growth of Ultrathin Au Nanowires with High Areal Density over Large Areas by in Situ Functionalization of Substrate

Although ultrathin Au nanowires (similar to 2 nm diameter) are expected to demonstrate several interesting properties, their extreme fragility has hampered their use in potential applications. One way to improve the stability is to grow them on substrates; however, there is no general method to grow these wires over large areas. The existing methods suffer from poor coverage and associated formation of larger nanoparticles on the substrate. Herein, we demonstrate a room temperature method for growth of these nanowires with high coverage over large areas by in situ functionalization of the substrate. Using control experiments, we demonstrate that an in situ functionalization of the substrate is the key step in controlling the areal density of the wires on the substrate. We show that this strategy works for a variety of substrates ranging like graphene, borosil glass, Kapton, and oxide supports. We present initial results on catalysis using the wires grown on alumina and silica beads and also extend the method to lithography-free device fabrication. This method is general and may be extended to grow ultrathin Au nanowires on a variety of substrates for other applications.

Rapid reduction of GO by hydrogen spill-over mechanism by in situ generated nanoparticles at room temperature and their catalytic performance towards 4-nitrophenol reduction and ethanol oxidation

Here, we report the clean and facile synthesis of Pt and Pd nanoparticles decorated on reduced graphene oxide (rGO) by the simultaneous reduction of graphene oxide (GO) and the metal ions in Mg/acid medium. As-generated Pt and Pd nanoparticles serve as a heterogeneous catalyst for the further reduction of the rGO by the hydrogen spill-over process. The C/O ratio is much higher as compared to the rGO obtained by the reduction of GO by only Mg/acid. Overall, the process is rapid, facile and green that does not require any toxic chemical agent or any rigorous chemical reactions. We perform the catalytic reduction of 4-nitophenol (4-NP) to 4-aminophenol (4-AP) at room temperature by Pd@rGO and Pt@rGO. The reduction is complete within 35 s for Pd@rGO and 60 s for Pt@rGO when 50 mu g of hybrid catalyst is used for 0.5 ml of 1 mM of 4-NP. In case of ethanol oxidation, the current density for Pd@rGO is comparable to commercial Pt/C but is doubled for Pt@rGO. Overall, both structures show highly stable catalytic activity compared to commercial Pt/C. (C) 2014 Elsevier B.V. All rights reserved.

Room-temperature bandlike transport and Hall effect in a high-mobility ambipolar polymer

The advent of a new class of high-mobility semiconducting polymers opens up a window to address fundamental issues in electrical transport mechanism such as transport between localized states versus extended state conduction. Here, we investigate the origin of the ultralow degree of disorder (E-a similar to 16 meV) and the ``bandlike'' negative temperature (T) coefficient of the field effect electron mobility: mu(e)(FET) (T) in a high performance (mu(e)(FET) > 2.5 cm(2) V-1 s(-1)) diketopyrrolopyrrole based semiconducting polymer. Models based on the framework of mobility edge with exponential density of states are invoked to explain the trends in transport. The temperature window over which the system demonstrates delocalized transport was tuned by a systematic introduction of disorder at the transport interface. Additionally, the Hall mobility (mu(e)(Hall)) extracted from Hall voltage measurements in these devices was found to be comparable to field effect mobility (mu(e)(FET)) in the high T bandlike regime. Comprehensive studies with different combinations of dielectrics and semiconductors demonstrate the effectiveness of rationale molecular design, which emphasizes uniform-energetic landscape and low reorganization energy.

Metastable monoclinic and orthorhombic phases and electric field induced irreversible phase transformation at room temperature in the lead-free classical ferroelectric BaTiO3

For decades it has been a well-known fact that among the few ferroelectric compounds in the perovskite family, namely, BaTiO3, KNbO3, PbTiO3, and Na1/2Bi1/2TiO3, the dielectric and piezoelectric properties of BaTiO3 are considerably higher than the others in polycrystalline form at room temperature. Further, similar to ferroelectric alloys exhibiting morphotropic phase boundary, single crystals of BaTiO3 exhibit anomalously large piezoelectric response when poled away from the direction of spontaneous polarization at room temperature. These anomalous features in BaTiO3 remained unexplained so far from the structural standpoint. In this work, we have used high-resolution synchrotron x-ray powder diffraction, atomic resolution aberration-corrected transmission electron microscopy, in conjunction with a powder poling technique, to reveal that at 300 K (i) the equilibrium state of BaTiO3 is characterized by coexistence of metastable monoclinic Pm and orthorhombic (Amm2) phases along with the tetragonal phase, and (ii) strong electric field switches the polarization direction from the 001] direction towards the 101] direction. These results suggest that BaTiO3 at room temperature is within an instability regime, and that this instability is the fundamental factor responsible for the anomalous dielectric and piezoelectric properties of BaTiO3 as compared to the other homologous ferroelectric perovskite compounds at room temperature. Pure BaTiO3 at room temperature is therefore more akin to lead-based ferroelectric alloys close to the morphotropic phase boundary where polarization rotation and field induced ferroelectric-ferroelectric phase transformations play a fundamental role in influencing the dielectric and piezoelectric behavior.

On the Room Temperature Ferromagnetic and Ferroelectric Properties of Pb(Fe1/2Nb1/2)O-3

We report the origin of room temperature (RT) ferromagnetic and ferroelectric properties of Pb(Fe1/2Nb1/2)O-3 (PFN) ceramic sample prepared by modified solid-state reaction synthesis by a single-step method, based on X-ray diffraction (XRD), neutron diffraction (ND), Mossbauer spectroscopy and electron paramagnetic resonance (EPR) spectroscopy results. Formation of single-phase monoclinic PFN ceramic with Cm space group was confirmed by XRD and ND at RT. The morphology studied by scanning electron microscopy (SEM) confirmed uniform microstructure of the sample with average grain size of similar to 2 mu m. The ND, Mossbauer spectroscopy, M-H loop and EPR studies were carried out to confirm the existence of weak ferromagnetism at RT. A clear opening of hysteresis (M-H) loop is evidenced as the existence of weak ferromagnetism at RT. EPR spectrum clearly shows the ferromagnetism through a good resonance signal. The symmetric EPR line shape with g = 1.9895 observed in PFN sample was identified to be due to Fe3+ ions. Mossbauer spectroscopy at RT shows superparamagnetic behaviour with presence of Fe in 3+ valence state. Ferroelectric P-E loops on PFN at RT confirm the existing ferroelectric ordering. Our observation is in agreement with literature, and it supports that the origin of ferromagnetism and ferroelectricity is isolated, i.e. from different regions in the sample. Our results do not support the multiferroic nature of PFN at RT.

Al based ultra-fine eutectic with high room temperature plasticity and elevated temperature strength

Developments of aluminum alloys that can retain strength at and above 250 degrees C present a significant challenge. In this paper we report an ultrafine scale Al-Fe-Ni eutectic alloy with less than 3.5 aa transition metals that exhibits room temperature ultimate tensile strength of similar to 400 MPa with a tensile ductility of 6-8%. The yield stress under compression at 300 degrees C was found to be 150 MPa. We attribute it to the refinement of the microstructure that is achieved by suction casting in copper mold. The characterization using scanning and transmission electron microscopy (SEM and TEM) reveals an unique composite structure that contains the Al-Al3Ni rod eutectic with spacing of similar to 90 nm enveloped by a lamellar eutectic of Al-Al9FeNi (similar to 140 nm). Observation of subsurface deformation under Vickers indentation using bonded interface technique reveals the presence of extensive shear banding during deformation that is responsible for the origin of ductility. The dislocation configuration in Al-Al3Ni eutectic colony indicates accommodation of plasticity in alpha-Al with dislocation accumulation at the alpha-Al/Al3Ni interface boundaries. In contrast the dislocation activities in the intermetallic lamellae are limited and contain set of planner dislocations across the plates. We present a detailed analysis of the fracture surface to rationalize the origin of the high strength and ductility in this class of potentially promising cast alloy. (C) 2015 Elsevier B.V. All rights reserved.

Imaging cellular signalling: many `moving tales' in MAP kinase odyssey

Cellular signalling events are at the core of every adaptive response. Signalling events link environmental changes to physiological responses, consequently allowing cellular and organismal sustenance and survival. Classical approaches to study cellular signalling have relied on a variety of cell disruptive techniques which yield limited kinetic information, while the underlying events are much more complex. In this article, we discuss how modern live cell imaging microscopy has found increasing utilization in revealing spatio temporal dynamics of various signalling pathways. Utilizing the well studied mitogen-activated protein kinase (MAPK) signalling cascade as a template, the design, construction and utilization of `mobile' (translocation proficient) biosensors, suitable for studying MAPK signalling in living cells are described in detail. Experimental setup and results obtained from these biosensors, based on different proteins involved in the MAPK signalling cascade, have been described along with the setup of a microscope optimal for live cell imaging applications. Utilizing the ability to activate or deactivate signalling pathways using defined activators and specific pharmacological inhibitors, we also show how these sensors can yield unique spatial and temporal kinetic information of signalling in living cells.

Effect of ultra-fast mixing in a microchannel due to a soft wall on the room temperature synthesis of gold nanoparticles

The room-temperature synthesis of mono-dispersed gold nanoparticles, by the reduction of chlorauric acid (HAuCl4) with tannic acid as the reducing and stabilizing agent, is carried out in a microchannel. The microchannel is fabricated with one soft wall, so that there is a spontaneous transition to turbulence, and thereby enhanced mixing, when the flow Reynolds number increases beyond a critical value. The objective of the study is to examine whether the nanoparticle size and polydispersity can be modified by enhancing the mixing in the microchannel device. The flow rates are varied in order to study nanoparticle formation both in laminar flow and in the chaotic flow after transition, and the molar ratio of the chlorauric acid to tannic acid is also varied to study the effect of molar ratio on nanoparticle size. The formation of gold nanoparticles is examined by UV-visual spectroscopy and the size distribution is determined using scanning electron microscopy. The synthesized nanoparticles size decreases from a parts per thousand yen6 nm to a parts per thousand currency sign4 nm when the molar ratio of chlorauric acid to tannic acid is increased from 1 to 20. It is found that there is no systematic variation of nanoparticle size with flow velocity, and the nanoparticle size is not altered when the flow changes from laminar to turbulent. However, the standard deviation of the size distribution decreases by about 30% after transition, indicating that the enhanced mixing results in uniformity of particle size.

Origin of room temperature weak-ferromagnetism in antiferromagnetic Pb(Fe2/3W1/3)O-3 ceramic

We report the origin of room temperature weak ferromagnetic behavior of polycrystalline Pb(Fe2/3W1/3)O-3 (PFW) powder. The structure and magnetic properties of the ceramic powder prepared by a Columbite method were characterized by X-ray and neutron diffraction, Mossbauer spectroscopy and magnetization measurements. Rietveld analysis of diffraction data confirm the formation of single phase PFW, without traces of any parasitic pyrochlore phase. PFW was found to crystallize in the cubic structure at room temperature. The Rietveld refinement of neutron diffraction data measured at room temperature confirmed the G-type antiferromagnetic structure of PFW in our sample. However, along with the antiferromagnetic (AFM) ordering of the Fe spins, we have observed the existence of weak ferromagnetism at room temperature through: (i) a clear opening of hysteresis (M-H) loop, (ii) bifurcation of the field cooled and zero-field cooled susceptibility; supported by Mossbauer spectroscopy results. The P-E loop measurements showed a non-linear slim hysteresis loop at room temperature due to the electronic conduction through the local inhomogeneities in the PFW crystallites and the inter-particle regions. By corroborating all the magnetic measurements, especially the spin glass nature of the sample, with the conduction behavior of the sample, we report here that the observed ferromagnetism originates at these local inhomogeneous regions in the sample, where the Fe-spins are not perfectly aligned antiferromagnetically due to the compositional disordering. (C) 2015 Elsevier Ltd and Techna Group S.r.l. All rights reserved.

Organic alloys of room temperature liquids thiophenol and selenophenol

The first examples of organic alloys of two room temperature liquids, obtained and characterized via in situ cryo-crystallography, are presented. Thiophenol and selenophenol, which exhibit isostructurality and similar modes of S center dot center dot center dot S and Se center dot center dot center dot Se homo-chalcogen interactions along with weak and rare S-H center dot center dot center dot S and Se-H center dot center dot center dot Se hydrogen bonds, are shown to form solid solutions exhibiting Veggard's law-like trends.

Mg/BN nanocomposites: Nano-BN addition for enhanced room temperature tensile and compressive response

The present study elucidates the effects of nanoscale boron nitride particles addition on the microstructural and mechanical characteristics of monolithic magnesium. Novel light-weight Mg nanocomposites containing 0.3, 0.6 and 1.2vol% nano-size boron nitride particulates were synthesized using the disintegrated melt deposition method followed by hot extrusion. Microstructural characterization of developed Mg/x-boron nitride composites revealed significant grain refinement due to the uniform distribution of nano-boron nitride particulates. Texture analysis of selected Mg-1.2 boron nitride nanocomposite showed an increase in the intensity of fiber texture alongside enhanced localized recrystallization when compared to monolithic Mg. Mechanical properties evaluation under indentation, tension and compression loading indicated superior response of Mg/x-boron nitride composites in comparison to pure Mg. The uniform distribution of nanoscale boron nitride particles and the modified crystallographic texture achieved due to the nano-boron nitride addition attributes to the superior mechanical characteristics of Mg/boron nitride nanocomposites.