Natural Abundant Solid State NMR Studies in Designed Tripeptides for Differentiation of Multiple Conformers

Solid state NMR (SSNMR) experiments on heteronuclei in natural abundance are described for three synthetically designed tripeptides Piv-(L)Pro_(L)Pro-(L)Phe-OMe (1), Piv-(D)Pro_(L)Pro_(L)Phe-OMe (2), and Piv-(D)Pro_(L)Pro_(L)Phe-NHMe (3). These peptides exist in different conformation as shown by solution state NMR and single crystal X-ray analysis (Chatterjee et al., Chem Eur J 2008, 14, 6192). In this study, SSNMR has been used to probe the conformations of these peptides in their powder form. The C-13 spectrum of peptide (1) showed doubling of resonances corresponding to cis/cis form, unlike in solution where the similar doubling is attributed to cis/trans form. This has been confirmed by the chemical shift differences of C-beta and C-gamma carbon of Proline in peptide (1) both in solution and SSNMR. Peptide (2) and (3) provided single set of resonances which represented all transform across the di-Proline segment. The results are In agreement with the X-ray analysis. Solid state N-15 resonances, especially from Proline residues provided additional information, which is normally not observable in solution state NMR. H-1 chemical shifts are also obtained from a two-dimensional heteronuclear correlation experiment between H-1-C-13. The results confirm the utility of NMR as a useful tool for identifying different conformers in peptides in the solid state. (C) 2009 Wiley Periodicals, Inc. Biopolymers 91: 851-860, 2009.

Mechanoformation of ammonium perchlorate-potassium perchlorate solid solutions

Ammonium perchlorate-potassium perchlorate mixtures, upon pelletization, form a series of homogeneous solid solutions as manifested by X-ray powder diffractograms. Scanning electron microscopic studies throw light on the mechanism of the solid-solution formation. Solid solutions of ammonium perchlorate-potassium perchlorate have also been obtained by a modified cocrystallization technique. The thermal and combustion behavior of the solid solutions have also been studied, using the DTA technique and the Crawford strand burner.

The UPAL process: a direct method of preparing cast aluminium alloy-graphite particle composites

A direct method of preparing cast aluminium alloy-graphite particle composites using uncoated graphite particles is reported. The method consists of introducing and dispersing uncoated but suitably pretreated graphite particles in aluminium alloy melts, and casting the resulting composite melts in suitable permanent moulds. The optical pretreatment required for the dispersion of the uncoated graphite particles in aluminium alloy melts consists of heating the graphite particles to 400° C in air for 1 h just prior to their dispersion in the melts. The effects of alloying elements such as Si, Cu and Mg on the dispersability of pretreated graphite in molten aluminium have also been reported. It was found that additions of about 0.5% Mg or 5% Si significantly improve the dispersability of graphite particles in aluminium alloy melts as indicated by the high recoveries of graphite in the castings of these composites. It was also possible to disperse upto 3% graphite in LM 13 alloy melts and retain the graphite particles in a well distributed fashion in the castings using the pre-heat-treated graphite particles. The observations in this study have been related to the information presently available on wetting between graphite and molten aluminium in the presence of different elements and our own thermogravimetric analysis studies on graphite particles. Physical and mechanical properties of LM 13-3% graphite composite made using pre-heat-treated graphite powder, were found to be adequate for many applications, including pistons which have been successfully used in internal combustion engines.

Photocatalytic activity of Ag-substituted and impregnated nano-TiO2

Ag-substituted (Ag sub) and Ag-impregnated (Ag imp), anatase phase nano-TiO2 have been synthesized by solution combustion technique and reduction technique, respectively. The catalysts were characterized extensively by powder XRD, TEM, XPS, FT-Raman, UV absorption, FT-IR, TGA, photoluminescence, BET surface area and isoelectric pH measurements. These catalysts were used for the photodegradation of dyes and for the selective photooxidation of cyclohexane to cyclohexanone. The photoactivities of the combustion-synthesized catalysts were compared with those of commercial Degussa P 25 (DP 25) TiO2, and Ag-impregnated DP 25 (Ag DP). For the photocatalytic degradation of dyes, unsubstituted combustion-synthesized TiO2 (CS TiO2) exhibited the highest activity, followed by 1% Ag imp and 1% Ag sub. For the photoconversion of cyclohexane, the total conversion of cyclohexane and the selectivity of cyclohexanone followed the order: 1% Ag sub > DP 25 > CS TiO2 > 1% Ag imp > 1% Ag DP. The kinetics of the photodegradation of dyes and of the photooxidation of cyclohexane were modeled using Langmuir–Hinshelwood rate equation and a free radical mechanism, respectively, and the rate coefficients were determined. The difference in activity values of the catalysts observed for these two reactions and the detailed characterization of these catalysts are described in this study.

Preparation, Characterisation and Thermal Properties of Hydrazinium Magnesium Sulfate

Hydrazinium magnesium sulfate, (N2H5)2Mg(SO4)2, has been prepared by dissolving magnesium powder in a solution of ammonium sulfate in hydrazine hydrate, by the reaction of ammonium magnesium sulfate with hydrazine hydrate, and by the cocrystallisation of dihydrazinium sulfate and magnesium sulfate. The product has been characterized by chemical analysis and infrared spectra. Thermal analysis of (N2H5)2Mg(SO4)2 by TG and DTA show exothermic decomposition at 302°C giving Mg(N2H4)SO4 as an intermediate and an endother-mic decomposition at 504°C producing MgSO4.

Thermal decomposition of rare-earth trioxalatocobaltates

The thermal decomposition of rare-earth trioxalatocobaltates LnCo(C2O4)3 · x H2O, where Ln = La, Pr, Nd, has been studied in flowing atmospheres of air/oxygen, argon/ nitrogen, carbon dioxide and a vacuum. The compounds decompose through three major steps, viz. dehydration, decomposition of the oxalate to an intermediate carbonate, which further decomposes to yield rare-earth cobaltite as the final product. The formation of the final product is influenced by the surrounding gas atmosphere. Studies on the thermal decomposition of photodecomposed lanthanum trioxalatocobaltate and a mechanical mixture of lanthanum oxalate and cobalt oxalate in 1 : 2 molar ratio reveal that the decomposition behaviour of the two samples is different. The drawbacks of the decomposition scheme proposed earlier have been pointed out, and logical schemes based on results obtained by TG, DTA, DTG, supplemented by various physico-chemical techniques such as gas and chemical analyses, IR and mass spectroscopy, surface area and magnetic susceptibility measurements and X-ray powder diffraction methods, have been proposed for the decomposition in air of rare-earth trioxalatocobaltates as well as for the photoreduced lanthanum salt and a mechanical mixture of lanthanum and cobalt oxalates.

Production of cast aluminium-graphite particle composites using a pellet method

Copper- and nickel-coated graphite particles can be successfully introduced into aluminium-base alloy melts as pellets to produce cast aluminium-graphite particle composites. The pellets were made by pressing mixtures of nickel- or copper-coated graphite particles and aluminium powders together at pressures varying between 2 and 20 kg mm–2. These pellets were dispersed in aluminium alloy melts by plunging and holding them in the melts using a refractory coated mild steel cone, until the pellets disintegrated and the powders were dispersed. The optimum pressure for the preparation of pellets was 2 to 5 kg mm–2 and the optimum size and percentage of aluminium powder were 400 to 1000mgrm and 35 wt% respectively. Under optimum conditions the recovery of the graphite particles in the castings was as high as 96%, these particles being pushed into the last freezing interdendritic regions. The tensile strength and the hardness of the graphite aluminium alloys made using the pellet method are comparable to those of similar composites made using gas injection or the vortex method. The pellet method however has the advantage of greater reproducibility and flexibility. Dispersion of graphite particles in the matrix of cast aluminium alloys using the pellet method increases their resistance to wear.

Thermal decomposition of titanyl oxalates-I : Barium titanyl oxalate

Thermal decomposition of barium titanyl oxalate tetrahydrate (BTO) has been investigated employing TGA, DTG and DTA techniques and gas and chemical analysis. The decomposition proceeds through five steps and is not affected much by the surrounding gas atmosphere. The first step which is the dehydration of the tetrahydrate is followed by a low-temperature decomposition of the oxalate groups. In the temperature range 190–250°C half a mole of carbon monoxide is evolved with the formation of a transient intermediate containing both oxalate and carbonate groups. The oxalate groups are completely destroyed in the range 250–450°C, resulting in the formation of a carbonate which retains free carbon dioxide in the matrix. The trapped carbon dioxide is released in the temperature range of 460–600°C. The final decomposition of the carbonate takes place between 600–750°C and yields barium titanate. The i.r. spectra, surface area measurements and X-ray, powder diffraction data support entrapment of carbon dioxide in the matrix.

Carbon-Supported Pt-TiO2 as a Methanol-Tolerant Oxygen-Reduction Catalyst for DMFCs

Carbon-supported Pt-TiO2 (Pt-TiO2/C) catalysts with varying at. wt ratios of Pt to Ti, namely, 1:1, 2:1, and 3:1, are prepared by the sol-gel method. The electrocatalytic activity of the catalysts toward oxygen reduction reaction (ORR), both in the presence and absence of methanol, is evaluated for application in direct methanol fuel cells (DMFCs). The optimum at. wt ratio of Pt to Ti in Pt-TiO2/C is established by fuel cell polarization, linear sweep voltammetry, and cyclic voltammetry studies. Pt-TiO2/C heattreated at 750 degrees C with Pt and Ti in an at. wt ratio of 2:1 shows enhanced methanol tolerance, while maintaining high catalytic activity toward ORR. The DMFC with a Pt-TiO2/C cathode catalyst exhibits an enhanced peak power density of 180 mW/cm(2) in contrast to the 80 mW/cm(2) achieved from the DMFC with carbon-supported Pt catalyst while operating under identical conditions. Complementary data on the influence of TiO2 on the crystallinity of Pt, surface morphology, and particle size, surface oxidation states of individual constituents, and bulk and surface compositions are also obtained by powder X-ray diffraction, scanning and transmission electron microscopy, X-ray photoelectron spectroscopy, energy dispersive analysis by X-ray, and inductively coupled plasm optical emission spectrometry.

Synthesis, Structural Characterization and Formation Mechanism of Ferroelectric Bismuth Vanadate Nanotubes

We report the synthesis and structural characterization of ferroelectric bismuth vanadate (Bi2VO5.5) (BVO) nanotubes within the nanoporous anodic aluminum oxide (AAO) templates via sol-gel method. The as-prepared BVO nanotubes were characterized by X-ray powder diffraction (XRD), Scanning Electron Microscope (SEM), High-Resolution Transmission Electron Microscope (HRTEM) and the stoichiometry of the nanotubes was established by energy-dispersive X-ray spectroscopy (EDX). Postannealed (675 degrees C for 1 h), BVO nanotubes were a polycrystalline and the XRD studies confirmed the crystal structure to be orthorhombic. The uniformity in diameter and length of the nanotubes as reveled by the TEM and SEM suggested that these were influenced to a guest extent by the thickness and pore diameter of the nanoporous AAO template. EDX analysis demonstrated the formation of stoichiometric Bi2VO5.5 phase. HRTEM confirmed that the obtained BVO nanotubes were made up of nanoparticles of 5-9 nm range. The possible formation mechanism of nanotubes was elucidated.

The plant Banjauri (Vicoa indica) exhibits antifertility activity in adult female bonnet monkeys (Macaca radiata)

The antifertility activity of the plant Vicoa indica was tested in proven fertile bonnet monkeys. The dry powder of the whole plant was fed to the cycling monkeys on day 1 to 14 of menstrual cycle or day 9 to 14 of cycle or on day 2 to 5 after delivery and the fertility was evaluated in the following cycle in cycle fed monkey or after weaning the young one in the post-partum fed monkeys. Results indicated that while feeding in the post-partum monkeys did not confer any protection against pregnancy feeding during day 1 to 14 of cycle, protected from pregnancy. The monkeys did not become pregnant even after exposure to the proven fertile male monkeys for 13 ovulatory cycles while all the vehicle fed monkeys became pregnant within 3 cycles.

Structural, dielectric, impedance and optical properties of CaBi2B2O7 glasses and glass-nanocrystal composites

Optically clear glasses were fabricated by quenching the melt of CaCO3-Bi2O3-B2O3 (in equimolecular ratio). The amorphous and glassy characteristics of the as-quenched samples were confirmed via the X-ray powder diffraction (XRD) and differential scanning calorimetric (DSC) studies These glasses were found to. have high thermal stability parameter (S). The optical transmission studies carried out in the 200-2500 nm wavelength range confirmed both the as-quenched and heat-treated samples to be transparent between 400 nm and 2500 nm. The glass-plates that were heat-treated just above the glass transition temperature (723 K) for 6 h retained approximate to 60% transparency despite having nano-crystallites (approximate to 50-100 nm) of CaBi2B2O7 (CBBO) as confirmed by both the XRD and transmission electron microscopy (TEM) studies. The dielectric properties and impedance characteristics of the as-quenched and heat-treated (723 K/6 h) samples were studied as a function of frequency at different temperatures. Cole-Cole equation was employed to rationalize the impedance data.

Synthesis, structural and ferromagnetic properties of La1-xKxMnO3 (0.0 <= x <= 0.25) phases by solution combustion method

We describe the solution combustion synthesis and characterization of La1-xKxMnO3 (0.0 <= x <= 0.25) perovskite phases, which is a low temperature initiated, rapid route to prepare metal oxides. As-synthesized compounds are amorphous in nature; crystallinity was observed on heating at 800 degrees C for 5 min. Structural parameters were determined by the Rietveld refinement method using powder XRD data. Parent LaMnO3 compound crystallizes in the orthorhombic structure (space group Pbnm, No. 62). Potassium substituted compounds were crystallized with rhombohedral symmetry (space group R-3c, No. 167). The ratio of the Mn3+/Mn4+ was determined by the iodometric titration. The Fourier transform infrared spectrum (FTIR) shows two absorption bands for Mn-O stretching vibration (v, mode), Mn-O-Mn deformation vibration (v(b) mode) around 600 cm(-1) and 400 cm(-1) for the compositions, x = 0.0, 0.05 and 0-10. Four-probe electrical resistivity measurements reveal a composition controlled metal to insulator transition (TM-1), the maximum TM-1 was observed for the composition La0.85K0.15MnO3 at 287 K. Room temperature vibrating sample magnetometer data indicate that for the composition up to x = 0-10, the compounds are paramagnetic whereas composition with x = 0.15, 0.20 and 0.25 show magnetic moments of 27, 29 and 30 emu/g, respectively.

Spinodal Decomposition in Tellurite-Based Glasses Induced by Excimer Laser Irradiation

Tellurite-based glasses in the TeO2-K3Li2Nb5O15, TeO2-Ba5Li2Ti2Nb8O30, and V2Te2O9 were fabricated by the conventional melt-quenching technique. Amorphous and glassy characteristics of the as-quenched samples were established via the X-ray powder diffraction technique and differential thermal analysis, respectively. The as-quenched samples were irradiated by an excimer laser (248 nm). The effect of laser power, duration of irradiation, and the frequency of the laser pulses on the surface features of the above glasses were studied. The optical microscopic studies carried out on the above systems revealed the presence of quasi-periodic and periodic structures on their surfaces. The local compositional variations of these structures were confirmed by back-scattered electron imaging using scanning electron microscope accompanied by energy-dispersive X-ray analysis. These results were convincing enough to state that the glasses in the present investigations had undergone spinodal decomposition on laser irradiation. The incidence of the interconnected texture of two different phases was observed owing to the quenching effect produced by the heating and cooling cycle of the successive laser pulses. Ring- and line-shaped patterns were also observed, respectively, when the pulse frequency of the laser and the duration of irradiation were increased.

Possible mechanism of charge transport and dielectric relaxation in SrO-Bi2O3-B2O3 glasses

Transparent SrBi2B2O7 glasses were prepared via melt-quenching technique and characterized using differential scanning calorimetry and x-ray powder diffraction. The ac conductivities of the glasses were studied as a function of frequency (100 Hz-10 MHz) at different temperatures. The frequency dependence of conductivity has been analyzed using Almond-West expression. The exponent n was nearly unaffected by temperature. Impedance and modulus spectroscopies were employed to further examine the electrical data. Dielectric relaxation exhibited a stretched exponential behavior with a stretching exponent beta independent of temperature. From conductivity analysis we have proposed that the charge transport occurs through the participation of nonbridging oxygen (NBO), which switches positions in a facile manner. The stretched exponential behavior appears to be a direct consequence of the NBO switching mechanism of charge transport.