Preparation of the layered double hydroxide (LDH) LiAl2(OH)(7)center dot 2H(2)O, by gel to crystallite conversion and a hydrothermal method, and its conversion to lithium aluminates

A layered double hydroxide (LDH) with chemical composition LiAl2(OH)(7) . 2H(2)O was prepared via a wet chemical route of gel to crystallite (G-C) conversion at 80 degrees C involving the reaction of hydrated alumina gel, Al2O3.yH(2)O (80 < y < 120) with LiOH (Li2O/Al2O3 greater than or equal to 0.5) in presence of hydrophilic solvents such as ethanol under refluxing conditions. The hydrothermal synthesis was carried out using the same reactants by heating to less than or equal to 140 degrees C in a Teflon-lined autoclave under autogenerated pressure (less than or equal to 20 MPa). Transmission electron microscopy showed needle-shaped aggregates of size 0.04-0.1 mu m for the gel to crystallite conversion product, whereas the hydrothermal products consisted of individual lamellar crystallites of size 0.2-0.5 mu m with hexagonal morphology. The LDH prepared through the gel to crystallite conversion could be converted into LiAl(OH)(4) . H2O or LiAl(OH)(3)NO3 . H2O by imbibition of LiOH or LiNO3, respectively, under hydrothermal conditions. Thermal decomposition of LDH above 1400 degrees C gave rise to LiAl5O8 accompanied by the evaporation of Li2O. LiAl(OH)(4) . H2O and LiAl(OH)(3)NO3 . H2O decomposed in the temperature range 400-1000 degrees C to alpha- or beta-LiAlO2. The compositional dependence of the product, the intermediate phases formed during the heat treatment and the possible reactions involved are described in detail.

Synthesis and structural characterization of perovskite 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) nanotubes

We report the synthesis and structural characterization of 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) (PMN-PT) nanotubes prepared by a novel sal-gel template method. X-ray diffraction (XRD) and selected-area electron diffraction (SAED) investigations demonstrated that the postannealed (650 degrees C for 1 h) PMN-PT nanotubes were polycrystalline with perovskite crystal structure. The field emission scanning electron microscope (FE-SEM) shows that as prepared PMN-PT nanotubes were hollow with diameter to be about 200 nm. High resolution transmission electron microscope (HRTEM) analysis confirmed that the obtained PMN-PT nanotubes made up of nanoparticles (10-20 nm) which were randomly aligned in the nanotubes. Energy-dispersive X-ray spectroscopy (EDX) analysis confirmed the stoichiometric 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3). The possible formation mechanism of PMN-PT nanotubes was proposed at the end. (C) 2011 Elsevier B.V. All rights reserved.

Structural evolution and electronic properties of La1+xSr2-xMn2O7

A detailed study of the layered manganite La1+xSr2-xMn2O7 has been performed, establishing that within the composition range 0.1 less than or equal to x less than or equal to 0.45 the phases crystallize in the I4/mmm space group. The evolution of structural parameters with x: in this composition range has been followed using a novel application of an existing program for the Rietveld analysis of powder diffraction data. The structure, a familiar intergrowth of rock-salt (La,Sr)O slabs and double perovskite (La,Sr)(2)Mn2O6 units, is characterized by a reluctance to deform the latter. This manifests as a ''pumping'' of the larger Sr-II ion into the 12-coordinate site of the structure as x is increased. We report these features of the structure as well as electrical transport and magnetic properties, in light of recent observations of giant, negative magnetoresistance in these systems.

Investigation of valence states in the perovskite oxides, LaAFeNbO(6) (A = Ca, Sr)

Compounds of the type, LaAFeNbO(6) (A = Ca Sr) have been synthesized to study the electrical and magnetic properties and to examine valence degeneracy. The results show that valence degeneracy is not operative and the compounds are insulating. Magnetic susceptibility data show that part of the Fe is in Fs(2+) state, thus oxidizing part of Nb4+ to Nb5+ by an internal redox mechanism. The presence of mixed valent Fe is confirmed by Mossbauer spectra. (C) 1999 Elsevier Science B.V. All rights reserved.

LiSr1.65 square 0.35B1.3B ' O-1.7(9) (B = Ti, Zr; B ' = Nb, Ta): New lithium ion conductors based on the perovskite structure

We describe the design and synthesis of new lithium ion conductors with the formula, LiSr(1.65)rectangle(0.35)B(1.3)B'O-1.7(9) (rectangle = vacancy; B = Ti, Zr; B' = Nb, Ta), on the basis of a systematic consideration of the composition-structure-property correlations in the well-known lithium-ion conductor, La-(2/3-x)Li(3x)rectangle((1/3)-2x)TiO3 (I), as well as the perovskite oxides in Li-A-B,B'-O (A = Ca, Sr, Ba; B = Ti, Zr; B' = Nb, Ta) systems. A high lithium-ion conductivity of ca. 0.12 S/cm at 360 degrees C is exhibited by LiSr(1.65)rectangle(0.35)Ti(1.3)Ta(1.7)O(9) (III) and LiSr(1.65)rectangle(0.35)Zr(1.3)Ta(1.7)O(9) (IV), of which the latter containing stable Zr(IV) and Ta(V) oxidation states is likely to be a candidate electrolyte material for all-solid-state lithium battery application. More importantly, we believe the approach described here could be extended to synthesize newer, possibly better, lithium ion conductors.

Magnetism in MnPSe3: a layered 3d(5) antiferromagnet with unusually large XY anisotropy

The anisotropic magnetic susceptibilities of single crystals of the isostructural layered antiferromagnets, MnPS3 (T-N = 78 K) and MnPSe3 (T-N = 74 K), have been measured as functions of temperature. In both compounds, divalent manganese is present in the high-spin S = 5/2 state. The anisotropies in the susceptibilities of the two are, however, very different; while the susceptibility of MnPS3 is isotropic, that of MnPSe3 shows a large XY anisotropy, unusual for a manganese compound. The anisotropic susceptibilities are described by the zero-field spin Hamiltonian: H = DSiz2 - Sigma J(ij).(S) over right arrow (S) over right arrow(j) with the quadratic single-ion anisotropy term introducing anisotropy in an otherwise isotropic situation. The exchange J and the single-ion zero-field-splitting (ZFS) parameter D were evaluated using the correlated effective-field theory of Lines. For MnPSe3, J/k = -5.29 K and D/k = 26.6 K, while for isotropic MnPS3, J/k = -8.1 K. It is suggested that the large value of the ZFS parameter for MnPSe3 as compared to MnPS3 could be due to the large ligand spin-orbit contribution of the heavier selenium.

Magnetoresistance of the metallic perovskite oxide LaNiO3-delta

We report a study of the magnetoresistance (MR) of the metallic perovskite oxide LaNiO3-delta as a function of the oxygen stoichiometry delta (delta less than or equal to 0.14), magnetic field (H less than or equal to 6 T) and temperature (1.5 K less than or equal to T less than or equal to 25 K). We find a strong dependence of the nature of the MR on the oxygen stoichiometry. The MR at low temperatures changes from positive to negative as the sample becomes more oxygen deficient (i.e. delta increases). Some of the samples, which are more resistive, show resistivity minima at T-min approximate to 20 K. We find that in these samples the MR is positive for T > T-min and negative for T < T-min. We conclude that in the absence of strong magnetic interaction, the negative MR in these oxides can arise from weak-localization effects.

A new layered iron fluorophosphate

A new iron fluorophosphate of the composition, [C6N4H21] [Fe2F2(HPO4)(3)][H2PO4](.)2H(2)O, I has been prepared by the hydrothermal route. This compound contains iron fluorophosphate layers and the H2PO4- anions are present in the interlayer space along with the protonated amine and water molecules. The compound crystallizes in the monoclinic space group P2(1)/c. (a = 13-4422(10) Angstrom, b = 9 7320(10) Angstrom, c = 18-3123(3) Angstrom, beta = 92-1480degrees, V = 2393-92(5) Angstrom 3, Z = 4, M = 719-92, d(calc). = 1.997 g cm(-3), R-1 = 0.03 and wR(2) = 0,09).

Crystal structure and thermal and electrical properties of the perovskite solid solution Nd1-xSrxFeO3-delta (0 <= x <= 0.4)

The crystal structure, thermal expansion and electrical conductivity of strontium-doped neodymium ferrite (Nd1-xSrxFeO3-delta where 0less than or equal toxless than or equal to0.4) were investigated. All compositions had the GdFeO3-type orthorhombic perovskite structure. The lattice parameters were determined at room temperature by X-ray powder diffraction. The orthorhombic distortion decreases with increasing Sr substitution. The pseudocubic lattice parameter shows a minimum at x=0.3. The thermal expansion curves for x=0.2-0.4 displayed rapid increase in slope at higher temperatures. The electrical conductivity increased with Sr content and temperature. The calculated activation energies for electrical conduction decreased with increasing x. The electrical conductivity can be described by the small polaron hopping mechanism. The charge compensation for divalent ion on the A-site is provided by the formation of Fe4+ ions on the B site and vacancies on the oxygen sublattice. The results indicate two defect domains: for low values of x, the predominant defect is Fe4+ ions, whereas for higher values of x, oxygen vacancies dominate. (C) 2002 Elsevier Science B.V. All rights reserved.

Organically templated linear and layered cadmium sulfates

By reacting cadmium salts with H2SO4 in the presence of organic amines or directly with amine sulfates under hydrothermal conditions, it has been possible to prepare three linear cadmium sulfates of linarite topology, with the compositions [H3N(CH2)(2)NH3](2)[CdCl2(SO4)][SO4].H2O, I, [HN(CH2)(6)NH][CdBr2(SO4)], II, [HN(CH2)(6)NH][CdCl2-(SO4)], III. A layered cadmium sulfate of composition [H3N(CH2)(3)NH3][Cd-2(H2O)(2)(SO4)(3)], IV, has also been obtained. These sulfates are the first examples of a family of organically templated metal sulfates with interesting structural features. In the linarite chains, the CdX4O2 (X = Cl, Br) octahedron shares two trans-edges to form an [Mphi(4)] (phi = anionic ligand) chain decorated by the SO4 tetrahedron that adopts a staggered arrangement on either side of the chain. IV is constructed by the fusion of four-membered ring ladders involving edge sharing between the sulfate tetrahedron and metal octahedron. IV appears to be the first member of a family of organically templated metal sulfates containing an octahedral-tetrahedral 2D net wherein the sulfate tetrahedron is connected at all four corners.

Spin-orbital ordering and mesoscopic phase separation in the double perovskite Ca2FeReO6

Neutron powder diffraction measurements on Ca2FeReO6 reveal that this double perovskite orders ferrimagnetically and shows anomalous lattice parameter behavior below T-C=521 K. Below similar to300 K and similar to160 K we observe that the high-T monoclinic crystal structure separates into two and three monoclinic phases, respectively. A magnetic field suppresses the additional phases at low T in favor of the highest-T phase. These manifestations of the orbital degree of freedom of Re 5d electrons indicate that these electrons are strongly correlated and the title compound is a Mott insulator, with competing spin-orbitally ordered states.

A layered chlorophosphate, Na-3[Cd4Cl3(HPO4)(2)(H2PO4)(4)], containing Na+ ions in the interlamellar space

Reaction between CdCl2.H2O and NaH2PO4.H2O Under hydrothermal conditions gives rise to a new cadmium chlorophosphate of the formula Na-3[Cd4Cl3(HPO4)(2)(H2PO4)(4)] I. This material crystallizes in the orthorhombic system with space group Fmm2(no. 42). I has macroanionic layers of [Cd4Cl3(HPO4)(2)(H2PO4)(4)](3-) with Na+ ions in the interlamellar space. The discovery of such compounds suggests that metathetic reactions carried out under hydrothermal conditions may provide a novel route for the synthesis of new open-framework structures.

A Layered Zinc Phosphate, [C6N4H22][Zn6(PO4)4(HPO4)2], Formed by One-Dimensional Tubes

An open-framework zinc phosphate, [C6N4H22][Zn6(PO4)4(HPO4)2] (I), with alternating inorganic and organic layers has been synthesized hydrothermally from a starting mixture of ZnO, HCl, H3PO4, H2C2O4, and triethylenetetramine. Single-crystal data for I: monoclinic, space GROUP =P21/c (No. 14), a=9.881(1), b=16.857(1), c=8.286(1) Å, β=96.7(1)°, V=1370.8(1) Å3, Z=2, R1=0.06, and wR2=0.13 [1408 observed reflections with I>2σ(I)]. The structure of I comprises a network of ZnO4, PO4, and PO3(OH) tetrahedra forming one-dimensional tubes. The tubes, in turn, are linked via oxygen atoms forming macroanionic inorganic layers with eight-membered apertures. The one-dimensional tube-like architecture in I is a novel feature worthy of note.

Transformations of two-dimensional layered zinc phosphates to three-dimensional and one-dimensional structures

Transformations of the layered zinc phosphates of the compositions [C6N4H22](0.5) [Zn-2 (HPO4)(3)], I, [C3N2H12][Zn-2 (HPO4)(3)], II and [C3N2OH12][Zn-2 (HPO4)(3)], III, containing triethylenetetramine, 1,3-diaminopropane, and 1,3-diamino-2-hydroxypropane, respectively, have been investigated under different conditions. On heating in water, I transforms to a one-dimensional (1-D) ladder and a three-dimensional (3-D) structure, while II gives rise to only a two-dimensional (2-D) layered structure. In the transformation reaction of I with zinc acetate, the same ladder and 3-D structures are obtained along with a tubular layer. Under similar conditions II gives a layered structure formed by the joining of two ladder motifs. III, on the other hand, is essentially unreactive when heated with water and zinc acetate, probably because the presence of the hydroxy group in the amine which hydrogen bonds to the framework. In the presence of piperazine, I, II and III give rise to a four-membered, corner-shared linear chain which is likely to be formed via the ladder structure. In addition, 2-D and 3-D structures derived from the 1-D linear chain or ladder structures are also formed. The primary result from the study is that the layers produce 1-D ladders, which then undergo other transformations. It is noteworthy that in the various transformations carried out, most of the products are single-crystalline.

Microwave preparation and sintering of industrially important perovskite oxides: LaMO3 (M = Cr, Co, Ni)

Perovskite oxides LaMO3 (M = Cr, Co, Ni), have been successfully prepared using microwaves of 2.45 GHz. Microwave preparation is rapid, clean and energy efficient. Preparation of LaCrO3, LaCoO3 and LaNiO3 has been achieved in 3 min, 5 min and 10 min respectively. Direct reaction between component oxides is used for the preparation of LaCrO3 and LaCoO3, whereas nitrates are used as starting materials for LaNiO3 preparation. Products have been characterized using XRD, IR spectroscopy and SEM. Their dc electrical conductivity has also been studied and their fracture behaviour has been examined. All three microwave prepared oxide powders are of submicron size. These perovskite oxides have been sintered to very high densities using microwaves. Possible mechanisms of the microwave-material interaction both during preparation and during sintering have been discussed.