The role of surface texture on friction and transfer layer formation during repeated sliding of Al-4Mg against steel

In the present investigation, various kinds of textures, namely, unidirectional, 8-ground, and random were attained on the die surfaces. Roughness of the textures was varied using different grits of emery papers or polishing powders. Then pins made of Al-4Mg alloys were slid against steel plates at various numbers of cycles, namely, 1, 3, 5, 10 and 20 using pin-on-plate reciprocating sliding tester. Tests were conducted at a sliding velocity of 2 minis in ambient conditions under both dry and lubricated conditions. A constant normal load of 35 N was applied in the tests. The morphologies of the worn surfaces of the pins and the formation of transfer layer on the counter surfaces were observed using a scanning electron microscope. Surface roughness parameters of the plates were measured using an optical profilometer. In the experiments, it was observed that the coefficient of friction and formation of the transfer layer depend on the die surface textures under both dry and lubricated conditions. More specifically, the coefficient of friction decreases for unidirectional and 8-ground surfaces while for random surfaces it increases with number of cycles. However, the coefficient of friction is highest for the sliding perpendicular to the unidirectional textures and least for the random textures under both dry and lubricated conditions. The difference in friction values between these two surfaces decreases with increasing number of cycles. The variation in the coefficient of friction under both dry and lubrication conditions is attributed to the change in texture of the surfaces during sliding. (C) 2011 Elsevier B.V. All rights reserved.

Friction and transfer layer formation in polymer-steel tribo-system: Role of surface texture and roughness parameters

In the present investigation, various kinds of surface textures were attained on the steel plates. Roughness of the textures was varied using various grinding or polishing methods. The surface textures were characterized in terms of roughness parameters using an optical profilometer. Then experiments were conducted using an inclined pin-on-plate sliding apparatus to identify the role of surface texture and its roughness parameters on coefficient of friction and transfer layer formation. In the experiments, a soft polymer (polypropylene) was used for the pin and hardened steel was used for the plate. Experiments were conducted at a sliding velocity of 2 minis in ambient conditions under both dry and lubricated conditions. The normal load was varied from 1 to 120 N during the tests. The morphologies of the worn surfaces of the pins and the formation of a transfer layer on the steel plate surfaces were observed using a scanning electron microscope. Based on the experimental results, it was observed that the transfer layer formation and the coefficient of friction along with its two components, namely adhesion and plowing, were controlled by the surface texture of the harder mating surfaces and were less dependent of surface roughness (R(a)) of the harder mating surfaces. The effect of surface texture on the friction was attributed to the variation of the plowing component of friction for different surfaces. Among the various surface roughness parameters studied, the mean slope of the profile, Delta(a), was found to most accurately characterize variations in the friction and wear behavior. (C) 2011 Elsevier B.V. All rights reserved.

Possibility of chaos in interval friction experiments of martensites

Wuttig and Suzuki's model on anelastic nonlinearities in solids in the vicinity of martensite transformations is analysed numerically. This model shows chaos even in the absence of applied forcing field as a function of a temperature dependent parameter. Even though the model exhibits sustained oscillations as a function of the amplitude of the forcing term, it does not exactly capture the features of the experimental time series. We have improved the model by adding a symmetry breaking term. The improved model shows period doubling bifurcation as a function of the amplitude of the forcing term. The solutions of our improved model shows good resemblance with the nonsymmetric period four oscillation seen in the experiment. (C) 1999 Elsevier Science B.V. All rights reserved.

A k-epsilon model for turbulent weld pool convection in gas metal arc welding process

In this paper, we present a modified k - epsilon model capable of addressing turbulent weld-pool convection in a GMAW process, taking into account the morphology of the phase change interface during a Gas Metal Arc Welding (GMAW) process. A three-dimensional turbulence mathematical model has been developed to study the heat transfer and fluid flow within the weld pool by considering the combined effect of three driving forces, viz., buoyancy, Lorentz force and surface tension (Marangoni convection). Mass and energy transports by the droplets are considered through the thermal analysis of the electrode. The falling droplet's heat addition to the molten pool is considered to be a volumetric heat source distributed in an imaginary cylindrical cavity ("cavity model") within the weld pool. This nature of heat source distribution takes into account the momentum and the thermal, energy of the falling droplets. The numerically predicted weld pool dimensions both from turbulence and laminar models are then compared with the experimental post-weld results sectioned across the weld axis. The above comparison enables us to analyze the overall effects of turbulent convection on the nature of heat and fluid flow and hence on the weld pool shape/size during the arc welding processes.

Analysis of Strain Rates and Microstructural Evaluation during Metal Forming: Role of Surface Texture and Friction

The surface texture of a die plays an important role in friction during metal forming. In the present study, unidirectional and random surface finishes were produced on hardened steel plate surfaces. To understand the influence of surface texture on friction, experiments were conducted using Al-Mg alloy pins that slid against steel plates of different surface textures. In the sliding experiments, a high coefficient of friction was observed when the pins slid perpendicular to the unidirectional grinding marks and low friction occurred when the pins slid on the random surfaces. Finite element simulations were performed using the measured friction values to understand the stress and strain evolutions in the deforming material using dies with various friction. The numerical results showed that the states of stress and strain rates are strongly influenced by the friction at the interface and hence would influence the final material microstructure. To substantiate the numerical results, laboratory compression tests were conducted. Different surface textures were obtained in order to experience different friction values at different locations. A large variation in the microstructure at these locations was observed during experiments, verifying that surface texture and die friction significantly influence fundamental material formation behavior.

Effect of Interfacial Microstructure of Adsorbed Poly(ethylene glycol) Monooleate on Steel Substrate on Sliding Friction in Oil in Water Emulsion

The concentration of a nonionic surfactant and water pH were varied in an oil-in-water emulsion to minimize the friction coefficient between a steel ball sliding on a steel flat. At a surfactant concentration near the CMC (critical micelle concentration) the oil droplet size was found to be minimum. In this paper we study the microstructure of the surfactant molecules self-assembled on the steel substrate in water to comment on the ability of the surfactant aggregate to attract and retain oil. We find that a near semicylindrical hemimiceller microstructure with hydrocarbon tails projecting into bulk water as obtained at CMC in near neutral water is best able to capture and retain oil in yielding a low coefficient of friction.