Synthesis and structural characterization of perovskite 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) nanotubes

We report the synthesis and structural characterization of 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3) (PMN-PT) nanotubes prepared by a novel sal-gel template method. X-ray diffraction (XRD) and selected-area electron diffraction (SAED) investigations demonstrated that the postannealed (650 degrees C for 1 h) PMN-PT nanotubes were polycrystalline with perovskite crystal structure. The field emission scanning electron microscope (FE-SEM) shows that as prepared PMN-PT nanotubes were hollow with diameter to be about 200 nm. High resolution transmission electron microscope (HRTEM) analysis confirmed that the obtained PMN-PT nanotubes made up of nanoparticles (10-20 nm) which were randomly aligned in the nanotubes. Energy-dispersive X-ray spectroscopy (EDX) analysis confirmed the stoichiometric 0.65Pb(Mg1/3Nb2/3)O-3-0.35PbTiO(3). The possible formation mechanism of PMN-PT nanotubes was proposed at the end. (C) 2011 Elsevier B.V. All rights reserved.

Stereospecific solid-state NaBH4-promoted reduction of 1-methylpentacyclo[5.4.0.0(2,6).0(3,10).0(5,9)]undecane-8,11-dione

NaBH4 reduction of a cage dione proceeds in a stereospecific fashion to give the endo,endo-diol. This reactivity is related to the crystal structure.

Synthesis based on cyclohexadienes. Part-27. Synthesis of functionalized tricyclo[5.2.2.0(1,5)]undecanes

A new methodology for the construction of tricyclo[5.2.2.0(1,5)]undecanes is described from indane-4-carboxylic acids. Birch reduction of indane-4-carboxylic acids followed by conjugation and cycloaddition with alpha-chloroacrylonitrile and hydrolysis lead to the tricyclic compounds 36 and 48 which are intermediates in the eremolactone synthesis.

The effect of preaging on the delayed aging of Al-7Si-0.3Mg

Al-7Si-0.3Mg is a commonly used commercial casting alloy because of its excellent castability combined with good mechanical properties. The post-casting heat treatment is one factor that affects the mechanical properties; during heat treat ment, a delay between solutionizing and artificial aging (delayed aging) leads to a reduction in hardness, ultimate tensile strength, and yield strength in the alloy. The investigation reported here was aimed at understanding the extent to which the harmful effect of delayed aging on hardness/strength can be nullified. The results obtained were explained using Pashley's kinetic model.

Local environmental structures of Mo in the superionic conducting glass (AgI)(0.6)(Ag2MoO4)(0.4) by anomalous X-ray scattering

The anomalous X-ray scattering (AXS) method using Mo K absorption edges has been employed for obtaining the local structural information of superionic conducting glass having the composition (AgI)(0.6)(Ag2MoO4)(0.4). The possible atomic arrangements in the near-neighbor region of this glass were estimated by coupling the results with the least-squares variational analysis so as to reproduce the differential intensity profile for Mo as well as the ordinary scattering profile. The coordination number of oxygen around Mo is found to be about 4 at the distance of 0.180 mn. This implies that the most probable structural entity in the glass is the MoO4 tetrahedral unit which has been proposed based on infrared spectroscopy. The value of the coordination number of I- around Ag+ is estimated as 4.4 at 0.287 nm, suggesting an arrangement similar to that of crystalline or molten AgI.

LiSr1.65 square 0.35B1.3B ' O-1.7(9) (B = Ti, Zr; B ' = Nb, Ta): New lithium ion conductors based on the perovskite structure

We describe the design and synthesis of new lithium ion conductors with the formula, LiSr(1.65)rectangle(0.35)B(1.3)B'O-1.7(9) (rectangle = vacancy; B = Ti, Zr; B' = Nb, Ta), on the basis of a systematic consideration of the composition-structure-property correlations in the well-known lithium-ion conductor, La-(2/3-x)Li(3x)rectangle((1/3)-2x)TiO3 (I), as well as the perovskite oxides in Li-A-B,B'-O (A = Ca, Sr, Ba; B = Ti, Zr; B' = Nb, Ta) systems. A high lithium-ion conductivity of ca. 0.12 S/cm at 360 degrees C is exhibited by LiSr(1.65)rectangle(0.35)Ti(1.3)Ta(1.7)O(9) (III) and LiSr(1.65)rectangle(0.35)Zr(1.3)Ta(1.7)O(9) (IV), of which the latter containing stable Zr(IV) and Ta(V) oxidation states is likely to be a candidate electrolyte material for all-solid-state lithium battery application. More importantly, we believe the approach described here could be extended to synthesize newer, possibly better, lithium ion conductors.

Magnetocaloric effect in La1-xSrxCoO3 (0.05 <= x <= 0.40)

We report studies of magnetocaloric effect in lanthanum cobaltate doped with different Sr-concentrations, La1-xSrxCoO3 (0.05 less than or equal to x less than or equal to 0.4). The study has revealed that La0.6Sr0.4CoO3, which exhibits a moderately large value of maximum entropy change of about 1.45 J/kg/K in 1.5 T DC-fieid around its Curie temperature (of 235 K), can be used as an active magnetic refrigerant (AMR) material at similar to 2.35 K. (C) 1999 Elsevier Science B.V. Al rights reserved.

Structural phase transitions in Bi2V1-xGexO5.5-x/2 (x=0.2, 0.4, and 0.6) single crystals: X-ray crystallographic study

Single crystals of Bi2V1-xGexO5.5-x/2 (x = 0.2, 0.4, and 0.6) were grown by slow cooling of melts. Bismuth vanadate transforms from an orthorhombic to a tetragonal structure and subsequently to an orthorhombic system when the Ge4+ concentration was varied from x = 0.2 to x = 0.6. All of these compositions crystallized in polar space groups (Aba2, F4mm, and Fmm2 for x = 0.2, 0.4, and 0.6, respectively). The structures were fully determined by single crystal X-ray diffraction studies, (C) 1999 Elsevier Science Ltd.

Crystal structure and thermal and electrical properties of the perovskite solid solution Nd1-xSrxFeO3-delta (0 <= x <= 0.4)

The crystal structure, thermal expansion and electrical conductivity of strontium-doped neodymium ferrite (Nd1-xSrxFeO3-delta where 0less than or equal toxless than or equal to0.4) were investigated. All compositions had the GdFeO3-type orthorhombic perovskite structure. The lattice parameters were determined at room temperature by X-ray powder diffraction. The orthorhombic distortion decreases with increasing Sr substitution. The pseudocubic lattice parameter shows a minimum at x=0.3. The thermal expansion curves for x=0.2-0.4 displayed rapid increase in slope at higher temperatures. The electrical conductivity increased with Sr content and temperature. The calculated activation energies for electrical conduction decreased with increasing x. The electrical conductivity can be described by the small polaron hopping mechanism. The charge compensation for divalent ion on the A-site is provided by the formation of Fe4+ ions on the B site and vacancies on the oxygen sublattice. The results indicate two defect domains: for low values of x, the predominant defect is Fe4+ ions, whereas for higher values of x, oxygen vacancies dominate. (C) 2002 Elsevier Science B.V. All rights reserved.

Crystal structure, thermal expansion and electrical conductivity of Nd0.7Sr0.3Fe1-xCoxO3 (0 <= x <= 0.8)

The crystal structure, thermal expansion and electrical conductivity of the solid solution Nd0.7Sr0.3Fe1-xCoxO3 for 0 less than or equal to x less than or equal to 0.8 were investigated. All compositions had the GdFeO3-type orthorhombic perovskite structure. The lattice parameters were determined at room temperature by X-ray powder diffraction (XRPD). The pseudo-cubic lattice constant decreased continuously with x. The average linear thermal expansion coefficient (TEC) in the temperature range from 573 to 973 K was found to increase with x. The thermal expansion curves for all values of x displayed rapid increase in slope at high temperatures. The electrical conductivity increased with x for the entire temperature range of measurement. The calculated activation energy values indicate that electrical conduction takes place primarily by the small polaron hopping mechanism. The charge compensation for the divalent ion on the A-site is provided by the formation of Fe4+ ions on the B-site (in preference to Co4+ ions) and vacancies on the oxygen sublattice for low values of x. The large increase in the conductivity with x in the range from 0.6 to 0.8 is attributed to the substitution of Fe4+ ions by Co4+ ions. The Fe site has a lower small polaron site energy than Co and hence behaves like a carrier trap, thereby drastically reducing the conductivity. The non-linear behaviour in the dependence of log sigmaT with reciprocal temperature can be attributed to the generation of additional charge carriers with increasing temperature by the charge disproportionation of Co3+ ions. (C) 2002 Elsevier Science B.V. All rights reserved.

Grain size effects on charge-ordering, phase segregation and related properties of rare-earth manganates, Nd(0.5)A(0.5)MnO(3) (A = Ca or Sr)

Grain size has marked effects on charge-ordering and other properties of Nd(0.5)A(0.5)MnO(3) (A=Ca or Sr). Thus, the anti-ferromagnetic (AFM) transition in Nd0.5Ca0.5MnO3 is observed distinctly only in samples sintered at 1273 K or higher. The sample with a small grain size (sintered at 1173 K) shows evidence for greater ferromagnetic (FM) interaction at low temperatures, probably due to phase segregation. The FM transition as well as the charge-ordering transition in Nd0.5Sr0.5MnO3 becomes sharper in samples sintered at 1273 K or higher. The sample sintered at 1173 K does not show the AFM-CO transition around 150 K and is FM down to low temperatures; the apparent T-c-T-co gap decreases with the increase in the grain size. The samples sintered at lower temperatures (<1673 K) show evidence for greater segregation of the AFM and FM domains. (C) 2002 Elsevier Science Ltd. All rights reserved.

Investigation of reversible and irreversible polarizations in thin films of SrBi2(Ta-0.5,Nb-0.5)(2)O-9

The reversible and irreversible components of the total polarization in a thin film of SrBi2(Ta-0.5,Nb-0.5)(2)O-9 were calculated. The C-V loop was integrated to obtain the reversible part of the total polarization. The reversible polarization was only 20% of the total polarization and showed almost no hysteresis. However, the dielectric constant due to the total polarization was almost the same as that for the reversible polarization in the saturation region of the large signal P-E hysteresis loop. The reversible part was subtracted from the total polarization to calculate the irreversible counterpart of it. The irreversible polarization showed a near-square shaped hysteresis loop, while the reversible polarization was obeying the Rayleigh law. The small signal hysteresis was simulated from the parameters obtained from the Rayleigh-curve fit with the experimental curve and then it was compared with the result obtained from direct measurement with small amplitude. (C) 2002 Elsevier Science B.V. All rights reserved.

Magnetic ordering in La0.85Pb0.15Mn1-xTixO3 (0 <= x <= 0.15)

Powder-neutron diffraction study has been carried out at 300 and 10 K in La0.85Pb0.15Mn1-xTixO3 (0 less than or equal to x less than or equal to 0.15). The samples crystallize in the rhombohedral phase. The magnetic moment reduces nonlinearly with increase in Ti and correlates well with the reported behavior of T-C. The change in the moment and T-C could not be related to change in the one electron bandwidth, W. The reduction is attributed to the effect of dilution and thereby reducing the double exchange ferromagnetic interaction. (C) 2002 Elsevier Science B.V. All rights reserved.

Mossbauer study of La1-xCaxMn1-y (57)FeyO(3) with x = 0, 0.25; y=0.01

Temperature dependent Mossbauer measurements are done on the samples of La1- xCaxMn1-y (FeyO3)-Fe-57 with x=0 and 0.25, and y=0.01. With decreasing temperature, the specimen with x=0.25 shows a paramagnetic to ferromagnetic transition around 175 K. In the specimen x=0.0, the temperature dependence of both the center shift (delta) and the recoilless fraction (f) can be fitted very well with the Debye theory with a theta(D)=320+/-50 K. But for the specimens with x=0.25, f and delta show distinct deviations from the Debye behavior in the temperature range in which the resistivity shows a sharp decrease. Dips observed in both the f and delta around the transition temperature suggest that the Jahn-Teller distortion observed in these systems is dynamic in nature.

Study of relaxor behavior of 0.7Pb(Mg1/3Nb2/3)O-3-0.3PbTiO(3) thin films

Relaxor properties of polycrystalline 0.7Pb(Mg1/3Nb2/3)O-3-0.3PbTiO(3) (PMN-PT) thin films were studied in terms of the diffuse nature of phase transition along with the frequency dispersion of temperature (T-m) at which the dielectric constant exhibits maximum value. Existence of remnant polarization (P-r) above the phase transition temperature, which is a characteristic property of typical relaxor ferroelectric has also been observed in the present case. The films exhibited a gradual decrease of remnant polarization with increase of temperature. Among the different models of relaxor ferroelectric, Vogel-Fulcher model has been found to be suitable to describe the frequency dispersion of T-m in this case. Freezing of dipole moment with decrease of temperature was thought to be the origin of the temperature dependence of dielectric dispersion.