Micro and macroscopic features of impact failed defect induced carbon-epoxy composites

Laminated composite structures are susceptible to damage under impacts with attendant properly degradation. While studies on damage tolerance behaviour are emphasised and the findings reported, the citations correlating impacts with the fracture features are limited. In the present study, therefore, attempts have been made to depict how the transition of the fracture features take place depending on the type and extent of defect introduced onto the carbon-epoxy system. The test specimens were subjected to differing levels of low energy pendulum impacts with a view to have specimens with varying levels of intial impacts history. Into such specimens, additional defect in the form of slits of varying depths were introduced by a mechanical process. The test coupons were then allowed to fail by impact. The fracture surface was studied under scanning electron microscope. The fractographic features that appear, based on the induced/inserted defects, are presented in this paper. It was noticed that the energy absorbed for final fracture could be associated with the defect introduced into the system. It was also observed that the size of the mechanically inserted defect had a significant influence on the features of the fracture surface.

Microstructural evolution and giant magnetoresistance in melt spun and annealed Cu-85(FeCo)(15) alloy

Granular alloys of Cu with FeCo were prepared by the melt-spinning technique. The alloy was characterized by x-ray, transmission electron microscopy, vibrating sample magnetometer, and magnetoresistance measurements. The alloys were heat treated for different temperatures to optimize the magnetoresistance properties. Structural characterization reveals that the FeCo phase initially precipitates out as fcc and later transforms to the bcc structure by martensitic transformation. It is seen that the trend in the magnetoresistance properties is different for the measurements carried out at room temperature and 4.2 K. This has been attributed to the transformation of fine fcc precipitates to the bcc structure during the low temperature measurements. It is seen that the presence of fine particles causes an increase in the field for saturation and is not suitable for applications where moderate field giant magnetoresistance is required. (C) 1999 American Institute of Physics. [S0021-8979(99)08317-6].

Sliding wear studies in epoxy containing alumina powders

The effect of hard and refractory alumina additions on the mechanical properties of polymer in general and wear behavior in particular is not well studied. In this work, therefore, the changes in wear behavior of epoxy resin due to the additions of alumina powders have been looked into. Using a pin-on-disc set up, dry sliding wear tests were done on both filled (4, 8, & 11 wt. % alumina) and unfilled samples. A sliding velocity of 0.83 m/sec. and a sliding distance of 2 km were employed for the study. Load range used varied from 9.8 N to about 29 N. The experiments point to an increased resistance to wear with an increased presence of filler in the matrix. Further, higher loads result in larger loss of material irrespective of the filler level in the composite.

Nanoscale embedded alloy particles through rapid solidification: the case of Al-Pb-In and Cu-Fe-Si

Rapid solidification techniques can be used to produce the embedded nanoparticles in a desired matrix. The origin and morphology of these small particles and their transformation behaviour are still not fully understood. In this paper, we discuss the issues involved and present some interesting results in Al-Pb-In and Cu-Fe-Si systems.

Role of corundum-adapted strains of Bacillus polymyxa in the separation of hematite and alumina

Strains of Bacillus polymyxa, preadapted and grown in the presence of corundum, were found to be capable of the efficient separation of hematite from alumina. Results of rests peformed using binary hematite-corundum and ternary hematite-quartz-corundum mixtures in the presence of cells and metabolic products separated from the adapted bacterial culture indicated that more than 99% of the hematite could he efficiently separated through selective flocculation after desliming. It was found that alumina-specific bioproteins and other nonproteinaceous compounds were secreted by bacterial cells after adaptation to the mineral. The utility of this bioprocessing is demonstrated in the removal of iron from bauxite ores through selective flocculation in the presence of the adapted bacteria.

Studies on grinding media wear and its effect on flotation of ferrugenous phosphate ore

Marked ball grinding rests were carried out in the laboratory with a low grade phosphate ore under different experimental conditions. Two types of balls were used, namely high carbon low alloy (HCLA) cast steel and high chrome cast iron. Results of marked ball grinding tests indicated that ball wear increased with time and showed a sharp increase for wet grinding over dry grinding. Ball wear under wet grinding conditions was also influenced by the gaseous atmosphere in the mill. The grinding ball materials could be arranged in the following order with respect to their overall wear resistance: High chrome cast iron > HCLA cast steel balls Methods to minimize ball wear through control of mill atmosphere and addition of flotation reagents are discussed. Effect of grinding media and additions of flotation reagents during grinding on phosphate ore flotation are also discussed. (C) 1999 Elsevier Science Ltd. All rights reserved.

Studies on indentation fracture toughness on ceramic and ceramic composite using acoustic emission technique

This paper is aimed at investigating the acoustic emission activities during indentation toughness tests on an alumina based wear resistant ceramic and 25 wt% silicon carbide whisker (SIC,) reinforced alumina composite. It has been shown that the emitted acoustic emission signals characterize the crack growth during loading. and unloading cycles in an indentation test. The acoustic emission results indicate that in the case of the composite the amount of crack growth during unloading is higher than that of loading, while the reverse is true in case of the wear resistant ceramics. Acoustic emission activity observed in wear resistant ceramic is less than that in the case of composite. An attempt has been made to correlate the acoustic emission signals with crack growth during indentation test.

Studies on the variations in compression strengths of graphite powders bearing glass-epoxy composites exposed to humid conditions

The moisture absorption and changes in compression strengths in glass-epoxy (G-E composites without and with discrete quantities of graphite powders introduced into the resin mix prior to its spreading on specific glass fabric (layers) during the lay-up (stacking) sequence forms the subject matter of this report. The results point to higher moisture absorption for graphite bearing specimens. The strengths of graphite-free coupons show a continuous decrease, while the filler bearing ones show an initial rise followed by a drop for larger exposure times. Scanning Fractographic features were examined for an understanding of the process. The observations were explained invoking the effect of matrix plasticizing and the role of interfacial regions.

Surface chemical studies on the competitive adsorption of poly(acrylic acid) and poly(vinyl alcohol) onto alumina

The adsorption of poly(acrylic acid) (PAA) and poly(vinyl alcohol) (PVA) onto alumina has been studied as a function of pH, both individually and in the presence of each other. The adsorption density of PAA is found to decrease with an increase of pH while that of PVA shows the opposite trend. In a binary system containing PAA and PVA, the presence of PVA does not affect the adsorption of PAA onto alumina, but the addition of PAA diminishes the adsorption of PVA in the pH range investigated. The adsorption isotherm of PAA at acidic pH exhibits high-affinity Langmuirian behavior. The isotherms for PVA appear rounded and are of the low-affinity type, Once again the adsorption isotherms of PAA remain unaltered in the presence of PVA whereas those of PVA are significantly affected resulting in a lowering of the adsorption density consequent to PAA addition. A variation in the sequence of addition of PAA and PVA does not affect the adsorption behavior of either of the polymers, The electrokinetic behavior of alumina with PAA is hardly influenced by the addition of PVA, On the other hand, the electrophoretic mobility of alumina in the presence of PVA is significantly altered in the presence of PAA and closely resembles the trend observed with PAA alone. Desorption studies reveal that over 80% of PVA could be desorbed in the pH range 3-9 whereas in the case of PAA, the percent desorption increases from 20 to about 70% as the pH is increased from about 3 to 8. Solution conductivity tests confirm interaction of aluminum species and PAA in the bulk solution. FTIR spectroscopic data provide evidence in support of hydrogen bonding and chemical interaction in the case of the PAA-alumina system and hydrogen bonding with respect to the PVA-alumina interaction. (C) 1999 Academic Press.

Synthesis of mesoporous materials based on titanium(IV)oxide and titanium nitride

Nanoparticles of titania were obtained by the controlled hydrolysis of Ti(i-OC3H7)(4) in the reverse micelles of dodecylamine derived from dodecylamine-isopropanol-water solution (water/oil microemulsion). The mesolamellar phase based on titanium nitride (TiN) was obtained by first decomposing TiN atleast partially using the 1:1 solution of acid mixture (HF and HNO3 in the ratio of 9:1) in water and then templating onto the cationic surfactant namely, cetyltrimethylammaniumbromide (abbreviated as CTAB) at 80 degrees C. The synthesis of mesolamellar phase based on TiN involves the charge matched templating approach following the counter-ion mediated pathway. The samples thus obtained were characterized by small angle x-ray diffraction using Cuk(a) radiation, scanning electron microscopy and transmission electron microscopy, which indicated some satisfactory results. (C) 1999 Acta Metallurgica Inc.

Synthesis of metastable, wurzite-based zinc oxide-cobalt(II) oxide solid solutions by spray pyrolysis

Aqueous solutions of acetates and nitrates of zinc and cobalt have been spray decomposed to study the production of extended solid solutions in the ZnO-CoO system. Examination of the products of a variety of synthesis conditions indicates that up to 70% CoO may be retained in the solid solution in the wurzite phase, even though a comparison of the equilibrium solubility in the phase diagram might be expected to favor the formation of a rock-salt-based solid solution.

Tensile flow behaviour of 2.25Cr-1Mo ferritic steel base metal and simulated heat affected zone structures of 2.25Cr-1Mo weld joint

Tensile tests in the temperature range 298 to 873 K have been performed on 2.25Cr-1Mo base metal and simulated heat affected zone (HAZ) structures of its weld joint, namely coarse grain bainite, fine grain bainite and intercritical structure. Tensile flow behaviour of all the microstructural conditions could be adequately described by the Hollomon equation (sigma = K-1 epsilon(n1)) at higher (> 623 K) temperatures. Deviation from the Hollomon equation was observed at low strains and lower (< 623 K) temperatures. The Ludwigson modification of Hollomon's equation, sigma = K-1 epsilon(n1) + exp (K-2 + n(2) epsilon), was found to describe the flow curve. In general, the flow parameters n(1), K-1, n(2) and K-2 were found to decrease with increase in temperature except in the intermediate temperature range (423 to 623 K). Peaks/plateaus were observed in their variation with temperature in the intermediate temperature range coinciding with the occurrence of serrated flow in the load-elongation curve. The n(1) Value increased and the K-1 value decreased with the type of microstructure in the order: coarse grain bainite, fine grain bainite, base metal and intercritical structure. The variation of nl with microstructure has been rationalized on the basis of mean free path (MFP) of dislocations which is directly related to the inter-particle spacing. Larger MFP of dislocations lead to higher strain hardening exponents n(1).

The effect of SiC particles on the size and morphology of eutectic silicon in cast A356/SiCp composites

Properties of cast aluminium matrix composites are greatly influenced by the nature of distribution of reinforcing phase in the matrix and matrix microstructural length scales, such as grain size, dendrite arm spacing, size and morphology of secondary matrix phases, etc. Earlier workers have shown that SIC reinforcements can act as heterogeneous nucleation sites for Si during solidification of Al-Si-SiC composites. The present study aims at a quantitative understanding of the effect of SiC reinforcements on secondary matrix phases, namely eutectic Si, during solidification of A356 Al-SiC composites. Effect of volume fraction of SiC particulate on size and shape of eutectic Si has been studied at different cooling rates. Results indicate that an increase in SiC volume fraction leads to a reduction in the size of eutectic Si and also changes its morphology from needle-like to equiaxed. This is attributed to the heterogeneous nucleation of eutectic Si on SiC particles. However, SiC particles are found to have negligible influence on DAS. Under all the solidification conditions studied in the present investigation, SiC particles are found to be rejected by the growing dendrites. (C) 1999 Elsevier Science Ltd. All rights reserved.

The melting and solidification of nanoscale Bi particles embedded in a glassy and crystalline matrix

We report the formation of an amorphous phase in nanosized Pi particles embedded in an Al-based glassy alloy matrix. High-resolution electron microscopy (HREM) has been used to show that the particles contain crystalline and amorphous portions. A depression of the melting point by more than 100 K of the crystalline portion of the Pi particles was found by differential scanning calorimetric studies and by in-situ electron microscopy using a heating stage. The same techniques established the absence of an amorphous phase in the particles when the matrix is crystallized. It is shown that the formation of the amorphous phase and the depression of the melting point cannot be explained by the pressure developed by the volume change during solidification in this constrained system.

Diffusion and Growth of the mu Phase (Ni6Nb7) in the Ni-Nb System

Incremental diffusion couple experiments are conducted to determine the average interdiffusion coefficient and the intrinsic diffusion coefficients of the species in the Ni6Nb7 (mu phase) in the Ni-Nb system. Further, the tracer diffusion coefficients are calculated from the knowledge of thermodynamic parameters. The diffusion rate of Ni is found to be higher than that of Nb, which indicates higher defect concentration in the Ni sublattice.