Ultra sensitive NO2 gas detection using the reduced graphene oxide coated etched fiber Bragg gratings

We report a simple and highly sensitive methodology for the room temperature NO2 gas sensing using reduced graphene oxide (RGO) coated clad etched fiber Bragg grating (eFBG). A significant shift (>10 pm) is observed in the reflected Bragg wavelength (lambda(B)) upon exposing RGO coated on the surface of eFBG to the NO2 gas molecules of concentration 0.5 ppm. The shift in Bragg wavelength is due to the change in the refractive index of RGO by charge transfer from the adsorbing NO2 molecules. The range of NO2 concentration is tested from 0.5 ppm to 3 ppm and the estimated time taken for 50% increase in Delta lambda(B) ranges from 20 min (for 0.5 ppm) to 6 min (for 3 ppm). (C) 2015 Elsevier B.V. All rights reserved.

A strategy to achieve enhanced electromagnetic interference shielding at ultra-low concentration of multiwall carbon nanotubes in P alpha MSAN/PMMA blends in the presence of a random copolymer PS-r-PMMA

A unique strategy was adopted to achieve an ultra-low electrical percolation threshold of multiwall carbon nanotubes (MWNTs) (0.25 wt%) in a classical partially miscible blend of poly-alpha-methylstyrene-co-acrylonitrile and poly(methyl methacrylate) (P alpha MSAN/PMMA), with a lower critical solution temperature. The polymer blend nanocomposite was prepared by standard melt-mixing followed by annealing above the phase separation temperature. In a two-step mixing protocol, MWNTs were initially melt-mixed with a random PS-r-PMMA copolymer and subsequently diluted with 85/15 P alpha MSAN/PMMA blends in the next mixing step. Mediated by the PS-r-PMMA, the MWNTs were mostly localized at the interface and bridged the PMMA droplets. This strategy led to enhanced electromagnetic interference (EMI) shielding effectiveness at 0.25 wt% MWNTs through multiple scattering from MWNT-covered droplets, as compared to the blends without the copolymer, which were transparent to electromagnetic radiation.

Enhanced photocatalytic activity of ultra-high aspect ratio ZnO nanowires due to Cu induced defects

We report the synthesis of ZnO nanowires in ambient air at 650 degrees C by a single-step vapor transport method using two different sources Zn (ZnO nanowires-I) and Zn:Cu (ZnO nanowires-II). The Zn:Cu mixed source co-vaporize Zn with a small amount of Cu at temperatures where elemental Cu source does not vaporize. This method provides us a facile route for Cu doping into ZnO. The aspect ratio of the grown ZnO nanowires-II was found to be higher by more than five times compared ZnO nanowires-I. Photocatalytic activity was measured by using a solar simulator and its ultraviolet-filtered light. The ZnO nanowires-II shows higher catalytic activity due to increased aspect ratio and higher content of surface defects because of incorporation of Cu impurities.