The machinability of a cast aluminium alloy-graphite particle composite

The microstructure of a cast Al---Si alloy-graphite particle composite is examined using optical and analytical scanning electron microscopy. Specimens containing different percentages of graphite were machined by orthogonal planning with 25° and 45° rake angle tools at both 6.5 and 13.2 m min−1. The machining forces are reported and the chip-rake-face friction coefficients and shear flow stresses are calculated. It is shown that the reduction in machining forces with increasing graphite content is due mostly to a decrease in the shear flow stress rather than to lower chip-rake-face friction. Both the polished and the machined surfaces of the composite are rougher than those of the simple alloy, apparently owing to the greater porosity, the tearing out of graphite particles, or the opening of cracks at the graphite particles in the wake of the tool.

High pressure induced crystallization of rapidly solidified Al---Fe and Al---Mn quasi-crystalline alloysstar

The presence of phases showing icosahedral point symmetry was reported by Shechtman, Blech, Gratias and Cahn in rapidly quenched alloys of Al---Mn, Al---Fe and Al---Cr, and subsequently many other splat-cooled alloys with the i phase have been reported. In this paper we present the first results of high pressure experiments carried out on Al---Fe and Al---Mn quasi-crystals. The experiments performed at room temperature showed irreversible quasi-crystal-to-crystal transitions in Al---Mn and Al---Fe alloys. The transition pressures are 49 kbar for Al78Mn22, 93 kbar for Al86Mn14, 79 kbar for Al86Fe14, 54 kbar for Al82Fe18 and 108 kbar for Al75Fe25. The high pressure phases are found to be the equilibrium phases.

Microstructural study of rapidly solidified titanium eutectoid alloysstar, open

Rapid solidification of Ti-7.3wt.%Cu (near-eutectoid composition), Ti-36.2wt.%Ni and Ti-34.3wt.% Ni-5.8wt.%Si alloys has been carried out by electron beam melting and splat quenching on a water-cooled rotating copper disc. The product obtained was in the form of thin ribbons 60–100 μm thick. Transmission electron microscopy studies of Ti---Cu alloy splats showed that the microstructure consisted of a mixture of martensite and a lamellar eutectoid product. The formation of the intermetallic compound Ti2Cu involved a diffusionless ω transformation and spinodal clustering. In the case of Ti---Ni alloy the as-quenched microstructure is complex, consisting of α, transformed β and intermetallic phases. This could have arisen possibly as a result of local variation in cooling rates. Rapid solidification of Ti---Ni---Si alloy resulted in partial quenching of an amorphous phase. The amorphous phase was seen to be extremely hard (a Vickers hardness of about 800 HV).

The effect of rapid solidification on the order-disorder transformation in iron-based alloys

The effect of rapid solidification on the ordering reaction in Fe---Si and Fe---Al alloys has been reported. It is shown that rapid solidification can influence the ordering reaction in alloys with higher critical ordering temperatures. For ordering reactions at lower temperatures, the effect is similar to that of solid-state quenching. Different factors influencing the ordering reactions and domain structures during rapid solidification of iron-based alloys are discussed.

Influence of heat-treatment on the strength and fracture-behavior of fe-12cr-6al ferritic stainless-steel

The changes in the tensile properties and fracture mode brought about by heat treatment of Fe-12Cr-6Al ferritic stainless steel have been studied. A favourable combination of high strength and good ductility is obtained by heating the material at 1370 K for 2 h followed by a water quench. The high-temperature treatment results in carbide dissolution as well as an increase in the grain size. The mechanism of strengthening has been evaluated from the apparent activation energy (28 kJ mol–1) and is identified to be the unpinning of dislocations from the atmosphere of carbon atoms. As the heat-treatment temperature is increased, the fracture behaviour changes from ductile to brittle mode and this is related to the changes in grain size and friction stress.

Preparation of cast aluminium alloy-mica particle composites

The optimum conditions for producing cast aluminium alloy-mica particle composites, by stirring mica particles (40 to 120 mgrm) in molten aluminium alloys (above their liquidus temperatures), followed by casting in permanent moulds, are described. Addition of magnesium either as pieces along with mica particles on the surface of the melts or as a previously added alloying element was found to be necessary to disperse appreciable quantities (1.5 to 2 wt.%) of mica particles in the melts and retain them as uniform dispersions in castings under the conditions of present investigation. These castings can be remelted and degassed with nitrogen at least once with the retention of about 80% mica particles in the castings. Electron probe micro-analysis of these cast composites showed that magnesium added to the surface of the melt along with mica has a tendency to segregate around the mica particles, apparently improving the dispersability for mica particles in liquid aluminium alloys. The mechanical properties of the aluminium alloy-mica particle composite decrease with an increase in mica content, however, even at 2.2% the composite has a tensile strength of 14.22 kg mm–2 with 1.1% elongation, a compression strength of 42.61 kg mm–2, and an impact strength of 0.30 kgm cm–2. The properties are adequate for certain bearing applications, and the aluminium-mica composite bearings were found to run under boundary lubrication, semi-dry and dry friction conditions whereas the matrix alloy (without mica) bearings seized or showed stick slip under the same conditions.

Micromechanisms of damage in a hypereutectic Ti-6Al-4V-B alloy

The tensile stress–strain response and fracture in a hypereutectic Ti–6Al–4V–1.7B (weight percent) alloy were investigated by employing interrupted tensile tests combined with acoustic emission measurements, with the aim to identify the cause for the observed low ductility in this alloy. These tests were complemented with microscopy. The alloy contains TiB whiskers of different length scales, the majority of which include micro-whiskers ( 5–10 μm length) and a few primary-whiskers ( 200–300 μm length). Although the fracture of both types of whiskers occur during deformation, the former leads to a gradual decrease in the secant modulus whereas initiation of the latter leads to a drastic drop in the modulus along with failure of the specimen, limiting the ductility.

Texture dependent stress corrosion failure of commercial titanium sheets in bromine-methanol solution

The stress corrosion cracking (SCC) characteristics of agr-titanium sheets in a bromine-methanol solution have been studied in the annealed and cold-rolled conditions using longitudinal and transverse specimens. The times to failure for annealed longitudinal specimens were longer than those for similarly tested transverse specimens. The cold-rolled specimens developed resistance to SCC, but failed by cleavage when notched, unlike the intergranular separation in annealed titanium. The apparent activation energy was found to be texture dependent and was in the range 30 to 51 kJ mol–1 for annealed titanium, and 15kJ mol–1 for cold-rolled titanium. The dependence of SCC behaviour on the texture is related to the changes in the crack initiation times. These are caused by changes in the passivation and repassivation characteristics of the particular thickness plane. The thickness planes are identified with the help of X-ray pole figures obtained on annealed and cold-rolled material. On the basis of the activation energy and the electrochemical measurements, the mechanism of SCC in annealed titanium is identified to be the one involving stress-aided anodic dissolution. On the other hand, the results on the cold-rolled titanium are in support of the hydrogen embrittlement mechanism consisting of hydride precipitation. The cleavage planes identified from the texture data match with the reported habit planes for hydride formation.

A study on the nature of the compound layer formed during the ion nitriding of En40B steel

Commercial-grade En40B steel has been ion nitrided in the temperature range 475–550°C in a 25%N2–75%H2 gas mixture. The nature of the compound layer formed was studied by the X-ray diffraction technique and optical metallography. It was observed that the structure of the compound layer gradually transforms from a predominantly epsilon (Porson) nitride to a predominantly γ′ nitride structure with increasing treatment time. Optical metallography studies on sections orthogonal to the nitrided surface showed that, after about 5 h of treatment, the thickness of the compound layer decreases with further increase in treatment time.

Gel growth and dielectric studies of K. Rb and Cs perchlorates

Single crystals of K, Rb and Cs perchlorates have been grown by the counter diffusion of the respective ions and CIO4 through the gel medium. Studies on nucleation, growth kinetics, morphological aspects and purity are discussed in this paper. The dielectric constant, ~b, as well as loss measured along the longest axis, exhibits an anomaly at the transition temperature, Tt, in all the three crystals. It is found that the peak values of Tt are approximately 800, 100 and 53 in K, Rb and Cs perchlorates, respectively. The dielectric anomaly and the large value of c b in the cubic phase are discussed in terms of the degree of disorder of the CIO~ group and the possible contribution from defects.

Ultrasonic velocities and thermal expansion coefficients of amorphous Se80Te20 and Se90Te10 alloys near glass transitions

Precise measurements of the ultrasonic velocities and thermal expansivities of amorphous Se80Te20 and Se90Te10 alloys are reported near the glass transition. The samples are produced by liquid quenching. The longitudinal and transverse velocities are measured at 10 MHz frequency using the McSkimin pulse superposition technique. The thermal expansivities,agr, are measured using a three-terminal capacitance bridge. Theagr-values show a sharp maximum near the glass transition temperature,T g. The ultrasonic velocities also show a large temperature derivative, dV/dT nearT g. The data are discussed in terms of existing theories of the glass transition. The continuous change inagr shows that the glass transition is not a first-order transition, as suggested by some theories. The samples are found to be deformed by small loads nearT g. The ultrasonic velocities and dV/dT have contributions arising from this deformation.

The study of oxidation state of manganese in lead oxyhalide glasses by optical spectroscopy

Abstaract is not available.

A one-step process for the preparation ofγ-Fe2O3

Abstract is not available.