Thermodynamic properties of Pb2PtO4 and PbPt2O4 and phase equilibria in the system Pb–Pt–O

The compounds Pb2PtO4 and PbPt2O4 were synthesized from an intimate mixture of yellow PbO and Pt metal powders by heating under pure oxygen gas at 973 K for periods up to 600 ks with intermediate grinding and recompacting. Both compounds were found to decompose on heating in pure oxygen to PbO and Pt, apparently in conflict with the requirements for equilibrium phase relations in the ternary system Pb–Pt–O. The oxygen chemical potential corresponding to the three-phase mixtures, Pb2PtO4 + PbO + Pt and PbPt2O4 + PbO + Pt were measured as a function of temperature using solid-state electrochemical cells incorporating yttria-stabilized zirconia as the solid electrolyte and pure oxygen gas at 0.1 MPa pressure as the reference electrode. The standard Gibbs free energies of formation of the ternary oxides were derived from the measurements. Analysis of the results indicated that the equilibrium involving three condensed phases Pb2PtO4 + PbO + Pt is metastable. Under equilibrium conditions, Pb2PtO4 should have decomposed to a mixture of PbO and PbPt2O4. Measurement of the oxygen potential corresponding to this equilibrium decomposition as a function of temperature indicated that decomposition temperature in pure oxygen is 1014(±2) K. This was further confirmed by direct determination of phase relations in the ternary Pb–Pt–O by equilibrating several compositions at 1023 K for periods up to 850 ks and phase identification of quenched samples using X-ray diffraction (XRD), scanning electron microscopy (SEM) and energy dispersive X-ray spectroscopy (EDS). Only one ternary oxide PbPt2O4 was stable at 1023 K under equilibrium conditions. Alloys and intermetallic compounds along the Pb–Pt binary were in equilibrium with PbO.

High temperature stability of oxysulfides containing Ce3+ and Y3+ ions

Standard Gibbs energies of formation of oxysulfides of cerium and yttrium from their respective oxedes were determined using solid oxide galvanic cells incorporating calcia-stabilized zirconia as the electrolyte in the temperature range 870–1120 K. The sulfur potential over the electrode containing the oxide and oxysulfide was fixed by a buffer mixture of Ag + Ag2S. A small amount of CaH2 was added to the buffer to generate an equilibrium ratio of H2S and H2 species in a closed system containing the buffer and the electrode. The sulfur potential is transmitted to the electrode via the gas phase. The results can be summarized by the equations 2left angle bracketCeO2right-pointing angle bracket+1/2(S2)→left angle bracketCe2O2Sright-pointing angle bracket+(O2) ΔG°=430600−109·7T(±400)J mol−1 left angle bracketY2O3right-pointing angle bracket+1/2(S2)→left angle bracketY2O2Sright-pointing angle bracket+1/2(O2) ΔG°=114780−1·45T(±200)J mol−1 The values are compared with data reported in the literature. The stability field diagram for the Ce---O---S system has been developed using the results of this study for Ce2O2S and data for other phases from the literature.

Material processing and surface reaction studies in free piston driven shock tube

Recently established moderate size free piston driven hypersonic shock tunnel HST3 along with its calibration is described here. The extreme thermodynamic conditions prevalent behind the reflected shock wave have been utilized to study the catalytic and non-catalytic reactions of shock heated test gases like Ar, N2 or O2 with different material like C60 carbon, zirconia and ceria substituted zirconia. The exposed test samples are investigated using different experimental methods. These studies show the formation of carbon nitride due to the non-catalytic interaction of shock heated nitrogen gas with C60 carbon film. On the other hand, the ZrO2 undergoes only phase transformation from cubic to monoclinic structure and Ce0.5Zr0.5O2 in fluorite cubic phase changes to pyrochlore (Ce2Zr2O7±δ) phase by releasing oxygen from the lattice due to heterogeneous catalytic surface reaction.

Fabrication and Phase Transformation in Crystalline Nanoparticles of PbZrO3 Derived By Sol-Gel

In this research fabrication of crystalline PbZrO3 (PZ) nanoparticles and their phase transformation behavior is investigated. A novel sol-gel method was used for the synthesis of air-stable and precipitate-free diol-based sol of PZ, which was dried at 150 degrees C and then calcined at 300-700 degrees C for 1 h. The morphology, crystallinity and phase formation of as synthesized nanoparticles were studied by the selected-area electron diffraction (SAED), X-ray diffraction (XRD), thermal gravimetric analysis/differential scanning calorimetry (TGA-DSC), and high resolution transmission electron microscope (HRTEM). The XRD, SAED, and TGA-DSC analyses confirmed the tetragonal lead rich zirconia phase (t-Z phase) and monoclinic zirconia phase (m-Z phase) as the intermediate phases during the calcinations process followed by crystallization of single orthorhombic PZ phase at about 700 degrees C. The average PZ particle size was observed about 20 nm as confirmed by TEM study. Energy-dispersive X-ray spectroscopy (EDX) analysis demonstrated that stoichiometric PbZrO3 was formed.

Novel organic-inorganic composite polymer-electrolyte membranes for DMFCs

Organic-inorganic composite membranes comprising Nation with inorganic materials such as silica, mesoporous zirconium phosphate (MZP) and mesoporous titanium phosphate (MTP) are fabricated and evaluated as proton-exchange-membrane electrolytes for direct methanol fuel cells (DMFCs). For Nation-silica composite membrane, silica is impregnated into Nation matrix as a sol by a novel water hydrolysis process precluding the external use of an acid. Instead, the acidic nature of Nation facilitates in situ polymerization reaction with Nation leading to a uniform composite membrane. The rapid hydrolysis and polymerization reaction while preparing zirconia and titania sols leads to uncontrolled thickness and volume reduction in the composite membranes, and hence is not conducive for casting membranes. Nafion-MZP and Nafion-MTP composite membranes are prepared by mixing pre-formed porous MZP and MTP with Nation matrix. MZP and MTP are synthesised by co-assembly of a tri-block co-polymer, namely pluronic-F127, as a structure-directing agent, and a mixture of zirconium butoxide/titanium isopropoxide and phosphorous trichloride as inorganic precursors. Methanol release kinetics is studied by volume-localized NMR spectroscopy (employing ``point resolved spectroscopy'', PRESS), the results clearly demonstrating that the incorporation of inorganic fillers in Nation retards the methanol release kinetics under osmotic drag. Appreciable proton conductivity with reduced methanol permeability across the composite membranes leads to improved performance of DMFCs in relation to commercially available Nafion-117 membrane.

Enhanced dielectric response of ZrO2 upon Ti doping and introduction of O vacancies

We determine the electronic properties and dielectric response of zirconia (ZrO2) with oxygen vacancies (O vacancies) and Ti doping using first-principles density functional theory calculations based on pseudopotentials and a plane wave basis. We find significantly enhanced static dielectric response in zirconia with Ti doping and introduction of oxygen vacancies. Softening of phonon modes are responsible for the enhanced dielectric response of doped samples compared to pure zirconia.

Thermodynamic activities in the Pb(Zr1-XTiX)O-3 solid solution at 1373 K

Although Pb(Zr1-XTiX)O-3 solid solution is the cornerstone of the piezoelectric ceramics, there is no information in the literature on thermodynamic activities of the component phases in the solid solution. Using inter-crystalline ion exchange equilibria between Pb(Zr1-XTiX)O-3 solid solution with cubic perovskite structure and (Zr1-YTiY)O-2 solid solutions with monoclinic and tetragonal structures, activities of PbTiO3 and PbZrO3 in the perovskite solid solution have been derived at 1373 K using the modified Gibbs-Duhem integration technique of Jacob and Jeffes. Tie-lines from the cubic solid solution are skewed towards the ZrO2 corner. Activities in the zirconia-rich (Zr1-YTiY)02 solid solutions are taken from a recent emf study. The results for the perovskite solid solution at 1373 K can be represented by a sub-regular solution model: Delta G(E.M) (J mol(-1)) = X-PbTiO3 X-PbZrO3(5280X(PbTiO3) - 1980X(PbZrO3)) where Delta G(E.M) is the excess Gibbs energy of mixing of the cubic solid solution and Xi represents the mole fraction of component i. There is a significant positive deviation from ideality for PbTiO3-rich compositions and mild negative deviation near the PbZrO3 corner. The cubic solid solution is intrinsically stable against composition fluctuations at temperatures down to 840 K. The results contrast sharply with the recent calorimetric data on enthalpy of mixing which signal instability of the cubic perovskite solid solution. (C) 2007 Elsevier B.V. All rights reserved.

Role of entropy in the stability of cobalt titanates

The standard molar Gibbs free energy of formation of Co2TiO4, CoTiO3,and CoTi2O5 as a function of temperature over an extended range (900 to 1675) K was measured using solid-state electrochemical cells incorporating yttria-stabilized zirconia as the electrolyte, with CoO as reference electrode and appropriate working electrodes. For the formation of the three compounds from their component oxides CoO with rock-salt and TiO2 with rutile structure, the Gibbs free energy changes are given by:Delta(f)G degrees((ox))(Co2TiO4) +/- 104/(J . mol(-1)) = -18865 - 4.108 (T/K)Delta(f)G degrees((ox))(CoTiO3) +/- 56/(J . mol(-1)) = -19627 + 2.542 (T/K) Delta(f)G degrees((ox))(CoTi2O5) +/- 52/(J . mol(-1)) = -6223 - 6.933 (T/K) Accurate values for enthalpy and entropy of formation were derived. The compounds Co2TiO4 with spinel structure and CoTi2O5 with pseudo-brookite structure were found to be entropy stabilized. The relatively high entropy of these compounds arises from the mixing of cations on specific crystallographic sites. The stoichiometry of CoTiO3 was confirmed by inert gas fusion analysis for oxygen. Because of partial oxidation of cobalt in air, the composition corresponding to the compound Co2TiO4 falls inside a two-phase field containing the spinet solid solution Co2TiO4-Co3O4 and CoTiO3. The spinel solid solution becomes progressively enriched in Co3O4 with decreasing temperature. (c) 2010 Elsevier Ltd. All rights reserved.

Vapour phase synthesis of salol over solid acids via transesterification

The transesterification of methyl salicylate with phenol has been studied in vapour phase over solid acid catalysts such as ZrO2, MoO3 and SO42- or Mo(VI) ions modified zirconia. The catalytic materials were prepared and characterized for their total surface acidity, BET surface area and powder XRD patterns. The effect of mole-ratio of the reactants, catalyst bed temperature, catalyst weight, flow-rate of reactants, WHSV and time-on-stream on the conversion (%) of phenol and selectivity (%) of salol has been investigated. A good yield (up to 70%) of salol with 90% selectivity was observed when the reactions were carried out at a catalyst bed temperature of 200 degrees C and flow-rate of 10 mL/h in presence of Mo(VI)/ZrO2 as catalyst. The results have been interpreted based on the variation of acidic properties and powder XRD phases of zirconia on incorporation of SO42- or Mo(VI) ions. The effect of poisoning of acid sites of SO42- or Mo(VI) ions modified zirconia on total surface acidity, powder XRD phases and catalytic activity was also studied. Possible reaction mechanisms for the formation of salol and diphenyl ether over acid sites are proposed.

Studies on nonisothermal solid state galvanic cells — effect of gradients on EMF

An expression for the EMF of a nonisothermal galvanic cell, with gradients in both temperature and chemical potential across a solid electrolyte, is derived based on the phenomenological equations of irreversible thermodynamics. The EMF of the nonisothermal cell can be written as a sum of the contributions from the chemical potential gradient and the EMF of a thermocell operating in the same temperature gradient but at unit activity of the neutral form of the migrating species. The validity of the derived equation is confirmed experimentally by imposing nonlinear gradients of temperature and chemical potential across galvanic cells constructed using fully stabilized zirconia as the electrolyte. The nature of the gradient has no effect on the EMF.

properties of Na2O in Nasicon solid solution, Na1+xZr2SixP3-xO12

The thermodynamic activity of sodium oxide (Na2O) in the Nasicon solid solution series, Na1+xZr2SixO12, has been measured in the temperature range 700–1100 K using solid state galvanic cells: Pt|CO2 + O2|Na2CO3?Na1+xZr2SixP3-xO12?(Y2O3)ZrO2?In + In2O3|Ta, Pt for 1 = ? = 2.5, and Pt?CO2 + O2?Na2CO3?ß-alumina?Na1+xZr2SixP3-xO12?Ar + O2?Pt for x = 0, 0.5, 2.5, and 3. The former cell, where the Nasicon solid solution is used as an electrolyte along with yttria-stabilized zirconia, is well suited for Nasicon compositions with high ionic conductivity. In the latter cell, ß-alumina is used as an electrolyte and the Nasicon solid solution forms an electrode. The chemical potential of Na2O is found to increase monotonically with x at constant temperature. The partial entropy of Na2O decreases continuously with x. However, the partial enthalpy exhibits a maximum at x = 2. This suggests that the binding energy is minimum at the composition where ionic conductivity and cell volume have maximum values.

Reducibility of Ce1-xZrxO2: origin of enhanced oxygen storage capacity

We combine first-principles calculations with EXAFS studies to investigate the origin of high oxygen storage capacity in ceria-zirconia solid solution, prepared by solution combustion method. We find that nanocrystalline Ce0.5Zr0.5O2 can be reduced to Ce0.5Zr0.5O1.57 by H-2 upto 850 degrees C with an OSC of 65 cc/gm which is extremely high. Calculated local atomic-scale structure reveals the presence of long and short bonds resulting in four-fold coordination of the cations, confirmed by the EXAFS studies. Bond valence analysis of the microscopic structure and energetics is used to evaluate the strength of binding of different oxide ions and vacancies. We find the presence of strongly and weakly bound oxygens, of which the latter are responsible for the higher oxygen storage capacity in the mixed oxides than in the pure CeO2.

Thermodynamic partial properties of Na2O in Nasicon solid solution, Na1+xZr2SixP3-xO12

The thermodynamic activity of sodium oxide (Na2O) in the Nasicon solid solution series, Na1+xZr2SixO12, has been measured in the temperature range 700�1100 K using solid state galvanic cells: Pt|CO2 + O2|Na2CO3?Na1+xZr2SixP3-xO12?(Y2O3)ZrO2?In + In2O3|Ta, Pt for 1 = ? = 2.5, and Pt?CO2 + O2?Na2CO3?ß-alumina?Na1+xZr2SixP3-xO12?Ar + O2?Pt for x = 0, 0.5, 2.5, and 3. The former cell, where the Nasicon solid solution is used as an electrolyte along with yttria-stabilized zirconia, is well suited for Nasicon compositions with high ionic conductivity. In the latter cell, ß-alumina is used as an electrolyte and the Nasicon solid solution forms an electrode. The chemical potential of Na2O is found to increase monotonically with x at constant temperature. The partial entropy of Na2O decreases continuously with x. However, the partial enthalpy exhibits a maximum at x = 2. This suggests that the binding energy is minimum at the composition where ionic conductivity and cell volume have maximum values.

Thermodynamic properties of RhO2

A solid-state electrochemical cell, with yttria-stabilized zirconia as the electrolyte and pure O-2 gas at 0.1 MPa as the reference electrode, has been used to measure the oxygen chemical potential corresponding to the equilibrium between beta-Rh2O3 and RhO2 in the temperature range from 850 to 1050K. Using standard Gibbs energy of formation of beta-Rh2O3 available in the literature and the measured oxygen potential, the standard Gibbs free energy of formation of RhO2 is derived as a function of temperature: Delta G(f)degrees(RhO2)(+/- 71)/J mol(-1) = 238,418 + 179.89T Using an estimated value of Delta C-p degrees; for the formation reaction of RhO2 from its elements, the standard enthalpy of formation, standard entropy and isobaric heat capacity of RhO2 at 298.15 K are evaluated: Delta H-f degrees (298.15 K)(+/- 164)/kJ mol(-1) = -244.94, S degrees (298.15 K)(+/- 3.00)/J mol(-1) K-1 = 45.11 and C-p degrees(298.15 K)(+/- 2.6)1mol(-1) K-1 =64.28. (C) 2010 Elsevier B.V. All rights reserved.

Laser-fused refractory oxides for optical coatings

Laser sintering was carried out using a high power continuous-wave CO2 laser to prepare pellets of zirconia (ZrO2), hafnia (HfO2) and yttria (Y2O3) mixed oxides as starting materials in the deposition of optical coatings. Hardened recrystallized pellets appeared to have been formed during laser treatment. X-ray diffraction analysis revealed a monoclinic-to-tetragonal phase transformation in the binary system while the ternary system was found to have a mixture of two crystalline phases. Cross-sectional scanning electron microscopy showed two isothermal crystalline regions in the ternary system. The optical inhomogeneity was low in the films deposited from the laser-fused pellets, but the absorption at a wavelength of 351 nm increased with increasing HfO2 content. The films deposited from laser-fused pellets were analysed by electron spectroscopy for chemical analysis and found to be stoichiometric and homogeneous.