Nanocrystalline TiO(2) preparation by microwave route and nature of anatase-rutile phase transition in nano TiO(2)

Nanopowders of TiO(2) has been prepared using a microwave irradiation-assisted route, starting from a metalorganic precursor, bis(ethyl-3-oxo-butanoato)oxotitanium (IV), [TiO(etob)(2)](2). Polyvinylpyrrolidone (PVP) was used as a capping agent. The as-prepared amorphous powders crystallize into anatase phase, when calcined. At higher calcination temperature, the rutile phase is observed to form in increasing quantities as the calcination temperature is raised. The structural and physicochemical properties were measured using XRD, FT-IR, SEM, TEM and thermal analyses. The mechanisms of formation of nano-TiO(2) from the metal-organic precursor and the irreversible phase transformation of nano TiO(2) from anatase to rutile structure at higher temperatures have been discussed. It is suggested that a unique step of initiation of transformation takes place in Ti(1/2)O layers in anatase which propagates. This mechanism rationalizes several key observations associated with the anatase rutile transformation.

Electroless Ni-W-P Coating and Its Nano-WS2 Composite: Preparation and Properties

The ternary alloy Ni-W-P and its WS2 nanocomposite coatings were successfully obtained on low-carbon steel using the electroless plating technique. The sodium tungstate (Na2WO4) concentration in the bath was varied to obtain Ni-W-P deposits containing various Ni and P contents. WS2 composite was obtained with a suitable concentration of Na2WO4 in Ni-P coating. These deposits were characterized by X-ray diffraction (XRD), scanning electron microscopy (SEM), and energy-dispersive X-ray analysis (EDX) studies. The corrosion behavior was investigated by potentiodynamic polarization and electrochemical impedance spectroscopy (EIS) studies in 3.5 wt % NaCl solutions, and the corrosion rates of the coatings for Ni-P, Ni-W-P, and Ni-W-P-WS2 were found to be 2.571 x 10(-5), 8.219 x 10(-7), and 7.986 x 10(-7) g/h, respectively. An increase in the codeposition of alloying metal tungsten (W) enhanced the corrosion resistance and microhardness and changed the structure and morphology of the deposits. Incorporation of WS2 nanoparticles to Ni-W-P alloy coating reduced the coefficient of friction from 0.16 to 0.11 and also helped in improving the corrosion resistance of the coating further.

Synthesis and characterization of nano silicon and titanium nitride powders using atmospheric microwave plasma technique

We have demonstrated a simple, scalable and inexpensive method based on microwave plasma for synthesizing 5 to 10 g/h of nanomaterials. Luminescent nano silicon particles were synthesized by homogenous nucleation of silicon vapour produced by the radial injection of silicon tetrachloride vapour and nano titanium nitride was synthesized by using liquid titanium tetrachloride as the precursor. The synthesized nano silicon and titanium nitride powders were characterized by XRD, XPS, TEM, SEM and BET. The characterization techniques indicated that the synthesized powders were indeed crystalline nanomaterials.

Preparation and characterization chemistry of nano-crystalline Ni-Cu-Zn ferrite

In submitted research; nanocrystalline powders having elements Ni0.5Cu0.25Zn0.25Fe2 xInxO4 with varied amounts of indium ( x = 0.0, 0.1, 0.2, 0.3 and 0.4) were grown-up by modified citrate to nitrate alchemy. The realism of single phase cubic spinel creation of the synthesized ferrite samples was studied by the DTA-TGA, XRD, SEM, EDX, FT-IR, VSM and dielectric measurements. SEM was applied to inspect the morphological variations and EDX was used to determine the compositional mass ratios. The studies on the dielectric constant (epsilon'), dielectric loss (epsilon `'), loss tangent (tan delta), ac conductivity (sigma(ac)), resistive and reactive parts of the impedance analysis (Z' and Z `') at room temperature were also carried out. The saturation magnetizations (Ms) were determined using the vibrating sample magnetometer (VSM). Ms. decreased with the increase In3+ doping content, as Fe3+ of 5(mu B) ions are replaced by In3+ of 5 mu(B) ions. (C) 2012 Elsevier B. V. All rights reserved.

Energy-efficient synthesis of ferrite powders and films

In recent years, there has been significant effort in the synthesis of nanocrystalline spinel ferrites due to their unique properties. Among them, zinc ferrite has been widely investigated for countless applications. As traditional ferrite synthesis methods are energy- and time-intensive, there is need for a resource-effective process that can prepare ferrites quickly and efficiently without compromising material quality. We report on a novel microwave-assisted soft-chemical synthesis technique in the liquid medium for synthesis of ZnFe2O4 powder below 100 °C, within 5 min. The use of β-diketonate precursors, featuring direct metal-to-oxygen bonds in their molecular structure, not only reduces process temperature and duration sharply, but also leads to water-soluble and non-toxic by-products. As synthesized powder is annealed at 300 °C for 2 hrs in a conventional anneal (CA) schedule. An alternative procedure, a 2-min rapid anneal at 300 °C (RA) is shown to be sufficient to crystallize the ferrite particles, which show a saturation magnetization (MS) of 38 emu/g, compared with 39 emu/g for a 2-hr CA. This signifies that our process is efficient enough to reduce energy consumption by ∼85% just by altering the anneal scheme. Recognizing the criticality of anneal process to the energy budget, a more energy-efficient variation of the reaction process was developed, which obviates the need for post-synthesis annealing altogether. It is shown that the process also can be employed to deposit crystalline thin films of ferrites.

Interconnected, ultrafine osmium nanoclusters: preparation and surface enhanced Raman scattering activity

Interconnected Os nanochains consisting of ultrafine particles prepared using a simple procedure yield a coupled surface plasmon peak in the visible region and can be used as substrates for surface enhanced Raman scattering of various analytes.

Preparation of Self Assembled Sodium Oleate Monolayer on Mild Steel and Its Corrosion Inhibition Behavior in Saline water

A self assembled monolayer (SAM) of sodium oleate was generated on mild steel by the dip coating method. Formation of the SAM on mild steel was examined using Infrared Reflection Absorption Spectroscopy (IRRAS) and contact angle measurements. The chemical and anticorrosive properties of the SAM were analyzed using different techniques. IRRAS and water contact angle data revealed the crystallinity and chemical stability of the SAM modified mild steel. The electrochemical measurements showed that the mild steel with the sodium oleate derived SAM exhibited better corrosion resistance in saline water. The effect of temperature and pH on the SAM formation and its anti corrosion ability was explored.

Preparation of zinc oxide coatings by using newly designed metal-organic complexes of Zn: Effect of molecular structure of the precursor and surfactant over the crystallization, growth and luminescence

We report large scale deposition of tapered zinc oxide (ZnO) nanorods on Si(100) substrate by using newly designed metal-organic complex of zinc (Zn) as the precursor, and microwave irradiation assisted chemical synthesis as a process. The coatings are uniform and high density ZnO nanorods (similar to 1.5 mu m length) grow over the entire area (625 mm(2)) of the substrate within 1-5 min of microwave irradiation. ZnO coatings obtained by solution phase deposition yield strong UV emission. Variation of the molecular structure/molecular weight of the precursors and surfactants influence the crystallinity, morphology, and optical properties of ZnO coatings. The precursors in addition with the surfactant and the solvent are widely used to obtain desired coating on any substrate. The growth mechanism and the schematics of the growth process of ZnO coatings on Si(100) are discussed. (c) 2013 Elsevier B.V. All rights reserved.

Mixture of Fuels Approach for the Synthesis of SrFeO3-delta Nanocatalyst and Its Impact on the Catalytic Reduction of Nitrobenzene

A modified solution combustion approach was applied in the synthesis of nanosize SrFeO3-delta (SFO) using single as well as mixture of citric acid, oxalic acid, and glycine as fuels with corresponding metal nitrates as precursors. The synthesized and calcined powders were characterized by Fourier transform infrared spectroscopy (FT-IR), X-ray diffraction (XRD), thermogravimetric analysis and derivative thermogravimetric analysis (TG-DTG), scanning electron microscopy, transmission electron microscopy, N-2 physisorption methods, and acidic strength by n-butyl amine titration methods. The FT-IR spectra show the lower-frequency band at 599 cm(-1) corresponds to metal-oxygen bond (possible Fe-O stretching frequencies) vibrations for the perovskite-structure compound. TG-DTG confirms the formation temperature of SFO ranging between 850-900 degrees C. XRD results reveal that the use of mixture of fuels in the preparation has effect on the crystallite size of the resultant compound. The average particle size of the samples prepared from single fuels as determined from XRD was similar to 50-35 nm, whereas for samples obtained from mixture of fuels, particles with a size of 30-25 nm were obtained. Specifically, the combination of mixture of fuels for the synthesis of SFO catalysts prevents agglomeration of the particles, which in turn leads to decrease in crystallite size and increase in the surface area of the catalysts. It was also observed that the present approach also impacted the catalytic activity of the SFO in the catalytic reduction of nitrobenzene to azoxybenzene.

A critical review on in situ reduction of graphene oxide during preparation of conducting polymeric nanocomposites

Graphene oxide (GO), prepared by chemical oxidation of graphite, serves as a building block for developing polymeric nanocomposites. However, their application in electrical conductivity is limited by the fact that the oxygen sites on GO trap electrons and impede charge transport. Conducting nanocomposites can be developed by reducing GO. Various strategies have been adopted to either reduce GO ex situ, before the composite preparation, or in situ during the development of the nanocomposites. The current state of research on in situ reduction of GO during the preparation of conducting polymeric nanocomposites is discussed in this review. The mechanism and the efficiency of reduction is discussed with respect to various strategies employed during the preparation of the nanocomposite, the type of polymer used, and the processing conditions employed, etc. Its overall effect on the electrical conductivity of the nanocomposites is also discussed and the future outlook in this area is presented.

One-step synthesis of a cyclic 2,17-dioxo3,3](4,4 `)biphenylophane and first preparation of a microporous polymer network from a macrocyclic precursor by cyclotrimerization

One-step synthesis of a cyclic 2,17-dioxo3,3](4,4') biphenylophane (MC) was achieved in high yield; its structure was verified by single crystal X-ray analysis. As a first example, a microporous polymer network was formed from macrocycle MC via acid-catalysed cyclotrimerization yielding a BET surface area of ca. 570 m(2) g(-1).

Growth and electron effective mass measurements of strained Si and Si0.94Ge0.06 on relaxed Si0.62Ge0.38 buffers grown by rapid thermal chemical vapor deposition

Abstract: We report the growth and the electron cyclotron resonance measurements of n-type Si/Si0.62Ge0.38 and Si0.94Ge0.06/Si0.62Ge0.38 modulation-doped heterostructures grown by rapid thermal chemical vapor deposition. The strained Si and Si0.94Ge0.06 channels were grown on relaxed Si0.62Ge0.38 buffer layers, which consist of 0.6 mu m uniform Si0.62Ge0.38 layers and 0.5 mu m compositionally graded relaxed SiGe layers from 0 to 38% Ge. The buffer layers were annealed at 800 degrees C for 1 h to obtain complete relaxation. A 75 Angstrom Si(SiGe) channel with a 100 Angstrom spacer and a 300 Angstrom 2 X 10(19) cm(-3) n-type supply layer was grown on the top of the buffer layers. The cross-sectional transmission electron microscope reveals that the dense dislocation network is confined to the buffer layer, and relatively few dislocations terminate on the surface. The plan-view image indicates the threading dislocation density is about 4 X 10(6) cm(-2). The far-infrared measurements of electron cyclotron resonance were performed at 4 K with the magnetic field of 4-8 T. The effective masses determined from the slope of the center frequency of the absorption peak versus applied magnetic field plot are 0.203m(0) and 0.193m(0) for the two dimensional electron gases in the Si and Si0.94Ge0.06 channels, respectively. The Si effective mass is very close to that of a two dimensional electron gas in an Si MOSFET (0.198m(0)). The electron effective mass of Si0.94Ge0.06 is reported for the first time and is about 5% lower than that of pure Si.

Surface chemical studies of Thiobacillus ferrooxidans with reference to copper tolerance

A strain of Thiobacillus ferrooxidans was adapted to grow at higher concentrations of copper by single step culturing in the presence of 20 g/L (0.314 mol/L) cupric ions added to 9K medium. Exposure to copper results in change in the surface chemistry of the microorganism. The isoelectric point of the adapted strain (pI=4.7) was observed to be at a higher pH than that of the wild unadapted strain(pI=2.0). Compared to the wild strain, the copper adapted strain was found to be more hydrophobic and showed enhanced attachment efficiency to the pyrite mineral. The copper adsorption ability of the adapted strain was also found to be higher than that of the wild strain. Fourier transform infrared spectroscopy of adapted cells suggested that a proteinaceous new cell surface component is synthesized by the adapted strain. Treatment of adapted cells with proteinase-K, resulted in complete loss of tolerance to copper, reduction in copper adsorption and hydrophobicity of the adapted cells. These observations strongly suggest a role played by cell surface modifications of Thiobacillus ferrooxidans in imparting the copper tolerance to the cells and bioleaching of sulphide minerals.

Surface chemical studies on mica and galena using dextrin

The interactions of dextrin with biotite mica and galena have been investigated through adsorption, flotation, and electrokinetic measurements. The adsorption densities of dextrin onto mica continuously increase with increase of pH, while those onto galena show a maximum at pH 11.5. It is observed that the adsorption density of dextrin onto galena is quite high compared to that on mica. Both the adsorption isotherms exhibit Langmuirian behavior. Electrokinetic measurements portray conformational rearrangements of macromolecules with the loading, resulting in a shift of the shear plane, further away from the interface. Dissolution experiments indicate release of the lattice metal ions from mica and galena. Coprecipitation tests confirm polymer-metal ion interaction in the bulk solution. Dextrin does not exhibit any depressant action toward mica, whereas, with galena, the flotation recovery is decreased with an increase in pH beyond 9, in the presence of dextrin, complementing the adsorption results. Differential flotation results on a synthetic mixture of mica and galena show that mica can be selectively separated from galena using dextrin as a depressant for galena above pH 10. Possible mechanisms of interaction between dextrin and mica/galena are discussed.

Synthesis based on cyclohexadienes. Part 25. Total synthesis of (+/-)-allo-cedrol (khusiol)

The first stereoselective total synthesis of (+/-)-allo-cedrol 20, an enantiomer of khusiol and a complex sesquiterpene having a novel tricyclo[5.2.2.0(1,5)]undecane framework, is reported from 8-methoxytricyclo[6.2.2.0(1,6)]dodec-6-en-9-one 6c. The methodology involves preparation of 9-methoxytricyclo[7.2.1.0(1,6)]dodec-6-en-8-one 12 from 6c and its conversion through the compounds 8-benzyloxy-7,7-dimethyl-9-methoxytricyclo[7.2.1.0(1,6)]dodec-5-ene 38, 7-benzyloxy-8-methoxy-2,6,6-trimethyltricyclo[6.2.1.0(1,5)]undecane 48 into 8-methoxy-2,6,6-trimethyltricyclo[6.2.1.0(1,5)]undecan-7-one 49. Wittig reaction of 49 affords the olefin 50 which has been smoothly rearranged into khusione 51. Metal-ammonia reduction of khusione under specific conditions affords (+/-)-allo-cedrol. Thus, bridgehead substitution of a methoxy group by a methyl group is the key reaction in this synthesis. In an alternative strategy, attempted conversion of 8-methoxy-2-methyltricyclo[6.2.1.0(1,5)]undec-5-en-7-one 16 into khusione 37 results in an inseparable mixture of the isomers. A notable observation in this synthesis is the unusual formation of a gamma-alkylated product 27 during Woodward methylation of 16.