Mechanism of enhanced corrosion of alumina graphite refractories near slag/metal interface

All refractories show enhanced corrosion near the slag/metal interface due to Marangoni and convective flows. However, in the case of oxide refractories containing graphite flakes, corrosion is severe due to periodic oscillations in the contact angle at the slag/metal interface, resulting in cyclic dissolution of oxide and graphite into the slag and metal, respectively. Alumina--graphite (AG) refractories should be used only where they are not in simultaneous contact with slag (flux) and low carbon steel.

Influence of Tempered Microstructures on the Transformation Behaviour of Cold Deformed and Intercritically Annealed Medium Carbon Low Alloy Steel

This research is focused on understanding the role of microstructural variables and processing parameters in obtaining optimised dual phase structures in medium carbon low alloy steels. Tempered Martensite structures produced at 300, 500, and 650 degrees C, were cold rolled to varied degrees ranging from 20 to 80% deformation. Intercritical annealing was then performed at 740, 760, and 780 degrees C for various time duration ranging from 60 seconds to 60 minutes before quenching in water. The transformation behaviour was studied with the aid of optical microscopy and hardness curves. From the results, it is observed that microstructural condition, deformation, and intercritical temperatures influenced the chronological order of the competing stress relaxation and decomposition phase reactions which interfered with the rate of the expected alpha -> gamma transformation. The three unique transformation trends observed are systematically analyzed. It was also observed that the 300 and 500 degrees C tempered initial microstructures were unsuitable for the production of dual structures with optimized strength characteristics.

Microstructure and Texture Evolution in Interstitial-free (IF) Steel processed by Multi-Axial Forging

In this study, severe plastic deformation (SPD) of Ti-bearing interstitial-free steel was carried out by multi-axial forging (MAF) technique. The grain refinement achieved was comparable to that by other SPD techniques. A considerable heterogeneity was observed in the microstructure and texture. Texture of multi-axially forged steels has been evaluated and reported for the first time. The material exhibited a six-fold increase in the yield strength after four cycles of MAF.

Effect of boron addition and processing of Ti-6Al-4V on corrosion behaviour and biocompatibility

Ti-6Al-4V is widely used to prepare biomedical implant for orthopaedic and dental applications, but it is an expensive choice relative to other implant materials such as stainless steels and Co-Cr alloys, in large part due to the high manufacturing cost. Adding boron to refine the as cast microstructure of Ti-6Al-4V can eliminate the need for extensive hot working and thereby reduce processing costs. The effect of 0.1 wt-% boron addition and the choice of processing route (forging or extrusion) was studied in the context of potential biomedical applications. Corrosion tests in simulated body fluid indicated that the presence of boron increased the corrosion rate of Ti-6Al-4V and that the increase was higher for forged alloys than for extruded alloys. Boron addition and processing route were found to have a minimal effect on the viability of osteoblasts on the alloy surfaces. It is concluded that the addition of boron could offer advantages during the processing of Ti-6Al-4V for biomedical applications.

Damage quantification under sliding and seizure condition using first-of-a-kind fretting machine

In a practical situation, it is difficult to model exact contact conditions clue to challenges involved in the estimation of contact forces, and relative displacements between the contacting bodies. Sliding and seizure conditions were simulated on first-of-a-kind displacement controlled system. Self-mated stainless steels have been investigated in detail. Categorization of contact conditions prevailing at the contact interface has been carried out based on the variation of coefficient of friction with number of cycles, and three-dimensional fretting loops. Surface and subsurface micro-cracks have been observed, and their characteristic shows strong dependence on loading conditions. Existence of shear bands in the subsurface region has been observed for high strain and low strain rate loading conditions. Studies also include the influence of initial surface roughness on the damage under two extreme contact conditions. (C) 2013 Elsevier B.V. All rights reserved.