Deffect Structure of LAMNO3

LaMnO3 compositions possessing orthorhombic, rhombohedral and cubic structures and containing 12, 24 and 33% Mn4+ respectively have been investigated by X-ray diffraction, electron diffraction and high resolution electron microscopy. The study shows that the defect structure of LaMnO3 is best described in terms of the random distribution of La and Mn vacancies, rather than by anion excess. Density measurements confirm the cation vacancy model involving an equal number of La and Mn vacancies.

Preparation and dielectric properties of zinc and cadmium doped barium tantalates, Ba3Zn1?xCdxTa2O9

Members of the Ba2Zn1-xCdxTa2O9 (0 less than or equal to x less than or equal to 1) series have been synthesized by solid state reactions at 1473K. Powder x-ray diffraction studies show a cubic perovskite cell with a similar to 4.1 Angstrom which increases with increase in x. Electron diffraction studies show the presence of hexagonal ordered perovskite structure in addition to the cubic structure seen by x-rays, the x = 0.5 composition showing more ordered crystallites. These samples show high dielectric constants with a maximum (epsilon(r) = 30 at 1 kHz) for the x = 0.5 member. The dielectric loss increases with increase in x at all the frequencies under study.

Icosahedral quasicrystalline and hexagonal approximant phases in the Al-Mn-Be alloy system

We report the formation of a primitive icosahedral quasicrystal with increased stability in Al Mn-Be alloys close to the compound Al15Mn13Be2, by melt spinning and injection casting. The crystal structure of this compound was unknown. We show that in as-cast as well as heat treated condition the intermetallic phase H1 has a hexagonal structure with lattice parameters a = 1.2295 run and c = 2.4634 nm. The space group is P6(3)/mmc In the injection-cast samples, the quasicrystal coexists with another closely related hexagonal phase H2 with a = 1.2295 nm and c = 1.2317 nm with a possible space group of P6/mmm. This phase exhibits specific orientation relationships with the icosahedral quasicrystal given by [0001](hex)//2f(QC) and [01 (1) over bar0](hex)//5f(QC) where 2f(QC) and 5f(QC) represent twofold and fivefold axes respectively. Electron diffraction patterns from both phases exhibit a close resemblance to the quasicrystalline phase. It is shown that the H1 phase is closely related to mu-Al4Mn with the same e parameter while the a parameter is reduced by tau. Following Kreiner and Franzen, it is postulated that both structures (H1 and H2) can be understood by a simple hexagonal packing of I13 clusters.

A Study of Nanostructures of Thin Films in B–C–N System Produced by Pulsed Laser Deposition and Nitrogen Ion-Beam-Assisted Pulsed Laser Deposition

We report the synthesis of thin films of B–C–N and C–N deposited by N+ ion-beam-assisted pulsed laser deposition (IBPLD) technique on glass substrates at different temperatures. We compare these films with the thin films of boron carbide synthesized by pulsed laser deposition without the assistance of ion-beam. Electron diffraction experiments in the transmission electron microscope shows that the vapor quenched regions of all films deposited at room temperature are amorphous. In addition, shown for the first time is the evidence of laser melting and subsequent rapid solidification of B4C melt in the form of micrometer- and submicrometer-size round particulates on the respective films. It is possible to amorphize B4C melt droplets of submicrometer sizes. Solidification morphologies of micrometer-size droplets show dispersion of nanocrystallites of B4C in amorphous matrix within the droplets. We were unable to synthesize cubic carbon nitride using the current technique. However, the formation of nanocrystalline turbostratic carbo- and boron carbo-nitrides were possible by IBPLD on substrate at elevated temperature and not at room temperature. Turbostraticity relaxes the lattice spacings locally in the nanometric hexagonal graphite in C–N film deposited at 600 °C leading to large broadening of diffraction rings.

Structural, optical, and electrical properties of bulk single crystals of InAsxSb(1-x) grown by rotatory Bridgman method

Radially-homogeneous and single-phase InAsxSb(1−x) crystals, up to 5.0 at. % As concentration, have been grown using the rotatory Bridgman method. Single crystallinity has been confirmed by x-ray and electron diffraction studies. Infrared transmission spectra show a continuous decrease in optical energy gap with the increase of arsenic content in InSb. The measured values of mobility and carrier density at room temperature (for x = .05) are 5.6×104 cm2/V s and 2.04×1016 cm−3, respectively.

Relaxor behavior of K0.5La0.5Bi2Nb2O9 ceramics

K0.5La0.5Bi2Nb2O9, a relaxor, was synthesized and the structural studies confirmed it to be an n = 2 member of the Aurivillius oxides. The ½{h00} and ½{hk0} types of superlattice reflections in the electron diffraction patterns reflected the presence of ordered polar regions. A broad dielectric peak with frequency dependent dielectric maximum temperature was observed. The dielectric relaxation obeyed the Vogel-Fulcher relation wherein Ea = 0.04 eV, Tf = 428 K,and ωo = 1010 Hz. The diffuseness parameter γ = 2.003 established the relaxor nature and it was attributed to the A-site cationic disorder. The piezoelectric d31 coefficient was 0.5 pC/N at 300 K and 2 pC/N at 480 K.

Quasicrystals and their crystalline homologues in the Al–Mn–Cu ternary alloys

Electron diffraction and high-resolution electron microscopy have been employed to differentiate among icosahedral, decagonal and crystalline particles that occur in as-cast and rapidly solidified Al-Mn-Cu alloys. The resemblance between decagonal quasicrystals and crystals in their electron diffraction patterns is striking. The crystalline structure is based on the orthorhombic ‘Al3Mn’ structure, but also a new monoclinic phase called ‘X’ has been discovered and described here. The present observations are also closely related to the orthorhombic structures in Al60Mn11Ni4. The occurrence of fine-scale twinning and fragmentation into domains explains the complex diffraction effects.

Studies towards synthesis, evolution and alignment characteristics of dense, millimeter long multiwalled carbon nanotube arrays

We report the synthesis of aligned arrays of millimeter long carbon nanotubes (CNTs), from benzene and ferrocene as the molecular precursor and catalyst respectively, by a one-step chemical vapor deposition technique. The length of the grown CNTs depends on the reaction temperature and increases from similar to 85 mu m to similar to 1.4 mm when the synthesis temperature is raised from 650 to 1100 degrees C, while the tube diameter is almost independent of the preparation temperature and is similar to 80 nm. The parallel arrangement of the CNTs, as well as their tube diameter can be verified spectroscopically by small angle X-ray scattering (SAXS) studies. Based on electron diffraction scattering (EDS) studies of the top and the base of the CNT films, a root growth process can be deduced.

Complex structural phase transitions in slightly Ca modified Na0.5Bi0.5TiO3

A temperature dependent neutron powder diffraction study, in conjunction with dielectric and ferroelectric characterization, of slightly Ca modified Na0.5Bi0.5TiO3 (NBT) revealed an instability with regard to a non-polar orthorhombic (Pbnm) distortion above room temperature. This intermediate orthorhombic phase has earlier been reported for unmodified NBT by electron diffraction studies, but has never been captured by global (x-ray/neutron) diffraction techniques. Calcium substitution seems to amplify the magnitude of this intermediate orthorhombic distortion thereby making the corresponding superlattice reflections become visible in the neutron diffraction pattern. The study revealed the following sequence of very complex structural evolution with temperature: Cc -> Cc + Pbnm -> Pbnm + P4/mbm -> P4/mbm -> Pm (3) over barm.

Metastable morphotropic phase boundary state in the multiferroic BiFeO3-PbTiO3

Temperature-time study of the magnetoelectric multiferroic (1-x)BiFeO3-(x)PbTiO3 by x-ray and electron diffraction on the reported morphotropic phase boundary (MPB) compositions revealed that this MPB does not correspond to the equilibrium state. The MPB like state is rather of metastable nature and arise due to kinetic arrest of metastable rhombohedral (R3c) phase, along with the equilibrium tetragonal (P4mm) phase. The life time of the metastable R3c nuclei is very sensitive to composition and temperature, and nearly diverges at x -> 0.27. The MPB like state appears only if the system is cooled before the metastable R3c nuclei could vanish. These findings resolve the long standing controversy with regard to seemingly erratic phase formation behaviour reported by different groups and provides a rational basis for developing genuine equilibrium MPB compositions in this system for better piezoelectric properties. (C) 2013 AIP Publishing LLC.

Structural characterization of electrodeposited boron

Structural characterization of electrodeposited boron was carried out by using transmission electron microscopy and Raman spectroscopy. Electron diffraction and phase contrast imaging were carried out by using transmission electron microscopy. Phase identification was done based on the analysis of electron diffraction patterns and the power spectrum calculated from the lattice images from thin regions of the sample. Raman spectroscopic examination was carried out to study the nature of bonding and the allotropic form of boron obtained after electrodeposition. The results obtained from transmission electron microscopy showed the presence of nanocrystallites embedded in an amorphous mass of boron. Raman microscopic studies showed that amorphous boron could be converted to its crystalline form at high temperatures.

Relaxor behaviour in BaBi4Ti4O15 ceramics fabricated using the powders obtained by mechanochemically assisted synthesis route

Mechanochemically activated reactants were found to facilitate the synthesis of fine powders comprising 200-400 nm range crystallites of BaBi4Ti4O15 at a significantly lower temperature (700 A degrees C) than that of solid-state reaction route. Reactants (CaCO3, Bi2O3 and TiO2) in stoichiometric ratio were ball milled for 48 h to obtain homogeneous mixture. The evolution of the BaBi4Ti4O15 phase was systematically followed using X-ray powder diffraction (XRD) technique. Scanning electron microscopy (SEM) and transmission electron microscopy (TEM) were employed to probe its structural and microstructural details. The electron diffraction studies established the presence of correlated octahedral rotations and associated long-range polar ordering. High-resolution TEM imaging nevertheless revealed structural inhomogeneities leading to intergrowth defects. Dense BaBi4Ti4O15 ceramics with an average grain size of 0.9 mu m were fabricated using mechanochemically assisted synthesized powders at relatively low temperature (1000 A degrees C). The effect of grain size on the dielectric and relaxor behaviour of BaBi4Ti4O15 ceramics was investigated. Fine-grained ceramics (average grain size similar to 0.9 mu m) showed higher diffusion in phase transition, lower temperature of phase transition, lower Vogel-Fulcher freezing temperature and higher activation energy for the polarization reversal than those for coarse-grained ceramics (average grain size similar to 7 mu m) fabricated via the conventional solid-state reaction route.

Electron and x-ray diffraction studies on Al86Fe14, Al82Fe18 and Al75Fe25 quasicrystals

Electron and x-ray diffraction experiments on the metlt-spun Al100−x Fe x (x=14, 18, 25) alloys are carried out. It is observed that all the melt-spun alloys possessing the quasi-crystalline phases have icosahedral point-group symmetry.

Electron microscopy and diffraction of icosahedral twins in an aluminium—manganese alloy

The existence of icosahedral twins has been established in Al-10at.% Mn alloy. By a stereographic approach a close resemblance to the decagonal phase is pointed out. The simulation of twin diffraction patterns has been done based on the projection formalism. The physical significance of twinning in terms of hyperdimensional projection is discussed.