Process induced electroactive beta-polymorph in PVDF: effect on dielectric and ferroelectric properties

The effects of various processing conditions, like annealing, poling, mechanical rolling and their combinations, on the dielectric and ferroelectric properties of PVDF poly(vinylidene fluoride)] were systematically studied in this work. Further, the effect of processing sequence on the structure and properties was investigated. While all the processing conditions adopted here resulted in phase transformation of the alpha- to electroactive beta-polymorph in PVDF, the fraction of beta-phase developed was observed to be strongly contingent on the adopted process. The transformation of alpha- to electroactive beta-polymorph was determined by X-ray diffraction and FTIR. The neat PVDF showed only beta-phase, whereas mechanically rolled samples exhibited the highest ca. 85% beta-phase in PVDF. Both the permittivity and the loss tangent decreased in the samples which had undergone different processing conditions. The polarization-electric field (P-E) loops for all the samples were evaluated. Interestingly, the energy density, estimated from the electrical displacement-electric field (D-E) loops, was observed to be highest for the poled samples which were initially rolled. The results indicate that various processing conditions can influence the dielectric and the ferroelectric properties differently.

Dielectric Impedance Studies of Poly(vinyl butyral)-Cenosphere Composite Films

In the current study, amino silane functionalized cenosphere particles was used as a reinforcing filler in poly(vinyl butyral) matrix and were made by melt blending. The changes observed in the dielectric performance of the composite films with varying weight percentage of cenosphere particle in the matrix were investigated. The dielectric property and impedance spectroscopy were evaluated as a function of applied frequency in the range of 50 Hz to 5 MHz. It is observed that, because of orientation polarization of the PVB polymer, the permittivity and impedance decrease, whereas conductivity increases. Tangent loss graph indicates that the property of the matrix is associated with geometrical fill factor and the lowest quality factor. Therefore, above 10 kHz, these composites can be considered as dielectric loss-less material. (C) 2013 Society of Plastics Engineers

Perovskite ceramic nanoparticles in polymer composites for augmenting bone tissue regeneration

There is increasing interest in the use of nanoparticles as fillers in polymer matrices to develop biomaterials which mimic the mechanical, chemical and electrical properties of bone tissue for orthopaedic applications. The objective of this study was to prepare poly(epsilon-caprolactone) (PCL) nanocomposites incorporating three different perovskite ceramic nanoparticles, namely, calcium titanate (CT), strontium titanate (ST) and barium titanate (BT). The tensile strength and modulus of the composites increased with the addition of nanoparticles. Scanning electron microscopy indicated that dispersion of the nanoparticles scaled with the density of the ceramics, which in turn played an important role in determining the enhancement in mechanical properties of the composite. Dielectric spectroscopy revealed improved permittivity and reduced losses in the composites when compared to neat PCL. Nanofibrous scaffolds were fabricated via electrospinning. Induction coupled plasma-optical emission spectroscopy indicated the release of small quantities of Ca+2, Sr+2, Ba+2 ions from the scaffolds. Piezo-force microscopy revealed that BT nanoparticles imparted piezoelectric properties to the scaffolds. In vitro studies revealed that all composites support osteoblast proliferation. Expression of osteogenic genes was enhanced on the nanocomposites in the following order: PCL/CT>PCL/ST>PCL/BT>PCL. This study demonstrates that the use of perovskite nanoparticles could be a promising technique to engineer better polymeric scaffolds for bone tissue engineering.

Effect of Ni-Zr codoping on dielectric and magnetic properties of SrFe12O19 via sol-gel route

Nanocrystalline strontium hexaferrites SrFe12-2x (Ni2+-Zr4+)(x)O-19] nanoparticles were successfully synthesized by sal gel process. For densification the powders were sintered at 950 degrees C/4 h. The sintered samples were characterized by X-ray diffraction (XRD), surface area measurement, and field emission scanning electron microscope (FESEM). The lattice parameter a is almost constant but c increased with x upto 0.8 and then decreased. The frequency dependent complex permittivity (epsilon and epsilon `' and permeability (mu' and mu `') and magnetic properties such as saturation magnetization (M-s), coercive field (H-c) were studied. If is observed that saturation magnetization increased gradually from 57.82 emuig to 67.2 emufg as x increased from 0.2 to 0.4 and then decreased from 672 emufg to 31.63 ernufg for x=1.0. In present study, x=0.4 shows high value of M-s 67.2 emu/g. The real part of permittivity (epsilon') remains constant upto a frequency 1 GHz and increases further with an increase of frequency, a resonance and anti resonance peak was observed above 1 GHz for all the samples. In real part of permeability (mu') the relaxation frequency is observed above 1 GHz for all the samples and it is attributed to the domain wall motion. It is well known that the permeability for polycrystalline ferrites can be described as the superposition of two different magnetizing mechanisms: spin rotation and domain wall motion. These low coercive strontium hexaferrites are suitable for magnetic recording applications in hard disks, floppy disks, video tapes, etc. (C) 2015 Elsevier B.V. All rights reserved.

Contrasting Effects of Graphene Oxide and Poly(ethylenimine) on the Polymorphism in Poly(vinylidene fluoride)

The nature of interaction between a heteronucleating agent (graphene oxide, GO) and a strongly polar macromolecule (poly(ethylenimine), PEI) with poly(vinylidene fluoride) (PVDF) influencing the crystalline structure and morphology has been systematically investigated in this work. PEI interacts with PVDF via ion-dipole interaction, which helps in lowering the free energy barrier for nucleation thereby promoting faster crystallization. In contrast, besides interacting with PVDF, GO also promotes heteronucleation in PVDF. We observed that both GO and PEI have very different effects on the overall crystalline morphology of PVDF. For instance, the neat PVDF showed a mixture of both alpha and beta phases when cooled from the melt. However, incorporation of 0.1 wt % GO resulted in phase transformation from the stable alpha-phase to polar beta-polymorph in PVDF. In contrast, PEI, which also resulted in faster crystallization in PVDF predominantly, resulted in the stable alpha- phase. Various techniques like Fourier transform infrared spectroscopy, X-ray diffraction, and differential scanning calorimetry were employed to confirm the phase transformations in PVDF. PEI was further grafted onto GO nanosheets to understand the combined effects of both GO and PEI on the polymorphism in PVDF. The PVDF/PEI-GO composite showed a mixture of phases, predominantly rich in a. These phenomenal effects were further analyzed and corroborated with the specific interaction between GO and PEI with PVDF using X-ray photon scattering (XPS) and NMR. In addition, the dielectric permittivity increased significantly in the presence of GO and PEI in the composites. For instance, PVDF/PEI-GO showed the highest permittivity of 39 at 100 Hz.

Tuning of dielectric, pyroelectric and ferroelectric properties of 0.715Bi(0.5)Na(0.5)TiO(3)-0.065BaTiO(3)-0.22SrTiO(3) ceramic by internal clamping

This study systematically investigates the phenomenon of internal clamping in ferroelectric materials through the formation of glass-ceramic composites. Lead-free 0.715Bi(0.5)Na(0.5)TiO(3)-0.065BaTiO(3)-0.22SrTiO(3) (BNT-BT-ST) bulk ferroelectric ceramic was selected for the course of investigation. 3BaO - 3TiO(2) - B2O3 (BTBO) glass was then incorporated systematically to create sintered samples containing 0%, 2%, 4% and 6% glass (by weight). Upon glass induction features like remnant polarization, saturation polarization, hysteresis losses and coercive field could be varied as a function of glass content. Such effects were observed to benefit derived applications like enhanced energy storage density similar to 174 k J/m(3) to similar to 203 k J/m(3) and pyroelectric coefficient 5.7x10(-4) Cm-2K-1 to 6.8x10(-4) Cm-2K-1 by incorporation of 4% glass. Additionally, BNT-BT-ST depolarization temperature decreased from 457K to 431K by addition of 4% glass content. Glass incorporation could systematically increases diffuse phase transition and relaxor behavior temperature range from 70 K to 81K and 20K to 34 K, respectively when 6% and 4% glass content is added which indicates addition of glass provides better temperature stability. The most promising feature was observed to be that of dielectric response tuning. It can be also used to control (to an extent) the dielectric behavior of the host ceramic. Dielectric permittivity and losses decreased from 1278 to 705 and 0.109 to 0.107 for 6% glass, at room temperature. However this reduction in dielectric constant and loss increases pyroelectric figures of merit (FOMs) for high voltage responsivity (F-v) high detectivity (F-d) and energy harvesting (F-e) from 0.018 to 0.037 m(2)C(-1), 5.89 to 8.85 mu Pa-1/2 and 28.71 to 61.55 Jm(-3)K(-2), respectively for 4% added ceramic-glass at room temperature. Such findings can have huge implications in the field of tailoring ferroelectric response for application specific requirements. (C) 2015 Author(s).

Solution processible Cu2SnS3 thin films for cost effective photovoltaics: Characterization

Thin films of Cu2SnS3 (CTS) were deposited by the facile solution processed sol-gel route followed by a low-temperature annealing. The Cu-Sn-thiourea complex formation was analysed using Fourier Transform Infrared spectrophotometer (FTIR). The various phase transformations and the deposition temperature range for the initial precursor solution was determined using Thermogravimetric analysis (TGA) and Differential Scanning Calorimetry (DSC). X-Ray Diffraction (XRD) studies revealed the tetragonal phase formation of the CTS annealed films. Raman spectroscopy studies further confirmed the tetragonal phase formation and the absence of any deterioratory secondary phases. The morphological investigations and compositional analysis of the films were determined using Scanning Electron Microscopy (SEM) and Energy Dispersive Spectroscopy (EDS) respectively. Atomic Force Microscopy (AFM) was used to estimate the surface roughness of 1.3 nm. The absorption coefficient was found to be 10(4) cm(-1) and bandgap 1.3 eV which qualifies CTS to be a potential candidate for photovoltaic applications. The refractive index, extinction coefficient and relative permittivity of the film were measured by Spectroscopic ellipsometry. Hall effect measurements, indicated the p type nature of the films with a hole concentration of 2 x 10(18) cm(-3), electrical conductivity of 9 S/cm and a hole mobility of 29 cm(2)/V. The properties of CTS as deduced from the current study, present CTS as a potential absorber layer material for thin film solar cells. (C) 2015 Elsevier B.V. All rights reserved.