Solution processed Cu2SnS3 thin films for visible and infrared photodetector applications

The Cu2SnS3 thin films were deposited using an economic, solution processible, spin coating technique. The films were found to possess a tetragonal crystal structure using X-ray diffraction. The film morphology and the particle size were determined using scanning electron microscopy. The various planes in the crystal were observed using transmission electron microscopy. The optimum band gap of 1.23 eV and a high absorption coefficient of 104 cm-1 corroborate its application as a photoactive material. The visible and infrared (IR) photo response was studied for various illumination intensities. The current increased by one order from a dark current of 0.31 mu A to a current of 1.78 mu A at 1.05 suns and 8.7 mu A under 477.7 mW/cm(2) IR illumination intensity, at 3 V applied bias. The responsivity, sensitivity, external quantum efficiency and specific detectivity were found to be 10.93 mA/W, 5.74, 2.47% and 3.47 x 10(10) Jones respectively at 1.05 suns and 16.32 mA/W, 27.16, 2.53% and 5.10 x 10(10) Jones respectively at 477.7 mW/cm(2) IR illumination. The transient photoresponse was measured both for visible and IR illuminations. (C) 2016 Author(s).

Multiple emissive triarylborane-A(2)H(2) and triarylborane-Zn-A(2)H(2) porphyrin conjugates

Triarylborane-A(2)H(2) (1) and triarylborane-Zn-A(2)H(2) porphyrins (2) have been synthesized by acid catalyzed condensation of 4-dimesitylboryl-benzaldehyde and dipyrromethane under ambient conditions. Compounds 1 and 2 showed multiple emission bands upon excitation at the triarylborane dominated absorption region (350 nm). Detailed experimental and computational studies show that the multiple emission features of 1 and 2 arise as a result of a partial energy transfer from the donor (triarylborane) to the acceptor (porphyrin) moieties. Compounds 1 and 2 showed very high selectivities towards fluoride ions compared to other competing anions.