Investigations into the structural and down-shifting and up-conversion luminescence properties of Ba2Na1-3xErxNb5O15 (0 <= x <= 0.06) nanocrystalline phosphor synthesized via sol-gel route

The present work deals with the structural and efficient down-shifting (DS) and up-conversion (UC) luminescence properties of erbium ion (Er3+) doped nanocrystalline barium sodium niobate (Ba2Na1-3xErxNb5O15, where x = 0, 0.02, 0.04 and 0.06) powders synthesized via novel citrate-based sol-gel route. The monophasic nature of the title compound was confirmed via x-ray powder diffraction followed by FT-IR studies. High-resolution transmission electron microscopy (HRTEM) facilitated the establishment of the nanocrystalline phase and the morphology of the crystallites. The Kubelka-Munk function, based on diffused reflectance studies and carried out on nano-sized crystallites, was employed to obtain the optical band-gap. The synthesized nanophosphor showed efficient DS/PL-photoluminescence and UC luminescence properties, which have not yet been reported so far in this material. The material emits intense DS green emission on excitation with 378 nm radiation. Interestingly, the material gives intense UC emission in the visible region dominated by green emission and relatively weak red emission on 976 nm excitation (NIR laser excitation). Such a dual-mode emitting nanophosphor could be very useful in display devices and for many other applications.

Development of an automated ultrasonic spray pyrolysis system and the growth of Cu2ZnSnS4 thin films

An automated ultrasonic spray pyrolysis system is fabricated for the growth of thin films. The system is equipped with x-y movement and enables film deposition in different patterns and spray rates. Cu-2(Zn,Sn)S-4 (CZTS) films are deposited using this setup. The substrate temperature (T-s) is varied from 240 to 490 degrees C. Kesterite CZTS phase is observed in all the films together with binary phases. The films prepared at T-s <340 degrees C showed SnxSy phase and those at T-s >340 degrees C showed Cu2S phase. Sulfur incorporation is maximum (40%) at 440 degrees C and the films showed better morphology. The Cu and S concentrations are varied to remove binary phases. Depth wise elemental analysis confirmed the existence of single phase CZTS. p-Type CZTS films of resistivity in the range of 10(2)-10(3) Omega cm are obtained. (C) 2015 Elsevier B.V. All rights reserved.