Combustion synthesis of rare earth cuprates

Rare earth cuprates, La2CuO4 Nd2CuO4, La1.8M0.2CuO4 (M=Ca.Sr) and Nd1.85Ce0.15CuO4 have been prepared by the combustion of redox mixtures containing corresponding metal nitrates and maleic hydrazide, C4H4N2O2, at 350°C. The solid combustion products are submicron size amorphous powders which on heat treatment (700°C, 30 minutes) yield crystalline single phase cuprates. Strontium doped lanthanum cuprate, La1.8Sr0.2CuO4, shows an onset of superconductivity at 36K.

Electroless nickel hydroxide: synthesis and characterization

An electroless method of nickel hydroxide synthesis through the complexation-precipitation route which yields a fine particle material having a specific surface area of 178 m2 g–1 has been described. The morphology of this material as revealed by electron microscopy is distinctly different from the turbostratic nature of electrosynthesized nickel hydroxide. While the long range structure as shown by the X-ray diffraction pattern is similar to that of beta-Ni(OH)2, the short range structure as revealed by infrared spectroscopy incorporates characteristics similar to that of agr-Ni(OH)2. Cyclic voltammetry studies show that the electroless nickel hydroxide has a higher coulombic efficiency (>90%), a more anodic reversible potential and a higher degree of reversibility compared to the electrosynthesized nickel hydroxide and conventionally prepared nickel hydroxide.

A Convenient High-Yield Room-Temerature Synthesis of Mixed Tri(Amino) Silanes by Transmination of Tris(Dicyclohexylamino) Silane And-Their Characterization

Tris(dicyclohexylamino)silane. (DCA)3SiH. is prepared by the reaction of trichlorosilane with dicyclohexylamine. This is found to undergo transamination reactions with other secondary amines (R2NH). such as pyrrolidine, piperidine, hexamethyleneimine. morpholine. N-methylpiperazine and diethylamine to yield mixed tri(amino)silanes of the formula (DCA)(R2N)2SiH in quantitative yields. These new derivatives are found to be moisture sensitive and hydrolyze to yield their respective amines, hydrogen and silica. They are found to be stable in an inert atmosphere. They have been characterized by IR, NMR (H-1, Si-29), mass spectroscopy and CHN analysis. N-15 NMR for one of the compounds has been done.

Bile-Acids in Asymmetric-Synthesis.2. Cholic-Acid Derived Novel Chiral Auxiliaries For Asymmetric Diels-Alder Reactions

Cholic acid-based chiral acrylate 5 yields a Diels-Alder adduct with cyclopent

Bridging the Ruddlesden–Popper and the Dion–Jacobson series of layered perovskites: synthesis of layered oxides, A2–xLa2Ti3–xNbxO10(A = K, Rb), exhibiting ion exchange

Solid solutions of the formula, A2–xLa2Ti3–xNbxO10(A = K, Rb), exist for the range 0[less-than-or-eq]x[less-than-or-eq]1.0, bridging n= 3 members of the Ruddlesden–Popper series (A2La2Ti3O10) and the Dion–Jacobson series (ALa2Ti2NbO10). For 0[less-than-or-eq]x[less-than-or-eq]0.75, the phases possess body-centred structures characteristic of the Ruddlesden–Popper phases, while the x= 1 members are isostructural with KCa2Nb3O10(A = K) and CsCa2Nb3O10(A = Rb). Protonated derivatives, H2–xLa2Ti3–xNbxO10, which are prepared by ion exchange, retain the structural difference of the parent phases. A difference in the Brønsted acidity of the protonated derivatives revealed by intercalation experiments with organic bases seems to be related to this structural difference.

Chiral polyhydroxylated tetrahydrothiophene derivatives: novel synthesis and structural elucidation by X-ray crystallography, NMR spectroscopy and molecular mechanics calculations

The dideoxygenation reaction of 1,3;4,6-di-O-alkylidene-2,5-di-S-methylthiocarbonyl-D-mannitol derivatives under Barton-McCombie reaction conditions gave the hexahydrodipyranothiophenes 4 and 7 instead of the expected 2,5-dideoxy products. Structural and conformational information on these novel derivatives has been obtained by NMR spectroscopy, single-crystal X-ray crystallography and molecular mechanics calculations.

Combustion synthesis and properties of fine-particle rare-earth-metal zirconates, Ln2Zr2O7

Fine-particle rare-earth-metal zirconates, Ln2Zr2O7, where Ln = La, Ce, Pr, Nd, Sm, Gd and Dy having the pyrochlore structure have been prepared using a novel combustion process. The process employs aqueous solutions of the corresponding rare-earth-metal nitrate, zirconium nitrate and carbohydrazide/urea in the required molar ratio. When the solution is rapidly heated to 350–500 °C it boils, foams and burns autocatalytically to yield voluminous oxides. The formation of single-phase Ln2Zr2O7 has been confirmed by powder X-ray diffraction, infrared and fluorescence spectroscopy. The solid combustion products are fine, having surface areas in the range 6–20 m2 g–1. The cold-pressed Pr2Zr2O7 compact when sintered at 1500 °C, 4 h in air, achieved 99% theoretical density.

Combustion Synthesis and Properties of Fine Particle Spinel Manganites

Fine particle spinel manganites have been prepared by thermal decomposition of the precursors N2H5M1/3Mn2/3(N2H3COO)3 · H2O (M = Co and Ni) and M1/3 Mn2/3(N2H3COO)2 · 2H2O (M = Mg and Zn), as well as by the combustion of redox mixtures containing M(II) nitrate (M = Mg, Co, Ni, Cu, and Zn), Mn(II) nitrate, and maleic hydrazide (MH) in the required molar ratio. Both the precursor and redox mixtures undergo self-propagating, gas-producing, exothermic reactions once ignited at 250-375°C to yield corresponding manganites in less than 5 min. Formation of single phase products was confirmed by X-ray powder diffraction patterns. The manganites are of submicrometer size and have surface area in the range 20-76 m2/g.

Coupled substitution of niobium and silicon in potassium titanyl phosphate and arsenate (KTiOPO4 and KTiOAsO4. Synthesis and nonlinear optical properties of KTi1-xNbxOX1-xSixO4 (X = P, As)

Coupled substitution of Nb(V) and Si(IV) for Ti(IV) and P(V)/As(V) in KTiOP04 (KTP) and KTiOAsO4 (KTA) giving new series of nonlinear optical materials, KTi1-xNbxOX1-xSixO4 (X=P,As), has been investigated. Substitution up to x = 0.40 readily occurs, the members retaining the orthorhombic (Pna2(1)) structure of KTP. The second harmonic generation (SHG) property of the parent KTP and KTA is not adversely affected by the coupled substitution. SHG intensity of the powder samples of the X = P series shows a slight increase with x up to x = 0.15; for 0.15 < x less-than-or-equal-to 0.40, there is a decrease in SHG intensity as compared to that for KTP. A similar trend in SHG intensity is seen for the arsenic analogs.

Mechanical alloying—a novel synthesis route for amorphous phases

Mechanical alloying (MA) pioneered by Benjamin is a technique for the extension of solid solubility in systems where the equilibrium solid solubility is limited. This technique has, in recent years, emerged as a novel alternate route for rapid solidification processing (RSP) for the production of metastable crystalline, quasicrystalline, amorphous phases and nanocrystalline materials. The glass-forming composition range (GFR), in general, is found to be much wider in case of MA in comparison with RSP. The amorphous powders produced by MA can be compacted to bulk shapes and sizes and can be used as precursors to obtain high strength materials. This paper reports the work done on solid state amorphization by MA in Ti-Ni-Cu and Al-Ti systems where a wide GFR has been obtained. Al-Ti is a classic case where no glass formation has been observed by RSP, while a GFR of 25–90 at.% Ti has been obtained in this system, thus demonstrating the superiority of MA over RSP. The free energy calculations made to explain GFR are also presented.

One pot synthesis of polycyclic oxygen aromatics. Part IV reaction of THP ether of 2-bromomethyl phenols

Reaction of 2-bromomethyl-1-(2′-tetrahydropyranyloxy) benzene 3a with tetrachlorocatechol(TCC) in acetone in presence of anhydrous K2CO3 resulted in the formation of diastereomeric products to which cis- & trans- 6-chloro-8-hydroxy-8-(2-oxopropyl)spiro[9H-benzo[a]xanthen- 9,2′(1′H) benzofuran]-7(8H)-one (7a & 8a) structures were assigned, along with tetrachlorocatechol ethers (5a & 6a). Similar reaction of 3a with tetrabromocatechol(TBC) gave the expected monobromo compounds 7d & 8d along with the ethers 5d & 6d. When the reaction was repeated with substrates 3b–c with TCC/TBC in ketonic solvents(acetone/methyl ethyl ketone), the corresponding compounds 5b–c to 8b–c, 5e–f to 6e–f, 7e–g & 8e–h were obtained. A suitable explanation has been given for the formation of acetonyl compound 6 in this reaction.

Organometallic chemistry of diphosphazanes *1: VIII. Synthesis, spectroscopic studies and crystal structure of fac-[Mo(CO)3(MeCN)Ph2PN(iPr)P(Ph)(DMP)], and its reactions with tertiary phosphines

The reaction of fac-[Mo(CO)3(MeCN)3] with the unsymmetrical diphosphazane Ph2PN(iPr)P(Ph)(DMP) (L) gives the complex fac-[Mo(CO)3(MeCN)(L)] (2) in almost quantitative yield. The structure of the complex has been determined by an X-ray diffraction study. The compound reacts with PR3 (where R = Ph, OPh) to give fac-[Mo(CO)3(PR3)(L)] (3a, 4a), which undergoes an intramolecular isomerization to afford mer-[Mo(CO)3(PR3)(L)] (3b, 4b). Synthesis of cis-[Mo(CO)4(L)] (1) and fac-[MO(CO)3L] (2a) and their spectroscopic data are also reported.