Influence of melt pouring temperature and plate inclination on solidification and microstructure of A356 aluminum alloy produced using oblique plate

The preparation of semisolid slurry of A356 aluminum alloy using an oblique plate was investigated. A356 alloy melt undergoes partial solidification when it flows down on an oblique plate cooled from underneath by counter flowing water. It results in continuous formation of columnar dendrites on plate wall. Due to forced convection, these dendrites are sheared off into equiaxed/fragmented grains and then washed away continuously to produce semisolid slurry at plate exit. Melt pouring temperature provides required condition of solidification whereas plate inclination enables necessary shear for producing semisolid slurry of desired quality. Slurry obtained was solidified in metal mould to produce semisolid-cast billets of desired microstructure. Furthermore, semisolid-cast billets were heat treated to improve surface quality. Microstructures of both semisolid-cast and heat-treated billets were analyzed. Effects of melt pouring temperature and plate inclination on solidification and microstructure of billets produced using oblique plate were described. The investigations involved four different melt pouring temperatures (620, 625, 630 and 635 degrees C) associated with four different plate inclinations (30 degrees, 45 degrees, 60 degrees and 75 degrees). Melt pouring temperature of 625 degrees C with plate inclination of 60 degrees shows fine and globular microstructures and it is the optimum.

Simultaneous measurements of thickness and temperature profile of the lubricant film at chip-tool interface during machining process using luminescent sensors

Simultaneous measurements of thickness and temperature profile of the lubricant film at chip-tool interface during machining have been studied in this experimental programme. Conventional techniques such as thermography can only provide temperature measurement under controlled environment in a laboratory and without the addition of lubricant. The present study builds on the capabilities of luminescent sensors in addition to direct image based observations of the chip-tool interface. A suite of experiments conducted using different types of sensors are reported in this paper, especially noteworthy are concomitant measures of thickness and temperature of the lubricant. (C) 2014 Elsevier Ltd.

Growth of TiO2 Films by RF Magnetron Sputtering for MOS Gate Dielectrics: Influence of Substrate Temperature

Titanium dioxide thin films were deposited by RF reactive magnetron sputtering technique on p-type silicon(100) substrates held at temperatures in the range 303-673 K. The influence of substrate temperature on the core level binding energies, chemical bonding configuration, crystallographic structure and dielectric properties was investigated. X-ray photoelectron spectroscopy studies and Fourier transform infrared transmittance data confirmed the formation of stoichiometric films with anatase phase at a substrate temperature of 673 K. The films formed at 303 K were nanocrystalline with amorphous matrix while those deposited at 673 K were transformed in to crystalline phase and growth of grains in pyramidal like structure as confirmed by X-ray diffraction and atomic force microscopy respectively. Metal-oxide-semiconductor capacitors were fabricated with the configuration of Al/TiO2/Si structures. The current voltage, capacitance voltage and conductance voltage characteristics were studied to understand the electrical conduction and dielectric properties of the MOS devices. The leakage current density (at gate voltage of 2 V) decreased from 2.2 x 10(-6) to 1.7 x 10(-7) A/cm(2), the interface trap density decreased from 1.2 x 10(13) to 2.1 x 10(12) cm(-2) eV(-1) and the dielectric constant increased from 14 to 36 with increase of substrate temperature from 303 to 673 K.

Electric field and temperature dependence of the local structural disorder in the lead-free ferroelectric Na0.5Bi0.5TiO3: An EXAFS study

The complex nature of the structural disorder in the lead-free ferroelectric Na1/2Bi1/2TiO3 has a profound impact on the perceived global structure and polar properties. In this paper, we have investigated the effect of electric field and temperature on the local structure around theBi and Ti atoms using extended x-ray absorption fine structure. Detailed analysis revealed that poling brings about a noticeable change in the bond distances associated with the Bi-coordination sphere, whereas the Ti coordination remains unaffected. We also observed discontinuity in the Bi-O bond lengths across the depolarization temperature of the poled specimen. These results establish that the disappearance of the monoclinic-like (Cc) global distortion, along with the drastic suppression of the short-ranged in-phase octahedral tilt after poling B. N. Rao et al., Phys. Rev. B 88, 224103 (2013)] is a result of the readjustment of theA-O bonds by the electric field, so as to be in conformity with the rhombohedral R3c structure.

High temperature thermoelectric properties of Zr and Hf based transition metal dichalcogenides: A first principles study

We investigate the electronic and thermal transport properties of bulk MX2 compounds (M = Zr, Hf and X = S, Se) by first-principles calculations and semi-classical Boltzmann transport theory. The band structure shows the confinement of heavy and light bands along the out of plane and in-plane directions, respectively. This results in high electrical conductivity (sigma) and large thermopower leading to a high power factor (S-2 sigma) for moderate n-type doping. The phonon dispersion demonstrates low frequency flat acoustical modes, which results in low group velocities (v(g)). Consequently, lowering the lattice thermal conductivity (kappa(latt)) below 2 W/m K. Low kappa(latt) combined with high power factor results in ZT > 0.8 for all the bulk MX2 compounds at high temperature of 1200 K. In particular, the ZT(max) of HfSe2 exceeds 1 at 1400 K. Our results show that Hf/Zr based dichalcogenides are very promising for high temperature thermoelectric application. (C) 2015 AIP Publishing LLC.

The nature of the charge-ordered state in Y0.5Ca0.5MnO3 with a very small average radius of the A-site cations

A detailed investigation of Y0.5Ca0.5MnO3 with a very small radius of the A-site cations ([r(A)] approximate to 1.13 Angstrom reveals the occurrence of a charge-ordering transition in the paramagnetic state, at a relatively high temperature of 260 K. The orthorhombic lattice distortion, as measured by the dimensionless index D, is large (similar to 1.75%) over the entire 300-100 K range, but the antiferromagnetic interactions become prominent only at low temperatures (< 160 K). The charge-ordering gap in Y0.5Ca0.5MnO3, measured by low-temperature vacuum tunnelling spectroscopy, is large (similar to 0.5 eV) and the charge-ordered state is unaffected by the application of a magnetic field of 6 T. The study indicates that the nature of charge-ordering in Y0.5Ca0.5MnO3 which is dominated by the cooperative Jahn-Teller effect and the associated lattice distortion is distinctly different from analogous manganates with larger [r(A)].

Effect of antimony addition on the thermal and electrical-switching behavior of bulk Se-Te glasses

The thermal properties and electrical-switching behavior of semiconducting chalcogenide SbxSe55-xTe45 (2 <= x <= 9) glasses have been investigated by alternating differential scanning calorimetry and electrical-switching experiments, respectively. The addition of Sb is found to enhance the glass forming tendency and stability as revealed by the decrease in non-reversing enthalpy Delta H-nr. and an increase in the glass-transition width Delta T-g. Further, the glass-transition temperature of SbxSe55-xTe45 glasses, which is a measure of network connectivity, exhibits a subtle increase, suggesting a meager network growth with the addition of Sb. The crystallization temperature is also observed to increase with Sb content. The SbxSe55-xTe45 glasses (2 <= x <= 9) are found to exhibit memory type of electrical switching, which can be attributed to the polymeric nature of network and high devitrifying ability. The metallicity factor has been found to dominate over the network connectivity and rigidity in the compositional dependence of switching voltage. which shows a profound decrease with the addition of Sb.

Use of microwaves for the synthesis and processing of materials

An overview of the synthesis of materials under microwave irradiation has been presented based on the work performed recently. A variety of reactions such as direct combination, carbothermal reduction, carbidation and nitridation have been described. Examples of microwave preparation of glasses are also presented. Great advantages of fast, clean and reduced reaction temperature of microwave methods are emphasized. The example of ZrO2-CeO2 ceramics has been used show the extraordinarily fast and effective sintering which occurs in microwave irradiation.

Towards rational synthesis of inorganic solids

There have been major advances in the past couple of years in the rational synthesis of inorganic solids: synthesis of mercury-based superconducting cuprates showing transition temperatures up to 150 K; ZrP2-xVxO7 solid solutions showing zero or negative thermal expansion; copper oxides possessing ladder structures such as La1-xSrxCuO2.5; synthesis of mesoporous oxide materials having adjustable pore size in the range 15-100 Angstrom; and synthesis of a molecular ferromagnet showing a critical temperature of 18.6 K. Despite great advances in probing the structures of solids and measurement of their physical properties, the design and synthesis of inorganic solids possessing desired structures and properties remain a challenge today. With the availability of a variety of mild chemistry-based approaches, kinetic control of synthetic pathways is becoming increasingly possible, which, it is hoped, will eventually make rational design of inorganic solids a reality.

Influence of lanthanum doping on the dielectric, ferroelectric and relaxor behaviour of barium bismuth titanate ceramics

Barium lanthanum bismuth titanate (Ba1−(3/2)xLaxBi4Ti4O15, x = 0–0.4) ceramics were fabricated using the powders synthesized via the solid-state reaction route. X-ray powder diffraction analysis confirmed the above compositions to be monophasic and belonged to the m = 4 member of the Aurivillius family of oxides. The effect of the partial presence of La3+ on Ba2+ sites on the microstructure, dielectric and relaxor behaviour of BaBi4Ti4O15 (BBT) ceramics was investigated. For the compositions pertaining to x ≤ 0.1, the dielectric constant at both room temperature and in the vicinity of the temperature of the dielectric maximum (Tm) of the parent phase (BBT) increased significantly with an increase in x while Tm remained almost constant. Tm shifted towards lower temperatures accompanied by a decrease in the magnitude of the dielectric maximum (εm) with an increase in the lanthanum content (0.1 < x ≤ 0.4). The dielectric relaxation was modelled using the Vogel–Fulcher relation and a decrease in the activation energy for frequency dispersion with increasing x was observed. The frequency dispersion of Tm was found to decrease with an increase in lanthanum doping, and for compositions corresponding to x ≥ 0.3, Tm was frequency independent. Well-developed P(polarization)–E(electric field) hysteresis loops were observed at 150 °C for all the samples and the remanent polarization (2Pr) was improved from 6.3 µC cm−2 for pure BBT to 13.4 µC cm−2 for Ba0.7La0.2Bi4Ti4O15 ceramics. Dc conductivities and associated activation energies were evaluated using impedance spectroscopy.

Effect of Dietary Unsaturated Oils on the Biosynthesis of Cholesterol, and on Biliary and Fecal Excretion of Cholesterol and Bile Acids in Rats1

The aim of the present work was to investigate whether the hypocholesterolemic effect of polyunsaturated oils is due to inhibition of cholesterol synthesis or increased excretion of cholesterol and bile acids through the bile and feces of animals. Separate groups of rats were fed diets containing 10% safflower oil, coconut oil or hydrogenated vegetable oils for 30 days, after which the hepatic cholesterol and bile acid synthesis and their excretion through the bile and feces were studied. As compared to the rats in the other two groups, those given the diet containing 10% safflower oil showed markedly increased rates of bile flow and excreted through their bile and feces markedly higher amounts of cholesterol and bile acids. At the same time incorporation of [1-14C] acetate and [2-14C] mevalonate into the liver cholesterol and conversion of [4-14C] cholesterol into 14C-bile acids were also higher in the same rats. In the light of these observations it has been discussed that in the animals given polyunsaturated oils, biliary and fecal loss of cholesterol and bile acids far outweighs the activation of cholesterol synthesis and thereby effectively lowers the serum cholesterol levels.

Size-dependent melting of nanoparticles: Hundred years of thermodynamic model

Thermodynamic model first published in 1909, is being used extensively to understand the size-dependent melting of nanoparticles. Pawlow deduced an expression for the size-dependent melting temperature of small particles based on the thermodynamic model which was then modified and applied to different nanostructures such as nanowires, prism-shaped nanoparticles, etc. The model has also been modified to understand the melting of supported nanoparticles and superheating of embedded nanoparticles. In this article, we have reviewed the melting behaviour of nanostructures reported in the literature since 1909.

Characterization of alinite cements through X-ray diffraction and mas 29Si NMR studies

Alinite cements have been synthesized using mining and steel plant wastes and pulverized fuel ash (fly ash) as raw materials and a clinkering temperature of 1150°C. The cements possess hydration characteristics comparable to those of portland cements. X-ray diffraction studies on these samples confirm the presence of alinite as the predominant phase. MAS 29Si NMR spectra have been used to distinguish alinite and alite cements. While both show resonances characteristic of Q° type silicate species, the portland cements exhibit three distinct peaks corresponding to three inequivalent SiO4 units present, while alinite shows a single sharp peak corresponding to the unique Si position.

Cation-induced crown porphyrin dimers of oxovanadium(IV)

Oxovanadium(1V) porphyrins appended with crown ether (benzo-15-crown-5) at the 5 (mono), the 5 and 10115 (cis/trans bis), the 5, 10, and 15 (tris), and the 5, 10, 15, and 20 (tetrakis) positions have been synthesized. The cation complexation behavior of these cavity-bearing porphyrins has been studied by using optical aborption and ESR spectral methods. The cations K+, Cs+, NH4+, and Ba2+, which require two crown ether cavities for complexation, induce dimerization of the porphyrins. The cation-induced dimerization constants for a representative tetrasubstituted porphyrin vary as K+ > Ba2+ > Cs+ - NH4+, and the relative stabilities of the dimers are dependent on the type of the substitution, tetrakis > tris > cis bis. ESR spectra recorded at a sample temperature of 77 K have low-field components attributed to Ah& = f 2 transitions, providing further evidence for the existence of dimers in solutions. The eclipsed sandwich dimers have V-V distances in the range 4.70 A. The relative distributions of oxovanadium crown porphyrins in terms of monomeric and dimeric forms rest on the geometric dispositions of the crown ether appendages.

An investigation of structural, magnetic and dielectric properties of R2NiMnO6 (R = rare earth, Y)

We have investigated the structure, magnetic and dielectric properties of the double perovskite oxides, R2NiMnO6 (R = Pr, Nd, Sm, Gd, Tb, Dy, Ho and Y). We could refine powder X-ray diffraction patterns of all the phases on the basis of monoclinic (P2(1)/n) double perovskite structure where Ni and Mn atoms are ordered at 2c and 2d sites, respectively. All the phases are ferromagnetic insulators exhibiting relatively low dielectric loss and dielectric constants in the range 15-25. The ferromagnetic ordering temperature of the R2NiMnO6 series seems to correlate better with the radius of R3+ atoms than with the average Ni-O-Mn angle (phi) in the double perovskite structure. These results are consistent with all samples having Mn4+ and Ni2+ With minimal antisite disorder.