Thermal Crystallization Studies On Ga-Te Glasses

Semieonducting GaxTe~oo-x (17 -< x _< 25) glasses have been prepared by melt quenching method and thermal crystallization studies carried out using differential scanning calorimetry. On heating, virgin GaxTel0o-x glasses exhibit one glass transition and two crystallization reactions.The first crystallization reaction corresponds to the precipitation of hexagonal Te and the second one to the crystallization of the matrix into zinc blende Ga2Te3 phase. If GaxTeloo-x glasses are quenched to ambient temperature from Tcrl and reheated, they exhibit the phenomenon of double glass transition.

Influence of non-stoichiometric defects on nonlinear absorption and refraction in Nd:Zn co-doped lithium niobate

Nonlinear absorption and refraction phenomena in stoichiometric lithium niobate (SLN) pure and co-doped with Zn and Nd, and congruent lithium niobate (CLN) were investigated using Z-scan technique. Femtosecond laser pulses from Ti:Sapphire laser (800 nm, 110 fs pulse width and 1 kHz repetition rate) were utilized for the experiment. The process responsible for nonlinear behavior of the samples was identified to be three photon absorption (3PA). This is in agreement with the band gap energies of the samples obtained from the linear absorption cut off and the slope of the plot of Ln(1 − TOA) vs. Ln(I0) using Sutherland’s theory (s = 2.1, for 3PA). The nonlinear refractive index (n2) of Zn doped samples was found to be lower than that of pure samples. Our experiments show that there exists a correlation between the nonlinear properties and the stoichiometry of the samples. The values of n2 fall into the same range as those obtained for the materials of similar band gap.

Analysis of Raman bandwidths and bandshapes of glasses through their glass-transition temperatures

Raman bandwidths and bandshapes of some molecular and ionic glasses have been investigated through the glass-transition region. Widths of both polarised and depolarised bands exhibit step-like changes during the glass transition. Molecular and ionic glasses differ with respect to the magnitude and the nature of variations in bandwidths and reorientational times. An attempt has been made to understand the changes in bandwidths around the glass-transition temperature.

Bismuth-doped amorphous-germanium sulfidesemiconductors

A study of the effect of bismuth dopant on the electronic transport properties of the amorphous semiconductors Ge20S80-xBix under high pressure (up to 140 kbar) has been carried out down to liquid-nitrogen temperature. The experiments reveal that the electronic conduction is strongly composition dependent and is thermally activated with a single activation energy at all pressures and for all compositions. A remarkable resemblance between the electronic conduction process, x-ray diffraction studies, and differential thermal analysis results is revealed. It is proposed that the n-type conduction in germanium chalcogenides doped with a large Bi concentration is due to the effect of Bi dopants on the positive correlation energy defects present in germanium chalcogenides. The impurity-induced chemical modification of the network creates a favorable environment for such an interaction.

Morphological structure of bismuth-doped n-type amorphous germanium sulphide semiconductors

Recent observation of n-type conduction in amorphous Ge20Ss_xBix at large bismuth concentrations (x = 11), which otherwise shows p-type conduction, has aroused considerable interest in the international scientific community [1]. The mechanism of such impurity incorporation in a germanium chalcogenide glass is not understood and is a topic of current interest. In our recent publications [2-10] we have brought to light some hitherto unknown and interesting features of bismuth dopants in chalcogen-rich Ge-X (X -- S, Se) glassy compositions. In this communication we present our new results of investigations on vitreous semiconductors Ge20S80 Bi using electron microscopy, electron diffraction of as-prepared and annealed/pressure quenched compositions. Our results provide conclusive support to the formation of composite clusters containing all the three elements, germanium, sulphur and bismuth, which crystallize in simpler stoichiometric compounds Bi2S3 and GeS2.

Phase relations and dielectric properties of BaTi03 ceramics heavily substituted with neodymium

Investigations on the phase relations and dielectric properties of (1 -x)BaTiO3 + xNd2/3TiO 3 (BNT) ceramics sintered in air below 1650 K have been carried out. X-ray powder diffraction studies indicate apparent phase singularity for compositions with x < 0.3. Nd2Ti207 is detected at higher neodymium concentrations. The unit cell parameter changes continuously with neodymium content, and BaTiO3 is completely cubic at room temperature with x -- 0.0525, whereas electron diffraction studies indicate that the air-sintered BNT ceramics with x > 0.08 contain additional phases that are partly amorphous even to an electron beam. SEM observations reveal that BaTiO3 grains are mostly covered by a molten intergranular phase, and show the presence of randomly distributed Nd2Ti207 grains. Energy dispersive X-ray analysis shows the Ba-Nd-Ti ternary composition of the intergranular phase. Differential thermal analysis studies support the formation of a partial melt involving dissolution-precipitation of boundary layers of BaTiO3 grains. These complex phase relations are accounted for in terms of the phase instability of BaTiO3 with large cation-vacancy concentration as a result of heavy Nd 3+ substitution. The absence of structural intergrowth in (1 - x)BaTiO3 + xNd2/3TiO3 under oxidative conditions leads to a separation of phases wherein the new phases undergo melting and remain X-ray amorphous. BNT ceramics with 0.1 < x < 0.3 have ~eff >~ 104 with tan 6 < 0.1 and nearly flat temperature capacitance characteristics. The grain-size dependence of ee,, variations of ~eff and tan 6 with the measuring frequency, the non-ohmic resistivities, and the non-linear leakage currents at higher field-strengths which are accompanied by the decrease in eeff and rise in tan 3, are explained on the basis of an intergranular (internal boundary layer) dielectric characteristic of these ceramics.

Co-assembly of a Nafion-Mesoporous Zirconium Phosphate Composite Membrane for PEM Fuel Cells

Synthesis of mesoporous zirconium phosphate (MZP) by co-assembly of a tri-block copolymer, namely pluronic-F127, as a structure-directing agent, and a mixture of zirconium butoxide and phosphorous trichloride as inorganic precursors is reported. MZP with a specific surface area of 84 m(2) g(-1) average pore diameter of about 17 nm and pore volume of 0.35 cm(3) g(-1) has been prepared, and characterised by X-ray diffraction (XRD) and transmission electron microscopy. Nafion-MZP composite membrane is obtained by employing MZP as a surface-functionalised solid-super-acid-proton-conducting medium as well as all inorganic filler with high affinity to absorb water and fast proton-transport across the electrolyte membrane even under low relative humidity (RH) conditions. The composite membranes have been evaluated in H-2/O-2 polymer electrolyte fuel cells (PEFCs) at varying RH values between 18 and 100%; a peak power density of 355 mW cm(-2) at a load current density of 1,100 mA cm(-2) is achieved with the PEFC employing Nafion-MZP composite membrane while operating at optimum temperature (70 degrees C) under 18% RH and ambient pressure. On operating the PEFC employing Nafion-MZP membrane electrolyte with hydrogen and air feeds at ambient pressure and a RH value of 18%, a peak power density of 285 mW cm(-2) at the optimum temperature (60 degrees C) is achieved. In contrast, operating under identical conditions, a peak power density of only similar to 170 mW cm(-2) is achieved with the PEFC employing Nafion-1135 membrane electrolyte.

Phonon renormalization in doped bilayer graphene

We report phonon renormalization in bilayer graphene as a function of doping. The Raman G peak stiffens and sharpens for both electron and hole doping as a result of the nonadiabatic Kohn anomaly at the Gamma point. The bilayer has two conduction and valence subbands, with splitting dependent on the interlayer coupling. This gives a change of slope in the variation of G peak position with doping which allows a direct measurement of the interlayer coupling strength.

Dielectric Relaxation in SrLiB9O15 Glasses

Transparent SrLiB9O15 (SLBO) glasses were fabricated via the conventional melt-quenching technique. X-ray powder diffraction and differential thermal analysis carried out on the as-quenched samples confirmed their amorphous and glassy nature, respectively. The dielectric constants in the 100 Hz to 10 MHz frequency range for SLBO glasses were measured as a function of temperature (300–1023 K). The dielectric relaxation characteristics were rationalized using the electric modulus formalism. The electrode polarization effect was subtracted from the low-frequency dielectric constant to have an insight into the intrinsic dielectric behavior of SLBO glasses. The imaginary part of electric modulus spectra was modeled using an approximate solution of Kohlrausch–Williams–Watts relation. The dielectric constant for the as-quenched glass increased with increasing temperature and exhibited anomalies in the vicinity of the glass transition and crystallization temperatures.

High-Pressure Studies Of SE100-XTEX Glasses

High pressure resistivity measurements on Se100-xTex, glasses for 0≤x≤30 are reported. Two composition regions, where the transport and transformation behaviour are different, are identified. For 0≤x≤6, there is a first-order-like transformation to metallic crystalline states, while for x>6 the transformation appears to be continuous. Glass-transition temperatures also show differences in trends as a function of composition around 6% Te. An attempt is made to explain the composition-dependent trends on the basis of known structural features of selenium glasses and of the nature of tellurium bonding. At concentrations with up to 6% tellurium, Te most likely enters selenium chain terminations, substituting for negatively charged Se1- defects, while at larger concentrations, tellurium probably enters chains and rings by a random substitution.

Effect of pressure on the resistivity of lead oxide-lead halide glasses

Resistivity behaviour of PbO---PbX2 (X=F,Cl) glasses has been investigated as a function of pressure at laboratory temperature. All PbO---PbX2 glasses undergo crystallization under pressure and the resistivities of crystallized samples are lower than the corresponding glasses. Transitions in PbO---PbF2 glasses exhibit a first order behaviour while transitions in PbO---PbCl2 glasses possess features of a continuous transition. The differences in the pressure behaviour of the two glass systems have been attributed to the differences in the ionic sizes of F− and Cl− ions and also to pressure induced modifications of Pb---O bonding.

Characterization studies of AgI---Ag2O---MoO3 glasses

Glass formation has been investigated in the system AgI---Ag2O---MoO3. X-ray absorption edge chemical shifts, infrared spectra and heat capacities of the various glass compositions have been measured. The probable anion structures in the oxygen excess and deficient regions have been discussed

Influence of seeding on crystallization behaviour of BaNaB9O15 glasses

Transparent BaNaB9O15 (BNBO) glasses were fabricated via the conventional melt-quenching technique. X-ray powder diffraction (XRD) followed by differential scanning calorimetric (DSC) studies confirmed the amorphous and glassy nature of the as-quenched samples, respectively. The effect of seeding on the crystallization of BNBO glasses was studied by non-isothermal DSC method and was modeled using the Johnson-Mehl-Avrami and Ozawa equations. The activation energy for seeded glasses decreased with the increase in fraction of crystallization. The values for the onset of crystallization and Avrami exponent were found to be lower for seeded samples which were associated with the heterogeneous nucleation and epitaxial processes.