Fluidity of mica particle dispersed aluminium alloy

Cast aluminium alloy-mica particle composites were made by dispersing mica particles in a vortex produced by stirring the liquid Al-4 wt% Cu-1.5 wt% Mg alloy and then casting the melt containing the suspended particles into permanent moulds. Spiral fluidity and casting fluidity of the alloy containing mica particles in suspension were determined. Both the spiral fluidity and the casting fluidity of the base alloy were found to decrease with an increase in volume or weight percent of mica particles (of a given size), and with a decrease in particle size (for a given amount of particles). The fluidities of Al-4 wt% Cu-1.5 wt% Mg alloys containing suspended mica particles were found to correlate very well with the surface area of suspended mica particles. The regression equation for spiral fluidity Y (cm) as a function of surface area of mica particles per gram of spiral X (cm2 g–1) at 700° C was found to be Y=42.62–0.42X with a correlation coefficient of 0.9634. The regression equations for casting fluidity Yprime (cm) as a functiono of surface area of mica particles per gram of fluidity test piece Xprime (cm2 g–1) at 710 and 670° C were found to be Yprime=19.71–0.17Xprime and Yprime=13.52–0.105Xprime with correlation coefficients of 0.9194 and 0.9612 respectively. The percentage decrease in casting fluidity of composite melts containing up to 2.5 wt% mica with a drop in temperature is quite similar to the corresponding decrease in the casting fluidity of base alloy melts (without mica). The change in fluidity due to mica dispersions has been discussed in terms of changes in viscosity of the composite melts. However, the fluidities of these composite alloys containing up to 2.5 wt% mica are adequate for making a variety of simple castings including bearings for which these alloys have been developed.

Subsurface deformation in dry sliding of hypo-eutectic Al-Si alloys

The subsurface deformation during dry sliding of Al-Si alloys is studied by fragmentation of silicon particles. The size of the fragmented particles does not vary with load. The depth of deformation is found to increase with increase in normal load. This experimental observation agrees with load-deformation depth characteristics obtained by a slip line field model.

Phase transformations and metastable phase equilibria in Al-Ge alloy

In this paper the results of a detailed investigation on the metastable phase relations in undercooled as well as rapidly solidified Al---Ge alloys containing 2–50 at.% Ge are reported. Data obtained on the structure and morphology of phases enable us to arrive at the phase relations and transformation processes occurring in undercooled and rapidly quenched melts of this system. These results are explained with the help of a metastable phase diagram consisting of a peritectic and eutectic reaction involving metastable phases.

Influence of heat treatment on the strength and fracture behaviour of Fe-12Cr-6Al ferritic stainless steel

The changes in the tensile properties and fracture mode brought about by heat treatment of Fe-12Cr-6Al ferritic stainless steel have been studied. A favourable combination of high strength and good ductility is obtained by heating the material at 1370 K for 2 h followed by a water quench. The high-temperature treatment results in carbide dissolution as well as an increase in the grain size. The mechanism of strengthening has been evaluated from the apparent activation energy (28 kJ mol–1) and is identified to be the unpinning of dislocations from the atmosphere of carbon atoms. As the heat-treatment temperature is increased, the fracture behaviour changes from ductile to brittle mode and this is related to the changes in grain size and friction stress.

Some Considerations on the Occurrence of Intergranular Fracture during Fatigue Crack growth in Steels

The occurrence of a maximum in the percentage of intergranular fracture on the fracture surface during the transition from intermediate to low fatigue crack growth rates has been observed for a high strength steel. It is suggested that transgranular planar slip leading to slip localization is essential in promoting intergranular fracture when the cyclic plastic zone size becomes equal to the prior austenite grain size.

Contribution of texture to the strengthening and fracture in hot-rolled magnesium-12.7 at % cadmium alloy

The grain size dependencies of the yield and fracture stresses in hot rolled Mg-12.7 at % Cd alloy have been measured in the temperature range 77 to 420 K and are found to be in accordance with HalI-Petch type of equations. In hot rolled Mg-12.7 Cd alloy, the HalI-Petch intercept a w is higher than that in hot rolled magnesium, while the slope ky is comparable. The fracture is intercrystalline at 77 K, mixed mode at 300 K and ductile at 420 K. The above flow and fracture behaviours are interpreted in terms of the complimentary effects of texture hardening and solid solution strengthening.

Crystallization behaviour of Metglas 2826 MB (Fe40Ni38Mo4B18)

Differential scanning calorimetry, x-ray diffraction and transmission electron microscopy have been employed to determine the thermal stability and identify the crystalline phases on devitrification of Metglas 2826 MB. The glass crystallizes intoγ-FeNiMo and fcc (FeNi)23B6 with activation energies of 270 and 375 kJ mol−1 respectively. The reactions are primary and polymorphic in nature. The influence of Mo towards crystallization of Fe40Ni40B20 has been to enhance the formation of the fcc (FeNi)23B6 phase in preference to orthorhombic (FeNi)3B phase and to raise the thermal stability of the amorphous state.

An absolute method for the determination of surface tension of liquids using pendent drop profiles

Drop formation at conical tips which is of relevance to metallurgists is investigated based on the principle of minimization of free energy using the variational approach. The dimensionless governing equations for drop profiles are computer solved using the fourth order Runge-Kutta method. For different cone angles, the theoretical plots of XT and ZT vs their ratio, are statistically analyzed, where XT and ZT are the dimensionless x and z coordinates of the drop profile at a plane at the conical tip, perpendicular to the axis of symmetry. Based on the mathematical description of these curves, an absolute method has been proposed for the determination of surface tension of liquids, which is shown to be preferable in comparison with the earlier pendent-drop profile methods.

Numerical studies on columnar-to-equiaxed transition in directional solidification of binary alloys

A numerical study on columnar-to-equiaxed transition (CET) during directional solidification of binary alloys is presented using a macroscopic solidification model. The position of CET is predicted numerically using a critical cooling rate criterion reported in literature. The macroscopic solidification model takes into account movement of solid phase due to buoyancy, and drag effect on the moving solid phase because of fluid motion. The model is applied to simulate the solidification process for binary alloys (Sn-Pb) and to estimate solidification parameters such as position of the liquidus, velocity of the liquidus isotherm, temperature gradient ahead of the liquidus, and cooling rate at the liquidus. Solidification phenomena under two cooling configurations are studied: one without melt convection and the other involvin thermosolutal convection. The numerically predicted positions of CET compare well with those of experiments reported in literature. Melt convection results in higher cooling rate, higher liquidus isotherm velocities, and stimulation of occurrence of CET in comparison to the nonconvecting case. The movement of solid phase aids further the process of CET. With a fixed solid phase, the occurrence of CET based on the same critical cooling rate is delayed and it occurs at a greater distance from the chill.

Trimming studies on polymer thick-film resistors

PVC-graphite polymer thick-film resistors were trimmed by a conventional air abrasive technique and the post-trim drift in resistance with time was found to be negative. The net decrease in resistance of trimmed resistors in a given time was found to be a function of resistor composition, cutting speed and temperature. Detailed studies showed this decrease to be due to a decrease in cut width with time. Two new methods, namely bombardment trimming and radiation trimming, were also tried for adjusting the resistance of these resistors and the results were compared with those obtained from abrasive trimming studies.

Reactivity in the spinel formation reaction in CuO/Al2O3, Fe2O3, Cr2O3 systems

Abstract is not available.