Thermodynamics of Al(1-x)Ga(x)N solid solution: Inclination for phase separation and ordering

Although Al(1-x)Ga(x)N semiconductors are used in lighting, displays and high-power amplifiers, there is no experimental thermodynamic information on nitride solid solutions. Thermodynamic data are useful for assessing the intrinsic stability of the solid solution with respect to phase separation and extrinsic stability in relation to other phases such as metallic contacts. The activity of GaN in Al(1-x)Ga(x)N solid solution is determined at 1100 K using a solid-state electrochemical cell: Ga + Al(1-x)Ga(x)N/Fe, Ca(3)N(2)//CaF(2)//Ca(3)N(2), N(2) (0.1 MPa), Fe. The solid-state cell is based on single crystal CaF(2) as the electrolyte and Ca(3)N(2) as the auxiliary electrode to convert the nitrogen chemical potential established by the equilibrium between Ga and Al(1-x)Ga(x)N solid solution into an equivalent fluorine potential. Excess Gibbs free energy of mixing of the solid solution is computed from the results. Results suggest an unusual mixing behavior: a mild tendency for ordering at three discrete compositions (x = 0.25, 0.5 and 0.75) superimposed on predominantly positive deviation from ideality. The lattice parameters exhibit slight deviation from Vegard's law, with the a-parameter showing positive and the c-parameter negative deviation. Although the solid solution is stable in the full range of compositions at growth temperatures, thermodynamic instability is indicated at temperatures below 410 K in the composition range 0.26 <= x <= 0.5. At 355 K, two biphasic regions appear, with terminal solid solutions stable only for 0 <= x <= 0.26 and 0.66 <= x <= 1. The range of terminal solid solubility reduces with decreasing temperature. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

A Generalized Enthalpy Update Scheme for Solidification of a Binary Alloy with Solid Phase Movement

A generalized enthalpy update scheme is presented for evaluating solid and liquid fractions during the solidification of binary alloys, taking solid movement into consideration. A fixed-grid, enthalpy-based method is developed such that the scheme accounts for equilibrium as well as for nonequilibrium solidification phenomena, along with solid phase movement. The effect of solid movement on the solidification interface shape and macrosegregation is highlighted.

Developments in solid-state under-frequency relays

Simpler circuits for frequency-sensitive relays responding to change and rate of change of system frequency have been developed employing phase-locked loops. A new relay responding to time intergral of the fall in system frequency has also been developed and its performance has been compared with those responding to change and rate of change of system frequency. The relays have been tested and calibrated with the help of a specially designed calibration kit.

Temperature-pressure-induced solid-solid < 100 > to < 110 > reorientation in FCC metallic nanowire: a molecular dynamic study

Atomistic simulation of initial < 100 > oriented FCC Cu nanowires shows a novel coupled temperature-pressure dependent reorientation from < 100 > to < 110 > phase. A temperature-pressure-induced solid-solid < 100 > to < 110 > reorientation diagram is generated for Cu nanowire with varying cross-sectional sizes. A critical pressure is reported for Cu nanowires with varying cross-sectional sizes, above which an initial < 100 > oriented nanowire shows temperature independent reorientation into the < 110 > phase. The effect of surface stresses on the < 100 > to < 110 > reorientation is also studied. The results indicate that above a critical cross-sectional size for a given temperature-pressure, < 100 > to < 110 > reorientation is not possible. It is also reported here that for a given applied pressure, an increase in temperature is required for the < 100 > to < 110 > reorientation with increasing cross-sectional size of the nanowire. The temperature-pressure-induced solid-solid < 100 > to < 110 > reorientation diagram reported in the present paper could further be used as guidelines for controlling the reorientations/shape memory in nano-scale applications of FCC metallic nanowires.

Phase relations and Gibbs energies of spinel phases and solid solutions in the system Mg-Rh-O

Pure stoichiometric MgRh(2)O(4) could not be prepared by solid state reaction from an equimolar mixture of MgO and Rh(2)O(3) in air. The spinel phase formed always contained excess of Mg and traces of Rh or Rh(2)O(3). The spinel phase can be considered as a solid solution of Mg(2)RhO(4) in MgRh(2)O(4). The compositions of the spinel solid solution in equilibrium with different phases in the ternary system Mg-Rh-O were determined by electron probe microanalysis. The oxygen potential established by the equilibrium between Rh + MgO + Mg(1+x)Rh(2-x)O(4) was measured as a function of temperature using a solid-state cell incorporating yttria-stabilized zirconia as an electrolyte and pure oxygen at 0.1 MPa as the reference electrode. To avoid polarization of the working electrode during the measurements, an improved design of the cell with a buffer electrode was used. The standard Gibbs energies of formation of MgRh(2)O(4) and Mg(2)RhO(4) were deduced from the measured electromotive force (e.m.f.) by invoking a model for the spinel solid solution. The parameters of the model were optimized using the measured composition of the spinel solid solution in different phase fields and imposed oxygen partial pressures. The results can be summarized by the equations: MgO + beta -Rh(2)O(3) -> MgRh(2)O(4); Delta G degrees (+ 1010)/J mol(-1) = -32239 + 7.534T; 2MgO + RhO(2) -> Mg(2)RhO(4); Delta G degrees(+/- 1270)/J mol(-1) = 36427 -4.163T; Delta G(M)/J mol(-1) = 2RT(xInx + (1-x)In(1-x)) + 4650x(1-x), where Delta G degrees is the standard Gibbs free energy change for the reaction and G(M) is the free energy of mixing of the spinel solid solution Mg(1+x)Rh(2-x)O(4). (C) 2011 Elsevier B. V. All rights reserved.

Recent advances in auto exhaust catalysis

In last 30 years innovative research in the area of auto exhaust catalysis is being developed and CeO2 has been found to play a major role in this area due to its unique redox properties. In this review, auto exhaust emission and its impact on earth’s environment, global concern and recent advances in science and technology in automotive exhaust catalysis have been documented. A new preparative method of dispersing metal ions by solution combustion technique over CeO2 and TiO2 resulting mainly Ce1−xMxO2−δ, Ti1−xMxO2−δ and Ce1−x−yTixMyO2−δ (M = Pd, Rh and Pt) catalysts, structure of these materials, their catalytic properties towards auto exhaust catalysis, structure–property relation and mechanism of catalytic reactions are accounted here. In these materials, metal ions are incorporated into substrate matrix to a certain limit in the solid solution form and we have established a new direction in heterogeneous catalysis by turning to the concept of dispersed metal ions as catalytically active sites from the conventionally nurtured idea of metal particles as active centers for catalysis.

Dynamical Evolution of Wear Particles in Nanocontacts

Nanoscale surface modification, by the interaction of sliding surfaces and mobile nanoparticles, is a critical parameter for controlling friction, wear and failure of surface structures. Here we demonstrate how nanoparticles form and interact in real-time at moving nanocontacts, with reciprocating wear tests imaged in situ at the nanoscale over > 300 cycles in a transmission electron microscope. Between sliding surfaces, friction-formed nanoparticles are observed with rolling, sliding and spinning motions, dependant on localised contact conditions and particle geometry. Over periods of many scratch cycles, nanoparticles dynamically agglomerate into elongated clusters, and dissociate into smaller particulates. We also show that the onset of rolling motion of these particles accompanies a reduction in measured friction. Introduction of nanoparticles with optimum shape and property can thus be used to control friction and wear in microdevices.

Colloidal calcium nanoparticles: digestive ripening in the presence of a capping agent and coalescence of particles under an electron beam

The nanochemistry of calcium remains unexplored, which is largely due to the inaccessibility of calcium nanoparticles in an easy to handle form by conventional methods of synthesis as well as its highly reactive and pyrophoric nature. The synthesis of colloidal Ca nanoparticles by the solvated metal atom dispersion (SMAD) method is described. The as-prepared Ca-THF nanoparticles, which are polydisperse, undergo digestive ripening in the presence of a capping agent, hexadecyl amine (HDA) to afford highly monodisperse colloids consisting of 2-3 nm sized Ca-HDA nanoparticles. These are quite stable towards precipitation for long periods of time, thereby providing access to the study of the nanochemistry of Ca. Particles synthesized in this manner were characterized by UV-visible spectroscopy, high resolution electron microscopy, and powder X-ray diffraction methods. Under an electron beam, two adjacent Ca nanoparticles undergo coalescence to form a larger particle.

Management of Municipal Solid Waste

Solid material thrown away as unused from various sectors such as agricultural, commercial, domestic, industrial and institutional constitutes solid wastes. This places an enormous strain on natural resources and seriously undermines efficient and sustainable development. Management of Municipal Solid Waste discusses the ways to salvage the situation through efficient management of solid wastes from waste generation to final disposal. The various processes such as waste generation, collection, storage, processing, recovery, transport, and disposal, are explained with the support of case studies. The book discusses reduction of waste at the source and to foster implementation of integrated solid waste management systems that are cost-effective and protect human health and the environment.

The omega phase formation during laser cladding and remelting of quasicrystal forming AlCuFe on pure aluminum

We report the formation omega phase in the remelted layers during laser cladding and remelting of quasicrystal forming Al65Cu23.3Fe11.7 alloy on pure aluminum. The omega phase is absent in the clad layers. In the remelted layer, the phase nucleates at the periphery of the primary icosahedral phase particles. A large number of omega phase particles forms enveloping the icosahedral phase growing into aluminum rich melt, which solidify as alpha-Al solid solution. On the other side it develops an interface with aluminum. A detailed transmission electron microscopic analysis shows that omega phase exhibits orientation relationship with icosahedral phase. The composition analysis performed using energy dispersive x-ray analyzer suggests that this phase has composition higher aluminum than the icosahedral phase. The analysis of the available phase diagram information indicates that the present results represent large departure from equilibrium conditions. A possible scenario of the evolution of the omega phase has been suggested.

Towards sustainability: a new, solid-state synthetic route for supported metal nanocatalysts

Noble metal ions like Pt(IV) and Pd(II) were impregnated on gamma-alumina and aerosol 300 silica surfaces. Reduction of these ions using ammonia borane in the solid state resulted in the formation of the respective metal nanoparticles embedded in BNHx polymer which is dispersed on the oxide support. Removal of the BNH polymer was accomplished by washing the samples repeatedly with methanol. In this process the polymer undergoes solvolysis to release H-2 accompanied by the formation of ammonium methoxy borate salt, which has been removed by repeated methanol washings. As a result, metal nanoparticles well dispersed on gamma-alumina and aerosol 300 silica were obtained. These samples have been characterized by a combination of techniques, including electron microscopy, powder X-ray diffraction, NMR spectroscopy and surface area analyser.

General classical theory of spinning particles in a meson field

An exact classical theory of the motion of a point dipole in a meson field is given which takes into account the effects of the reaction of the emitted meson field. The meson field is characterized by a constant $\chi =\mu /\hslash $ of the dimensions of a reciprocal length, $\mu $ being the meson mass, and as $\chi \rightarrow $ 0 the theory of this paper goes over continuously into the theory of the preceding paper for the motion of a spinning particle in a Maxwell field. The mass of the particle and the spin angular momentum are arbitrary mechanical constants. The field contributes a small finite addition to the mass, and a negative moment of inertia about an axis perpendicular to the spin axis. A cross-section (formula (88 a)) is given for the scattering of transversely polarized neutral mesons by the rotation of the spin of the neutron or proton which should be valid up to energies of 10$^{9}$ eV. For low energies E it agrees completely with the old quantum cross-section, having a dependence on energy proportional to p$^{4}$/E$^{2}$ (p being the meson momentum). At higher energies it deviates completely from the quantum cross-section, which it supersedes by taking into account the effects of radiation reaction on the rotation of the spin. The cross-section is a maximum at E $\sim $ 3$\cdot $5$\mu $, its value at this point being 3 $\times $ 10$^{-26}$ cm.$^{2}$, after which it decreases rapidly, becoming proportional to E$^{-2}$ at high energies. Thus the quantum theory of the interaction of neutrons with mesons goes wrong for E $\gtrsim $ 3$\mu $. The scattering of longitudinally polarized mesons is due to the translational but not the rotational motion of the dipole and is at least twenty thousand times smaller. With the assumption previously made by the present author that the heavy partilesc may exist in states of any integral charge, and in particular that protons of charge 2e and - e may occur in nature, the above results can be applied to charged mesons. Thus transversely polarised mesons should undergo a very big scattering and consequent absorption at energies near 3$\cdot $5$\mu $. Hence the energy spectrum of transversely polarized mesons should fall off rapidly for energies below about 3$\mu $. Scattering plays a relatively unimportant part in the absorption of longitudinally polarized mesons, and they are therefore much more penetrating. The theory does not lead to Heisenberg explosions and multiple processes.