Synthesis of new (Bi, La)(3)MSb(2)O(11) phases (M = Cr, Mn, Fe) with KSbO(3)-type structure and their magnetic and photocatalytic properties

Synthesis and structure of new (Bi, La)(3)MSb(2)O(11) phases (M = Cr, Mn, Fe) are reported in conjunction with their magnetic and photocatalytic properties. XRD refinements reflect that Bi(3)CrSb(2)O(11), Bi(2)LaCrSb(2)O(11), Bi(2)LaMnSb(2)O(11) and Bi(2)LaFeSb(2)O(11) adopt KSbO(3)-type structure (space group, Pn (3) over bar). The structure can be described through three interpenetrating networks where the first is the (M/Sb)O(6) octahedral network and other two are the identical networks having Bi(6)O(4) composition. The magnetic measurements on Bi(2)LaCrSb(2)O(11) and Bi(2)LaMnSb(2)O(11) show paramagnetic behaviour with magnetic moments close to the expected spin only magnetic moments of Cr(+3) and Mn(+3). The UV-Visible diffuse reflectance spectra are broad and indicate that these materials possess a bandgap of similar to 2 eV. The photocatalytic activity of these materials has been investigated by degrading Malachite Green (MG) under exposure to UV light.

Interacting magnetic sublattices and ferrimagnetism in Sr-doped DyMnO3

We present the magnetic properties of polycrystalline Dy1−xSrxMnO3 (0.1 ≤ x ≤ 0.4) with an orthorhombic (o) crystal structure. The parent compound, o-DyMnO3, undergoes an incommensurate antiferromagnetic ordering of the Mn spins at 39 K, followed by a spiral order at 18 K. A further antiferromagnetic transition at 5 K marks an ordering of the Dy-sublattice. Doping of divalent Sr ions results in diverse magnetization phenomena. The zero-field cooled (ZFC) and field cooled (FC) magnetization curves display the presence of strongly interacting magnetic sublattices. For x = 0.1 and 0.2, a bifurcation between the ZFC and FC magnetization sets in at around 30 and 32 K, respectively. The ZFC magnetization peaks at about 5 K, indicating antiferromagnetic Dy-couplings similar to the case of o-DyMnO3. For x = 0.3, clear signatures of ferrimagnetism and strong anisotropy are found, including negative magnetization. The compound with x = 0.4 behaves as a spin glass, similar to Dy0.5Sr0.5MnO3.

Onset of sphalerite to wurtzite transformation in ZnS nanoparticles

In this work, the incubation period for the onset of sphalerite to wurtzite transformation in isolated ZnS nanoparticles 2 to 7 nm in size was determined via the in situ isothermal annealing of as-synthesized sphalerite nanoparticles in a transmission electron microscope (TEM). Nanoparticles sitting on the TEM grid were well separated from each other in order to minimize particle sintering during the annealing operation. The phase transformation onset was observed at 300 degrees C, 350 degrees C, and 400 degrees C after 90, 10, and 4 min, respectively. These time-temperature data for the phase transformation onset were then used to calculate the activation energy for the nucleation of the wurtzite phase in 2 to 7 nm sphalerite particles. The activation energy determined was 24 Kcal/mol. (C) 2011 American Institute of Physics. [doi: 10.1063/1.3622625]

Size dependent microstructure for Ag-Ni nanoparticles

The Ag-Ni system is characterized by large differences in atomic sizes (14%) and a positive heat of mixing (+23 kJ mol(-1)). The binary equilibrium diagram for this system therefore exhibits a large miscibility gap in both solid and liquid state. This paper explores the size-dependent changes in microstructure and the suppression of the miscibility gap which occurs when free alloy particles of nanometer size are synthesized by co-reduction of Ag and Ni metal precursors. The paper reports that complete mixing between Ag and Ni atoms could be achieved for smaller nanoparticles (<7 nm). These particles exhibit a single-phase solid solution with face-centered cubic (fcc) structure. With increase in size, the nanoparticles revealed two distinct regions. One of the regions is composed of pure Ag. This region partially surrounds a region of fcc solid solution at an early stage of decomposition. Experimental observations were compared with the results obtained from the thermodynamic calculations, which compared the free energies corresponding to a physical mixture of pure Ag and Ni phases and a fcc Ag-Ni solid solution for different particle sizes. Results from the theoretical calculations revealed that, for the Ag-Ni system, solid solution was energetically preferred over the physical mixture configuration for particle sizes of 7 nm and below. The experimentally observed two-phase microstructure for larger particles was thus primarily due to the growth of Ag-rich regions epitaxially on initially formed small fcc Ag-Ni nanoparticles. (C) 2011 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Ferromagnetism Exhibited by Nanoparticles of Noble Metals

Gold nanoparticles with average diameters in the range 2.515 nm, prepared at the organic/aqueous interface by using tetrakis( hydroxymethyl) phosphonium chloride (THPC) as reducing agent, exhibit ferromagnetism whereby the saturation magnetization M(S) increases with decreasing diameter and varies linearly with the fraction of surface atoms. The value of M(S) is higher when the particles are present as a film instead of as a sol. Capping with strongly interacting ligands such as alkane thiols results in a higher M(S) value, which varies with the strength of the metal-sulfur bond. Ferromagnetism is also found in Pt and Ag nanoparticles prepared as sols, and the M(S) values vary as Pt > Au > Ag. A careful study of the temperature variation of the magnetization of Au nanoparticles, along with certain other observations, suggests that small bare nanoparticles of noble metals could indeed possess ferromagnetism, albeit weak, which is accentuated in the presence of capping agents, specially alkane thiols which form strong metal-sulfur bonds.

Threshold-like features in the magnetic response of iron-filled multi-walled carbon nanotube and polymer composite

The magnetic properties of iron-filled multi-walled carbon nanotubes dispersed in polystyrene (Fe-MWNT/PS) have been investigated as a function of Fe-MWNT concentration (0.1-15 wt%) from 300 to 10 K. Electron microscopy studies indicate that Fe nanorods (aspect ratio similar to 5) remain trapped at various lengths of MWNT and are thus, prevented from oxidation as well as aggregation. The magnetization versus applied field (M-H loop) data of 0.1 wt% of Fe-MWNTs in PS show an anomalous narrowing at low temperatures which is due to the significant contribution from shape anisotropy of Fe nanorods. The remanence shows a threshold feature at 1 wt%. The enhanced coercivity shows a maximum at 1 wt% due to the dominant dipolar interactions among Fe nanorods. Also the squareness ratio shows a maximum at 1 wt%.