NaOsO3: A high Neel temperature 5d oxide

The origin of a high Neel temperature in a 5d oxide, NaOsO3, has been analyzed within the mean-field limit of a multiband Hubbard model and compared with the analogous 4d oxide, SrTcO3. Our analysis shows that there are a lot of similarities in both of these oxides on the dependence of the effective exchange interaction strength (J(0)) on the electron-electron interaction strength ( U). However, the relevant value of U in each system puts them in different portions of the parameter space. Although the Neel temperature for NaOsO3 is less than that for SrTcO3, our results suggest that there could be examples among other 5d oxides that have a higher Neel temperature. We have also examined the stability of the G-type antiferromagnetic state found in NaOsO3 as a function of electron doping within GGA + U calculations and find a robust G-type antiferromagnetic metallic state stabilized. The most surprising aspect of the doped results is the rigid bandlike evolution of the electronic structure, which indicates that the magnetism in NaOsO3 is not driven by Fermi surface nesting.

Evolution of superconductivity in PrFe1-xCoxAsO (x=0.0-1.0)

We report the synthesis and physical property characterization of Prfe(1-x)Co(x)AsO (x=0.0-1.0). The studied samples are synthesized by through the solid state reaction route via the vacuum encapsulation method. The pristine compound PrFeAsO does not show superconductivity, but rather exhibits a metallic step like transition due to spin density wave (SOW) ordering of Fe moments (Fe-SDW) below 150 K, Followed by another upward step due to anomalous ordering of Pr moments (Pr-TN) at 12 K. Both the Fe-SDW and Pr-TN temperatures decrease monotonically with Co substitution at Fe site Superconductivity appears in a narrow range of x from 0.07 to 0.25 with maximum T-c at 11.12 K for x=0.15. Samples with x >= 0.25 exhibit metallic behavior right from 300 K down to 2 K, without any Fe-SDW or Pr-TN steps in resistivity. In fact, though Fe-SDW decreases monotonically, the pr(TN) disappeared even with x=0.02. The magneto transport measurements below 14 Ton superconducting polycrystalline Co doped Pi FeAs0 lead to extrapolated values of the upper critical fields H-c2(0)] of up to 60 T. (C) 2014 Elsevier Ltd. All rights reserved.

Near-infrared photoactive Cu3BiS3 thin films by co-evaporation

Semiconducting Cu3BiS3 (CBS) thin films were deposited by co-evaporation of Cu, Bi elemental metallic precursors, with in situ sulphurisation, using a quartz effusion cell. Cu3BiS3 thin films were structurally characterized by XRD and FE-SEM. The chemical bonding of the ions was examined by XPS. As deposited films were demonstrated for metal-semiconductor-metal near IR photodectection under lamp and laser illuminations. The photo current amplified to three orders and two orders of magnitude upon the IR lamp and 60 m W cm(-2) 1064 nm IR laser illuminations, respectively. Larger grains, made up of nano needle bunches aided the transport of carriers. Transport properties were explained based on the trap assisted space charge conduction mechanism. Steady state detector parameters like responsivity varied from 1.04 AW(-1) at 60 m Wcm(-2) to 0.22 AW(-1) at 20 m Wcm(-2). Detector sensitivity of 295 was found to be promising and further could be tuned for better responsivity and efficiency in utilization of near infra-red photodetector. (C) 2014 AIP Publishing LLC.

Film thickness mediated transition in the kinetics of electric current induced flow of thin liquid metal films

Application of high electric-field between two points in a thin metallic film results in liquefaction and subsequent flow of the liquid-film from one electrode to another in a radially symmetric fashion. Here, we report the transition of the flow kinetics driven by the liquid film thickness varying from 3 to 100 nm. The mechanism of the flow behavior is observed to be independent of the film thickness; however, the kinetics of the flow depends on the film thickness and the applied voltage. An analytical model, incorporating viscosity and varying electrical resistivity with film thickness, is developed to explain the experimental observations. (C) 2014 AIP Publishing LLC.

Room temperature electrical spin injection into GaAs by an oxide spin injector

Spin injection, manipulation and detection are the integral parts of spintronics devices and have attracted tremendous attention in the last decade. It is necessary to judiciously choose the right combination of materials to have compatibility with the existing semiconductor technology. Conventional metallic magnets were the first choice for injecting spins into semiconductors in the past. So far there is no success in using a magnetic oxide material for spin injection, which is very important for the development of oxide based spintronics devices. Here we demonstrate the electrical spin injection from an oxide magnetic material Fe3O4, into GaAs with the help of tunnel barrier MgO at room temperature using 3-terminal Hanle measurement technique. A spin relaxation time tau similar to 0.9 ns for n-GaAs at 300 K is observed along with expected temperature dependence of t. Spin injection using Fe3O4/MgO system is further established by injecting spins into p-GaAs and a tau of similar to 0.32 ns is obtained at 300 K. Enhancement of spin injection efficiency is seen with barrier thickness. In the field of spin injection and detection, our work using an oxide magnetic material establishes a good platform for the development of room temperature oxide based spintronics devices.