Gibbs free energies of formation of indium (III) oxide and sulphate

Emf measurements on the galvanic cell Pt, Ta, In + In,O, / Tho,-Y,03 / Cu + C+O, Pt were used to obtain the standard free energy of formation of 1%03fr om 600 to 900°C. Differential thermal analysis was used to detect the decomposition of In2(S0,), under controlled SO2 + O2 + Ar mixtures in thqtemperature range 640-8wC. X-ray diffraction analysis indicated that the decomposition product was 1%03 without an oxywlphate intermediate. The following equations were obtained for the variation of the standard free-energy change(Jlmole) with temperature:

Gibbs energy of formation of lead zirconate

The Gibbs energy of formation of zirconia-saturated lead zirconate was determined by emf measurements on the solid state cells and at 800 to 1400 K. The results obtained differ significantly from those reported in the literature based on vapor-pressure measurements, using Knudsen effusion and transportation techniques and assuming that the vapor phase consisted entirely of monomeric PbO molecules. A reanalysis of the data obtained in the earlier vapor-pressure studies, using mass-spectrometric measurements on polymeric PbO species in the gas phase, gives Gibbs energies of formation of lead zirconate which are in better agreement with those obtained in this study. Recent electrochemical measurements using CaO-ZrO2 and PbF2 solid electrolytes are in good agreement with the present study. The results obtained in this study are also consistent with the phase diagram which shows decomposition of the zirconate to tetragonal zirconia and a liquid phase rich in PbO at 1843 K.

Gibbs energy formation of lead titanate

The Gibbs energy of formation of titania-saturated lead titanate has been determined by e.m.f. measurements on the solid state cell;Pt,Ir,Pb + Pb1−xTiO3−x + TiO2(rutile)/CaO-ZrO2/Ni + NiO,Pt in the temperature range 1075–1350 K. The results obtained are significantly different from those reported in the literature based upon vapour pressure measurements, employing Knudsen effusion and transportation techniques, and assuming that the vapor phase consisted entirely of monomeric PbO molecules. A reanalysis of the data obtained in the earlier vapor pressure studies using mass spectrometric measurements on polymeric PbO species in the gas phase, gives Gibbs energies of formation of lead titanate which are in better agreement with those obtained in this study. Earlier electrochemical measurements by Mehrotra et al. and more recent electrochemical measurements by Schmahl et al. both employing CaO-ZrO2 solid electrolytes are in good agreement with the present study. The electro-chemical measurements by Schmahl et al. using PbF 2 solid electrolyte give a slightly more positive Gibbs energy of formation. There was no evidence supporting the formation of compounds other than Pb1−xTiO3−x from yellow PbO and rutile form of TiO2 in the temperature range covered in this study.Résumé L'enthalpie libre de formation du titanate de plomb saturé en oxyde de titane a été déterminée par des mesures de FEM de la pile: Pt,Ir,Pb + Pb1−xTiO3−x + TiO2(rutile)/CaO-ZrO2/Ni + NiO,Pt dans le domaine de températures 1075–1350 K. Les résultats obtenus, different appréciablement de ceux publiés, déterminés par mesures de tensions de vapeur (techniques de transport et d'effusion de Knudsen) en supposant que la phase gazeuse etait uniquement constituée de molécules monomériques de PbO. Une réanalyse des résultats de la littérature, à partir de mesures par spectrométrie de masse sur les polymères de PbO gazeux, donne des enthalpies libres de formation du titanate de plomb se rapprochant de celles obtenues dans cette étude. Les mesures de Mehrotra et al. et plus récemment de Schmahl et al. utilisant toutes deux l'électrolyte CaO-ZrO2 concordent bien avec celles de la présente étude. Les mesures de Schmahl et al., à l'aide de l' électrolyte solide PbF2, donnent une enthalpie de formation légèrement plus positive. Pour la gammede températures étudiée, rien ne permet de supposer que des composés autres que Pb1−x TiO3−x puissent se former à partir du PbO Gaune) et du rutile (TiO2).

Potentiometric determination of the Gibbs energies of formation of lead aluminates

The Gibbs energies of formation of three compounds in the PbO-Al2O3 system—2PbO · Al2O3, PbO · Al2O3, andPbO· 6Al2O3—have been determined from potentiometric measurements on reversible solid-state galvanic cells [dformula Pt, Ir | Pb, alpha-Al[sub 2]O[sub 3], PbO [center-dot] 6Al[sub 2]O[sub 3] | ZrO[sub 2]-CaO | NiO, Ni | Pt] [dformula Pt | NiO, Ni | ZrO[sub 2]-CaO | Pb, PbO [center-dot] 6Al[sub 2]O[sub 3], PbO [center-dot] Al[sub 2]O[sub 3] | Ir, Pt] and [dformula Pt | NiO, Ni | ZrO[sub 2]-CaO | Pb, PbO [center-dot] Al[sub 2]O[sub 3], 2PbO [center-dot] Al[sub 2]O[sub 3] | Ir, Pt] in the temperature range 850–1375 K. The results are discussed in the light of reported phase diagrams for the PbO-Al2O3system. The partial pressures of different lead oxide species, PbnOn, n = 1–6, in the gas phase in equilibrium withthe aluminates are calculated by combining the results of this study with the mass-spectrometric data of Drowart et al.(1) for polymerization equilibria in the gas phase. The concentration of oxygen in lead in equilibrium with the aluminatesare also derived from the results and the literature data on the Gibbs energy of solution of oxygen in liquid lead.

Gibbs energy of formation of nickel orthosilicate (Ni2SiO4)

Two solid state galvanic cells:Pt, Ni + Ni2Si04 + Si02/(Y203)Zr02/Ni + + NiO, Pt (1) and Pt, Ni + NizSiOj + Si02/CaF2/Ni + + NiO, Pt (11) have been employed for the determination of the Gibbs' energy of formation of nickel orthosilicate(Ni2Si04) from nickel oxide and quartz. The emf of cell (I) was reversible and reproducible in the temperature range 925 to 1375K whereas emf of cell (11) drifted with time and changed polarity. From the results of cell (I), the Gibbs' energy of formation of nickel silicate is obtained as,2Ni0 (r.s.) + Si02 (quartz) + Ni2Si04 (olivine)Gibbs' energy of formation of the spinel form of Ni2Si04 is obtained by combining the data for olivine obtained in this study with high pressure data on olivine to spinel transition reported in the literature. The complex time dependence of the emf of cell (11) can be rationalised on the basis of formation of calcium silicates from calcium oxide, generally present as an impurity in the calcium fluoride electrolyte, and silica. The emf of cell (11) is shown to be the function of the activity of calcium oxide at the electrolyte/ electrode interface. The results provide strong evidence against the recent suggestion of mixed anionic conduction in calcium fluoride.

Measurement of Gibbs energies of formation of CoF2 and MnF2 using a new composite dispersed solid electrolyte

Gibbs energies of formation of CoF2 and MnF2 have been measured in the temperature range from 700 to 1100 K using Al2O3-dispersed CaF2 solid electrolyte and Ni+NiF2 as the reference electrode. The dispersed solid electrolyte has higher conductivity than pure CaF2 thus permitting accurate measurements at lower temperatures. However, to prevent reaction between Al2O3 in the solid electrolyte and NiF2 (or CoF2) at the electrode, the dispersed solid electrolyte was coated with pure CaF2, thus creating a composite structure. The free energies of formation of CoF2 and MnF2 are (± 1700) J mol−1; {fx37-1} The third law analysis gives the enthalpy of formation of solid CoF2 as ΔH° (298·15 K) = −672·69 (± 0·1) kJ mol−1, which compares with a value of −671·5 (± 4) kJ mol−1 given in Janaf tables. For solid MnF2, ΔH°(298·15 K) = − 854·97 (± 0·13) kJ mol−1, which is significantly different from a value of −803·3 kJ mol−1 given in the compilation by Barinet al.

Optical, electrical and dielectric properties of TiO(2)-SiO(2) films prepared by a cost effective sol-gel process

Titanium dioxide (TiO(2)) and silicon dioxide (SiO(2)) thin films and their mixed films were synthesized by the sol-gel spin coating method using titanium tetra isopropoxide (TTIP) and tetra ethyl ortho silicate (TEOS) as the precursor materials for TiO(2) and SiO(2) respectively. The pure and composite films of TiO(2) and SiO(2) were deposited on glass and silicon substrates. The optical properties were studied for different compositions of TiO(2) and SiO(2) sols and the refractive index and optical band gap energies were estimated. MOS capacitors were fabricated using TiO(2) films on p-silicon (1 0 0) substrates. The current-voltage (I-V) and capacitance-voltage (C-V) characteristics were studied and the electrical resistivity and dielectric constant were estimated for the films annealed at 200 degrees C for their possible use in optoelectronic applications. (C) 2011 Elsevier B.V. All rights reserved.

Gibbs energies of formation of intermetallic phases in the systems Pt Mg, Pt Ca and Pt Ba and some applications

The standard Gibbs energies of formation of platinum-rich intermetallic compounds in the systems Pt-Mg, Pt-Ca, and Pt-Ba have been measured in the temperature range of 950 to 1200 K using solid-state galvanic cells based on MgF2, CaF2, and BaF2 as solid electrolytes. The results are summarized by the following equations: ΔG° (MgPt7) = −256,100 + 16.5T (±2000) J/mol ΔG° (MgPt3) = −217,400 + 10.7T (±2000) J/mol ΔG° (CaPt5) = −297,500 + 13.0T (±5000) J/mol ΔG° (Ca2Pt7) = −551,800 + 22.3T (±5000) J/mol ΔG° (CaPt2) = −245,400 + 9.3T (±5000) J/mol ΔG° (BaPt5) = −238,700 + 8.1T (±4000) J/mol ΔG° (BaPt2) = −197,300 + 4.0T (±4000) J/mol where solid platinum and liquid alkaline earth metals are selected as the standard states. The relatively large error estimates reflect the uncertainties in the auxiliary thermodynamic data used in the calculation. Because of the strong interaction between platinum and alkaline earth metals, it is possible to reduce oxides of Group ILA metals by hydrogen at high temperature in the presence of platinum. The alkaline earth metals can be recovered from the resulting intermetallic compounds by distillation, regenerating platinum for recycling. The platinum-slag-gas equilibration technique for the study of the activities of FeO, MnO, or Cr2O3 in slags containing MgO, CaO, or BaO is feasible provided oxygen partial pressure in the gas is maintained above that corresponding to the coexistence of Fe and “FeO.”

Gibbs energies of formation of rare earth MPt5 compounds

The Gibbs energies of formation of MPt5 (MNd, Dy, Ho, Er) intermetallic compounds were determined in the temperature range 900–1100 K using the solid state cell Ta,M+MF3¦CaF2¦MPt5+Pt+MF3,Ta For M ≡ Sm, a mixture of Gd + GdF3 was used as the reference electrode. In the case of Eu, a mixture of Eu + EuF2 served as the reference electrode. The trifluorides of Sm and Eu are not stable in equilibrium with the metal. The fluoride phase coexisting with a SmPt5 + Pt mixture is SmF3, whereas EuF2 is the equilibrium phase in contact with EuPt5 + Pt. All the MPt5 compounds studied (except EuPt5) exhibit similar stability. Europium is divalent in the pure metal and trivalent in EuPt5. The energy required for the promotion of divalent Eu to the trivalent state accounts for the less negative Gibbs energy of formation of EuPt5. The enthalpies of formation of all the MPt5 compounds obtained in this study are in good agreement with Miedema's model.

The standard molar Gibbs energy of formation of YbPt3 and LuPt3 intermetallics

The standard molar Gibbs energies of formation of YbPt3 and LuPt3 intermetallic compounds have been measured in the temperature range 880 K to 1100 K using the solid-state cells:View the MathML source and View the MathML source The trifluoride of Yb is not stable in equilibrium with Yb or YbPt3. The results can be expressed by the equations: View the MathML source View the MathML source The standard molar Gibbs energy of formation of LuPt3 is −41.1 kJ · mol−1 more negative than that for YbPt3 at 1000 K. Ytterbium is divalent in the pure metal and trivalent in the intermetallic YbPt3. The energy required for the promotion of divalent Yb to the trivalent state is responsible for the less negative ΔfGmo of YbPt3. The enthalpies of formation of the two intermetallics are in reasonable agreement with Miedema's model. Because of the extraordinary stability of these compounds it is possible to reduce oxides of Yb and Lu with hydrogen in the presence of platinum at View the MathML source. The equilibrium chemical potential of oxygen corresponding to the reduction of Yb2O3 and Lu2O3 by hydrogen in the presence of platinum is presented in the form of an Ellingham diagram.

Measurement of the Gibbs energy of formation of URh3 using an oxide solid electrolyte

The Gibbs' energy offormation of the intermetallic compound URh3has been measured in the temperature range 980 to 1320 K using an oxide solid state cell incorporating yttria-doped thoria as the solid electrolyte and a mixture of manganese and manganese oxide as the reference electrode. The cell can be represented as Pt, Mn + MnO I (Y203)Th02 I Rh + URh3 + U02 + x' Rh, Pt The reversible emf of the cell was a linear function of temperature E = 15.60 +0.0237 T (±0.8) mY. Using auxiliary thermodynamic data for MnO and U02+ x the Gibbs' energy of formation of URh3 from component metals has been computed. The results can be expressed by the equation L'.G?< URh3 > = -316240 + 13.22 T (± 3000) J mol-1. The "third-law" enthalpy of formation of URh3at 298 K is -293.2 (± 4) kJ mol-1, significantly more negative than the value of -181.5 kJ mol-1 calculated using Miedema's model.

Gibbs’ energy of formation of YBa2Cu3O7-x (tetragonal)

The high temperature ceramic oxide superconductor YBa2Cu3O7-x (1–2–3 compound) is generally synthesized in an oxygen-rich environment. Hence any method for determining its thermodynamic stability should operate at a high oxygen partial pressure. A solid-state cell incorporating CaF2 as the electrolyte and functioning under pure oxygen at a pressure of 1·01 × 105 Pa has been employed for the determination of the Gibbs’ energy of formation of the 1–2–3 compound. The configuration of the galvanic cell can be represented by: Pt, O2, YBa2Cu3O7−x , Y2BaCuO5, CuO, BaF2/CaF2/BaF2, BaZrO3, ZrO2, O2, Pt. Using the values of the standard Gibbs’ energy of formation of the compounds BaZrO3 and Y2BaCuO5 from the literature, the Gibbs’ energy of formation of the 1–2–3 compound from the constituent binary oxides has been computed at different temperatures. The value ofx at each temperature is determined by the oxygen partial pressure. At 1023 K for O content of 6·5 the Gibbs’ energy of formation of the 1–2–3 compound is −261·7 kJ mol−1.

Gibbs energy of formation of CuCrO4 and phase relations in the system Cu-Cr-O below 735 K

A solid state galvanic cell incorporating yttria-stabilized zirconia electrolyte and ruthenium(IV) oxide electrodes has been used to measure the equilibrium chemical potential of oxygen corresponding to the decomposition of CuCrO4 in the range 590–760 K. For the reaction CuO(tenorite) + CuCr2O4(spinel) + 1.5O2(g)→2CuCrO4(orth), ΔGXXX = −183540 + 249.6T(±900) J mol−1. The decomposition temperature of CuCrO4 in pure oxygen at a pressure of 1.01 × 105 Pa is 735(±1) K. By combining the results obtained in this study with data on the Gibbs energy of formation of CuCr2O4 and CuCrO2 reported earlier, the standard Gibbs energy of formation of CuCrO4 and the phase relations in the system Cu-Cr-O at temperatures below 735 K have been deduced. Electron microscopic studies have indicated that the decomposition of CuCrO4 to CuCr2O4 is topotactic.

Gibbs’ free energies of formation of Cu2Ln2O5 (Ln = Tb, Dy, Er, Yb) compounds

The standard Gibbs' free energies of formation of compounds of type Cu2L%05 (Ln = Tb,Dy,Er,Yb) were measured using the solid state cell in the temperature range of 970 to 1323 K For formation of Cu2L?O5 compounds from their binary component oxides according to the reaction 2 CUO (s) + L%03 (s) -, Cu,,L%05 (s),the Gibbs' free energy changes can be represented by the following equations:AGO = 13 080 - 13.70 'I" (+80) J mol-' (Ln = Tb)AGq = 11 480 - 13.51 T (260) J mol-I (Ln = Dy)AGO = 10 750 - 13.99 T (260) J mol-I (Ln = Er)AGO = 9 920 - 13.90 T (260) J mol-' (Ln = Yb) Since formation of the compounds is endothermic, the compounds become thermodynamically unstable with respect to their component oxides below 955 K for Cu2Tb205, 850 K for Cu2Dy205, 768 K for Cu2Er205 and 714 K for Cu2Yb2OS When the oxygen partial pressure over Cu2L%05 is lowered, they decompose according to the scheme, 2 CU,L%O, (s) -r 2 L%03 (s) +2 cu20 (s) + 02(g)The equilibrium chemical potentials of oxygen corresponding to the dissociation reactions are computed from the emf data and auxiliary information on Cu20 and CuO. The computed decomposition temperatures at an oxygen partial pressure of 5.0 x ld Pa are compared with those obtained directly from combined thermogravimetric (TGA) and differential thermal analyses (DTA).The free energy, enthalpy and entropy of formation of Cu2Ln205 compounds show systematic variation with the ionic radius of the trivalent lanthanide ion. The trends obtained in this study are compared with information available in the literature. The staZbility of Cu2Ln205 compounds increases with the decrease in ionic radii of the ~ n ion~. +