A nano-scale instability in the beta phase of dilute Ti-Mo alloys

A nano-scale instability in the beta phase resulting in the formation of the disordered orthorhombic O' phase has been discovered in a fairly dilute binary Ti-Mo alloy, using selected area electron diffraction and high resolution scanning transmission electron microscopy. The O' phase informed in the alloy when the Mo content exceeds a critical value. The instability occurs in beta-solutionized samples that have been quenched to room temperature and is found to co-exist with athermal omega to phase. Interestingly, this nano-scale instability, involving the {110}<1<(1)over bar>0> soft-phonon shuffle, occurs in the beta phase without deliberate additions of either interstitial or substitutional solutes. (C) 2016 Elsevier Ltd. All rights reserved.

Effect of current density on the microstructure and corrosion properties of plasma electrolytic oxidation (PEO) coatings on AM50 Mg alloy produced in an electrolyte containing clay additives

Plasma electrolytic oxidation coatings were produced on AM50 Mg alloy in alkaline phosphate based electrolyte with montmorillonite clay additives employing current densities of 30, 60, and 120 mA/cm(2). The effect of current density on the microstructure and corrosion properties of the coating was investigated. The clay additives got melted and reactively incorporated into the coating forming an amorphous phase, at all the current densities. However, the coating was predominantly amorphous only at 30 mA/cm(2) and with increasing current density, increasing fractions of crystalline phases were formed. Higher current densities resulted in increased thickness of the coating, but reduced the compactness of the coatings. Electrochemical impedance spectroscopy tests in 0.5 wt.% (0.08 M) and 3.5 wt.% (0.6 M) NaCl solution revealed that the coatings processed at 30 mA/cm(2) exhibited a relatively better initial corrosion resistance owing to its relatively defect-free barrier layer and compactness of the coating. However, the presence of amorphous phases in significant amounts and lack of MgO in the coating resulted in increased rate of dissolution of the coatings and degradation of corrosion resistance. Coatings produced at higher current densities exhibited initial inferior corrosion resistance due to a more defective barrier layer and increased porosity in pore band and outer porous layer. However, the increased amount of crystalline phases and an increased amount of MgO, which resisted dissolution, counterbalanced the negative effects of defective barrier and increased porosity resulting in a relatively lower rate of the degradation of the corrosion resistance. Thus, the corrosion resistance of all the coatings continuously decreased with time and became similar after prolonged immersion in NaCl solution. Increasing current density, therefore, did not prove to be beneficial for the improvement of the corrosion performance of the PEO coatings. (C) 2016 Elsevier B.V. All rights reserved.

Tailored specular reflectance properties of bulk Cu based novel intermetallic alloys

Significant research has been pursued to develop solar selective metallic coatings using a variety of coating deposition techniques, with limited attempts to assess the properties of bulk metallic materials for solar energy applications. In developing bulk solar reflectors with good reflectance in the entire solar range, we report a new class of reflector materials based on Cu-Sn intermetallics with tailored substitution of aluminium or zinc. Our experimental results suggest that the arc melted-suction cast Cu (78.8 at%)-Al (21.2 at%) alloy with nanoscale surface roughness can exhibit a combination of 89% bulk specular reflectance and 83% bulk solar reflectance, together with a hardness of 2 GPa. We show that the present alloy design approach paves the way for further opportunities of tuning the spectral properties of this new class of solar reflector material. (C) 2016 Elsevier B.V. All rights reserved.