Normal state tunneling conductance of perovskite oxides: Implications for high-Tc superconductors

We have investigated tunneling conductances in disordered, normally conducting perovskite oxides close to the metal�insulator transition. We show that the normal state tunneling conductance of perovskite oxides can be cast in a general form G(V) = G0[1 + curly logical orV/V*curly logical orn] with 1?n?0.5 and where V* is an intrinsic energy scale. The exponent n graduall y increases from 0.5 to 1 as the metal-insulator (M-I) transition is approached. In the high-Tc Bi(2212) cuprates, the normally observed, linear G(V)(n=1) can be made sub-linear (n<1) by substitution of Ca with Y. From the similarity of the linear conductances, we suggest proximity to the M-I transition as a likely cause for this G(V)logical or, bar below V dependence. In systems showing linear conductances (nreverse similar, equals1), we find that ?G/?Vreverse similar, equalsG?0 with ?reverse similar, equals 1 and the intrinsic energy scale V*reverse similar, equals25�75 meV in the different oxides investigated.

A new approach for understanding ion transport in glasses; example of complex alkali diborate glasses containing lead, bismuth and tellurium oxides

Mechanism of ion transport in glasses continues to be incompletely understood. Several of the theoretical models in vogue fail to rationalize conductivity behaviour when d.c. and a.c. measurements are considered together. While they seem to involve the presence of at least two components in d.c. activation energy, experiments fail to reveal that feature. Further, only minor importance is given to the influence of structure of the glass on the ionic conductivity behaviour. In this paper, we have examined several general aspects of ion transport taking the example of ionically conducting glasses in pseudo binary, yNa(2)B(4)O(7)center dot(1-y) M (a) O (b) (with y = 0 center dot 25-0 center dot 79 and M (a) O (b) = PbO, TeO2 and Bi2O3) system of glasses which have also been recently characterized. Ion transport in them has been studied in detail. We have proposed that non-bridging oxygen (NBO) participation is crucial to the understanding of the observed conductivity behaviour. NBO-BO switching is projected as the first important step in ion transport and alkali ion jump is a subsequent event with a characteristically lower barrier which is, therefore, not observed in any study. All important observations in d.c. and a.c. transport in glasses are found consistent with this model.

Morphology and electrostatics play active role in neuronal differentiation processes on flexible conducting substrates

This commentary discusses and summarizes the key highlights of our recently reported work entitled ``Neuronal Differentiation of Embryonic Stem Cell Derived Neuronal Progenitors Can Be Regulated by Stretchable Conducting Polymers.'' The prospect of controlling the mechanical-rigidity and the surface conductance properties offers a unique combination for tailoring the growth and differentiation of neuronal cells. We emphasize the utility of transparent elastomeric substrates with coatings of electrically conducting polymer to realize the desired substrate-characteristics for cellular development processes. Our study showed that neuronal differentiation from ES cells is highly influenced by the specific substrates on which they are growing. Thus, our results provide a better strategy for regulated neuronal differentiation by using such functional conducting surfaces.

Virtues of marginally metallic oxides

Transition-metal oxides at the metal-insulator boundary, especially those belonging to the perovskite family, exhibit fascinating phenomena such as insulator-metal transitions controlled by composition, high-temperature superconductivity and giant magnetoresistance (GMR), Interestingly, many of these marginally metallic oxides obey the established criteria for metallicity and have a finite density of states at the Fermi;level. The perovskite manganates exhibiting GMR, on the other hand, are unusual in that they possess very high resistivities in the 'metallic' state and show no significant density of states at the Fermi level, Marginal metallicity in oxide systems is a problem of great complexity and contemporary interest and its understanding is of crucial significance to the diverse phenomena exhibited by these materials.

Structural and optical investigations of TiO2 films deposited on transparent substrates by sol-gel technique

An inexpensive and effective simple method for the preparation of nano-crystalline titanium oxide (anatase) thin films at room temperature on different transparent substrates is presented. This method is based on the use of peroxo-titanium complex, i.e. titanium isopropoxide as a single initiating organic precursor. Post-annealing treatment is necessary to convert the deposited amorphous film into titanium oxide (TiO2) crystalline (anatase) phase. These films have been characterized for X-ray diffraction (XRD) studies, atomic force microscopic (AFM) studies and optical measurements. The optical constants such as refractive index and extinction coefficient have been estimated by using envelope technique. Also, the energy gap values have been estimated using Tauc's formula for on glass and quartz substrates are found to be 3.35 eV and 3.39 eV, respectively.

Structural and optical investigations of TiO2 films deposited on transparent substrates by sol-gel technique

An inexpensive and effective simple method for the preparation of nano-crystalline titanium oxide (anatase) thin films at room temperature on different transparent substrates is presented. This method is based on the use of peroxo-titanium complex, i.e. titanium isopropoxide as a single initiating organic precursor. Post-annealing treatment is necessary to convert the deposited amorphous film into titanium oxide (TiO2) crystalline (anatase) phase. These films have been characterized for X-ray diffraction (XRD) studies, atomic force microscopic (AFM) studies and optical measurements. The optical constants such as refractive index and extinction coefficient have been estimated by using envelope technique. Also, the energy gap values have been estimated using Tauc's formula for on glass and quartz substrates are found to be 3.35 eV and 3.39 eV, respectively. (C) 2008 Elsevier B.V. All rights reserved.

Relative Stabilities of Layered Perovskite and Pyrochlore Structures in Transition Metal-Oxides Containing Trivalent Bismuth

In order to investigate the factors determining the relative stabilities of layered perovskite and pyrochlore structures of transition metal oxides containing trivalent bismuth, several ternary and quaternary oxides have been investigated. While d0 cations stabilize the layered perovskite structure, cations containing partially-filled d orbitals (which suppress ferroelectric distortion of MO6 octahedra) seem to favor pyrochlore-related structures. Thus, the vanadium analogue of the layered perovskite Bi4Ti3O12 cannot be prepared; instead the composition consists of a mixture of pyrochlore-type Bi1.33V2O6, Bi2O3, and Bi metal. The distortion of Bi1.33V2O6 to orthorhombic symmetry is probably due to an ordering of anion vacancies in the pyrochlore structure. None of the other pyrochlores investigated, Bi2NbCrO7, Bi2NbFeO7, TlBiM2O7 (M = Nb, Ta), shows evidence for cation ordering in the X-Ray diffraction patterns, as indeed established by structure refinement of TlBiNb2O7.

Action of Transition Metal Oxides on Composite Solid Propellants

The catalytic effects of Fe2O3, Ni2O3, MnO2, and Co2O3 transition metal oxides (TMO) on the combustion of polystyrene and carboxyl-terminated polybutadiene were investigated. The order of activity of TMO's was explained by the presence of Co and absence of Fe and Ni in their lattice systems along with a reduced electron-transfer process; in systems which induce the metal ions to enter the lattice, the electron transfer process is much greater. The thermal decomposition of ammonium perchlorate propellants was enhanced to a greater extent by Co2O3 and MnO2 than by Fe2O3 and Ni2O3.

Magnetic-properties of quasi-2-dimensional la1-xsr1+xmno4 and the evolution of itinerant electron ferromagnetism in the sro.(la1-xsrxmno3)n system

Quasi-two-dimensional oxides of the La,+,Sr,+,Mn04 system, possessing the KZNiF4 structure, show no evidence for ferromagnetic ordering in contrast to the corresponding three-dimensional La,+.Sr,MnO~ perovskites. Instead, there is an increasing tendency toward antiferromagnetic ordering with mcreasmg x m La,+,Sr,,, MnOp. Furthermore, these oxides are relatively high-resistivity materials over the entire compositional range. Substitution of Ba for Sr in La&r,.5Mn04 decreases the ferromagnetic interaction. Increasing the number of perovskite layers in SrO (La,-,Sr,MnO& causes an increase in electrical conductivity as well as ferromagnetic interaction. The oxide becomes a highly conducting ferromagnet when n 2 2.

High-temperature superconductivity in La- and Lu-substituted YBa2,Cu3,O7, and related oxides

The perovskites, Y0.75La0.25Ba2Cu3O7 and Y0.75Lu0.25Ba2Cu3O7, show high-Tc superconductivity (with zero resistance at or above 80 K), just as the parent compound YBa2Cu3O7. The Lu-substituted oxide, with the smallest unit-cell parameters, shows the highest Tc besides exhibiting a 100% Meissner effect. Hc1, in these oxides is around 25 mT, but the Hc2, is large. The thermopower of YBa2Cu3O7 shows a sharp transition to zero at the superconducting transition, reinforcing the bulk nature of the superconductivity. Preliminary studies show that ErBa2Cu3O7 and Er0.5Y0.5Ba2Cu3O7 are both high-temperature superconductors with zero resistance in the 82-90 K range.

HIGH-Tc superconductivity in perovskite oxides of the Y-Ba-Cu-O system

Several biphasic compositions of the type Y3-xBa3+xCu6O14 show an onset of superconductivity in the 90-115K range, attaining zero resistance in the 70-85K range. The phase responsible for superconductivity in these compositions is a perovskite oxide of composition YBa2Cu3 O7. This oxide annealed in oxygen shows the onset of superconductivity at 120K and zero resistance at 87K. YBa2,Cu3O7 shows the highest Meissner effect of all oxide superconductors. The superconducting behaviour of the two perovskite oxides, Y0.95Ba1.95,Cu3O7 and Y1.05Ba1.95Cu3O7 show interesting features; a marked decrease in resistivity is observed from room temperature itself in the former oxide with zero resistance at 89K. Electron microscopy and infrared spectra of these oxides are briefly discussed.

Mechanism of catalytic activity of metal oxides and chromites on ammonium perchlorate pyrolysis

This study investigates the mechanism of action of transition metal chromites on the decomposition of ammonium perchlorate.

HNbWO6 and HTaWO6: Novel oxides related to ReO3 formed by ion exchange of rutile-type LiNbWO6 and LiTaWO6

Both LiNbWO6 and LiTaWO6 undergo ion exchange in hot aqueous H2SO4 yielding the hydrates HMWO6 · H2O (M = Nb or Ta). The reaction is accompanied by a structural transformation from the rutile to the ReO3 structure. The cell constants are a = 3.783(3)Å for HNbWO6 · H2O and a = 3.785(5)Å for HTaWO6 · H2O. The ReO3 structure is retained by the dehydration products HMWO6 and MWO5.5 as well. HMWO6 phases yield H1+xMWO6 hydrogen bronzes on exposure to hydrogen in the presence of platinum catalyst.

Studies on vacuum pyrolysis of ammonium perchlorate and ammonium perchlorate/polystyrene propellant in the presence of transition metal oxides

Vacuum pyrolysis of ammonium perchlorate (AP) and ammonium perchlorate/polystyrene (PS) propellant has been studied by differential thermal analysis (DTA) in order to observe the effect of transition metal oxides on sublimation. Sublimation and decomposition being competitive processes, their proportions depend on the pressure of the pyrolysis chamber. The enthalpies for complete decomposition and complete sublimation are available from the literature and by using these data together with DTA area measurements, the extents of sublimation and decomposition have been calculated for AP and the propellant system. The effect of the metal ions on the extent and rate of sublimation depends on their nature. For AP the extent of sublimation increases with a decrease in particle size. For the propellants the powder sublimes more readily than the bulk material, but in the presence of metal ions the bulk material sublimes more readily than the powder. To substantiate this finding, the effect of MnO2 on AP sublimation as a function of particle size was examined, and it was observed that the extent of sublimation decreases as the particle size decreases.