Phonon anomalies, orbital-ordering and electronic raman scattering in iron-pnictide Ca(Fe0.97Co0.03)(2)As-2: temperature-dependent Raman study

We report inelastic light scattering studies on Ca(Fe0.97Co0.03)(2)As-2 in a wide spectral range of 120-5200 cm(-1) from 5 to 300 K, covering the tetragonal to orthorhombic structural transition as well as magnetic transition at T-sm similar to 160 K. The mode frequencies of two first-order Raman modes B-1g and E-g, both involving the displacement of Fe atoms, show a sharp increase below T-sm. Concomitantly, the linewidths of all the first-order Raman modes show anomalous broadening below T-sm, attributed to strong spin-phonon coupling. The high frequency modes observed between 400 and 1200 cm(-1) are attributed to electronic Raman scattering involving the crystal field levels of d-orbitals of Fe2+. The splitting between xz and yz d-orbital levels is shown to be similar to 25 meV, which increases as temperature decreases below T-sm. A broad Raman band observed at similar to 3200 cm(-1) is assigned to two-magnon excitation of the itinerant Fe 3d antiferromagnet.

Surface Enhanced Raman Scattering on Anodized Alumina Templates for Bio-sensing Applications

SERS substrate was fabricated by depositing silver on anodized aluminum oxide (AAO) template. The thickness of the AA0 template was 200 nm with 40 nm circular pore and 15 nm spacing. SERS effect was observed on these metal coated structures due to electric field enhancement around the edge of the pores. Para-Nitrophenol (pnp) solution of 10(-6) M concentration was detected which refers to an enhancement factor of 10(4).

Ultrafast Raman loss spectroscopy: a new approach to vibrational structure determination

The rapid data acquisition, natural fluorescence rejection and experimental ease are the advantages of the ultra-fast Raman loss scattering (URLS) which makes it a unique and valuable molecular structure-determining technique. URLS is an analogue of stimulated Raman scattering (SRS) but far more sensitive than SRS. It involves the interaction of two laser sources, viz. a picosecond (ps) pulse and white light, with the sample leading to the generation of loss signal on the higher energy (blue) side with respect to the wavelength of the ps pulse, unlike the gain signal observed on the red side in SRS. These loss signals are at least 1.5 times more intense than the SRS signals. Also, the very prerequisite of the experimental protocol for signal detection to be on the higher energy side by design eliminates the interference from fluorescence, which always appears on the red side. Unlike coherent anti-Stokes Raman scattering, URLS signals are not precluded by non-resonant background under resonance condition and also being a self-phase matched process, it is experimentally easier.

Investigation of short-time isomerization dynamics in p-nitroazobenzene from resonance Raman intensity analysis

Resonance Raman (RR) spectra are presented for p-nitroazobenzene dissolved in chloroform using 18 excitation Wavelengths, covering the region of (1)(n --> pi*) electronic transition. Raman intensities are observed for various totally symmetric fundamentals, namely, C-C, C-N, N=N, and N-O stretching vibrations, indicating that upon photoexcitation the excited-state evolution occurs along all of these vibrational coordinates. For a few fundamentals, interestingly, in p-nitroazobenzene, it is observed that the RR intensities decrease near the maxima of the resonant electronic (1)(n --> pi*) transition. This is attributed to the interference from preresonant scattering due to the strongly allowed (1)(pi --> pi*) electronic transition. The electronic absorption spectrum and the absolute Raman cross section for the nine Franck-Condon active fundamentals of p-nitroazobenzene have been successfully modeled using Heller's time-dependent formalism for Raman scattering. This employs harmonic description of the lowest energy (1)(n --> pi*) potential energy surface. The short-time isomerization dynamics is then examined from a priori knowledge of the ground-state normal mode descriptions of p-nitroazobenzene to convert the wave packet motion in dimensionless normal coordinates to internal coordinates. It is observed that within 20 fs after photoexcitation in p-nitroazobenzene, the N=N and C-N stretching vibrations undergo significant changes and the unsubstituted phenyl ring and the nitro stretching vibrations are also distorted considerably.

Ultrafast Raman loss spectroscopy (URLS): instrumentation and principle

In this paper, we report on the concept and the design principle of ultrafast Raman loss spectroscopy (URLS) as a structure-elucidating tool. URLS is an analogue of stimulated Raman scattering (SRS) but more sensitive than SRS with better signal-to-noise ratio. It involves the interaction of two laser sources, namely, a picosecond (ps) Raman pump pulse and a white-light (WL) continuum, with a sample, leading to the generation of loss signals on the higher energy (blue) side with respect to the wavelength of the Raman pump unlike the gain signal observed on the lower energy (red) side in SRS. These loss signals are at least 1.5 times more intense than the SRS signals. An experimental study providing an insight into the origin of this extra intensity in URLS as compared to SRS is reported. Furthermore, the very requirement of the experimental protocol for the signal detection to be on the higher energy side by design eliminates the interference from fluorescence, which appears on the red side. Unlike CARS, URLS signals are not precluded by the non-resonant background and, being a self-phase-matched process, URLS is experimentally easier. Copyright (C) 2011 John Wiley & Sons, Ltd.

Intensity of a Raman Overtone Band

Placzek [1] was the first to derive general expressions for the intensities of overtones in case of Raman scattering. He assumed electrical anharmonicity. However, he left the expressions for the derivations of the polarizability tensor undetermined. In 1941, a classical and semiempirical theory was developed by Wolkenstein [2]. He assumed the validity of the additivity of bond polarizabilities. However, the expressions derived by him for the intensities of overtones remain yet to be verified. It is the purpose of this paper to derive a formula for Raman polarizability tensor for overtones of (intramolecular) vibrational spectra along the lines of Kondilenko et al. [3,4].

Pressure-induced band gap reduction, orientational ordering and reversible amorphization in single crystals of C70: Photoluminescence and Raman studies

Photoluminescence and Raman scattering experiments have been carried out on single crystals of C70 up to 31 GPa to investigate the effect of pressure on the optical band gap, vibrational modes and stability of the molecule. The photoluminescence band shifts to lower energies and the pressure dependence of the band maxima yields the hydrostatic deformation potential to be 2.15 eV. The slope changes in the pressure dependence of peak positions and linewidths of the Raman modes associated with the intramolecular vibrations at 1 GPa mark the known face-centred cubic-->rhombohedral orientational ordering transition. The reversible amorphization in C70 at P > 20 GPa has been compared with the irreversible amorphization in C60 at P > 22 GPa in terms of carbon-carbon distance between the neighbouring molecules at the threshold transition pressures, in conjunction with the interplay between the intermolecular and intramolecular interactions.

Raman phase conjugator

We have developed a multipurpose high pressure gas cell which can be used to generate phase conjugate beams using various stimulated scattering processes. This high pressure cell can also be used as a tunable laser source using the process of stimulated Raman scattering. The phase conjugate nature of backward scattered Raman signals was investigated through distortion correction studies.

Raman study of pressure-induced structural transitions in CsIO4 to 12 GPa

High pressure Raman scattering studies have been carried out on cesium periodate (CsIO4) using the diamond anvil cell. Three pressure-induced phase transitions occur in the range 0.1�12 GPa as indicated by abrupt changes in the Raman spectra, and pressure dependence of the phonon frequencies. The transitions are observed at 1.5, 4.5 and 6.2 GPa in the increasing pressure cycle. A large hysteresis is noticed for the reverse transition when releasing the pressure. The high pressure phase is nearly quenchable to ambient pressure. The nature of the pressure-induced transitions are discussed in terms of the sequence of pressure-induced transitions expected for scheelite-pseudoscheelite structure ABO4 compounds from crystal chemical considerations. For the softening of the two high frequency internal modes, a pressure-induced electronic change involving the 5 d states of cesium and 5 p states of iodine is invoked.

Phonons and fractons in sol-gel alumina: Raman study

We report Raman scattering from the boehmite, gamma-, delta- and alpha-phases of the alumina gel. Samples are characterized by transmission and scanning electron microscopy, X-ray diffraction and density measurements. The main Raman line in the boehmite phase is red-shifted as well as asymmetrically broadened with respect to that in the crystalline boehmite, signifying the nanocrystalline nature of the gel. Raman signatures are absent in the gamma- and delta-phases due to the disorder in cation vacancies. We also show that low frequency Raman scattering from the boehmite phase resembles that from a fractal network, characterized in terms of fraction dimension ($) over tilde d. Taking Hausdorff dimension D of the boehmite gel to be 2.5 (or 3.0), the value of ($) over tilde d is 1.33 +/- 0.02 (or 1.44 +/- 0.02), which is close to the theoretically predicted value of 4/3.

Structural changes in single-walled carbon nanotubes under non-hydrostatic pressures: x-ray and Raman studies

Using in situ x-ray diffraction and Raman scattering techniques, we have investigated the behaviour of single-walled carbon nanotubes bundles under non-hydrostatic pressures. It is seen that the diffraction line corresponding to the two-dimensional triangular lattice in the bundles is not reversible for pressures beyond 5 GPa, in sharp contrast to earlier results under hydrostatic pressure conditions. Most interestingly, radial breathing and tangential Raman modes of the pressure-cycled samples from 21 and 30 GPa match very well with those of the starting sample. Raman and x-ray results put together clearly suggest that the ordering of tubes in the bundles is only marginally regained with a very short coherence length on decompression.

Pyrochlore ``dynamic spin-ice'' Pr(2)Sn(2)O(7) and monoclinic Pr(2)Ti(2)O(7): A comparative temperature-dependent Raman study

Here we report a temperature-dependent Raman study of the pyrochlore ``dynamic spin-ice'' compound Pr(2)Sn(2)O(7) and compare the results with its non-pyrochlore (monoclinic) counterpart Pr(2)Ti(2)O(7). In addition to phonon modes, we observe two bands associated with electronic Raman scattering involving crystal field transitions in Pr(2)Sn(2)O(7) at similar to 135 and 460 cm(-1) which couple strongly to phonons. Anomalous temperature dependence of phonon frequencies that are observed in Pyrochlore Pr(2)Sn(2)O(7) are absent in monoclinic Pr(2)Ti(2)O(7). This, therefore, confirms that the strong phonon-phonon anharmonic interactions, responsible for the temperature-dependent anomalous behavior of phonons, arise due to the inherent vacant sites in the pyrochlore structure. (C) 2011 Elsevier Inc. All rights reserved.

Combustion synthesis, characterization and Raman studies of ZnO nanopowders

Spherical shaped ZnO nanopowders (14-50 nm) were synthesized by a low temperature solution combustion method in a short time <5 min. Rietveld analysis show that ZnO has hexagonal wurtzite structure with lattice constants a = 3.2511(1) angstrom, c = 5.2076(2) angstrom, unit cell volume (V) = 47.66(5) (angstrom)(3) and belongs to space group P63mc. SEM micrographs reveal that the particles are spherical in shape and the powders contained several voids and pores. TEM results also confirm spherical shape, with average particle size of 14-50 nm. The values are consistent with the grain sizes measured from Scherrer's method and Williamson-Hall (W-H) plots. A broad UV-vis absorption spectrum was observed at similar to 375 nm which is a characteristic band for the wurtzite hexagonal pure ZnO. The optical energy band gap of 3.24 eV was observed for nanopowder which is slightly lower than that of the bulk ZnO (3.37 eV). The observed Raman peaks at 438 and 588 cm(-1) were attributed to the E(2) (high) and E(1) (LO) modes respectively. The broad band at 564 cm(-1) is due to disorder-activated Raman scattering for the A(1) mode. These bands are associated with the first-order Raman active modes of the ZnO phase. The weak bands observed in the range 750-1000 cm(-1) are due to small defects. (C) 2011 Elsevier B.V. All rights reserved.

Unusual dependence of raman mode frequency on excitation wavelength in graphite and single walled carbon nanotubes

In this paper we report resonance Raman scattering from graphite covering excitation energies in the range 2.4 eV to 6 eV. The Raman excitation profile shows a maximum at 4.94 eV (lambda = 251nm) for the G - band (1582 cm(-1)). The D-band at similar to 1350 cm(-1), attributed to disorder activated Raman scattering, does not show up in Raman spectra recorded with excitation wavelengths smaller than 257.3 nm, revealing that the resonance enhancements of the G and D-modes are widely different. Earlier Raman measurements in carbon materials have also revealed a very large and unusual dependence of the D - mode frequency on excitation laser wavelength. This phenomenon is also observed in carbon nanotubes. In this paper we show for the first time that the above unusual dependence arises from the disorder - induced double resonance mechanism.

Coupled phonons, magnetic excitations, and ferroelectricity in AlFeO3: Raman and first-principles studies

We determine the nature of coupled phonons and magnetic excitations in AlFeO3 using inelastic light scattering from 5 to 315 K covering a spectral range from 100 to 2200 cm(-1) and complementary first-principles density functional theory-based calculations. A strong spin-phonon coupling and magnetic ordering-induced phonon renormalization are evident in (1) anomalous temperature dependence of many modes with frequencies below 850 cm(-1), particularly near the magnetic transition temperature T-c approximate to 250 K, and (2) distinct changes in band positions of high-frequency Raman bands between 1100 and 1800 cm(-1); in particular, a broad mode near 1250 cm(-1) appears only below T-c, attributed to the two-magnon Raman scattering. We also observe weak anomalies in the mode frequencies similar to 100 K due to a magnetically driven ferroelectric phase transition. Understanding of these experimental observations has been possible on the basis of first-principles calculations of the phonons' spectrum and their coupling with spins.