Al based ultra-fine eutectic with high room temperature plasticity and elevated temperature strength

Developments of aluminum alloys that can retain strength at and above 250 degrees C present a significant challenge. In this paper we report an ultrafine scale Al-Fe-Ni eutectic alloy with less than 3.5 aa transition metals that exhibits room temperature ultimate tensile strength of similar to 400 MPa with a tensile ductility of 6-8%. The yield stress under compression at 300 degrees C was found to be 150 MPa. We attribute it to the refinement of the microstructure that is achieved by suction casting in copper mold. The characterization using scanning and transmission electron microscopy (SEM and TEM) reveals an unique composite structure that contains the Al-Al3Ni rod eutectic with spacing of similar to 90 nm enveloped by a lamellar eutectic of Al-Al9FeNi (similar to 140 nm). Observation of subsurface deformation under Vickers indentation using bonded interface technique reveals the presence of extensive shear banding during deformation that is responsible for the origin of ductility. The dislocation configuration in Al-Al3Ni eutectic colony indicates accommodation of plasticity in alpha-Al with dislocation accumulation at the alpha-Al/Al3Ni interface boundaries. In contrast the dislocation activities in the intermetallic lamellae are limited and contain set of planner dislocations across the plates. We present a detailed analysis of the fracture surface to rationalize the origin of the high strength and ductility in this class of potentially promising cast alloy. (C) 2015 Elsevier B.V. All rights reserved.

Stable isotopic signature of Southern Ocean deep water CO2 ventilation

The link between atmospheric CO2 level and ventilation state of the deep ocean is poorly understood due to the lack of coherent observations on the partitioning of carbon between atmosphere and ocean. In this Southern Ocean study, we have classified the Southern Ocean into different zones based on its hydrological features and have binned the variability in latitudinal air-CO2 concentration and its isotopic ratios. Together with air-CO2, we analysed the surface water for the isotopic ratios in dissolved inorganic carbon (DIC). Using the binary mixing approach on the isotopic ratio of atmospheric CO2 and its concentration, we identified the delta C-13 value of source CO2. The isotopic composition of source CO2 was around -9.22 +/- 0.26 parts per thousand for the year 2011 and 2012, while a composition of -13.49 +/- 4.07 parts per thousand was registered for the year 2013. We used the delta C-13 of DIC to predict the CO2 composition in air under equilibrium and compared our estimates with actual observations. We suggest that the degeneration of the DIC in presence of warm water in the region was the factor responsible for adding the CO2 to the atmosphere above. The place of observation coincides with the zone of high wind speed which promotes the process of CO2 exsolution from sea water. (C) 2015 Elsevier Ltd. All rights reserved.