Damage mechanisms in stainless steel and chromium carbide coatings under controlled environment fretting conditions

Fretting is of a serious concern in many industrial components, specifically, in nuclear industry for the safe and reliable operation of various component and/or system. Under fretting condition small amplitude oscillations induce surface degradation in the form of surface cracks and/or surface wear. Comprehensive experimental studies have been carried out simulating different fretting regimes under ambient and vacuum (10(-9) MPa) conditions and, temperature up to 400 degrees C. Studies have been carried out with stainless steel spheres on stainless steel flats, and stainless steel spheres against chromium carbide, with 25% nickel chrome binder coatings. Mechanical responses are correlated with the damage observed. It has been observed that adhesion plays a vital role in material degradation process, and its effectiveness depends on mechanical variables such as normal load, interfacial tangential displacement, characteristics of the contacting bodies and most importantly on the environment conditions. Material degradation mechanism for ductile materials involved severe plastic deformation, which results in the initiation or nucleation of cracks. Ratcheting has been observed as the governing damage mode for crack nucleation under cyclic tangential loading condition. Further, propagation of the cracks has been observed under fatigue and their orientation has been observed to be governed by the contact conditions prevailing at the contact interface. Coated surfaces show damage in the form of brittle fracture and spalling of the coatings. Existence of stick slip has been observed under high normal load and low displacement amplitude. It has also been observed that adhesion at the contact interface and instantaneous cohesive strength of the contacting bodies dictates the occurrence of material transfer. The paper discusses the mechanics and mechanisms involved in fretting damage under controlled environment conditions. (C) 2015 Elsevier B.V. All rights reserved.

Effect of electroslag refining on the fracture toughness and fatigue crack propagation rates in heat treated AISI 4340 steel

The AISI 4340 steel has been electroslag refined and the improvement in mechanical properties has been assessed. Electroslag refining (ESR) has improved tensile ductility, plane strain fracture toughness, Charpy fracture energy, and has decreased fatigue crack growth rates. The KIC values for the ESR steel are nearly twice those estimated in the unrefined steel and higher than those obtained in the vacuum arc remelted steel. Fatigue crack growth rates in region I and in region III are found to be decreased considerably in the ESR steel, while they are unaffected in region II. Measurements on heat treated samples have shown that the ESR steel has a better response to heat treatment. Both the suggested heat treatments namely austenitizing at 1140–1470 K as well as the conventional heat treatment of austenitizing at 1140 K have been followed. The improvement in the mechanical properties of ESR steel has been explained on the basis of removal of nonmetallic inclusions and reduction in sulfur content in the steel.

Effect of surfactant dispersed in oil on interaction force between an oil film and a steel substrate in water

The oil phase, in an oil-in-water emulsion on a steel substrate, is strongly repelled by the substrate. The oil in this situation does not wet the steel and steel/steel friction is high. In this work we disperse anionic surfactants in an oil film and study the effect of this dispersion on the force of interaction between a silica colloid probe (AFM) carrying the oil film and a steel substrate in water. It is observed that when the surfactant is oil insoluble and the interaction time is short the strong entropic repulsion (without the surfactant) is replaced by a strong attraction. The steel on steel sliding friction in this case is low compared to that what is achieved when the surfactant is soluble in oil. The rationale underlying these interactions is explored here. (C) 2011 Elsevier B.V. All rights reserved.

Sliding wear of YTZP ceramic against steel: observations on ceramic transfer and wear transition

Sliding tests were conducted, in air, of YTZP ceramic pins against steel discs at an applied pressure of 15.5 MPa over a speed range of 0.3 to 4.0 ms(-1). Pin wear was not detectable until 2.0 m s(-1), after which a finite but small wear rate was observed at 3.0 m s(-1), accompanied by a red glow at the contacting surface. A transition in wear behaviour and friction (mu) occurred at 4.0 ms(-1), increasing the former by over two orders of magnitude. Both mu and wear behaviour changed with time at 4.0 m s(-1). During initial periods mu was high and wear rate increased steadily with time accompanied by ceramic transfer onto the disc, which increased with time. When disc coverage exceeds a certain threshold value, mu decreased rapidly and the wear rate stabilized at a very high value. Metal transfer was not observed at any speed. High surface temperatures brought about significant adhesion between TZP and steel and this together with enhanced plastic deformation brought about a transition in wear behaviour.

Studies on grinding media wear and its effect on flotation of ferrugenous phosphate ore

Marked ball grinding rests were carried out in the laboratory with a low grade phosphate ore under different experimental conditions. Two types of balls were used, namely high carbon low alloy (HCLA) cast steel and high chrome cast iron. Results of marked ball grinding tests indicated that ball wear increased with time and showed a sharp increase for wet grinding over dry grinding. Ball wear under wet grinding conditions was also influenced by the gaseous atmosphere in the mill. The grinding ball materials could be arranged in the following order with respect to their overall wear resistance: High chrome cast iron > HCLA cast steel balls Methods to minimize ball wear through control of mill atmosphere and addition of flotation reagents are discussed. Effect of grinding media and additions of flotation reagents during grinding on phosphate ore flotation are also discussed. (C) 1999 Elsevier Science Ltd. All rights reserved.

Crucible Steel in South India-Preliminary Investigations on Crucibles from Some Newly Identified Sites

European accounts from the 17th century onwards have referred to the repute and manufacture of “wootz’, a traditional crucible steel made especially in parts of southern India in the former provinces of Golconda, Mysore and Salem. Pliny's Natural History mentions the import of iron and steel from the Seres which have been thought to refer to the ancient southern Indian kingdom of the Cheras. As yet the scale of excavations and surface surveys is too limited to link the literary accounts to archaeometallurgical evidence, although pioneering exploratory investigations have been made by scholars, especially on the pre-industrial production sites of Konasamudram and Gatihosahalli discussed in 18th-19th century European accounts. In 1991–2 during preliminary surveys of ancient base metal mining sites, Srinivasan came across unreported dumps with crucible fragments at Mel-Siruvalur in Tamil Nadu, and Tintini and Machnur in Karnataka and she collected surface specimens from these sites as well as from the known site of Gatihosahalli. She was also given crucible fragments by the Tamil University, Tanjavur, from an excavated megalithic site at Kodumanal, dated to ca 2nd c. Bc, mentioned in Tamil Sangam literature (ca 3rd c. BC-3rd c. AD), and very near Karur, the ancient capital of the Sangam Cheras. Analyses of crucible fragments from the surface collection at Mel-Siruvalur showed several iron prills with a uniform pearlitic structure of high-carbon hypereutectoid steel (∼1–1.5% C) suggesting that the end product was uniformly a high-carbon steel of a structure consistent with those of high-carbon steels used successfully to experimentally replicate the watered steel patterns on ‘Damascus’ swords. Investigations indicate that the process was of carburisation of molten low carbon iron (m.p. 1400° C) in crucibles packed with carbonaceous matter. The fabric of crucibles from all the above mentioned sites appears similar. Preliminary investigations on these crucibles are thus reported to establish their relationship to crucible production of carbon steel and to thereby extend the known horizons of this technology further.

Thermal shock characteristics of plasma sprayed mullite coatings

Commercially available mullite (3Al(2)O(3). 2SiO(2)) powders containing oxides of calcium and iron as impurities, have been made suitable for plasma spraying by using an organic binder. Stainless steel substrates covered with Ni-22Cr-10Al-1.0Y bond coat were spray coated with mullite, The 425 mu m thick coatings were subjected to thermal shock cycling under burner rig conditions between 1000 and 1200 degrees C and less than 200 degrees C with holding times of 1, 5, and 30 min. While the coatings withstood as high as 1000 shock cycles without failure between 1000 and 200 degrees C, spallation occurred early at 120 cycles when shocked from 1200 degrees C, The coatings appeared to go through a process of self erosion at high temperatures resulting in loss of material. Also observed were changes attributable to melting of the silicate grains, which smooth down the surface. Oxidation of the bond coat did not appear to influence the failure, These observations were supported by detailed scanning electron microscopy and quantitative chemical composition analysis, differential thermal analysis, and surface roughness measurements.

Corrosive and abrasive wear in ore grinding

The relative significance of corrosive and abrasive wear in ore grinding is discussed. Laboratory marked ball wear tests were carried out with magnetic taconite and quartzite under different conditions, namely dry, wet and in the presence of an organic liquid. The effect of different modes of aeration and of pyrrhotite addition on the ball wear using mild steel, high carbon low alloy steel and austenitic stainless steel balls was evaluated. Results indicate that abrasive wear plays a significant role in ore grinding in the absence of sulfides, and rheological properties of the ore slurry influenced such wear. The effect of oxygen on corrosive wear becomes increasingly felt in the presence of a sulfide mineral such as pyrrhotite. Wear characteristics of the three types of ball materials under different grinding conditions are illustrated.

Role of Thiobacillus ferrooxidans and sulphur (sulphide)-dependent ferric-ion-reducing activity in the oxidation of sulphide minerals

Thiobacillus ferrooxidans oxidized the sulphide minerals e.g., pyrite, pyrrhotite and copper concentrate under anaerobic conditions in the presence of ferric ion as sole electron acceptor. Copper and iron were solubilized from sulphide ores by the sulphur (sulphide)-dependent ferric-ion oxidoreductase activity. Treatment of resting cells of T. ferrooxidans with 0.5% phenol for 30 min completely destroyed the iron- and copper-solubilizing activity. The above treatment destroyed the sulphur(sulphide)-dependent ferric-ion-reducing activity completely but did not affect the iron-oxidizing activity. The results suggest that sulphur(sulphide)-dependent ferric-ion-reducing activity actively participates in the oxidation of sulphide minerals under anaerobic conditions. The activity of sulphur(sulphide)-dependent ferric ion reduction in the solubilization of iron and copper from the sulphide ores were also observed under aerobic conditions in presence of sodium azide (0.1 μmol), which completely inhibits the iron-oxidizing activity.

Geochemistry of fluoride rich groundwater in Kolar and Tumkur Districts of Karnataka

Groundwater is a significant water resource in India for domestic, irrigation, and industrial needs. By far the most serious natural groundwater-quality problem in India, in terms of public health, derives from high fluoride, arsenic, and iron concentrations. Hydrogeochemical investigation of fluoride contaminated groundwater samples from Kolar and Tumkur Districts in Karnataka are undertaken to understand the quality and potability of groundwater from the study area, the level of fluoride contamination, the origin and geochemical mechanisms driving the fluoride enrichment. Majority of the groundwater samples did not meet the potable water criteria as they contained excess (>1.5 mg/L) fluoride, dissolved salts (>500 mg/L) and total hardness (75-924 mg/L). Hydrogeochemical facies of the groundwater samples suggest that rock weathering and evaporation-crystallization control the groundwater composition in the study area with 50-67% of samples belonging to the Ca-HCO3 type and the remaining falling into the mixed Ca-Na-HCO3 or Ca-Mg-Cl type. The saturation index values indicated that the groundwater in the study area is oversaturated with respect to calcite and under-saturated with respect to fluorite. The deficiency of calcium ion concentration in the groundwater from calcite precipitation favors fluorite dissolution leading to excess fluoride concentration.

Effect of densification and TiB2 reinforcement on the wear of molybdenum disilicide

Wear tests were done in a pin-on-disc machine by sliding MoSi2 pins against hard-steel discs in a normal load range of 5-140 N and a speed of 0.5 m/s under nominally dry conditions in the ambient. The specific wear rate of the pin undergoes two transitions: severe to mild at low load and mild to severe at high load. The mild-wear domain is distinguished by the formation of a protective mechanically mixed layer of steel and its oxides, transferred from the counterface in particulate form. Increasing the hardness by densification and TiB2 reinforcement lowers the specific wear rate and expands the mild-wear load domain. However, even when the volume wear rate is normalised with respect to the real contact area (load/hardness) the non-dimensional wear factor is still seen to decrease with densification and reinforcement. This indicates that fracture toughness may also play an important role in determining the wear-resistance of these materials. The surface coverage on the pin by the mechanically mixed layer increases with densification and reinforcement.

Diphosphazanes as Ligands: Links Betwen Phospeorus Ceiwistry and Organohetallic Cejmistry

The reactivity of several new acyclic, cyclic and bicyclic diphosphazanes towards Group-6 metal and iron carbonyls, and Pd, Pt and Rh derivatives has been studied. The structures of the products have been elucidated by IR and NMR spectroscopy and confirmed in a few instances by single crystal X-ray analyses.

In vitro and in vivo effects of methyl isocyanate on rat brain mitochondrial respiration

The present study deals with the in vitro and in vivo effects of methyl isocyanate (MIC) on rat brain mitochondrial function. Addition of MIC to tightly coupled brain mitochondria in vitro resulted in a mild stimulation of state 4 respiration, abolition of respiratory control, decrease in ADP/0 ratio, and inhibition of state 3 oxidation. The oxidation of NAD+-linked substrates (glutamate + malate) was more sensitive (fourfold) to the inhibitory action of MIC than succinate while cytochrome oxidase was unaffected. Administration of MIC subcutaneously at a lethal dose affected respiration only with glutamate + malate as the substrate (site I) and caused a 20% decrease in state 3 oxidation leading to a significant decrease in respiratory control index while state 4 respiration and ADP/O ratio remained unaffected. As both the malondialdehyde and iron contents of brain mitochondria were not altered, it may be inferred that the observed in vivo inhibition of state 3 oxidation is induced by MIC through systemic stagnant hypoxia leading to ischemia of brain, which further contributes to the cerebral hypoxia.

Reverse flotation of silica from Kudremukh iron ore .1. Selection of cationic reagents

Four types of cationic collectors were tested and evaluated for their performance in the reverse flotation of silica from the spiral preconcentrate of Kudremukh iron ore. A stagewise flotation was conducted by adding the reagent in three stages. Starch was used to depress hematite. Silica flotation was found to be very sensitive to the amount of cationic reagent added. The performance of the reagents was evaluated based on the percentage of silica and iron in the concentrate and percent recovery of iron obtained in the concentrate. Tests of significance, namely, t-test and F-test were performed to select the best two reagents for further investigations.

Boron nitride nanotubes and nanowires

Simple methods of preparing boron nitride nanotubes and nanowires have been investigated. The methods involve heating boric acid with activated carbon, multi-walled carbon nanotubes, catalytic iron particles or a mixture of activated carbon and iron particles, in the presence of NH3. While with activated carbon, boron nitride nanowires constitute the primary product, high yields of clean boron nitride nanotubes are obtained with multi-walled carbon nanotubes. Aligned boron nitride nanotubes are produced when aligned multi-walled carbon nanotubes are employed as the starting material suggesting the templating role of the nanotubes. Boron nitride nanotubes with different structures have been obtained by reacting boric acid with NH3 in the presence of a mixture of activated carbon and Fe particles. (C) 2002 Elsevier Science B.V. All rights reserved.