Dielectric response in pulsed laser ablated (Ba,Sr)TiO3 thin films

The dielectric response of pulsed laser ablated barium strontium titanate thin films were studied as a function of frequency and ambient temperature (from room temperature to 320 degrees C) by employing impedance spectroscopy. Combined modulus and impedance spectroscopic plots were used to study the response of the film, which in general may contain the grain, grain boundary, and the electrode/film interface as capacitive elements. The spectroscopic plots revealed that the major response was due to the grains, while contributions from the grain boundary or the electrode/film interface was negligible. Further observation from the complex impedance plot showed data points lying on a single semicircle, implying the response originated from a single capacitive element corresponding to the bulk grains. Conductivity plots against frequency at different temperatures suggested a response obeying the 'universal power law'. The value of the activation energies computed from the Arrhenius plots of both ac and dc conductivities with 1000/T were 0.97 and 1.04 eV, respectively. This was found to be in excellent agreement with published literature, and was attributed to the motion of oxygen vacancies within the bulk. (C) 2000 American Institute of Physics. [S0021-8979(00)02801-2].

Dielectric properties of glasses prepared by quenching melts of superconducting Bi‐Ca‐Sr‐Cu‐O cuprates

Glasses obtained from quenching melts of superconducting bismuth cuprates of the formula Bi2(Ca,Sr)n+1CunO2n+4 with n=1 and 3 exhibit novel dielectric properties. They possess relatively high dielectric constants as well as high electrical conductivity. The novel dielectric properties of these cuprate glasses are likely to be of electronic origin. They exhibit a weak microwave absorption due to the presence of microcrystallites.

Neutron diffraction evidence for oxygen dimers in Bi-Ca-Sr-Cu-O superconductors

A comparative neutron diffraction study of Bi2CaSr2Cu2O8+δ, Bi2Ca2SrCu2O8+δ and Bi2Ca1.5Y0.5SrCu2O8+δ has not only shown the presence of considerable oxygen excess in the Bi layers, but also evidence for oxygen pairing giving rise to O1−2 or O2−2 type species, probably the latter. The proportion of the paired species increases when Y partly replaces Ca. Furthermore, the Tc decreases with an increase in paired species.

Bi2−xPbx(Ca, Sr)n+1CunO2n+4+δ (n = 1, 2, 3, and 4) family of superconductors

Superconducting oxides of the Bi1.5Pb0.5(Ca, Sr)n+1CunO2n+4+δ series with n = 1, 2, 3 and 4 have been characterized. The superconducting transition temperature increases markedly with n up to n = 3, but the Tc of the n = 4 member is not much higher than that of the n = 3 member. The Tc does not change significantly in Bi2−xPbxCaSr2Cu2O8+δ with x (0.1 < x ≤ 0.5).

Nonlinear I-V characteristics of nanocrystalline SnO2

Current versus voltage characteristics (I-V) of nanocrystalline SnO2 materials have been investigated in air at room temperature. The samples were prepared by the inert gas condensation technique (IGCT) as well as by chemical methods. X-ray diffraction studies showed a tetragonal rutile structure for all the samples. Microstructural studies were performed with transmission electron microscopy. All the samples exhibited nonlinear I-V characteristics of the current-controlled negative resistance (CCNR) type. The results show that the threshold field (break down) voltage is higher for the samples prepared by the IGCT method than for those prepared by the chemical method due to the formation of a tin oxide layer over the crystalline tin. It is also found that the threshold field increases with the decrease in grain size.

Synthesis of S-functionalized thioesters using thioaroylate ions derived from carboxylic acids and tetrathiomolybdate via acyloxyphosphonium intermediates

Thioaroylate ions generated in situ from acyloxyphosphonium salts and tetrathiomolybdate upon Michael addition or ring opening of three membered systems led to a facile synthesis of S-funcationalized thioesters. While the ring opening of aziridines gave very good yield of the products, Micheal addition and epoxide ring opening gave moderate yields.(C) 2010 Elsevier Ltd. All rights reserved.

Trends in the stability of ternary oxides: Systems M-Pb-O (M = Ca, Sr, Ba)

Recent experimental investigations of phase equilibria and thermodynamic properties of the systems M-Pb-O, where M = Ca, Sr or Ba, indicate a regular increase in thermodynamic stability of ternary oxides, MPbO3 and M2PbO4, with increasing basicity of the oxide of the alkaline-earth metal. Number of stable interoxide compounds at 1100 K in the systems M-Pb-O (M = Mg, Ca, Sr, Ba) increases in unit increments from Mg to Ba. In this paper, experimentally determined standard Gibbs energies of formation of M2PbO4 (M = Ca, Sr, Ba) and MPbO3 (M = Sr, Ba) from their component binary monoxides and oxygen gas are combined with an estimated value for CaPbO3 to delineate systematic trends in thermodynamic stability of the ternary oxides. The trends are interpreted using concepts of tolerance factor and acid-base interactions. All the ternary oxides in these systems contain lead in the tetravalent state. The small Pb4+ ions polarize the surrounding oxygen ions and cause the formation of oxyanions which are acidic in character. Hence, the higher oxidation state of lead is stabilized in the presence of basic oxides of alkaline-earth group. A schematic subsolidus temperature-composition phase diagram is presented for the system BaO-PbO-O-2 to illustrate the change in oxidation states in binary and ternary oxides with temperature.

Microstructure related influence on the electrical properties of pulsed laser ablated (Ba, Sr)TiO3 thin films

The microstructural dependence of electrical properties of (Ba, Sr)TiO3(BST) thin films were studied from the viewpoint of dc and ac electrical properties. The films were grown using a pulsed laser deposition technique in a temperature range of 300 to 600 degrees C, inducing changes in grain size, structure, and morphology. Consequently, two different types of films were realized, of which type I, was polycrystalline, multigrained, while type II was [100] oriented possessing a densely packed fibrous microstructure. Leakage current measurements were done at elevated temperatures to provide evidence of the conduction mechanism present in these films. The results revealed a contribution from both electronic and ionic conduction. In the case of type I films, two trapping levels were identified with energies around 0.5 and 2.73 eV, which possibly originate from oxygen vacancies V-O and Ti3+ centers, respectively. These levels act as shallow and deep traps and are reflected in the current-voltage characteristics of the BST thin films. The activation energy associated with oxygen vacancy motion in this case was obtained as 1.28 eV. On the contrary, type II films showed no evidence of deep trap energy levels, while the identified activation energy associated with shallow traps was obtained as 0.38 eV. The activation energy obtained for oxygen vacancy motion in type II films was around 1.02 eV. The dc measurement results were further elucidated through ac impedance analysis, which revealed a grain boundary dominated response in type I in comparison to type II films where grain response is highlighted. A comparison of the mean relaxation time of the two films revealed three orders of magnitude higher relaxation time in the case of type I films. Due to smaller grain size in type I films the grains were considered to be completely depleted giving rise to only grain boundary response for the bulk of the film. The activation energy obtained from conductivity plots agree very well with that of dc measurements giving values 1.3 and 1.07 eV for type I and type II films, respectively. Since oxygen vacancy transport have been identified as the origin of resistance degradation in BST thin films, type I films with their higher value of activation energy for oxygen ion mobility explains the improvement in breakdown characteristics under constant high dc field stress. The role of microstructure in controlling the rate of degradation is found useful in this instance to enhance the film properties under high electric field stresses. (C) 2000 American Institute of Physics. [S0021-8979(00)00418-7].

High-temperature superconductivity in bismuth-copper oxides of the type BimMnCupOx (M=Mg, Ca, Sr, Ba, Bi)

Several oxides of the Bi m M n Cu p O x family (m=2, 3;n=2, 3, 4;p=1, 2, 3 and M=alkaline earth or Bi), possessing structures similar to the Aurivillius family of oxides, show highT c superconductivity.

Indications of superconductivity in the 200–300K range in the Bi-Ca-Sr-Cu-O system

Some of the Bi-Ca-Sr-Cu-O compositions show indications of onset of superconductivity in the 200–300 K region, possibly due to the intergrowth of different layered sequences.

Studies on LDPE-cyanoethylated lignocellulosics blends using epoxy functionalized LDPE as compatibilizer

Rubberwood flour and cellulose have been plasticized by cyanoethylation and then blended with low-density polyethylene (LDPE). A small quantity of epoxy functionalized polyethylene i.e., polyethylene-co-glycidyl methacrylate (PEGMA) has been added to further enhance the mechanical properties. The mechanical properties were measured according to the standard ASTM methods. SEM analysis was performed for both fractured and unfractured blend specimens. The mechanical properties were improved by the addition of PEGMA compatibilizer. LDPE blends with cyanoethylated wood flour (CYWF) showed higher tensile strength and modulus than cyanoethylated cellulose CYC-LDPE blends. However CYC-LDPE blends exhibited higher relative elongation at break values as compared with the former. The TGA analysis showed lowering of thermal stability as the filler content is increased and degradation temperature of LDPE is shifted slightly to lower temperature. DSC analysis showed loss of crystallinity for the LDPE phase as the filler content is increased for both types of blends. Dielectric properties of the blends were similar to LDPE, but were lowered on adding PEGMA. (c) 2006 Wiley Periodicals, Inc.

Crystal Chemistry of the Noncentrosymmetric Eulytites: A(3)Bi(XO4)(3) (X = V, A = Pb; X = P, A = Ca, Cd, Sr, Pb)

Eulytite compounds, A(3)Bi(XO4)(3) (X = P, A = Ca, Cd, Sr, Pb), belong to the noncentrosymmetric space group l (4) over bar 3d (No. 220) as determined by single-crystal X-ray diffraction studies. The crystals were grown from the melt-cool technique with considerable difficulty as the compounds melt incongruently at their melting temperature, except for the compound Pb3Bi(PO4)(3). The unit cell parameter a is 9.984(5), 9.8611(3), 10.2035(3), and 10.3722(2) angstrom for Ca3Bi(PO4)(3), Cd3Bi(PO4)(3), Sr3Bi(PO4)(3), and Pb3Bi(PO4)(3) respectively, and there are four formula units in the unit cell. The structure of Pb3Bi(VO4)(3), a unique eulytite with vanadium substitution, is compared with all these phosphorus substituted eulytites. The A(2+) and Bi3+ cations occupy the special position (16c) while the O anions occupy the general Wyckoff position (48e) in the crystal structure. Only one O position has been identified for Pb3Bi(PO4)(3) and Pb3Bi(VO4)(3), whereas two O atom sites were identified for Ca3Bi(PO4)(3), Cd3Bi(PO4)(3), and Sr3Bi(PO4)(3). The UV-vis diffuse reflectance spectra indicate large band gaps for all the phosphate eulytites while a lower band gap is observed for the vanadate eulytite. The feasibility of the use of these compounds in optoelectronic devices has been tested by measuring the second-harmonic generation (SHG) values which have been found to be of a magnitude equivalent to the commercially used KDP (KH2PO4).

Synthesis and characterization of flexible epoxy nanocomposites reinforced with amine functionalized alumina nanoparticles: a potential encapsulant for organic devices

Research on conducting polymers, organic light emitting diodes and organic solar cells has been an exciting field for the past decade. The challenge with these organic devices is the long term stability of the active material. Organic materials are susceptible to chemical degradation in the presence of oxygen and moisture. The sensitivity of these materials towards oxygen and moisture makes it imperative to protect them by encapsulation. Polymer nanocomposites can be used as encapsulation materials in order to prevent material degradation. In the present work, amine functionalized alumina was used as a cross-linking and reinforcing material for the polymer matrix in order to fabricate the composites to be used for encapsulation of devices. Fourier transform infrared spectroscopy, X-ray photoelectron spectroscopy and Raman spectroscopy were used to elucidate the surface chemistry. Thermogravimetric analysis techniques and CHN analysis were used to quantify grafting density of amine groups over the surface of the nanoparticles. Mechanical characterizations of the composites with various loadings were carried out with dynamic mechanical analyzer. It was observed that the composites have good thermal stability and mechanical flexibility, which are important for an encapsulant. The morphology of the composites was evaluated using scanning electron microscopy and atomic force microscopy.

Formation and preservation of pedogenic carbonates in South India, links with paleo-monsoon and pedological conditions: Clues from Sr isotopes, U-Th series and REEs

The influence of the pedogenic and climatic contexts on the formation and preservation of pedogenic carbonates in a climosequence in the Western Ghats (Karnataka Plateau, South West India) has been studied. Along the climosequence, the current mean annual rainfall (MAR) varies within a 80 km transect from 6000 mm at the edge of the Plateau to 500 mm inland. Pedogenic carbonates occur in the MAR range of 500-1200 mm. In the semi-arid zone (MAR: 500-900 mm), carbonates occur (i) as rhick hardpan calcretes on pediment slopes and (ii) as nodular horizons in polygenic black soils (i.e. vertisols). In the sub-humid zone (MAR: 900-1500 mm), pedogenic carbonates are disseminated in the black soil matrices either as loose, irregular and friable nodules of millimetric size or as indurated botryoidal nodules of centimetric to pluricentimetric size. They also occur at the top layers of the saprolite either as disseminated pluricentimetric indurated nodules or carbonate-cemented lumps of centimetric to decimetric size. Chemical and isotopic (Sr-87/Sr-86) compositions of the carbonate fraction were determined after leaching with 0.25 N HCl. The corresponding residual fractions containing both primary minerals and authigenic clays were digested separately and analyzed. The trend defined by the Sr-87/Sr-86 signatures of both labile carbonate fractions and corresponding residual fractions indicates that a part of the labile carbonate fraction is genetically linked to the local soil composition. Considering the residual fraction of each sample as the most likely lithogenic source of Ca in carbonates, it is estimated that from 24% to 82% (55% on average) of Ca is derived from local bedrock weathering, leading to a consumption of an equivalent proportion of atmospheric CO2. These values indicate that climatic conditions were humid enough to allow silicate weathering: MAR at the time of carbonate formation likely ranged from 400 to 700 mm, which is 2- to 3-fold less than the current MAR at these locations. The Sr, U and Mg contents and the (U-234/U-238) activity ratio in the labile carbonate fraction help to understand the conditions of carbonate formation. The relatively high concentrations of Sr, U and Mg in black soil carbonates may indicate fast growth and accumulation compared to carbonates in saprolite, possibly due to a better confinement of the pore waters which is supported by their high (U-234/U-238) signatures, and/or to higher content of dissolved carbonates in the pore waters. The occurrence of Ce, Mn and Fe oxides in the cracks of carbonate reflects the existence of relatively humid periods after carbonate formation. The carbonate ages determined by the U-Th method range from 1.33 +/- 0.84 kyr to 7.5 +/- 2.7 kyr and to a cluster of five ages around 20 kyr, i.e. the Last Glacial Maximum period. The young occurrences are only located in the black soils, which therefore constitute sensitive environments for trapping and retaining atmospheric CO2 even on short time scales. The maximum age of carbonates depends on their location in the climatic gradient: from about 20 kyr for centimetric nodules at Mule Hole (MAR = 1100 mm/yr) to 200 kyr for the calcrete at Gundlupet (MAR = 700 mm/yr, Durand et al., 2007). The intensity of rainfall during wet periods would indeed control the lifetime of pedogenic carbonates and thus the duration of inorganic carbon storage in soils. (C) 2010 Elsevier Ltd. All rights reserved.