Synthesis of One-Dimensional ZnO Nanostructures from Zn Powder/Granule

We report the growth of one-dimensional ZnO nanostructures with different morphologies such as nanoneedles, nanorods, nanobelts from Zn powder/granule. The growth process is different from the conventional vapor-solid mechanism. The advantage of this method is that neither a catalyst nor any gas flow is required for the synthesis of nanostructures. Depending upon the Zn powder or Zn granules as the starting material different nanostructures have been synthesized which demonstrates the versatility of the technique.

Activities in the $FeTiO_{3}-NiTiO_{3}$ Solid Solution from Alloy-Oxide Equilibria at 1273 K

Nine tie-lines between Fe-Ni alloys and FeTiO3-NiTiO3 solid solutions were determined at 1273 K. Samples were equilibrated in evacuated quartz ampoules for periods up to 10 days. Compositions of the alloy and oxide phases at equilibrium were determined by energy-dispersive x-ray spectroscopy. X-ray powder diffraction was used to confirm the results. Attainment of equilibrium was verified by the conventional tie-line rotation technique and by thermodynamic analysis of the results. The tie-lines are skewed toward the FeTiO3 corner. From the tie-line data and activities in the Fe-Ni alloy phase available in the literature, activities of FeTiO3 and NiTiO3 in the ilmenite solid solution were derived using the modified Gibbs-Duhem technique of Jacob and Jeffes [K.T. Jacob and J.H.E. Jeffes, An Improved Method for Calculating Activities from Distribution Equilibria, High Temp. High Press., 1972, 4, p 177-182]. The components of the oxide solid solution exhibit moderate positive deviations from Raoult's law. Within experimental error, excess Gibbs energy of mixing for the FeTiO3-NiTiO3 solid solution at 1273 K is a symmetric function of composition and can be represented as: Delta G(E) = 8590 (+/- 200) X-FeTiO3 X-NiTiO3 J/mol Full spectrum of tie-lines and oxygen potentials for the three-phase equilibrium involving Fe-Ni alloys, FeTiO3-NiTiO3 solid solutions, and TiO2 at 1273 K were computed using results obtained in this study and data available in the literature.

The Influence of Processing Parameters on Characteristics of an Aluminum Alloy Spray Deposition

In the present investigation, two nozzle configurations are used for spray deposition, convergent nozzle (nozzle-A), and convergent nozzle with 2 mm parallel portion attached at its end (nozzle-C) without changing the exit area. First, the conditions for subambient aspiration pressure, i.e., pressure at the tip of the melt delivery tube, are established by varying the protrusion length of the melt delivery tube at different applied gas pressures for both of the nozzles. Using these conditions, spray deposits in a reproducible manner are successfully obtained for 7075 Al alloy. The effect of applied gas pressure, flight distance, and nozzle configuration on various characteristics of spray deposition, viz., yield, melt flow rate, and gas-to-metal ratio, is examined. The over-spray powder is also characterized with respect to powder size distribution, shape, and microstructure. Some of the results are explained with the help of numerical analysis presented in an earlier article.

Structure of the noncubic phase in the ferroelectric state of Pr-substituted SrTiO3

Sr1−xPrxTiO3 has recently been shown to exhibit ferroelectricity at room temperature. In this paper powder x-ray and neutron-diffraction patterns of this system at room temperature have been analyzed to show that the system exhibits cubic (Pm-3m) structure for x<=0.05 and tetragonal (I4/mcm) for x>0.05. The redundancy of the noncentrosymmetric structural model (I4cm) in the ferroelectric state suggests the absence of long-range ordered ferroelectric domains and supports the relaxor ferroelectric model for this system.

Optical Properties of Nanocrystalline Potassium Lithium Niobate in the Glass System (100-x) TeO2-x(1.5K(2)O-Li2O-2.5Nb(2)O(5))

Optically clear glasses of various compositions in the system (100-x) TeO2-x(1.5K(2)O-Li2O-2.5Nb(2)O(5)) (2 <= x <= 12, in molar ratio) were prepared by the melt-quenching technique. The glassy nature of the as-quenched samples was established via differential scanning calorimetry (DSC). The amorphous and the crystalline nature of the as-quenched and heat-treated samples were confirmed by the X-ray powder diffraction and transmission electron microscopic (TEM) studies. Transparent glasses comprising potassium lithium niobate (K3Li2Nb5O15) microcrystallites on the surface and nanocrystallites within the glass were obtained by controlled heat-treatment of the as-quenched glasses just above the glass transition temperature (T-g). The optical transmission spectra of these glasses and glass-crystal composites of various compositions were recorded in the 200-2500 nm wavelength range. Various optical parameters such as optical band gap, Urbach energy, refractive index were determined. Second order optical non-linearity was established in the heat-treated samples by employing the Maker-Fringe method.

Anionic clay-Pt metal nanoparticle composite through intercalation of hexachloroplatinate in nickel zinc hydroxysalt

Nickel zinc hydroxysalt–Pt metal nanoparticle composite was prepared by intercalation of the anionic platinum complex, [PtCl6]2− in nickel zinc hydroxysalt through ion exchange reaction and subsequent reduction of the platinum complex by ethanol. Powder X-ray diffraction and microscopy studies indicate that the process of reduction of the platinum complex in the interlayer region of the anionic clay takes place topotactically without destroying the layers.

Size effect on the lattice parameter of KCl during mechanical milling

The size effect on the lattice parameter of ionic KCl nanocrystals was studied systematically during mechanical milling of Pure KCl powder under vacuum. The results suggest anomalous lattice expansion, with the lattice parameter increasing from 6.278 angstrom at d = 6 mu m to 6.30307 angstrom at d = 85 mn. The defects generated during ball milling of KCl and surface stress are deemed to be responsible for this lattice parameter expansion. (C) 2009 Acta Materialia Inc. Published by Elsevier Ltd. All rights reserved.

Degenerate rhombohedral and orthorhombic states in Ca-substituted Na0.5Bi0.5TiO3

Neutron powder diffraction and temperature dependent dielectric studies were carried out on Ca-substituted Na0.5Bi0.5TiO3, i.e., (Na0.5Bi0.5)(1-x)CaxTiO3. Stabilization of an orthorhombic phase even at a low Ca concentration (0.05 < x < 0.10) suggests that Na0.5Bi0.5TiO3 (NBT) is susceptible to orthorhombic distortion. The orthorhombic and rhombohedral phases coexist for x=0.10, suggesting these phases to be nearly degenerate. The orthorhombic distortion favoring tendency of Ca assists in promoting the inherent instability with regard to this structure in pure NBT, which was reported recently.

Competing tetragonal and monoclinic phases in Ni2.2Mn0.80Ga

Temperature dependent synchrotron x-ray powder diffraction, differential scanning calorimetry, and magnetic measurements were performed on Ni2+xMn1-xGa (x=0.20 and 0.35) magnetic shape memory alloys. For x=0.20, though the monoclinic phase is thermodynamically stable, a trace of residual stress can stabilize a tetragonal phase. The residual-stress-induced tetragonal phase transforms to the cubic austenite phase over an unusually large temperature range (348 K < T < 693 K), suggesting extremely slow kinetics of transformation. In contrast to x=0.20, the thermodynamically stable phase of x=0.35 is tetragonal and this composition exhibits the usual features of a reversible martensitic transformation. The results suggest that for x=0.20 the monoclinic and tetragonal phases are nearly degenerate.

Structural phase transition study of the morphotropic phase boundary compositions of Na0.5Bi0.5TiO3-PbTiO3

Neutron, synchrotron x-ray powder diffraction and dielectric studies have been performed for morphotropic phase boundary (MPB) compositions of the (1 - x )Na1/2Bi1/2TiO3-xPbTiO(3) system. At room temperature, the MPB compositions (0.10 < x <= 0.15) consist of a mixture of rhombohedral (space group R3c) and tetragonal ( space group P4mm) structures with the fraction of tetragonal phase increasing with increasing PbTiO3 content. On heating, while the rhombohedral phase just outside the MPB region, i.e. x = 0.10, transforms directly to a cubic phase, the rhombohedral phase of the MPB compositions transforms gradually to a tetragonal phase, until interrupted by a rhombohedral-cubic phase transition. The correspondence of the dielectric anomalies with the structural transitions of the different compositions has been examined and compared with earlier reports.

Fabrication and mechanisms of densification of ZrB2-based ultra high temperature ceramics by reactive hot pressing

Dense ZrB2-SiC (25-30 vol%) composites have been produced by reactive hot pressing using stoichiometric Zr, B4C, C and Si powder mixtures with and without Ni addition at 40 MPa, 1600 degrees C for 60 min. Nickel, a common additive to promote densification, is shown not to be essential; the presence of an ultra-fine microstructure containing a transient plastic ZrC phase is suggested to play a key role at low temperatures, while a transient liquid phase may be responsible at temperatures above 1350 degrees C. Hot Pressing of non-stoichiometric mixture of Zr, B4C and Si at 40 MPa, 1600 degrees C for 30 min resulted in ZrB2-ZrCx-SiC (15 vol%) composites of similar to 98% RD.

Phases in the (1-x)Na0.5Bi0.5TiO3-(x)CaTiO3 system

The structures of (1 - x) Na0.5Bi0.5TiO3-(x) CaTiO3 at room temperature have been investigated using neutron powder diffraction and dielectric studies. The system exhibits an orthorhombic (Pbnm) structure for x >= 0.15 and rhombohedral (R3c) for x <= 0.05. For x = 0.10, though the neutron diffraction pattern shows features of the orthorhombic (Pbnm) structure, Rietveld refinement using this structure shows a drastic reduction in the in-phase tilt angle (similar to 4 degrees) as compared to the corresponding value (similar to 8 degrees) for a neighbouring composition x = 0.15. The neutron diffraction pattern of x = 0.10 could be fitted equally well using a two-phase model (R3c + Pbnm) with orthorhombic as the minor phase (22%), without the need for a drastic decrease in the in-phase tilt angle. The dielectric studies of x = 0.10 revealed the presence of the polar R3c phase, thereby favouring the phase coexistence model, instead of a single-phase Pbnm structure, for this composition.

Dispersibility of Barium Titanate Suspension in the Presence of Polyelectrolytes: A Review

Dispersibility of colloidal barium titanate suspensions is reviewed with an emphasis on the use of various polyelectrolytes as dispersants. The fundamentals of colloidal stability are discussed followed by the colloidal properties of barium titanate powder. Dispersion behavior of BaTiO3 in both nonaqueous and aqueous media has been reviewed. Several studies on the stabilization of micron and nano-sized barium titanate using various polymeric dispersants and a rhamnolipid biosurfactant are presented and discussed. The article attempts to provide a comprehensive review of the current state-of-the-art in the area of colloidal processing of barium titanate.

Structural transformations in Mn2NiGa due to residual stress

Powder x-ray diffraction study of Mn2NiGa ferromagnetic shape memory alloy shows the existence of a 7M monoclinic modulated structure at room temperature (RT). The structure of Mn2NiGa is found to be highly dependent on residual stress. For higher stress, the structure is tetragonal at RT, and for intermediate stress it is 7M monoclinic. However, only when the stress is considerably relaxed, the structure is cubic, as is expected at RT since the martensitic transition temperature is 230 K.