Flexible poly(vinyl alcohol-co-ethylene)/modified MMT moisture barrier composite for encapsulating organic devices

Flexible, nano-composite moisture barrier films of poly(vinyl alcohol-co-ethylene) with surface modified montmorillonite fabricated by solution casting were used to encapsulate organic devices. The composite films were characterized by FTIR, UV-visible spectroscopy and SEM imaging. Thermal and mechanical properties of the composite films were studied by DSC and UTM. Calcium degradation test was used to determine the transmission rate of water vapour through the composite films, which showed a gradual reduction from similar to 0.1 g m(-2) day(-1) to 0.0001 g m(-2) day(-1) with increasing modified montmorillonite loading in the neat copolymer. The increase in moisture barrier performance is attributed to the decreased water vapour diffusivity due to matrix-filler interactions in the composite. The accelerated aging test was carried out for non-encapsulated and encapsulated devices to evaluate the efficiency of the encapsulants. The encapsulated devices exhibited longer lifetimes indicating the efficacy of the encapsulant.

Influence of initial degree of saturation on swell pressures of compacted Barmer bentonite specimens

Densely compacted bentonite or bentonite-sand mixture has been identified as suitable buffer in deep geological repositories as its exceptionally high swelling capacity enables tight contact between the waste canister and surrounding rock. The degree of saturation of the compacted bentonite buffer can increase upon ingress of groundwater from the surrounding rock mass or decrease from evaporation due to high temperature (50-210 degrees C) derived from the waste canister. Available studies indicate that the influence of initial moisture content or degree of saturation on the swell pressure or swell potential of compacted bentonites is unclear. Some studies suggest that initial degree of saturation has an influence, while others suggest that it does not have bearing on the swell pressure of compacted bentonites. This paper examines the influence of initial degree of saturation in montmorillonite voids (termed,S-r,S-MF) on swell pressure of compacted Barmer bentonite-sand mixtures (dry density range: 1.4-2 Mg/m(3)) from micro-structural considerations. The experimental results bring out that, constant dry density specimens that developed similar number of hydration layers upon wetting developed comparable swell pressures and were unaffected by variations in initial S-r,S-MF values. Comparatively, constant dry density specimens that developed dis-similar number of hydration layers upon wetting established different swell pressures and were responsive to variations in initial S-r,S-MF. (C) 2015 Elsevier Ltd. All rights reserved.

Effect of current density on the microstructure and corrosion properties of plasma electrolytic oxidation (PEO) coatings on AM50 Mg alloy produced in an electrolyte containing clay additives

Plasma electrolytic oxidation coatings were produced on AM50 Mg alloy in alkaline phosphate based electrolyte with montmorillonite clay additives employing current densities of 30, 60, and 120 mA/cm(2). The effect of current density on the microstructure and corrosion properties of the coating was investigated. The clay additives got melted and reactively incorporated into the coating forming an amorphous phase, at all the current densities. However, the coating was predominantly amorphous only at 30 mA/cm(2) and with increasing current density, increasing fractions of crystalline phases were formed. Higher current densities resulted in increased thickness of the coating, but reduced the compactness of the coatings. Electrochemical impedance spectroscopy tests in 0.5 wt.% (0.08 M) and 3.5 wt.% (0.6 M) NaCl solution revealed that the coatings processed at 30 mA/cm(2) exhibited a relatively better initial corrosion resistance owing to its relatively defect-free barrier layer and compactness of the coating. However, the presence of amorphous phases in significant amounts and lack of MgO in the coating resulted in increased rate of dissolution of the coatings and degradation of corrosion resistance. Coatings produced at higher current densities exhibited initial inferior corrosion resistance due to a more defective barrier layer and increased porosity in pore band and outer porous layer. However, the increased amount of crystalline phases and an increased amount of MgO, which resisted dissolution, counterbalanced the negative effects of defective barrier and increased porosity resulting in a relatively lower rate of the degradation of the corrosion resistance. Thus, the corrosion resistance of all the coatings continuously decreased with time and became similar after prolonged immersion in NaCl solution. Increasing current density, therefore, did not prove to be beneficial for the improvement of the corrosion performance of the PEO coatings. (C) 2016 Elsevier B.V. All rights reserved.