Hydrothermal synthesis of CdTe QDs: Their luminescence quenching in the presence of bio-molecules and observation of bistable memory effect in CdTe QD/PEDOT:PSS heterostructure

We report one-pot hydrothermal synthesis of nearly mono-disperse 3-mercaptopropionic acid capped water-soluble cadmium telluride (CdTe) quantum dots (QDs) using an air stable Te source. The optical and electrical characteristics were also studied here. It was shown that the hydrothermal synthesis could be tuned to synthesize nano structures of uniform size close to nanometers. The emissions of the CdTe QDs thus synthesized were in the range of 500-700 nm by varying the duration of synthesis. The full width at half maximum (FWHM) of the emission peaks is relatively narrow (40-90 nm), which indicates a nearly uniform distribution of QD size. The structural and optical properties of the QDs were characterized by transmission electron microscopy (TEM), photoluminescence (PL) and Ultraviolet-visible (UV-Vis) spectroscopy. The photoluminescence quenching of CdTe QDs in the presence of L-cysteine and DNA confirms its biocompatibility and its utility for biosensing applications. The room temperature current-voltage characteristics of QD film on ITO coated glass substrate show an electrically induced switching between states with high and low conductivities. The phenomenon is explained on the basis of charge confinement in quantum dots. (C) 2011 Elsevier B.V. All rights reserved.

ZnO-Au nanohybrids by rapid microwave-assisted synthesis for CO oxidation

We present a green method for the synthesis of ZnO-Au hybrids using an ultrafast microwave-based technique. This method provides good control over the nucleation of the metal nanoparticles on the oxide support, which governs the morphology and microstructure of the hybrids. The hybrids exhibit good catalytic activity for CO oxidation compared to similar hybrids reported in the literature. Detailed XPS investigation reveals the presence of Au-Zn and Au-O bonds at the interface. This surface doping leads to the formation of anionic and cationic Au sites that contribute to the enhanced activity. Our method is general and can be applied for designing other supported catalysts with controlled interfaces.

Hydrothermal synthesis of a monoclinic VO2 nanotube-graphene hybrid for use as cathode material in lithium ion batteries

The hydrothermal reaction of a mixture of a colloidal dispersion of graphite oxide and ammonium vanadate yielded a hybrid made of graphene and a nanotubular metastable monoclinic polymorph of VO2, known as VO2(B). The formation of VO2(B) nanotubes is accompanied by the reduction of graphite oxide. Initially the partially scrolled graphite oxide layers act as templates for the crystallization of VO2(B) in the tubular morphology. This is followed by the reduction of graphite oxide to graphene resulting in a hybrid in which VO2(B) nanotubes are dispersed in graphene. Electron microscopic studies of the hybrid reveal that the VO2(B) nanotubes are wrapped by and trapped between graphene sheets. The hybrid shows potential to be a high capacity cathode material for lithium ion batteries. It exhibits a high capacity (similar to 450 mAh/g) and cycling stability. The high capacity of the hybrid is attributed to the interaction between the graphene sheets and the VO2(B) tubes which improves the charge-transfer. The graphene matrix prevents the aggregation of the VO2(B) nanotubes leading to high cycling stability. (C) 2012 Elsevier Ltd. All rights reserved.

Effect of TiO2 on electrical and magnetic properties of Ni0.35Cu0.12Zn0.35Fe2O4 synthesized by the microwave-hydrothermal method

The nanocomposites of xTiO(2)+(1-x)Ni0.53Cu0.12Zn0.35Fe2O4 (where 0 <= x >= 1) were prepared using microwave hydrothermal (M H) method at 165 degrees C/45 min. The as-synthesized powders were characterized using X-ray diffraction (XRD), transmission electron microscopy (TEM) and Fourier transform infrared spectroscopy (FTIR). The particle size of the powder varies from 18 to 35 nm. The as prepared powders were densified at 500 degrees C/30 min using microwave sintering method. The sintered composites were characterized by XRD and scanning electron microscopy (SEM). The bulk densities of the present composites were increasing with the addition of TiO2. The grain sizes of all the composite vary between 65 nm and 90 nm. The addition of TiO2 to ferrite increased the dielectric properties (epsilon' and epsilon `') also the resonant frequency of all the composites was found to be greater than 1 GHz. The imaginary part of permeability mu `' was found to increase with an increase of TiO2.

Hydrothermal synthesis and characterization of bis(4,4 `-bipyridinium) dodecatungstosilicate dihydrate

Hydrothermal synthesis and structural characterization of a new organic polyoxometalate, namely, bis(4,4'-bipyridinium) dodecatungstosilicate dihydrate, 4,4'-bipyH(2)](2)SiW12O40]center dot 2H(2)O (1) is reported. The crystal structure of (1) consists of a SiW12O40](4-) Keggin anion situated on a two-fold axis, two unique 4,4'-bipyridinium cations, one of which is situated on a two-fold axis, and two independent lattice water molecules. The cations and anions are linked by H-bonding.

Pr6O11 micro-spherical nano-assemblies: microwave-assisted synthesis, characterization and optical properties

We report the synthesis of Pr6O11 microspheres self-assembled from ultra-small nanocrystals formed by the microwave irradiation of a solution of a salt of Pr in ethylene glycol (EG). The as-prepared product consists of microspheres measuring 200 to 500 nm in diameter and made of <5 nm nano-crystallites. The surface of these microspheres/nanocrystals is covered/capped with an organic layer of ethylene glycol as shown by TEM analysis and confirmed by IR spectroscopy measurements. The as-prepared product shows blue-green emission under excitation, which changes to orange-red when the product is annealed in air at 600 degrees C for 2 h. This change in luminescence behaviour can be attributed to presence of ethylene glycol layer in the as-prepared product. The samples were characterized by X-ray powder diffraction (XRD), field emission scanning electron microscopy (FE-SEM), IR Spectroscopy (IR), transmission electron microscopy (TEM), and thermogravimetric analysis (TGA). (C) 2013 Elsevier B.V. All rights reserved.

Hydrothermal synthesis of Gd2O3:Eu3+ nanophosphors: Effect of surfactant on structural and luminescence properties

Various morphologies of Eu3+ activated gadolinium oxide have been prepared by hydrothermal method using hexadecylamine (HDA) as surfactant at different experimental conditions. The powder X-ray diffraction studies reveal as-formed product is hexagonal Gd(OH)(3):Eu3+ phase and subsequent heat treatment at 350 and 600 degrees C transforms to monoclinic GdOOH:Eu3+ and cubic Gd2O3:Eu3+ phases respectively. SEM pictures of without surfactant show irregular shaped rods along with flakes. However, in the presence of HDA surfactant, the particles are converted into rods of various sizes. The temperature dependent morphological evolution of Gd2O3:Eu3+ without and with HDA surfactant is studied. TEM micrographs of Gd(OH)(3):Eu3+ sample with HDA confirms smooth nanorods with various diameters in the range 20-100 nm. FTIR studies reveal that HDA surfactant plays an important role in conversion of cubic to hexagonal phases. Among these three phases, cubic phase Gd2O3:Eu3+ (lambda(ex) = 254 nm) show red emission at 612 nm corresponding to D-5(0)-> F-7(2) and is more efficient host than the monoclinic counterpart. The band gap for hexagonal Gd(OH)(3):Eu3+ is more when compared to monoclinic GdOOH:Eu3+ and cubic Gd2O3:Eu3+. (C) 2013 Elsevier B. V. All rights reserved.

Facile hydrothermal synthesis of carbon nanoparticles and possible application as white light phosphors and catalysts for the reduction of nitrophenol

We report a simple hydrothermal synthesis of highly reproducible carbon nanoparticles in a size range between 2 and 7 nmfroma single precursor sucrose without either surface passivating agents or acids and bases. The carbon nanoparticles can be used as white light phosphors, especially for ultraviolet light emitting diodes and metal-free catalyst for the reduction of nitrophenol.

Novel spherical hierarchical structures of GdOOH and Eu:GdOOH: rapid microwave-assisted synthesis through self-assembly, thermal conversion to oxides, and optical studies

We report a novel, rapid, and low-temperature method for the synthesis of undoped and Eu-doped GdOOH spherical hierarchical structures, without using any structure-directing agents, through the microwave irradiation route. The as-prepared product consists of nearly monodisperse microspheres measuring about 1.3 mu m in diameter. Electron microscopy reveals that each microsphere is an assembly of two-dimensional nanoflakes (about 30 nm thin) which, in turn, result from the assembly of crystallites measuring about 9 nm in diameter. Thus, a three-level hierarchy can be seen in the formation of the GdOOH microspheres: from nanoparticles to 2D nanoflakes to 3D spherical structures. When doped with Eu3+ ions, the GdOOH microspheres show a strong red emission, making them promising candidates as phosphors. Finally, thermal conversion at modest temperatures leads to the formation of corresponding oxide structures with enhanced luminescence, while retaining the spherical morphology of their oxyhydroxide precursor.

Rapid, microwave-assisted synthesis of Gd2O3 and Eu:Gd2O3 nanocrystals: characterization, magnetic, optical and biological studies

Ultra-small crystals of undoped and Eu-doped gadolinium oxide (Gd2O3) were synthesised by a simple, rapid microwave-assisted route, using benzyl alcohol as the reaction solvent. XRD, XPS and TEM analysis reveal that the as-prepared powder material consists of nearly monodisperse Gd2O3 nanocrystals with an average diameter of 5.2 nm. The nanocrystals show good magnetic behaviour and exhibit a larger reduction in relaxation time of water protons than the standard Gd-DTPA complex currently used in MRI imaging. Cytotoxicity studies (both concentration- and time-dependent) of the Gd2O3 nanocrystals show no adverse effect on cell viability, evidencing their high biological compatibility. Finally, Eu:Gd2O3 nanocrystals were prepared by a similar route and the red luminescence of Eu3+ activator ions was used to study the cell permeability of the nanocrystals. Red fluorescence from Eu3+ ions observed by fluorescence microscopy shows that the nanocrystals (Gd2O3 and Eu:Gd2O3) can permeate not only the cell membrane but can also enter the cell nucleus, rendering them candidate materials not only for MRI imaging but also for drug delivery when tagged or functionalized with specific drug molecules.

Synthesis and characterization of spherical and rod like nanocrystalline Nd2O3 phosphors

Spherical and rod like nanocrystalline Nd2O3 phosphors have been prepared by solution combustion and hydrothermal methods respectively The Powder X-ray diffraction (PXRD) results confirm that hexagonal A-type Nd2O3 has been obtained with calcination at 900 C for 3 h and the lattice parameters have been evaluated by Rietveld refinement Surface morphology of Nd2O3 phosphors show the formation of nanorods in hydrothermal synthesis whereas spherical particles in combustion method TEM results also confirm the same Raman studies show major peaks which are assigned to F-g and combination of A(g) + E-g modes The PL spectrum shows a series of emission bands at similar to 326-373 nm (UV) 421-485 nm (blue) 529-542 nm (green) and 622 nm (red) The UV blue green and red emission in the PL spectrum indicates that Nd2O3 nanocrystals are promising for high performance materials and white light emitting diodes (LEDs) (C) 2010 Elsevier B V All rights reserved

Modelling transport processes during microwave heating: A review

The review is concerned with models that analyze transport:processes that occur during microwave heating. Early models on microwave. heating used Lambert's law to describe the microwave power absorption. Over the last decade, models for transport processes have been developed with the microwave power derived from Maxwell's equations. Those models, primarily based on plane waves, have been used for analyzing microwave heating of solids, liquids, emulsions, microwave thawing and drying. The models illustrate phenomena such a resonances, hot spots, edge and runaway heating. The literature on microwave sintering, susceptor heating and microwave assisted synthesis is largely experimental in nature and only key issues are highlighted. To fully appreciate the models for microwave heating, a section on the theory of electromagnetic wave propagation is included, where expressions for the electric field in dielectric slabs and cylinders are presented.

Preparation of the layered double hydroxide (LDH) LiAl2(OH)(7)center dot 2H(2)O, by gel to crystallite conversion and a hydrothermal method, and its conversion to lithium aluminates

A layered double hydroxide (LDH) with chemical composition LiAl2(OH)(7) . 2H(2)O was prepared via a wet chemical route of gel to crystallite (G-C) conversion at 80 degrees C involving the reaction of hydrated alumina gel, Al2O3.yH(2)O (80 < y < 120) with LiOH (Li2O/Al2O3 greater than or equal to 0.5) in presence of hydrophilic solvents such as ethanol under refluxing conditions. The hydrothermal synthesis was carried out using the same reactants by heating to less than or equal to 140 degrees C in a Teflon-lined autoclave under autogenerated pressure (less than or equal to 20 MPa). Transmission electron microscopy showed needle-shaped aggregates of size 0.04-0.1 mu m for the gel to crystallite conversion product, whereas the hydrothermal products consisted of individual lamellar crystallites of size 0.2-0.5 mu m with hexagonal morphology. The LDH prepared through the gel to crystallite conversion could be converted into LiAl(OH)(4) . H2O or LiAl(OH)(3)NO3 . H2O by imbibition of LiOH or LiNO3, respectively, under hydrothermal conditions. Thermal decomposition of LDH above 1400 degrees C gave rise to LiAl5O8 accompanied by the evaporation of Li2O. LiAl(OH)(4) . H2O and LiAl(OH)(3)NO3 . H2O decomposed in the temperature range 400-1000 degrees C to alpha- or beta-LiAlO2. The compositional dependence of the product, the intermediate phases formed during the heat treatment and the possible reactions involved are described in detail.

Synthesis of inorganic solids using microwaves

Use of microwaves in the synthesis of materials is gaining importance. Microwave-assisted synthesis is generally much faster, cleaner, and more economical than the conventional methods. A variety of materials such as carbides, nitrides, complex oxides, silicides, zeolites, apatite, etc. have been synthesized using microwaves. Many of these are of industrial and technological importance. An understanding of the microwave interaction with materials has been based on concepts of dielectric heating and of the resonance absorption due to rotational excitation. This review presents a summary of recent reports of microwave synthesis of inorganic materials. Various observations regarding microwave interaction with materials are also briefly discussed.

Ex Situ X-ray Diffraction, X-ray Absorption Near Edge Structure, Electron Spin Resonance, and Transmission Electron Microscopy Study of the Hydrothermal Crystallization of Vanadium Oxide Nanotubes: An Insight into the Mechanism of Formation

The nucleation and growth of vanadium oxide nanotubes (VOx-NT) have been followed by a combination of numerous ex situ techniques. long the hydrothermal process. Intermediate solid phases extracted at different reaction times have been characterized by powder X-ray diffraction, scanning and transmission electron microscopy, electron spin resonance, and V-K edge :X-ray absorption near-edge structure spectroscopy. The supernatant vanadate solutions extracted during the hydrothermal treatment have been studied by liquid V-51 NMR and flame. spectroscopy. For short durations of the hydrothermal synthesis, the initial V2O5-surfactant intercalate. is progressively transformed into VOx-NT whose crystallization starts to be detected after a hydrothermal treatment of 24 h. Upon heating from 24 h to 7 days, VOx-NT are obtained in larger amount and with an improved crystallinity. The detection of soluble amines and cyclic metavanadate V4O12](4-) in the supernatant solution along the hydrothermal process suggests that VOx-NT result from a dissolution precipitation mechanism. Metavanadate species V4O12](4-) could behave as molecular precursors in the polymerization reactions leading to VOx-NT.