A vertical jet of water impinging on a horizontal surface produces a radial film flow followed by a circular hydraulic jump. We report a phenomenon where fairly large (1 mi) drops of liquid levitate just upstream of the jump on a thin air layer between the drop and the film flow. We explain the phenomenon using lubrication theory. Bearing action both in the air film and the water film seems to be necessary to support large drops. Horizontal support is given to the drop by the hydraulic jump. A variety of drop shapes is observed depending on the volume of the drop and liquid properties. We show that interaction of the forces due to gravity, surface tension, viscosity and inertia produces these various shapes.

Response of Materials During Sliding on Various Surface Textures

In the present investigation, soft materials, such as Al-4Mg alloy, high-purity Al and pure Mg pins were slid against hard steel plates of various surface textures to study the response of materials during sliding. The experiments were conducted using an inclined pin-on-plate sliding apparatus under both dry and lubricated conditions in an ambient environment. Two kinds of frictional response, namely steady-state and stick-slip, were observed during sliding. In general, the response was dependent on material pair, normal load, lubrication, and surface texture of the harder material. More specifically, for the case of Al-4Mg alloy, the stick-slip response was absent under both dry and lubricated conditions. For Al, stick-slip was observed only under lubricated conditions. For the case of Mg, the stick-slip response was seen under both dry and lubricated conditions. Further, it was observed that the amplitude of stick-slip motion primarily depends on the plowing component of friction. The plowing component of friction was the highest for the surfaces that promoted plane strain conditions and was the lowest for the surfaces that promoted plane stress conditions near the surface.

The role of surface texture on friction and transfer layer formation during repeated sliding of Al-4Mg against steel

In the present investigation, various kinds of textures, namely, unidirectional, 8-ground, and random were attained on the die surfaces. Roughness of the textures was varied using different grits of emery papers or polishing powders. Then pins made of Al-4Mg alloys were slid against steel plates at various numbers of cycles, namely, 1, 3, 5, 10 and 20 using pin-on-plate reciprocating sliding tester. Tests were conducted at a sliding velocity of 2 minis in ambient conditions under both dry and lubricated conditions. A constant normal load of 35 N was applied in the tests. The morphologies of the worn surfaces of the pins and the formation of transfer layer on the counter surfaces were observed using a scanning electron microscope. Surface roughness parameters of the plates were measured using an optical profilometer. In the experiments, it was observed that the coefficient of friction and formation of the transfer layer depend on the die surface textures under both dry and lubricated conditions. More specifically, the coefficient of friction decreases for unidirectional and 8-ground surfaces while for random surfaces it increases with number of cycles. However, the coefficient of friction is highest for the sliding perpendicular to the unidirectional textures and least for the random textures under both dry and lubricated conditions. The difference in friction values between these two surfaces decreases with increasing number of cycles. The variation in the coefficient of friction under both dry and lubrication conditions is attributed to the change in texture of the surfaces during sliding. (C) 2011 Elsevier B.V. All rights reserved.

Tribological response of soft materials sliding against hard surface textures at various numbers of cycles

In the present investigation, various kinds of textures were attained on the steel surfaces. Roughness of the textures was varied using different grits of emery papers or polishing powders. Pins made of pure Al, Al-4Mg alloy and pure Mg were then slid against prepared steel plate surfaces at various numbers of cycles using an inclined pin-on-plate sliding tester. Tests were conducted at a sliding velocity of 2mms(-1) in ambient conditions under both dry and lubricated conditions. Normal loads were increased up to 110N during the tests. The morphologies of the worn surfaces of the pins and the formation of transfer layer on the counter surfaces were observed using a scanning electron microscope. Surface roughness parameters of the plate were measured using an optical profilometer. In the experiments, it was observed that the coefficient of friction and formation of a transfer layer (under dry and lubricated conditions) only depended on surface texture during the first few sliding cycles. The steady-state variation in the coefficient of friction under both dry and lubrication conditions was attributed to the self-organisation of texture of the surfaces at the interface during sliding. Copyright (C) 2012 John Wiley & Sons, Ltd.

Factors influencing stick-slip motion: effect of hardness, crystal structure and surface texture

In the present investigation, efforts were made to study the different frictional responses of materials with varying crystal structure and hardness during sliding against a relatively harder material of different surface textures and roughness. In the experiments, pins were made of pure metals and alloys with significantly different hardness values. Pure metals were selected based on different class of crystal structures, such as face centered cubic (FCC), body centered cubic (BCC), body centered tetragonal (BCT) and hexagonal close packed (HCP) structures. The surface textures with varying roughness were generated on the counterpart plate which was made of H-11 die steel. The experiments were conducted under dry and lubricated conditions using an inclined pin-on-plate sliding tester for various normal loads at ambient environment. In the experiments, it was found that the coefficient of friction is controlled by the surface texture of the harder mating surfaces. Further, two kinds of frictional response, namely steady-state and stick-slip, were observed during sliding. More specifically, stead-state frictional response was observed for the FCC metals, alloys and materials with higher hardness. Stick-slip frictional response was observed for the metals which have limited number of slip systems such as BCT and HCP. In addition, the stick-slip frictional response was dependent on the normal load, lubrication, hardness and surface texture of the counterpart material. However, for a given kind of surface texture, the roughness of the surface affects neither the average coefficient of friction nor the amplitude of stick-slip oscillation significantly.

SELF-ORGANIZATION AND FRICTION DURING SLIDING

In self-organized sliding processes, the surfaces align to each other during sliding. This alignment leads to a more ordered contact state and significantly influences the frictional behavior. To understand the self-organization sliding processes, experiments were conducted on a pin-on-plate reciprocating sliding tester for various numbers of cycles. In the experiments, soft magnesium pins were slid against hard steel plates of various surface textures (undirectional, 8-ground, and random). Experimental results showed that the transfer layer formation on the steel plates increased with increasing number of cycles for all surfaces textures under both dry and lubricated conditions. The friction also increased with the number of cycles under dry conditions for all of the textures studied. During lubricated conditions, the friction decreased for unidirectional and 8-ground surfaces and increased for random surfaces with the number of cycles. Furthermore, the friction and transfer layer formation depend on the surface textures under both dry and lubricated conditions during the first few sliding cycles. Later on, it is less dependent of surface textures. The variation in the coefficient of friction under both dry and lubrication conditions were attributed to the self-organization process that occurred during repeated sliding.