Phase transitions and rare-earth magnetism in hexagonal and orthorhombic $DyMnO_{3}$ single crystals

The floating-zone method with different growth ambiences has been used to selectively obtain hexagonal or orthorhombic DyMnO3 single crystals. The crystals were characterized by x-ray powder diffraction of ground specimens and a structure refinement as well as electron diffraction. We report magnetic susceptibility, magnetization and specific heat studies of this multiferroic compound in both the hexagonal and the orthorhombic structure. The hexagonal DyMnO3 shows magnetic ordering of Mn3+ (S = 2) spins on a triangular Mn lattice at T-N(Mn) = 57 K characterized by a cusp in the specific heat. This transition is not apparent in the magnetic susceptibility due to the frustration on the Mn triangular lattice and the dominating paramagnetic susceptibility of the Dy3+ (S = 9/2) spins. At T-N(Dy) = 3 K, a partial antiferromagnetic order of Dy moments has been observed. In comparison, the magnetic data for orthorhombic DyMnO3 display three transitions. The data broadly agree with results from earlier neutron diffraction experiments, which allows for the following assignment: a transition from an incommensurate antiferromagnetic ordering of Mn3+ spins at T-N(Mn) = 39 K, a lock-in transition at Tlock-in = 16 K and a second antiferromagnetic transition at T-N(Dy) = 5 K due to the ordering of Dy moments. Both the hexagonal and the orthorhombic crystals show magnetic anisotropy and complex magnetic properties due to 4f-4f and 4f-3d couplings.

Phase Equilibria in the System $Al_{2}O_{3}-CaO-CoO$ and Gibbs Energy of Formation of $Ca_{3}CoAl_{4}O_{10}$

The floating-zone method with different growth ambiences has been used to selectively obtain hexagonal or orthorhombic DyMnO3 single crystals. The crystals were characterized by x-ray powder diffraction of ground specimens and a structure refinement as well as electron diffraction. We report magnetic susceptibility, magnetization and specific heat studies of this multiferroic compound in both the hexagonal and the orthorhombic structure. The hexagonal DyMnO3 shows magnetic ordering of Mn3+ (S = 2) spins on a triangular Mn lattice at T-N(Mn) = 57 K characterized by a cusp in the specific heat. This transition is not apparent in the magnetic susceptibility due to the frustration on the Mn triangular lattice and the dominating paramagnetic susceptibility of the Dy3+ (S = 9/2) spins. At T-N(Dy) = 3 K, a partial antiferromagnetic order of Dy moments has been observed. In comparison, the magnetic data for orthorhombic DyMnO3 display three transitions. The data broadly agree with results from earlier neutron diffraction experiments, which allows for the following assignment: a transition from an incommensurate antiferromagnetic ordering of Mn3+ spins at T-N(Mn) = 39 K, a lock-in transition at Tlock-in = 16 K and a second antiferromagnetic transition at T-N(Dy) = 5 K due to the ordering of Dy moments. Both the hexagonal and the orthorhombic crystals show magnetic anisotropy and complex magnetic properties due to 4f-4f and 4f-3d couplings.

Numerical prediction of load-displacement behaviors of adhesively bonded joints at different extension rates and temperatures

The present work focuses on simulation of nonlinear mechanical behaviors of adhesively bonded DLS (double lap shear) joints for variable extension rates and temperatures using the implicit ABAQUS solver. Load-displacement curves of DLS joints at nine combinations of extension rates and environmental temperatures are initially obtained by conducting tensile tests in a UTM. The joint specimens are made from dual phase (DP) steel coupons bonded with a rubber-toughened adhesive. It is shown that the shell-solid model of a DLS joint, in which substrates are modeled with shell elements and adhesive with solid elements, can effectively predict the mechanical behavior of the joint. Exponent Drucker-Prager or Von Mises yield criterion together with nonlinear isotropic hardening is used for the simulation of DLS joint tests. It has been found that at a low temperature (-20 degrees C), both Von Mises and exponent Drucker-Prager criteria give close prediction of experimental load-extension curves. However. at a high temperature (82 degrees C), Von Mises condition tends to yield a perceptibly softer joint behavior, while the corresponding response obtained using exponent Drucker-Prager criterion is much closer to the experimental load-displacement curve.

Dynamic initiation toughness measu~ment using double Grooved discs

Among the multitude of test specimen geometries used for dynamic fiacture toughness evaluation, the most widely uscd specimen is lhc Chavpy specimen due its simple geomclry and availability of testing machines. The standard Chatpy specimen dimensions may llOl always give plane st~ain condilions and hence, it may be necessary Io coilduct lcs/s using specimens of dillEvcnt thicknesses to establish the plane strain K~a. An axisymmct/ic specimen, on the otlaev hand would always give flow constraints l~n a nominal specimen thickness i~rcspcctive of the test matctial. The notched disk specimen pVOl)oscd by Bcrn:ud ctal. [1] for static and dynamic initiation toughness measurement although p~ovicles plain-strain conditions, the crack plopagatcs at an angle to the direction of applied load. This makes inteq~retation of the test results difficult us it ~Ccluivcs ~actial slices to be cut fiom the fractured specimen to ascertain the angle o1 crack growth and a linite element model l~)r tl);t{ pa~ticulat ctack o~icntalion.

Influence of Elastic-Constants on Mode-I Stress-Intensity Factors in 3-Dimensional Crack Problems

Plates with V-through edge notches subjected to pure bending and specimens with rectangular edge-through-notches subjected to combined bending and axial pull were investigated (under live-load and stress-frozen conditions) in a completely nondestructive manner using scattered-light photoelasticity. Stress-intensity factors (SIFs) were evaluated by analysing the singular stress distributions near crack-tips. Improved methods are suggested for the evaluation of SIFs. The thickness-wise variation of SIFs is also obtained in the investigation. The results obtained are compared with the available theoretical solutions.

Photoelastic parametric studies of mode I stress intensity factors

Results of photoelastic investigations on single edge-notch tension specimens of varying notch angle and crack length are reported. The experimental results of Mode I stress intensity factors are compared with analytical results.

Cavitation erosion characteristics of poly(methyl methacrylate) in a rotating disk device

Experimental results pertaining to the initiation, dynamics and mechanism of cavitation erosion on poly(methyl methacrylate) specimens tested in a rotating disk device are described in detail. Erosion normally starts at the location nearest to the center of rotation (CR). As the exposure time to cavitation increases, additional erosion areas or sites appear away from the CR and secondary erosion (induced by eroded pits) spreads upstream and merges with the main pit. The microcracks increase in density towards the end of the incubation period and transform into macrocracks in most cases. A study of light optical photographs and scanning electron micrographs of the eroded area shows that material particles are removed from the network of cracks because of crack joining and pits indicate particle debris. Optical degradation (loss of transmittance) is observed to be greater on the back of the specimen than on the front.

On the wear of aluminium-corundum composites

The effect of corundum particle content on the wear of aluminium was studied. Composites of different corundum contents were tested for their wear characteristics. Hardness and density measurements were made on specimens before and after test. Specimens were examined by scanning electron microscopy in the as-compacted, sintered and worn states. The wear decreased as the oxide content increased, showing an optimum value at a composition range of 25 wt.%–35 wt.% of corundum. The mechanism of reinforcement and its effect on the operative wear mode are discussed.

Constraint effects on multiple void interaction in pressure sensitive plastic solids

In this work, effects of pressure sensitive yielding and plastic dilatancy on void growth and void interaction mechanisms in fracture specimens displaying high and low constraint levels are investigated. To this end, large deformation finite element simulations are carried out with discrete voids ahead of the notch. It is observed that multiple void interaction mechanism which is favored by high initial porosity is further accelerated by pressure sensitive yielding, but is retarded by loss of constraint. The resistance curves predicted based on a simple void coalescence criterion show enhancement in fracture resistance when constraint level is low and when pressure sensitivity is suppressed.

Re-use of fluoride contaminated bone char sludge in concrete

Managing sludge generated by treating groundwater contaminated with geogenic contaminants (fluoride, arsenic, and iron) is a major issue in developing nations. Their re-use in civil engineering applications is a possible pathway for reducing the impact on the geo-environment. This paper examines the re-use of one such sludge material, namely, fluoride contaminated bone char sludge, as partial replacement for fine aggregate (river-sand) in the manufacture of dense concrete specimens. Bone char sludge is being produced by defluoridation of contaminated groundwater in Nalagonda District, Andhra Pradesh, India. The impact of admixing 1.5-9% sludge contents on the compression strength and fluoride leaching potential of the sludge admixed concrete (SAC) specimens are examined. The compression strengths of the SAC specimensa re examined with respect to strength criteria for manufacture of dense, load-bearing concrete blocks. The fluoride release potential of the SAC specimens is examined with respect to standards specific to disposal of treated leachate into inland surface water.

Texture strengthening in warm-rolled cadmium-1% silver alloy

The variation in the tensile properties at 77 K and 300 K in warm-rolled (300 K) Cd-1% Ag alloy with deformation has been studied in longitudinal as well as transverse specimens. The low-temperature yield strength increases with warm rolling without much loss in ductility. The strength at 300 K, however, decreases with heavy warm deformation. From microstructural studies and X-ray investigations, it was observed that changes in grain size and texture occur during warm rolling. Both these changes are found to be important in deciding the tensile properties. The longitudinal and transverse strengths at 77 K vary linearly with l-frac12, where l is the average grain diameter, and thus they obey the Hall-Petch relation. The Hall-Petch slope, k, is lower in specimens with favourable lcub1013rcub texture while the intercept σo is higher when the lcub0002rcub texture is less favourable.

Deformation processing of an aluminum alloy containing particles: Studies on AI-5 pct Si alloy 4043

Al-5 wt pct Si alloy is processed by upset forging in the temperature range 300 K to 800 K and in the strain rate range 0.02 to 200 s−1. The hardness and tensile properties of the product have been studied. A “safe” window in the strain rate-temperature field has been identified for processing of this alloy to obtain maximum tensile ductility in the product. For the above strain rate range, the temperature range of processing is 550 K to 700 K for obtaining high ductility in the product. On the basis of microstructure and the ductility of the product, the temperature-strain rate regimes of damage due to cavity formation at particles and wedge cracking have been isolated for this alloy. The tensile fracture features recorded on the product specimens are in conformity with the above damage mechanisms. A high temperature treatment above ≈600 K followed by fairly fast cooling gives solid solution strengthening in the alloy at room temperature.

On the wear of aluminium-corundum composites

The effect of corundum particle content on the wear of aluminium was studied. Composites of different corundum contents were tested for their wear characteristics. Hardness and density measurements were made on specimens before and after test. Specimens were examined by scanning electron microscopy in the as-compacted, sintered and worn states. The wear decreased as the oxide content increased, showing an optimum value at a composition range of 25 wt.%–35 wt.% of corundum. The mechanism of reinforcement and its effect on the operative wear mode are discussed.

Toughness of as-cast and partially crystallized composites of a bulk metallic glass

The deformation and fracture response of a bulk metallic glass (BMG) post-annealing above the glass transition temperature is examined. The toughness of the glass-matrix composite exhibits a sharp transition beyond a critical volume fraction of crystallization to values as low as that of brittle silicate glass. Instrumented indentation tests supplemented by impact tests were used to study this ductile to brittle transition exhibited by the partially crystallized samples. Indentation on the anneal-embrittled specimens shows lateral cracks in addition to cracks along the corners. The applicability of the Poisson's ratio-toughness correlation with respect to partially crystallized samples is also investigated.

Determination of mode 1 notch stress intensity factor by the photoelastic technique

The structural integrity of any member subjected to a load gets impaired due to the presence of cracks or crack-like defects. The notch severity is one of the several parameters that promotes the brittle fracture. The most severe one is an ideal crack with infinitesimal width and infinitesimal or zero root radius. Though analytical investigations can handle an ideal crack, experimental work, either to validate the analytical conclusions or to impose the bounds, needs to be carried out on models or specimens containing the cracks which are far from the ideal ones. Thus instead of an ideal crack with infinitesimal width the actual model will have a slot or a slit of finite width and instead of a crack ending in zero root radius, the model contains a slot having a finite root radius. Another factor of great significance at the root is the notch angle along which the transition from the slot to the root takes place. This paper is concerned with the photoelastic determination of the notch stress intensity factor in the case of a “crack” subjected to Mode 1 deformation.