Solubility and activity of oxygen in liquid antimony

The solubility limit of oxygen in liquid antimony has been measured by a novel isopiestic technique in the temperature range 995--1175 deg K. The results can be expressed by the equation log c = --5500/T + 3.754 ( plus/minus 0.04) with c in at.% O and T in deg K. The oxygen potential over Sb + O alloys equilibrium with Sb2O3 has been measured by a solid state cell using a fully stabilized CaO.ZrO2 electrolyte. The cell was designed to contain the Sb + Sb2O3 mixture in a closed volume, that the vaporization of the oxide can be minimized and true equilibrium attained. The Gibbs free energy of the reaction 2 Sb(s) + 3/2 O2 = Sb2O3(s) is Delta G deg = --719560 + 274.51 T( plus/minus 500) and Sb(l) + 3/2 O2 = Sb2O3(l), Delta G deg = --704711 + ( plus/minus 500) ( Delta G deg in J/mole, T in deg K). The combination of these results with Sieverts' law yields the standard free energy of solution of oxygen in liquid antimony according to the reaction 1/2 O2 = \O\Sb,at.% as Delta G deg = --129620 + 14.23 T ( plus/minus 950). The standard enthalopy and entropy of the solution of oxygen in Sb are compared with values for other metal- oyxgen systems, and with the standard enthalpies of formation of corresponding oxides. The resulting correlations permit the estimation of the standard free energy of solution of oxygen in pure metals for which experimental information is lacking. 24 ref.--AA

A comparison of the structure of liquid alloys derived from thermodynamic and diffraction studies

A significant amount of research on the thermodynamic properties of molten alloys is undertaken for obtaining insights into their structure . The partial and integral molar enthalpies, entropies and volumes of mixing provide some general information on the nature and strength of atomic bonds and the distribution of atoms. However, until recently it has been difficult to derive specific quantitative information because the excess entropy of mixing contains configurational , vibrational , electronic , and sometimes magnetic contributions which cannot be easily separated.

A derivation of thermodynamic quantities of liquid alloys from their structure factors

A method of deriving the thermodynamic properties of mixing in liquid alloys Delta G, Delta S and Delta H, from low-Q scattering data has been presented. As an example, the method has been demonstrated with liquid Na-Ga alloys for which both thermodynamic and diffraction data have recently been obtained by the authors.

Computation of thermodynamic properties of liquid ferrous alloys from structural measurements

Relation between X-ray scattering intensities, mean square thermal fluctuations and thermodynamic properties. High temperature X-ray diffraction study of liquid Fe-Ni and Fe-Si alloys using reflection and transmission geometries. Calculation of the structure factor as a function of wave vector. Extrapolation to zero wave vector. Calculation of the concentration-concentration correlation function defined by A. B. Bhatia and D. E. Thorton. Computation of thermodynamic quantities of mixing A G, LlH and LlS for the binary alloys. Comparison with direct thermodynamic measurements reported in the literature.

Mass spectrometric and electrochemical studies of thermodynamic properties of liquid and solid phases in the CaO Al2O3 system

The activities of CaO and Al2O3 in lime-alumina melts were studied by Knudsen cell-mass spectrometry at 2060 K. Emf of solid state cells, with CaF2 as the electrolyte, was measured from 923 to 1223 K to obtain the free energies of formation of the interoxide compounds. The results are critically evaluated in the light of data reported in the literature on phase equilibria, activities in melts, and stabilities of compounds. A coherent set of data is presented, including the previously unknown free energy of formation of CaO.6Al2O3 and the temperature dependence of activities in the liquid phase.

Solubility and activity of oxygen in liquid manganese

The oxygen concentration of liquid manganese in equilibrium with MnAl2+2xO4+3x and α−Al2O3 has been determined in the temperature range 1520 to 1875 K. The oxygen content of quenched samples, wrapped in oxygen-free nickel foil, was determined by an inert gas fusion technique. The results are combined with accurate data now available on the Gibbs energies of formation of MnO and Al2O3−saturated MnAl2+2xO4+3x to derive the oxygen content of liquid manganese in equilibrium with MnO and the Gibbs energy of solution of diatomic oxygen gas in liquid manganese. The enthalpy and entropy of solution of oxygen in manganese are compared with similar data on other metal-oxygen systems.

Current views on microscopic thermodynamics of liquid alloys

An attempt has been made to review current information on the microscopic thermodynamics of liquid alloys. For complex alloys, and for alloys of simple metals with strong "compound-forming" tendencies, the fluctuation approach developed by Bhatia and his co-workers provides a useful link between the fluctuation in concentration and number density of atoms in the mixture on the one hand, and macroscopic thermodynamic properties on the other. Some selected examples of the application of structural data of liquid alloys to estimating macroscopic thermodynamic properties such as the Gibbs free energy of mixing, coupled with the fluctuation approach are given. The relevant thermodynamic quantities such as vapor pressure and entropy are also discussed, to facilitate the understanding of the present status of the fundamental and powerful links between macroscopic and microscopic (atomic scale) structure of liquid alloys (Mg--Sn, Li--Pb, Hg--K). 63 ref.--AA

Oxygen content of liquid cobalt in equilibrium with CoO.(1+x)Al2O3 and -Al2O3

The oxygen concentration of liquid cobalt in equilibrium with cobalt aluminate and a-alumina has been measured by suction sampling and crucible quenching techniques at temperatures between 1770 and 1975 K. Experiments were made with cobalt of high and low initial oxygen contents, and with and without the addition of cobalt aluminate. The effect of temperature on the equilibrium oxygen content is represented by the equation, log (at.% 0) = -10,4001T(K) + 4.64 (±0.008). The composition of the spinel phase, CoO.(1+x)AI20 3, saturated with alumina, has been determined by electron probe microanalysis. The values of x are 0.22 at 1770 Kand 0.28 at 1975 K. The oxygen potential corresponding to the three-phase equilibrium between cobalt, aluminate and alumina, and the standard Gibbs' energy of formation of nonstoichiometric cobalt aluminate are evaluated by combining the results of this study with recently published data on the activity of oxygen in liquid cobalt. Implications of the present results to aluminium deoxidation of liquid cobalt are discussed.

Solubility and activity of oxygen in liquid nickel in equilibrium with -Al2O3 and NiO.(1+x)Al2O3

The limiting solubility of oxygen in liquid nickel in equilibrium withα-alumina and nickel aluminate has been measured by inert gas fusion analysis of suction samples in the temperature range 1730 to 1975 K. The corresponding oxygen potential has been monitored by a solid electrolyte cell consisting of calcia stabilized zirconia as the electrolyte and Mo + MoO2 as the reference electrode. The results can be summarized by the following equations: log(at. pct O) = \frac - 10,005T + 4.944 ( ±0.015)log(atpctO)=T−10005+4944(0015) % MathType!MTEF!2!1!+-% feaafiart1ev1aaatCvAUfeBSjuyZL2yd9gzLbvyNv2CaerbuLwBLn DmO2 /4.606RT = log P O2 1/2 = \frac - 13,550T + 4.411 ( ±0.009)O24606RT=logPO212=T−13550+4411(0009) From simultaneous measurements of the potential and concentration of oxygen in melts, not in thermodynamic equilibrium with alumina and aluminate phases, information on the composition dependence of the activity coefficient and the standard free energy of solution of oxygen is obtained. For the reaction, $\frac{1}{2} O_2 \to \underset{\raise0.3em\hbox{$Missing close brace ΔG o = -72,930 - 7.11T (±840) J gr.at.–1 = + 0.216 at. pct OlogfO=T−500+0216atpctO where the standard state for dissolved oxygen is that which makes the value of activity equal to the concentration (in at. pct) in the limit as concentration approaches zero. The oxygen solubility in liquid nickel in equilibrium with solid NiO, evaluated from thermodynamic data, is compared with information reported in the literature. Implications of the results to the deoxidation equilibria of aluminum in nickel are discussed.

A thermodynamic study of liquid Cu-Cr alloys and metastable liquid immiscibility

he thermodynamic acitivity of chromium in liquid Cu-Cr alloys is measured in the temperature range from 1473 to 1873 K using the solid state cell: Pt, W, Cr + Cr2O3 |(Y2O3) ThO2|Cu - Cr + Cr2O3, Pt The activity of copper and the Gibbs energy of mixing of the liquid alloy are derived. Activities exhibit large positive deviations from Raoult's law. The mixing properties can be represented by a pseudo-subregular solution model in which the excess entropy has the same type of functional dependence on composition as the enthalpy of mixing: ΔGE = XCr(1 - XCr)[60880 - 18750 XCr)-- T(16.25 - 7.55 XCr)]J mol-1 Pure liquid Cu and Cr are taken as the reference states. The results predict a liquid-liquid metastable miscibility gap, with TC = 1787 (±3) K and XCr = 0.436 (±0.02), lying below the liquidus. The results obtained in this study are in general agreement with experimental information reported in the literature, but provide further refinement of the thermodynamic parameters.

Relation between Local Structure and Glass Forming Ability of Liquid Alloys

An attempt has been made to describe the glass forming ability (GFA) of liquid alloys, using the concepts of the short range order (SRO) and middle range order (MRO) characterizing the liquid structure.A new approach to obtain good GFA of liquid alloys is based on the following four main factors: (1) formation of new SRO and competitive correlation with two or more kinds of SROs for crystallization, (2) stabilization of dense random packing by interaction between different types of SRO, (3) formation of stable cluster (SC) or middle range order (MRO) by harmonious coupling of SROs, and (4) difference between SRO characterizing the liquid structure and the near-neighbor environment in the corresponding equilibrium crystalline phases. The atomic volume mismatch estimated from the cube of the atomic radius was found to be a close relation with the minimum solute concentration for glass formation. This empirical guideline enables us to provide the optimum solute concentration for good GFA in some ternary alloys. Model structures, denoted by Bernal type and the Chemical Order type, were again tested in the novel description for the glass structure as a function of solute concentration. We illustrated the related energetics of the completion between crystal embryo and different types of SRO. Recent systematic measurements also provide that thermal diffusivity of alloys in the liquid state may be a good indicator of their GFA.