Synthesis of Ti, Ga, and V nitrides: Microwave-assisted carbothermal reduction and nitridation

A simple, novel, and fast method of preparation of metal nitride powders (GaN, TiN, and VN) using microwave-assisted carbothermal reduction and nitridation has been demonstrated. The procedure uses the respective oxides and amorphous carbon powder as the starting materials. Ammonia gas is found to be more effective in nitridation than high-purity N-2 gas. Complete nitridation is achieved by the use of a slight excess of amorphous carbon. Metals themselves are not found to be effectively nitrided. The products were characterized using XRD, TEM, and SAED and found to possess good crystallinity and phase purity. The method can be of general applicability for the preparation of metal nitrides.

Magnetic properties of mechanically alloyed nanocrystalline Ni3Fe

Disordered nanocrystalline Ni3Fe alloy was prepared by mechanical alloying of elemental powders. X-ray diffractograms show the formation of Ni3Fe single phase. The chemical composition and morphology of the powder have been obtained by using EDAX and SEM analysis respectively. While the saturation magnetisation decreases with milling time, the coercivity increases. The width of the hyperfine field distributions obtained from Mossbauer studies shows that the alloy is highly disordered Atomic ordering is found to take place at a faster rate compared to that in the bulk alloy. (C) 1999 Acta Metallurgica Inc.

Mechanically activated synthesis of nanocrystalline powders of ferroelectric bismuth vanadate

Mechanical milling of a stoichiometric mixture of Bi2O3 and V2O5 yielded nanosized powders of bismuth vanadate, Bi2VO5.5 (BN). Structural evolution of the desired BiV phase, through an intermediate product (BiVO4), was monitored by subjecting the powders, ball milled for various durations to X-ray powder diffraction (XRD), differential thermal analysis (DTA), and transmission electron microscopic (TEM) studies. XRD studies indicate that the relative amount of the BiV phase present in the ball-milled mixture increases with increase in milling time and its formation reaches completion within 54 h of milling. Assynthesized powders were found to stabilize in the high-temperature tetragonal (gamma) phase. DTA analyses of the powders milled for various durations suggest that the BN phase-formation temperature decreases with increase in milling time. The nanometric size (30 nm) of the crystallites in the final product was confirmed by TEM and XRD studies. TEM studies clearly demonstrate the growth of BiV on Bi2O3 crystallites. (C) 1999 Academic Press.

Nonlinear optical activity of anhydrous and hydrated sodium p-nitrophenolate

Differently hydrated sodium p-nitrophenolate (NPNa) crystals were obtained while growing them from different solvents such as methanol and water. Thermal analysis and powder X-ray diffraction studies were carried out on these crystals. Kurtz powder SHG technique was used for qualitative assessment of their nonlinear optical (NLO) activity. From the detailed single-crystal X-ray diffraction studies it is established that NPNa has three different forms, of which only one is found to possess NLO activity. Additionally, a new NLO active crystal was also found to grow from aqueous solution. (C) 1999 Elsevier Science B.V. All rights reserved.

Preparation and characterization of nanocrystalline powders of bismuth vanadate

The influence of mechanical activation on the formation of Bi2VO5.5 bismuth vanadate (BiV) phase, was investigated by ball-milling a stoichiometric mixture of bismuth oxide and vanadium pentoxide. The structural evolution of the desired BN phase, via an intermediate BiVO4,phase, was investigated using X-ray powder diffraction; (XRD), differential thermal analysis (DTA) and transmission electron microscopy (TEM). Milling for 54h. yielded monophasic gamma-BiV powders with an average crystallite size of 30 nm. The electron paramagnetic resonance (EPR) peaks associated with the V4+ ions are stronger and broader in nanocrystalline (n) BN than in the conventionally prepared microcrystalline (m) BN, suggesting theta significant portion of V5+ has been transformed to V4+ during milling. The optical bandgap of n-BiV was found to be higher than that of m-BiV. High density (97% of the theoretical density), fine-grained (average grain-size of 2 tun) ceramics with uniform grain-size distribution could be fabricated using n-BiV powders. These fine-grained ceramics exhibit improved dielectric, pyre and ferroelectric properties. (C) 1999 Elsevier Science S.A. All rights reserved.

Relaxation behavior of twin nonlinear optical chromophores: Effect of the spacer length

A new series of twin nonlinear optical (NLO) molecules, having two 4-nitrophenol chromophores that are linked via a flexible polymethylene spacer of varying length [(CH2)(n), n = 1-12], were synthesized. Powder second harmonic generation measurements of these twin samples indicated a pronounced odd-even oscillation, with the odd twins exhibiting a high SHG value while the even ones gave no measurable SH signal. This behavior reflects the crystal packing preferences in such twin NLO systems that have odd and even numbers of atoms linking them - the even ones appear to prefer a centrosymmetric packing arrangement. The orientational/disordering dynamics of these twin NLO molecules, doped in a polymer (poly(methyl methacrylate)) matrix, has also been studied using SHG in electric field poled samples. Interestingly, the maximum attainable SH signal, chi((2)), in, the poled samples also showed an odd-even oscillation; the odd ones again having a higher value of chi((2)) This unprecedented odd-even oscillation in such molecularly doped systems is rationalized as being due to the intrinsically greater ease of a parallel alignment of the two chromophores in the twins with an odd spacer than in those with an even one. Further, the temporal stability of the SHG intensity at 70 degrees C, after the removal of the applied corona, was also studied. The relaxation of all the twin chromophores followed a biexponential decay; the characteristic relaxation time (tau(2)) for the slow decay component suggests that while the twin with a single methylene unit relaxes relatively slowly, the relaxation is significantly faster in cases where n = 2 and 3. In the twins with even longer spacer segments, the relaxation again becomes slower and reaches a saturation value. The observed minimum appears to reflect the interplay of two competing factors that affect the chromophore alignment in such twin systems, namely, the electrostatic repulsion between neighboring oriented dipoles and the intrinsic flexibility of the spacer.

Structural, dielectric and optical properties of lithium borate-bismuth tungstate glass-ceramicsc

Glasses in the system (1 - x)Li2B4O7-xBi(2)WO(6) (0.1 less than or equal to x less than or equal to 0.35) were prepared by splat quenching technique. Powder X-ray diffraction (XRD) and differential thermal analysis (DTA) were employed to characterize the as-quenched glasses. High-resolution transmission electron microscopy (HR TEM) revealed the presence of fine, nearly spherical crystallites of Bi2WO6 varying from 1.5 to 20 nm in size, depending on x in the as-quenched glasses. The glasses (corresponding to x = 0.3) heat-treated at 723 K for 6 h gave rise to a clear crystalline phase of Bi2WO6 embedded in the Li2B4O7 glass matrix, as observed by X-ray studies. The dielectric constants of the as-quenched glasses as well as the glass-ceramics decreased with increase in frequency (40Hz-100 kHz) at 300 K, and the value obtained for the glass-ceramic (x = 0.2) is in agreement with the values predicted using Maxwell's model and the logarithmic mixture rule. The dielectric constants for both the as-quenched glass and the glass-ceramic increased with increase in temperature (300 - 873 K) and exhibited anomalies close to the onset of the crystallization temperature of the host glass matrix. The optical transmission properties:of these glass-ceramics were found to be compositional dependant. (C) 2000 Elsevier Science Ltd.

Synthesis and properties of willemite Zn2SiO4, and M2+: Zn2SiO4 (M = Co and Ni)

Fine particles of willemite, alpha -Zn2SiO4, were prepared by both solution combustion and sol-gel methods. Both processes yield single-phase, large-surface area (26- and 78-m(2)/g), sinteractive willemite powders. Thermal evolution of crystalline phases was studied using X-ray powder diffraction patterns. The combustion method favors low-temperature formation of willemite compared to the sol-gel method. The powders, when uniaxially pressed and sintered at 1300 degreesC, achieved 78-80% theoretical density. The microstructures of the sintered body show the presence of equiaxed 0.5- to 4-mum grains. Blue pigments of willemite doped with Co2+ and Ni2+ were also prepared by the combustion process.

EPR and photoluminescence studies of ZnO:Mn nanophosphors prepared by solution combustion route

Nanocrystalline ZnO:Mn (0.1 mol%) phosphors have been successfully prepared by self propagating, gas producing solution combustion method. The powder X-ray diffraction of as-formed ZnO:Mn sample shows, hexagonal wurtzite phase with particle size of similar to 40 nm. For Mn doped ZnO, the lattice parameters and volume of unit cell (a=3.23065 angstrom, c=5.27563 angstrom and V=47.684 (angstrom)(3)) are found to be greater than that of undoped ZnO (a=3.19993 angstrom, c=5.22546 angstrom and V=46.336 (angstrom)(3)). The SEM micrographs reveal that besides the spherical crystals, the powders also contained several voids and pores. The TEM photograph also shows the particles are approximately spherical in nature. The FTIR spectrum shows two peaks at similar to 3428 and 1598 cm(-1) which are attributed to O-H stretching and H-O-H bending vibration. The PL spectra of ZnO:Mn indicate a strong green emission peak at 526 nm and a weak red emission at 636 nm corresponding to T-4(1) -> (6)A(1) transition of Mn2+ ions. The EPR spectrum exhibits fine structure transition which will be split into six hyperfine components due to Mn-55 hyperfine coupling giving rise to all 30 allowed transitions. From EPR spectra the spin-Hamiltonian parameters have been evaluated and discussed. The magnitude of the hyperfine splitting (A) constant indicates that there exists a moderately covalent bonding between the Mn2+ ions and the surrounding ligands. The number of spins participating in resonance (N), its paramagnetic susceptibility (chi) have been evaluated. (C) 2011 Elsevier B.V. All rights reserved.

Calorimetric studies on 2TeO(2)-V2O5 glasses

Glasses of the composition 2TeO(2)-V2O5 were fabricated via the conventional melt-quenching technique. The amorphous and the glassy nature of the as-quenched samples were confirmed by X-ray powder diffraction (XRD) and differential scanning calorimetry (DSC), respectively. The glass transition and crystallization parameters were evaluated under non-isothermal conditions using DSC. X-ray diffraction studies confirmed the presence of partially oriented crystallites in the heat-treated glasses. Kauzmann temperature (lower bound for the kinetically observed glass transition) was deduced from the heating rate dependent glass transition and crystallization temperatures.