Phase Relations in the System Cu-Gd-O and Gibbs Energy of Formation of CuGd204

The phase relations in the system Cu-Gd-O have been determined at 1273 K by X-ray diffrac- tion, optical microscopy, and electron microprobe analysis of samples equilibrated in quartz ampules and in pure oxygen. Only one ternary compound, CuGd2O4, was found to be stable. The Gibbs free energy of formation of this compound has been measured using the solid-state cell Pt, Cu2O + CuGd2O4 + Gd2O3 // (Y2O3) ZrO2 // CuO + Cu2O, Pt in the temperature range of 900 to 1350 K. For the formation of CuGd2O4 from its binary component oxides, CuO (s) + Gd2O3 (s) → CuGd2O4 (s) ΔG° = 8230 - 11.2T (±50) J mol-1 Since the formation is endothermic, CuGd2O4 becomes thermodynamically unstable with respect to CuO and Gd2O3 below 735 K. When the oxygen partial pressure over CuGd2O4 is lowered, it decomposes according to the reaction 4CuGd2O4 (s) → 4Gd2O3 (s) + 2Cu2O (s) + O2 (g) for which the equilibrium oxygen potential is given by Δμo 2 = −227,970 + 143.2T (±500) J mol−1 An oxygen potential diagram for the system Cu-Gd-O at 1273 K is presented.

Phase relations in the systems Cu–O–R2O3(R = Tm, Lu) and Gibbs energies of formation of Cu2R2O5 compounds

The phase relations in the systems Cu–O–R2O3(R = Tm, Lu) have been determined at 1273 K by X-ray diffraction, optical microscopy and electron probe microanalysis of samples equilibrated in evacuated quartz ampules and in pure oxygen. Only ternary compounds of the type Cu2R2O5 were found to be stable. The standard Gibbs energies of formation of the compounds have been measured using solid-state galvanic cells of the type, Pt|Cu2O + Cu2R2O5+ R2O3‖(Y2O3)ZrO2‖CuO + Cu2O‖Pt in the temperature range 950–1325 K. The standard Gibbs energy changes associated with the formation of Cu2R2O5 compounds from their binary component oxides are: 2CuO(s)+ Tm2O3(s)→Cu2Tm2O5(s), ΔG°=(10400 – 14.0 T/K)± 100 J mol–1, 2CuO(s)+ Lu2O3(s)→Cu2Lu2O5(s), ΔG°=(10210 – 14.4 T/K)± 100 J mol–1 Since the formation is endothermic, the compounds become thermodynamically unstable with respect to component oxides at low temperatures, Cu2Tm2O5 below 743 K and Cu2Lu2O5 below 709 K. When the chemical potential of oxygen over the Cu2R2O5 compounds is lowered, they decompose according to the reaction, 2Cu2R2O5(s)→2R2O3(s)+ 2Cu2O(s)+ O2(g) The equilibrium oxygen potential corresponding to this reaction is obtained from the emf. Oxygen potential diagrams for the Cu–O–R2O3 systems at 1273 K are presented.

Processing map for hot working of as cast magnesium

The constitutive flow behaviour in hot working of as cast magnesium has been studied with the help of a processing map developed in the temperature range 300-550°C and strain rate range 0·001-100 s−1. The map, interpreted using the dynamic materials model, revealed that the material undergoes dynamic recrystallisation at 425°C and 0·3 s−1, which are the optimum parameters for hot working. Ai temperatures higher than 450°C and strain rates lower than about 0·1 s−1, wedge cracking occurs in as cast magnesium. The wedge cracking domain has a high efficiency of power dissipation (60%), whereas the dynamic recrystallisation domain has a value of 34%. At temperatures below 450°C and strain rates above 10 s−1, the material exhibits flow instability in the form of mechanical twinning. At higher temperatures and strain rates, instability is manifested by flow localisation.

Processing map for hot working of stainless steel type AISI 316L

Processing and instability maps using a dynamic materials model have been developed for stainless steel type AISI 316L in the temperature range 600-1250-degrees-C and strain rate range 0.001-100 s-1 with a view to optimising its hot workability. Stainless steel type AISI 316L undergoes dynamic recrystallisation, with a peak efficiency of 35% at 1250-degrees-C and 0.05 s-1, which are the optimum parameters for hot working this material. The material undergoes dynamic recovery at 900-degrees-C and 0.001 s-1. The increase in the dynamic recrystallisation and dynamic recovery temperatures in comparison with stainless steel type AISI 304L is attributed to the presence of a backstress caused by the molybdenum additions. These results are in general agreement with those reported elsewhere on stainless steel type 316 deformed in hot extrusion and hot torsion. At temperatures < 850-degrees-C and strain rates > 10 s-1, the material exhibits flow localisation owing to adiabatic shear band formation, whereas at higher temperatures (> 850-degrees-C) and strain rates (> 10 s-1) mechanical twinning and wavy slip bands are observed. (C) 1993 The Institute of Materials.

Processing maps for hot working of Cu-Ni-Zn alloys. Part I - Alpha-nickel silver

The constitutive behaviour of agr — nickel silver in the temperature range 700–950 °C and strain rate range 0.001–100 s–1 was characterized with the help of a processing map generated on the basis of the principles of the ldquodynamic materials modelrdquo of Prasadet al Using the flow stress data, processing maps showing the variation of the efficiency of power dissipation (given by 2m/(m+1) wherem is the strain-rate sensitivity) with temperature and strain rate were obtained, agr-nickel silver exhibits a single domain at temperatures greater than 750 °C and at strain rates lower than 1s–1, with a maximum efficiency of 38% occurring at about 950 °C and at a strain rate of 0.1 s–1. In the domain the material undergoes dynamic recrystallization (DRX). On the basis of a model, it is shown that the DRX is controlled by the rate of interface formation (nucleation) which depends on the diffusion-controlled process of thermal recovery by climb. At high strain rates (10 and 100s–1) the material undergoes microstructural instabilities, the manifestations of which are in the form of adiabatic shear bands and strain markings.

Processing maps for hot working of Cu-Ni-Zn alloys Part II Alpha-Beta nickel silver

The constitutive behaviour of agr-beta nickel silver in the temperature range 600�850 °C and strainrate range 0.001�100s�1 was characterized with the help of a processing map generated on the principles of the dynamic materials model. On the basis of the flow-stress data, processing maps showing the variation of the efficiency of power dissipation (given by [2m/(m+1)], wherem is the strain-rate sensitivity) with temperature and strain rate were obtained, agr-beta nickel silver exhibits a single domain at temperatures greater than 700 °C and at strain rates lower than 1 s�1 with a maximum efficiency of power dissipation of about 42% occurring at about 850 °C and at 0.1 s�1. In the domain, the agr phase undergoes dynamic recrystallization and controls the deformation of the alloy, while the beta phase deforms superplastically. Optimum conditions for the processing of agr-beta nickel silver are 850 °C and 0.1 s�1. The material undergoes unstable flow at strain rates of 10 and 100 s�1 and in the temperature range 600�750 °C, manifestated in the form of adiabatic shear bands.

Proton NMR study of molecular dynamics in ammonium tribromo stannate (NH4SnBr3)

The proton second moment M2 and spin-lattice relaxation time T1 have been measured in ammonium tribromo stannate (NH4SnBr3) in the temperature range 77–300 K, to determine the ammonium dynamics. The continuous wave signal is strong and narrow at 77 and 300 K but has revealed an interesting intensity anomaly between 210 and 125 K. T1 shows a maximum (13 s) around 220 K. No minimum in the T1 vs 1000/T plot was observed down to 77 K. M2 and T1 results are interpreted in terms of NH+4 ion dynamics. The activation energy Ea for NH+4 ion reorientation is estimated to be 1.4 kcal mol−1.

Thermodynamic Study of Mixed Anionic Solid Solutions Using Gradient Solid Electrolytes System K2CO3 - K2SO4

The thermodynamic properties of K2CO3 -KSO, solid solutions with hexagonal structure have been measured using a solid-state cell, incorporating a composite solid electrolyte with step-changes in composition. The cell with the configuration Pt, CO2' + O2' || K2CO3 | K2(CO3)x(SO4)1-x || CO2'' + O2'' + Pt X =1 X=X was investigated in the temperature range of 925 to 1165 K. The composite gradient solid electrolyte consisted of pure K2CO3 at one extremity and the solid solution under study at the other. The Nernstian response of the cell to changes in partial pressures of CO2 and O2 at the electrodes and temperature was demonstrated. The activity of K2CO3 in the solid solution was measured by three techniques. All three methods gave identical results, indicating unit transport number for K+ ions and negligible diffusion potential due to concentration gradients of carbonate and sulfate ions. The activity of K2CO3 exhibits positive deviation from Raoult's law. The excess Gibbs energy of mixing of the solid solution can be represented using a subregular solution model DELTAG(E) = X(1 - X)[5030X + 4715(1 - X)] J mol-1 By combining this information with the phase diagram, mixing properties of the liquid phase were obtained.

(Ba3MTiMO9)-Ti-III-O-V (M-III = Fe, Ga, Y, Lu, M-V = Nb, Ta, Sb) perovskite oxides Synthesis, structure and dielectric properties

We describe the synthesis structures and dielectric properties of new perovskite oxides of the formula (Ba3MTiMO9)-Ti-III-O-V for M-III = Fe Ga Y Lu and M-V = Nb Ta Sb While M-V = Nb and Ta oxides adopt disordered/partially ordered 3C perovskite structures where M-III/Ti/M-V metal-oxygen octahedra are corner connected the M-V = Sb oxides show a distinct preference for the 6H structure where Sb-V/Ti-IV metal-oxygen octahedra share a common face forming (Sb Ti)O-9 dimers that are corner-connected to the (MO6)-O-III octahedra The preference of antimony oxides (Sb-V 4d(10)) for the 6H structure which arises from a special Sb-V-O chemical bonding that tends to avoid linear Sb-O-Sb linkages unlike Nb-V/Ta-V d(0) atoms which prefer similar to 180 degrees Nb/Ta-O-Nb/Ta linkages - is consistent with the crystal chemistry of M-V-O oxides in general The dielectric properties reveal a significant difference among Mill members All the oxides with the 3C structure excepting those with Mill = Fe show a normal low loss dielectric behaviour with epsilon = 20-60 in the temperature range 50-400 degrees C the M-III = Fe members with this structure (M-V = Nb Ta) display a relaxor-like ferroelectric behaviour with large E values at frequencies <= 1 MHz (50-500 degrees C) (C) 2010 Elsevier Masson SAS All rights reserved

Crystal structure and electrical properties of CaNaBi2Nb3O12 ceramics

Monophasic CaNaBi2Nb3O12 powders were synthesized via the conventional solid-state reaction route. Rietveld refinement of the X-ray powder diffraction (XRD) data and selected area electron diffraction (SAED) studies confirmed the phase to be a three-layer Aurivillius oxide associated with an orthorhombic B2cb space group. The dielectric properties of the ceramics have been studied in the 300-800 K temperature range at various frequencies (1 kHz to 1 MHz). A dielectric anomaly was observed at 676 K for all the frequencies corresponding to the ferroelectric to paraelectric phase transition as it was also corroborated by the high temperature X-ray diffraction studies. The incidence of the polarization-electric field (P vs. E) hysteresis loop demonstrated CaNaBi2Nb3O12 to be ferroelectric.

Microstructure evolution and hardness variation during annealing of equal channel angular pressed ultra-fine grained nickel subjected to 12 passes

The microstructure, thermal stability and hardness of ultra-fine grained (UFG) Ni produced by 12 passes of equal channel angular pressing (ECAP) through the route Bc were studied. Comparing the microstructure and hardness of the as-ECAPed samples with the published data on UFG Ni obtained after 8 passes of ECAP through the route Bc reveals a smaller average grain size (230 nm in the present case compared with 270 nm in 8-pass Ni), significantly lower dislocation density (1.08 x 10(14) m(-2) compared with 9 x 10(14) m(-2) in 8-pass Ni) and lower hardness (2 GPa compared with 2.45 GPa for 8-pass Ni). Study of the thermal stability of the 12-pass UFG Ni revealed that recovery is dominant in the temperature range 150-250A degrees C and recrystallisation occurred at temperatures > 250 A degrees C. The UFG microstructure is relatively stable up to about 400 A degrees C. Due to the lower dislocation density and consequently a lower stored energy, the recrystallisation of 12-pass ECAP Ni occurred at a higher temperature (similar to 250 A degrees C) compared with the 8-pass Ni (similar to 200 A degrees C). In the 12-pass Nickel, hardness variation shows that its dependence on grain size is inversely linear rather than the common grain size(-0.5) dependence.

A comparative-study of vapor-compression refrigeration working fluids, in the wake of the montreal protocal

A comparative study has been carried out of R-12, 22, 125, 134a, 152a, 218, 245, 500, 502, 507 and 717 as working fluids in a vapour-compression refrigeration system. Two performance parameters were defined, which are expressed in reduced quantities for a corresponding-states comparison of these refrigerants in the temperature range -20 to 50-degrees-C. One is based on the product of temperature drop to pressure penalty ratio and the available volumetric heat of vaporisation at the evaporator; the other considers the effect of isentropic compression in the ideal gas state. It was shown that R-125, 507 and 218 could be better alternatives to R-12 than R-134a. Among these, R-218 has a lower maximum cycle pressure.

Hybridization of carbon-glass epoxy composites: An approach to achieve low coefficient of thermal expansion at cryogenic temperatures

The paper is based on a study to develop carbon-glass epoxy hybrid composites with desirable thermal properties for applications at cryogenic temperatures. It analyzes the coefficient of thermal expansion of carbon-epoxy and glass-epoxy composite materials and compares it with the properties of carbon-glass epoxy hybrid composites in the temperature range 300 K to 125K. Urethane modified epoxy matrix system is used to make the composite specimens suitable for use even for temperatures as low as 20K. It is noted that the lay-up with 80% of carbon fibers in the total volume fraction of fibers oriented at 30 degrees and 20% of glass fibers oriented at 0 degrees yields near to zero coefficient of thermal expansion as the temperature is lowered from ambient to 125 K. (c) 2010 Elsevier Ltd. All rights reserved.

A simplified kinetic model for oxidative dehydrogenation of ethylbenzene over Pd-NaBr/Al2O3 catalyst

The oxidative dehydrogenation of ethylbenzene is gaining considerable importance in recent years as a promising alternative for styrene production. This vapour phase reaction has been studied over Pd-NaBr/Al2O3 catalyst in the temperature range 623-793 K in a fixed bed reactor. Kinetic analysis of this reaction has been done using a recursion procedure developed in this work from first principles. The advantage of this method is the absence of any restriction on the conversion level as it uses an integrated rate equation. The rate of styrene formation was found to follow a linear relationship with concentration of ethylbenzene and shows a Langmuir type dependence on the concentration of oxygen.

Bi2W1–xCuxO6–x(0.7[less-than-or-eq]x[less-than-or-eq]0.8): a new oxide-ion conductor

Anion-deficient Aurivillius phases of the general formula, Bi2Wi-xCuxO6-2x, possessing orthorhombic/tetragonal Bi2WO6-like structures, have been synthesized by quenching the oxide melts. The tetragonal phase stabilized for the compositions 0.7 less-than-or-equal-to x less-than-or-equal-to 0.8 is a good oxide-ion conductor in the temperature range 500-900 K, the x = 0.7 composition exhibiting the highest conductivity in the series.