Effect of High Pressure on the Electrical Conductivity of TlInX2 (X = Se, Te) Layered Semiconductors

The dc electrical conductivity of TlInX2 (X = Se, Te) single crystals, parallel and perpendicular to the (001) c-axis is studied under high quasi-hydrostatic pressure up to 7.0 GPa, at room temperature. Conductivity measurements parallel to the c-axis are carried out at high pressures and down to liquid nitrogen temperatures. These materials show continuous metallization under pressure. Both compounds have almost the same pressure coefficient of the electrical activation energy parallel to the c-axis, d(ΔE∥)/dP = −2.9 × 10−10 eV/Pa, which results from the narrowing of the band gap under pressure. The results are discussed in the light of the band structure of these compounds.

Electrical properties of cobalt‐zinc ferrites

The electrical properties of Co1−xZnxFe2O4 (x=0–1) spinel ferrites were investigated by impedance spectroscopy. The grain‐boundary resistance was found to increase as a function of composition up to x=0.6, and decreases beyond x=0.6. The variation in the bulk resistance and the activation energy as a function of composition is found to exhibit a similar trend whereas the grain resistance appears to be an independent parameter. The observed results suggest that the bulk properties of solid solution spinel ferrites are primarily controlled by the grain‐boundary phase.

Electrical-Resistivity Studies on GE-SE Glasses at High-Pressures and Low-Temperatures

High pressure electrical resistivity measurements were carried out on GexSe100-x (0 less-than-or-equal-to x less-than-or-equal-to 40) glasses at ambient and low temperatures using the Bridgman anvil system. All the melt quenched glasses show a discontinuous glassy semiconductor to crystalline metal transition at high pressures. The high pressure phases of Ge-Se samples do not correspond to any of the equilibrium phases of the system. Additionally, the variation of transition pressure (P(T)), ambient resistivity (rho0) and the activation energy (DELTAE(t)) with composition, exhibit a change in behaviour at x = 20 and 33. The unusual variations observed in these glasses are discussed in the light of chemical and percolation thresholds occurring in the glassy system.

Electrical switching and short-range order in As-Te glasses

The local structural order in chalcogenide network glasses is known to change markedly at two critical compositions, namely, the percolation and chemical thresholds. In the AsxTe100-x glassy system, both the thresholds coincide at the composition x = 40 (40 at. % of arsenic). It is demonstrated that the electrical switching fields of As-Te glasses exhibit a distinct change at this composition.

Numerical and experimental study of the thermal behaviour of coining and upsetting processes

A numerical simulation technique has been employed to study the thermal behavior of hot-forging type forming processes. Experiments on the coining and upsetting of an aluminum billet were conducted to validate the numerical predictions. Typical forming conditions for both the coining and upsetting processes were then studied in detail. an electrical analogy scheme was used to determine the thermal contact resistance. This scheme can conviniently provide the interface characteristics for typical processing conditions, which normally involve high pressures and temperatures. A single forging cycle was first considered, and then a batch of twenty-five forgings was studied. Each forging cycle includes the billet mounting, ascent, loading, dwelling, unloading, descent, and billet removal stages. The temperature distribution in the first forging to be formed is found to be significantly different from that at the end of the batch. In industry, forging is essentially a batch operation. The influence of forming speed and reduction on thermal characteristics was investigated also. The variations that can occur in the process design by considering differences in temperature characteristics are discussed also.

Evidence for decoupled two-dimensional vortex behavior of YBa2Cu3O7-delta in La0.7Sr0.3MnO3/YBa2Cu3O7-delta/La0.7Sr0.3MnO3 trilayer

We investigate the vortex behavior of YBa2Cu3O7-delta thin films sandwiched between two ferromagnetic layers (La0.7Sr0.3MnO3/YBa2Cu3O7-delta/La0.7Sr0.3MnO3). The magnetization study on La0.7Sr0.3MnO3/YBa2Cu3O7-delta/La0.7Sr0.3MnO3 trilayers conspicuously shows the presence of both ferromagnetic and diamagnetic phases. The magnetotransport study on the trilayers reveals a significant reduction in the activation energy (U) for the vortex motion in YBa2Cu3O7-delta. Besides, the ``U'' exhibits a logarithmic dependence on the applied magnetic field which directly indicates the existence of decoupled two-dimensional (2D) pancake vortices present in the CuO2 layers. The evidence of 2D decoupled vortex behavior in La0.7Sr0.3MnO3/YBa2Cu3O7-delta/La0.7Sr0.3MnO3 is believed to arise from (a) the weakening of superconducting coherence length along the c-axis and (b) enhanced intraplane vortex-vortex interaction due to the presence of ferromagnetic layers. (C) 2010 American Institute of Physics. doi: 10.1063/1.3524545]

V-CE Sensing for IGBT Protection in NPC Three Level Converters-Causes For Spurious Trippings and Their Elimination

Neutral point clamped (NPC), three level converters with insulated gate bipolar transistor devices are very popular in medium voltage, high power applications. DC bus short circuit protection is usually done, using the sensed voltage across collector and emitter (i.e., V-CE sensing), of all the devices in a leg. This feature is accommodated with the conventional gate drive circuits used in the two level converters. The similar gate drive circuit, when adopted for NPC three level converter protection, leads to false V-CE fault signals for inner devices of the leg. The paper explains the detailed circuit behavior and reasons, which result in the occurrence of such false V-CE fault signals. This paper also illustrates that such a phenomenon shows dependence on the power factor of the supplied three-phase load. Finally, experimental results are presented to support the analysis. It is shown that the problem can be avoided by blocking out the V-CE sense fault signals of the inner devices of the leg.

A Feature-Based Solution to Forward Problem in Electrical Capacitance Tomography of Conductive Materials

A new feature-based technique is introduced to solve the nonlinear forward problem (FP) of the electrical capacitance tomography with the target application of monitoring the metal fill profile in the lost foam casting process. The new technique is based on combining a linear solution to the FP and a correction factor (CF). The CF is estimated using an artificial neural network (ANN) trained using key features extracted from the metal distribution. The CF adjusts the linear solution of the FP to account for the nonlinear effects caused by the shielding effects of the metal. This approach shows promising results and avoids the curse of dimensionality through the use of features and not the actual metal distribution to train the ANN. The ANN is trained using nine features extracted from the metal distributions as input. The expected sensors readings are generated using ANSYS software. The performance of the ANN for the training and testing data was satisfactory, with an average root-mean-square error equal to 2.2%.

Multilayer Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 thin films for tunable microwave applications

Bi1.5Zn1.0Nb1.5O7/Ba0.6Sr0.4TiO3/Bi1.5Zn1.0Nb1.5O7 tunable multilayer thin film has been fabricated by pulsed laser ablation and characterized. Phase composition and microstructure of multilayer films were characterized by X-ray diffraction, scanning electron microscopy (SEM) and atomic force microscopy (AFM). The film has very smooth surface with RMS roughness of 1.5-2nm and grain size of 100-150 nm. Total film thickness has been measure to be 375 nm. The BZN thin films at 300 K, on Pt(1 1 1)/SiO2/Si substrate showed zero-field dielectric constant of 105 and dielectric loss tangent of 0.002 at frequency of 0.1 MHz. Thin films annealed at 700 degrees C shows the dielectric tunability of 18% with biasing field 500 kV/cm at 0.1 MHz. The multilayer thin film shows nonferroelectric behavior at room temperature. The good physical and electrical properties of multilayer thin films make them promising candidate for tunable microwave device applications. (C) 2010 Elsevier B.V. All rights reserved.

Resistivity imaging of a reconfigurable phantom with circular inhomogeneities in 2D-electrical impedance tomography

Resistivity imaging of a reconfigurable phantom with circular inhomogeneities is studied with a simple instrumentation and data acquisition system for Electrical Impedance Tomography. The reconfigurable phantom is developed with stainless steel electrodes and a sinusoidal current of constant amplitude is injected to the phantom boundary using opposite current injection protocol. Nylon and polypropylene cylinders with different cross sectional areas are kept inside the phantom and the boundary potential data are collected. The instrumentation and the data acquisition system with a DIP switch-based multiplexer board are used to inject a constant current of desired amplitude and frequency. Voltage data for the first eight current patterns (128 voltage data) are found to be sufficient to reconstruct the inhomogeneities and hence the acquisition time is reduced. Resistivity images are reconstructed from the boundary data for different inhomogeneity positions using EIDORS-2D. The results show that the shape and resistivity of the inhomogeneity as well as the background resistivity are successfully reconstructed from the potential data for single or double inhomogeneity phantoms. The resistivity images obtained from the single and double inhomogeneity phantom clearly indicate the inhomogeneity as the high resistive material. Contrast to noise ratio (CNR) and contrast recovery (CR) of the reconstructed images are found high for the inhomogeneities near all the electrodes arbitrarily chosen for the entire study. (C) 2010 Elsevier Ltd. All rights reserved.

Spectroscopic and electrical properties of SiO2 films prepared by simple and cost effective sol-gel process

Amorphous SiO2 thin films were prepared on glass and silicon substrates by cost effective sol-gel method. Tetra ethyl ortho silicate (TEOS) was used as the precursor material, ethanol as solvent and concentrated HCl as a catalyst. The films were characterized at different annealing temperatures. The optical transmittance was slightly increased with increase of annealing temperature. The refractive index was found to be 1.484 at 550 nm. The formation of SiO2 film was analyzed from FT-IR spectra. The MOS capacitors were designed using silicon (1 0 0) substrates. The current-voltage (I-V), capacitance-voltage (C-V) and dissipation-voltage (D-V) measurements were taken for all the annealed films deposited on Si (1 0 0). The variation of current density, resistivity and dielectric constant of SiO2 films with different annealing temperatures was investigated and discussed for its usage in applications like MOS capacitor. The results revealed the decrease of dielectric constant and increase of resistivity of SiO2 films with increasing annealing temperature. (C) 2010 Elsevier B.V. All rights reserved.

Crystal structure and electrical properties of CaNaBi2Nb3O12 ceramics

Monophasic CaNaBi2Nb3O12 powders were synthesized via the conventional solid-state reaction route. Rietveld refinement of the X-ray powder diffraction (XRD) data and selected area electron diffraction (SAED) studies confirmed the phase to be a three-layer Aurivillius oxide associated with an orthorhombic B2cb space group. The dielectric properties of the ceramics have been studied in the 300-800 K temperature range at various frequencies (1 kHz to 1 MHz). A dielectric anomaly was observed at 676 K for all the frequencies corresponding to the ferroelectric to paraelectric phase transition as it was also corroborated by the high temperature X-ray diffraction studies. The incidence of the polarization-electric field (P vs. E) hysteresis loop demonstrated CaNaBi2Nb3O12 to be ferroelectric.

Electrical Relaxation and Transport in 0.5Cs(2)O-0.5Li(2)O-3B(2)O(3) Glasses

The frequency and temperature dependence of the dielectric constant and the electrical conductivity of the transparent glasses in the composition 0.5Cs(2)O-0.5Li(2)O-3B(2)O(3) (CLBO) were investigated in the 100 Hz - 10 MHz frequency range. The dielectric constant for the as-quenched glass increased with increasing temperature, exhibiting anomalies in the vicinity of the glass transition and crystallization temperatures. The temperature coefficient of dielectric constant was estimated (35 +/- 2 ppm. K-1) using Havinga's formula. The dielectric loss at 313 K is 0.005 +/- 0.0005 at all the frequencies understudy. The activation energy associated with the electrical relaxation determined from the electric modulus spectra was found to be 1.73 +/- 0.05 eV, close to that of the activation energy obtained for DC conductivity (1.6 +/- 0.06 eV). The frequency dependent electrical conductivity was analyzed using Jonscher's power law. The combination of these dielectric characteristics suggests that these are good candidates for electrical energy storage device applications.

Behavior of Ca(OH)2/CaO pellet under dehydration and hydration

With construction of a thermochemical energy conversion prototype system to store solar heat, thermal dissociation of pellets of Ca(OH)2 and hydration of CaO have been investigated in some detail for its application to the system. The inorganic substance is very attractive as a material for long term heat storage, but molar density changes associated with the reaction are fairly large. Therefore, this factor has been taken into account in the kinetic equation. The importance of additives and pellet size has been discussed considering reactivity and strength of pellets. An analysis has been attempted when chemical reaction is important. The deformation of pellets was observed during hydration.