Quasicrystalline Coatings Through Laser Processing: A Study on Process Optimisation and Microstructure Evolution

Composite coatings containing quasicrystalline (QC) phases in Al-Cu-Fe alloys were prepared by laser cladding using a mixture of the elemental powders. Two substrates, namely pure aluminum and an Al-Si alloy were used. The clad layers were remelted at different scanning velocities to alter the growth conditions of different phases. The process parameters were optimized to produce quasicrystalline phases. The evolution of the microstructure in the coating layer was characterized by detailed microstructural investigation. The results indicate presence of quasicrystals in the aluminum substrate. However, only approximant phase could be observed in the substrate of Al-Si alloys. It is shown that there is a significant transport of Si atoms from the substrate to the clad layer during the cladding and remelting process. The hardness profiles of coatings on aluminum substrate indicate a very high hardness. The coating on Al-Si alloy, on the other hand, is ductile and soft. The fracture toughness of the hard coating on aluminum was obtained by nano-indentation technique. The K1C value was found to be 1.33 MPa m1/2 which is typical of brittle materials.

Nanocrystallisation and Nanoquasicrystallisation in (Ti/Hf)-Zr-(Ni/Cu) Ternary Alloys

The applicability of the confusion principle and size factor in glass formation has been explored by following different combinations of isoelectronic Ti, Zr and Hf metals. Four alloys of nominal composition Zr41.5Ti41.5Ni17, Zr41.5Hf41.5Ni17, Zr25Ti25Cu50 and Zr34Ti16Cu50 have been rapidly solidified to obtain an amorphous phase and their crystallisation behaviour has been studied. The Ti-Zr-Ni alloy crystallises in three steps. Initially this alloy precipitates icosahedral quasicrystalline phase, which on further heat treatment precipitates cF96 Zr2Ni phase. The Zr-Hf-Ni alloy can not be amorphised under the same experimental conditions. The amorphous Zr-Ti-Cu alloys at the initial stages of crystallisation phase-separateinto two amorphous phases and then on further heat treatment cF24 Cu5Zr and oC68 Cu10Zr7 phase are precipitated. The lower glass-forming abilityof Zr-Hf-Ni alloy and the crystallisation behaviour of the above alloys has been studied. The rationale behind nanoquasicrystallisation and the formation of other intermetallic phases has been explained.

Texture evolution in an Al-Cu alloy during equal channel angular pressing: the effect of starting microstructure

In this article, the effect of initial microstructure on the texture evolution in 2014 Al alloy during equal channel angular pressing (ECAP) through route A has been reported. Three heat treatment conditions were chosen to generate the initial microstructures, namely (i) the recrystallization anneal (as-received), (ii) solution treatment at 768 K for 1 h, and (iii) solution treatment (768 K for 1 h) plus aging at 468 K for 5 h. Texture analyses were performed using orientation distribution function (ODF) method. The texture strength after ECAP processing was different for the three samples in the order, solutionised > solutionised plus aged condition > as-received. The prominent texture components were A (E) /(A) over bar (E) and B(E)/(B) over bar (E) in addition to several weaker components for the three materials. The strong texture evolution in solutionised condition has been attributed to higher strain hardening of the matrix due to higher amount of solute. In case of the as-received as well as solutionised plus aged alloy, the weaker texture could be due to the strain scattering from extensive precipitate fragmentation and dissolution during ECAP.

Solidification Microstructure and Texture in Grain-refined Titanium alloys

In the present study, solidification microstructure and texture evolution in grain-refined Ti-6Al-4V and γ-TiAl alloys via trace boron addition are compared with their baseline counterparts. Boron addition resulted in dramatic grain refinement by almost an order of magnitude. The texture developed in these alloys is also markedly different from the baseline alloys.

Microstructural evolution in liquid metal processed Al-alloy/SiCp composites

Al-Zn-Mg/SiCP composites processed by a liquid metal processing (stir casting) technique have been microstructurally characterised in the as-cast and extruded conditions. Uniform distribution of SiCP is observed with few defects, such as particle clusters, which are due to partial wetting and associated gas porosity. The constituent particles are associated with SiCP although their composition remains unaffected compared with the control alloy. Hot extrusion of the composite using a shear type die showed banding of particles in the extruded direction with 9 vol.% composite. Such defects however, are not predominant in 18% SiCP extruded composites. The presence Of Mg2Si is detected at the particle matrix interface as well as in the matrix.

Temperature deformation behaviour of a Mg-0.8Al alloy

There is considerable interest currently in developing magnesium based alloys as replacements for aluminum alloys in automobile applications, due to their high specific strength as compared to aluminum alloys. However, the poor formability of magnesium alloys has restricted their applications; superplasticity can be utilized to form components with complex shapes. In the present study, the compressive deformation characteristics of a Mg-0.8 wt% Al alloy with an initial grain size of 19 +/- 1.0 mum have been studied in the temperature range of 623-673 K and at strain rates ranging from 10(-7) to 10(-3) s(-1). The stress exponent was observed to decrease with a decrease in stress. The results are analyzed in terms of the existing theoretical models for high temperature deformation. Furthermore, the potential for superplasticity in this alloy is explored, based on the mechanical and microstructural characteristics of the alloy.

Transient analysis in Al-doped barium strontium titanate thin films grown by pulsed laser deposition

Thin films of (Ba0.5Sr0.5)TiO3 (BST) with different concentrations of Al doping were grown using a pulsed laser deposition technique. dc leakage properties were studied as a function of Al doping level and compared to that of undoped BST films. With an initial Al doping level of 0.1 at. % which substitutes Ti in the lattice site, the films showed a decrease in the leakage current, however, for 1 at. % Al doping level the leakage current was found to be relatively higher. Current time measurements at elevated temperatures on 1 at. % Al doped BST films revealed space-charge transient type characteristics. A complete analysis of the transient characteristics was carried out to identify the charge transport process through variation of applied electric field and ambient temperature. The result revealed a very low mobility process comparable to ionic motion, and was found responsible for the observed feature. Calculation from ionic diffusivity and charge transport revealed a conduction process associated with an activation energy of around 1 eV. The low mobility charge carriers were identified as oxygen vacancies in motion under the application of electric field. Thus a comprehensive understanding of the charge transport process in highly acceptor doped BST was developed and it was conclusive that the excess of oxygen vacancies created by intentional Al doping give rise to space-charge transient type characteristics. © 2001 American Institute of Physics.

Texture and grain boundary character distribution during Equal Channel Angular Extrusion of some two-phase copper alloys

In the present work, a thorough investigation of evolution of microstructure and texture has been carried out to elucidate the evolution of texture and grain boundary character distribution (GBCD) during Equal Channel Angular Extrusion (ECAE) of some model two-phase materials, namely Cu-0.3Cr and Cu-40Zn. Texture of Cu-0.3Cr alloy is similar to that reported for pure copper. On the other hand, in Cu-40Zn alloy, texture evolution in α and β (B2) phases are interdependent. In Cu-0.3Cr alloy, there is a considerable decreases in volume fraction of low angle boundaries (LAGBs), only a slight increase in CSL boundaries, but increase in high angle grain boundaries (HAGBs) from 1 pass to 4 passes for both the routes. In the case of Cu-40Zn alloy, there is an appreciable increase in CSL volume fraction.