SrB4O7:Bi2VO5.5 - A novel nanocomposite

Glass composites of strontium tetraborate, SrB4O7 (SBO) with bismuth vanadate, Bi2VO5.5 (BiV) of the composition (1-x) SBO-x BN (0 less than or equal to x less than or equal to 0.75), have been synthesized. X-ray powder diffraction and electron microscopy indicate as-quenched composites to be amorphous and the annealed samples showed the presence of nanometer sized particles of BN dispersed in the glassy matrix of SBO. The dielectric constant of these composites increases with increase in the volume fraction of BiV, at 300 K. The measured dielectric constant of the composite very nearly obeys the Maxwell's relationship. Optical transmission studies confirm a steady shirt in the optical absorption edge towards longer wavelengths with increase in x

Synthesis and properties of rare earth doped lamp phosphors

Red, blue and green emitting lamp phosphors such as EU(3+) doped Y2O3 (red phosphor), EU(2+) doped Ba0.64Al12O18.64, BaMgAl10O17 and BaMg2Al16O27 (blue phosphors) and Ce0.67Tb0.33MgAl11O19 and Eu2+, Mn2+ doped BaMgAl10O17 (green phosphors) have been prepared by the combustion of the corresponding metal nitrates (oxidizer) and oxalyl dihydrazide/urea/carbohydrazide (fuel) mixtures at 400 degrees-500 degrees C within 5 min. The formation of these phosphors has been confirmed by their characteristic powder X-ray diffraction patterns and fluorescence spectra. The phosphors showed characteristic emission bands at 611 nm (red emission), 430-450 nm (blue emission) and 515-540 nm (green emission). The fine-particle nature of the combustion derived phosphors has been investigated using powder density, particle size and BET surface area measurements.

Synthesis and studies on pyridinium chlorofluoro complexes of indium and bismuth

Pyridinium trichlorotrifluoroindate, (C5H5NH)(3)InCl3F3, and pyridinium trichlorofluorobismuthate, C5H5NHBiCl3F, have been synthesised by the reaction of pyridinium poly(hydrogen fluoride), PPHF, with InCI3 and BiCl3, respectively. These new complexes have been characterised by chemical and thermal analysis, NMR (H-1 and F-19) and infrared spectroscopy, and powder X-ray diffraction methods

Milling maps and amorphization during mechanical alloying

The effect of various milling parameters such as, milling intensity, ball:powder weight ratio and number of balls on the glass forming ability of an elemental blend of composition Ti50Ni50 has been studied by mechanical alloying. In order to understand the results, all the milling parameters have been converted into two energy parameters, namely, impact energy of the ball and the total energy of milling. In a milling map of these two parameters, the conditions for amorphous phase formation have been isolated. A similar exercise has been carried out for Ti50Cu50 as a function of milling time at two milling intensities. The results indicate that a minimum impact energy of the ball and a minimum total energy are essential for amorphization by mechanical alloying.

Preparation and dielectric properties of zinc and cadmium doped barium tantalates, Ba3Zn1?xCdxTa2O9

Members of the Ba2Zn1-xCdxTa2O9 (0 less than or equal to x less than or equal to 1) series have been synthesized by solid state reactions at 1473K. Powder x-ray diffraction studies show a cubic perovskite cell with a similar to 4.1 Angstrom which increases with increase in x. Electron diffraction studies show the presence of hexagonal ordered perovskite structure in addition to the cubic structure seen by x-rays, the x = 0.5 composition showing more ordered crystallites. These samples show high dielectric constants with a maximum (epsilon(r) = 30 at 1 kHz) for the x = 0.5 member. The dielectric loss increases with increase in x at all the frequencies under study.

Pyridinidm Hexafluorotitanate and its Derivatives

Pyridinium hexafluorotitanate, (C5H5NH)(2)TiF6, has been prepared by the reaction of titanium metal with pyridinium poly(hydrogen fluoride), PPHF, at room temperature. Making use of (C5H5NH)(2)TiF6 as a precursor, ammonium and alkali metal hexafluorotitanates, M(2)TiF(6) (M = NH4, Na, K, Rb and Cs) have been synthesized by metathesis. These hexafluorotitanates have been characterized by chemical analyses, infrared and NMR (H-1 and F-19) spectroscopy and powder X-ray diffraction methods. Indexed powder X-ray diffraction data for Rb2TiF6 and Cs2TiF6 have been reported.

New open-framework phosphate and phosphite compounds of gallium

Five new open-framework compounds of gallium have been synthesized by hydrothermal methods and their structures determined by single crystal X-ray diffraction studies. The compounds, C8N4H26]Ga6F4(PO4)(6)], I, C5N3H11]Ga3F2(PO4)(3)]center dot H2O, II, C6N3H19]Ga-4(C2O4)(PO4)(4)(H2PO4)]center dot 2H(2)O, III, Ga2F3(HPO4)(PO4)]center dot 2H(3)O, IV, and C3N2H5](2)Ga-4(H2O)(3)(HPO3)(7)], V, possess three-dimensional structures. All the compounds are formed by the connectivity between the Ga polyhedra and phosphite/phosphate units. The observation of SBU-6 (I and II) and spiro-5 (IV) secondary building units (SBUs) are noteworthy. The flexibility of the formation of gallium phosphate frameworks has been established by the isolation of two related structures (I and II) from the same SBU units but different organic amines. Some of the present structures have close resemblance to the gallium phosphate phases known earlier. The compounds have been characterized by CHN analysis, powder XRD, IR, and TGA. (C) 2011 Elsevier B. V. All rights reserved.

Metamorphic-metasomatic fluids and Al, Si order/disorder of K-rich alkali feldspars from southern Indian high grade terrain

The structural state of K-feldspars in the quartzofeldspathic gneisses, charnockites, metapelites and pegmatites from the southern Kamataka, northern Tamil Nadu and southern Kerala high-grade regions of southern India has been characterized using petrographic and powder X-ray diffraction methods. The observed distribution pattern of structural state with a preponderance of disordered K-feldspar polymorphs in granulites compared to the ordered microclines in the amphibolite facies rocks is interpreted to reflect principally the varying H2O contents in the metamorphic-metasomatic fluids across metamorphic grade. The K-feldspars in the pegmatites of granitic derivation and in a pegmatite of inferred metamorphic origin also point to the important role of aqueous fluids in their structural state.

Mo3O5(OH)(2)(AsO4)2: A new solid with a structure related to beta VOPO4

Mo3O5(OH)(2)(AsO4)(2) was prepared at 100 degrees C from an aqueous solution of MoO3 containing arsenic and nitric acids. It crystallises in the monoclinic system, a = 13.024(1)Angstrom, b = 7.2974 (2) Angstrom, c = 13.281(1) Angstrom, beta = 121.124(8)degrees, Z = 4, space group C2/c. The structure was determined by Rietveld refinement from X-ray powder diffraction data. The three-dimensional structure is built up from MoO6 and MoO5OH octahedra and AsO4 tetrahedra sharing corners. The octahedra share two opposite vertices forming zigzag chains that run parallel to [10(1) over bar]. Each AsO4 tetrahedron is connected to four octahedra, two of which belong to the same chain, thus linking three chains. The resulting covalent framework is similar to that of beta VOPO4 in which one tetrahedral P site for every three is empty. The two protons are likely to be bonded to two (out of four) unshared oxygen atoms surrounding this empty site. All the Mo atoms are strongly off-centred in the octahedra; and the off-centring is disordered. The disorder is discussed in terms of Mo shifts perturbed by a disordered hydrogen bonding scheme.

Odd-even oscillations of SHG efficiencies in twin NLO chromophores

Twin NLO chromophores having two azobenzene units linked by a flexible polymethylene spacer of varying lengths are shown to exhibit odd-even oscillations in their second harmonic generation (SHG) efficiencies, when measured in the powder form. These twin systems were designed to also exhibit liquid cystallinity, and indeed most of them do exhibit a nematic mesophase. The anticipated odd-even oscillations, in both their isotropization transition temperatures (Ti) and isotropization entropies (Delta Si), were also observed. The odd-even oscillation of the SHG efficiencies has been ascribed to a more effective cancellation of mesogenic dipoles in the even twins as compared to their odd counterparts, due to a preferred centrosymmetric packing in the former case. Based on the behaviour of these twin chromophoric molecules, it may be anticipated that such odd-even oscillations will also be observed in the analogous main chain NLO polymers.

Phase evolution and densification of spray pyrolysed ZrO2-Al2O3 powders

Devitrification of spray pyrolysed, amorphous ZrO2-Al2O3 solid solution produces nanocrystalline microstructures (grain sizes 10-20 nm). In this study, spray pyrolysed amorphous ZrO2-40 mol% Al2O3 powder displayed good sinterability during decomposition, after spraying, of the nitrate precursors up to 1023K. Hot pressing of fully pyrolysed, pre-sintered (more than 70% dense) pellets at 923K and 750 MPa produced an amorphous pellet with less than 2% porosity. The results indicate the possibility of producing dense, amorphous pellets that can be heat treated further to produce nanocrystalline microstructures conducive for superplasticity.

Preliminary studies on the synthesis and characterisation of hydroxyapatites

Synthesis of calcium hydroxyapatite Ca-10(PO4)(6)(OH)(2) ceramic powders by a solid state reaction between commercially available tricalcium phosphate and calcium hydroxide powders has been attempted in the range 700-1000 degrees C. Reaction of tricalcium phosphate and calcium hydroxide in 3:2 molar ratio at 1000 degrees C leads to the formation of pure calcium hydroxyapatite phase. The sample has been characterised by XRD and IR spectral studies. The compacted powder is sintered to 93% of theoretical density when fired in air at 1300 degrees C for 2 hours.

Structural evolution and electronic properties of La1+xSr2-xMn2O7

A detailed study of the layered manganite La1+xSr2-xMn2O7 has been performed, establishing that within the composition range 0.1 less than or equal to x less than or equal to 0.45 the phases crystallize in the I4/mmm space group. The evolution of structural parameters with x: in this composition range has been followed using a novel application of an existing program for the Rietveld analysis of powder diffraction data. The structure, a familiar intergrowth of rock-salt (La,Sr)O slabs and double perovskite (La,Sr)(2)Mn2O6 units, is characterized by a reluctance to deform the latter. This manifests as a ''pumping'' of the larger Sr-II ion into the 12-coordinate site of the structure as x is increased. We report these features of the structure as well as electrical transport and magnetic properties, in light of recent observations of giant, negative magnetoresistance in these systems.

Synthesis of Ti, Ga, and V nitrides: Microwave-assisted carbothermal reduction and nitridation

A simple, novel, and fast method of preparation of metal nitride powders (GaN, TiN, and VN) using microwave-assisted carbothermal reduction and nitridation has been demonstrated. The procedure uses the respective oxides and amorphous carbon powder as the starting materials. Ammonia gas is found to be more effective in nitridation than high-purity N-2 gas. Complete nitridation is achieved by the use of a slight excess of amorphous carbon. Metals themselves are not found to be effectively nitrided. The products were characterized using XRD, TEM, and SAED and found to possess good crystallinity and phase purity. The method can be of general applicability for the preparation of metal nitrides.

Magnetic properties of mechanically alloyed nanocrystalline Ni3Fe

Disordered nanocrystalline Ni3Fe alloy was prepared by mechanical alloying of elemental powders. X-ray diffractograms show the formation of Ni3Fe single phase. The chemical composition and morphology of the powder have been obtained by using EDAX and SEM analysis respectively. While the saturation magnetisation decreases with milling time, the coercivity increases. The width of the hyperfine field distributions obtained from Mossbauer studies shows that the alloy is highly disordered Atomic ordering is found to take place at a faster rate compared to that in the bulk alloy. (C) 1999 Acta Metallurgica Inc.