Synthesis and photocatalytic properties of AgLi1/3Ru2/3]O-2: A new delafossite oxide

A new delafossite oxide, AgLi1/3Ru2/3]O-2, synthesized by ion-exchanging interlayer-Li+ with Ag+ in layered Li2RuO3, is reported. The transformation of layered Li2RuO3 (monoclinic, space group C2/c) to AgLi1/3Ru2/3]O-2 possessing a delafossite structure (space group R (3) over barm) has been established with powder X-ray diffraction. The successful conversion of LiLi1/3Ru2/3]O-2 to AgLi1/3Ru2/3]O-2 is further confirmed by EDAX analysis. The diffuse reflectance spectrum of AgLi1/3Ru2/3]O-2 shows broad absorption in the UV-visible region suggesting its use as a photocatalyst. The photocatalytic activity of AgLi1/3Ru2/3]O-2 has been investigated by degrading various dyes. It showed significant photocatalytic activity for dye degradation both under UV and solar radiation. (C) 2010 Elsevier B.V. All rights reserved.

Poly-ols Based Sol-Gel Synthesis of Zinc Oxide Thin Films

We demonstrate that the structural and optical properties of a sol-gel deposited zinc oxide thin film can be tuned by varying the composition of the sol, consisting of ethylene glycol and glycerol. A systematic study of the effect of the composition of sol on the mean grain size, thickness, and defect density of the zinc oxide film is presented. About 20% glycerol content in the sol is observed to improve the quality of the film, as evaluated by X-ray diffraction and photoluminescence studies. Thus, optimizing the composition of the sol for about 60 nm thick ZnO film using 20% glycerol resulted in the zinc oxide film that is about 80% transparent in visible spectrum, exhibiting electrical resistivity of about 18 Omega cm and field-effect mobility of 0.78 cm(2)/(V s). (C) 2010 The Electrochemical Society. DOI: 10.1149/1.3515894] All rights reserved.

Self-assembled composite nano-materials exploiting a thermo reversible n-acene fibrillar scaffold and organic-capped ZnO nanoparticles

An organic-inorganic composite material is obtained by self-assembly of 2,3-didecyloxy-anthracene (DDOA), an organogelator of butanol, and organic-capped ZnO nanoparticles (NPs). The ligand 3, 2,3-di(6-oxy-n-hexanoic acid)-anthracene, designed to cap ZnO and interact with the DDOA nanofibers by structural similarity, improves the dispersion of the NPs into the organogel. The composite material displays mechanical properties similar to those of the pristine DDOA organogel, but gelates at a lower critical concentration and emits significantly less, even in the presence of very small amounts of ZnO NPs. The ligand 3 could also act as a relay to promote the photo-induced quenching process.

Electrochemical preparation of few layer-graphene nanosheets via reduction of oriented exfoliated graphene oxide thin films in acetamide-urea-ammonium nitrate melt under ambient conditions

Electrochemical reduction of exfoliated graphene oxide, prepared from pre-exfoliated graphite, in acetamide-urea-ammonium nitrate ternary eutectic melt results in few layer-graphene thin films. Negatively charged exfoliated graphene oxide is attached to positively charged cystamine monolyer self-assembled on a gold surface. Electrochemical reduction of the oriented graphene oxide film is carried out in a room temperature, ternary molten electrolyte. The reduced film is characterized by atomic force microscopy (AFM), conductive AFM, Fourier-transform infrared spectroscopy and Raman spectroscopy. Ternary eutectic melt is found to be a suitable medium for the regulated reduction of graphene oxide to reduced graphene oxide-based sheets on conducting surfaces. (C) 2010 Elsevier B.V. All rights reserved.

Preparation and Characterization of MWCNT/ZnO nanoparticles Hybrid

ZnO nanoparticles (ZnO NPs) were grown on the surface of multiwall carbon nanotubes (MWCNTs) by a wet chemical synthesis route. The anchoring of ZnO NPs on acid-treated MWCNTs was achieved under remarkably mild reaction conditions (low temperature, atmospheric pressure, without any capping agents and no need for subsequent thermal annealing). MWCNT/ZnO NPs hybrid samples with varying loading of ZnO NPs are prepared. A very high degree of dispersion of ZnO NPs over the surface of MWCNT was achieved by suitably controlling the ratio of ZnO NPs and MWCNTs in the solution. The hybrid sample was characterized by electron microscopy, X-ray diffraction and X-ray photoelectron spectroscopy (XPS). Transmission electron microscope images of the as-prepared MWCNT/ZnO NPs hybrid reveal that mono-dispersed ZnO NPs are anchored stably on functionalized MWCNTs. The interaction of ZnO NPs with MWCNT surface was interpreted through XPS analysis.